Stimuli-Sensitive Poly(NIPA-co-APA) Hydrogels for the Controlled Release of Keterolac Tromethamine
Stimuli-Sensitive Poly(NIPA-co-APA) Hydrogels for the Controlled Release of Keterolac Tromethamine
Journal of the Korean Chemical Society. 2014. Feb, 58(1): 92-99
Copyright © 2014, Korea Chemical Society
  • Received : November 25, 2013
  • Accepted : January 03, 2014
  • Published : February 20, 2014
Download
PDF
e-PUB
PubReader
PPT
Export by style
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Yonghyun Kim
V. Ramesh Babu
K.S.V. Krishna Rao
Department of Chemistry, Yogi Vemana University, Kadapa-516003, India
Jae-Min Lim
T. Daniel Thangadurai
Department of Nanotechnology, College of Engineering, Sri Ramakrishna Institutions, Coimbatore 641022, India
Yong-Ill Lee

Abstract
The pH sensitive hydrogels composed of N-isopropylacrylamide (NIPA) and acryloyl phenylalanine (APA) were prepared by redox polymerization using N , N' -methylenebisacrylamide (MBA) as a crosslinker. Anti-inflammatory and analgesic agent, Keterolac Tromethamine (KT), was loaded successfully into poly(NIPA-co-APA) copolymeric hydrogels by swelling equilibrium method. To understand the nature of drug in the polymeric matrix, the newly synthesized drug loaded poly(NIPA-co-APA) copolymeric hydrogels were characterized by using differential scanning calorimetry (DSC) and X-ray diffraction (XRD) techniques. The scanning electron microscopy (SEM) technique result indicates the spherical smooth surface of the hydrogels. The drug (KT) releasing nature of the poly(NIPA-co-APA) hydrogels was studied in pH 1.2 and 7.4. Effects of drug loading, crosslinking agent, pH and the ionic strength of the external medium on swelling of hydrogels were also investigated.
Keywords
INTRODUCTION
In recent years, the incorporation of amino acids into synthetic polymers has been acknowledged a considerable interest because it can lead to new biomaterials with a wide range of properties that can be easily modulated by varying the components in the building block of the macromolecular backbone during synthesis. 1 5 Examples of amino acid-derived organic polymers based on polyacrylates, polyisobutylenes, polyurethanes, polyacetylenes, and hydrogels have been developed for diverse applications including controlled drug delivery systems, antibacterical activity, affinity based separators, and optobioelectronic devices. 6 12
Hydrogels have been an extensive research topic during last several decades due to their high water content and the possible control over the swelling kinetics make them very attractive for biomedical applications. Owing to their widely variable and adjustable properties, hydrogels based on synthetic polymers have principally been studied as the vehicles for the controlled release of both low-molecular mass drugs and macromolecular drugs including therapeutic proteins, enzymes, and DNA. 13 The gel properties like porosity, swelling behavior, stability, biodegradability, gel strength, and biocompatibility may be tailored for a particular application. A special class of hydrogels, which are called “intelligent” or “stimuli-responsive” hydrogels, exhibits significant volume change in response to small changes in external stimuli, such as pH, temperature, light, etc. The most interesting pH- and temperature-sensitive “intelligent” hydrogels have extensively been used in the development of drug delivery systems for pharmaceutical applications.
Poly( N' -isopropylacrylamide) (PNIPA) hydrogel which is an intelligent hydrogel with a lower critical solution temperature (LCST) 14 18 can be used for drug delivery systems, bioseparation, and other biotechnology applications. 19 20 The volume phase transition of PNIPA matrix at 32 ℃ is narrow and not practical at physiological temperature (37 ℃). It is easy to tune the release of drug by temperature- and pH-sensitive systems due to the wide range of physiological pH mean values (2.20 in stomach to 6.80 in intestine). 21 The thermosensitivity of hydrogel could be controlled with pH by incorporating the small amount of ionizable groups (such as carboxyl) into PNIPA chains. 22
Ketorolac tromethamine (KT, 1 ) is a non-steroidal anti-inflammatory drug with 4−6 h of biological halflife period. The recommended total daily dose of KT tablets (maximum 40 mg) is significantly lower than KT injection (maximum 120 mg). Dosage should be adjusted for patients 65 years or older, for patients under 50 kg (110 lbs) of body weight and for patients with moderately elevated serum creatinine. Furthermore, doses of KT injection are not to exceed 60 mg (total dose per day) in these patients. Therefore, it is necessary to enhance sustain action of drug for longer periods. If KT administrates directly as a conventional formulation, it causes gastro intestinal complications including irritation, ulcer, bleeding, and perforation. 23 24 Therefore, it is essential to develop a pH sensitive controlled drug delivery system to prevent the above problems. The present communication reports the development of amino acid based pH-sensitive hydrogels for the controlled release of drug KT. Swelling studies as well as drug release studies have been performed at pH 1.2 and 7.4 to meet gastro intestinal conditions.
PPT Slide
Lager Image
Chemical structure of Ketorolac Tromethamine (KT).
EXPERIMENTAL
- Materials
Ketorolac tromethamine (KT), N -isopropylacrylamide (NIPA), N,N' -methylenebisacrylamide (MBA), ammonium persulfate (APS) were purchased from Aldrich. N,N,N',N' - tetramethylethylenediamine (TEMED) was purchased from Alfa Aesar A Johnson Matthey Company. N -acryloyl-Lphenylalanine (APA) was synthesized by the procedure given in prior art. 25
- Preparation of Dissolution Media
The buffer solution at pH 1.2 was prepared by taking 50 mL of 0.2 M KCl and 7.8 mL of 0.2 N HCl in volumetric flask and diluted to 200 mL with distilled water. The pH 7.4 solution was prepared by taking 50 mL of 0.2 M KH 2 PO 4 and 39.1 mL of 0.2 N NaOH in volumetric flask and diluted to 200 mL with distilled water. 26
- Synthesis of Poly(N-isopropyl acrylamide-co-acryloyl phenyl alanine), Poly(NIPA-co-APA), Hydrogels
Poly(NIPA-co-APA) hydrogels were prepared by redox polymerization. NIPA (800 mg), APA (200 mg), and MBA (10 mg) were dissolved in 4 mL of distilled water at room temperature (APA dissolved in equimolar ratio of NaOH). To this homogeneous monomer solution, initiator APS (10 mg) and accelerator TEMED (50 μL) were added sequentially under continuous stirring. The free-radical crosslinking polymerization was continued for 24 h at 5 ℃ in order to complete the network formation. The reaction mechanism for the synthesis of hydrogels has been illustrated in 2 . The synthesized copolymeric hydrogels were taken out and immersed in distilled water for 3 days at room temperature by changing the water every 12 h in order to remove residual unreacted monomers. The resulting “swollen” hydrogels were dried in air for 2 days and then in a vacuum oven at 37 ℃ until attaining a constant weight. The copolymeric hydrogels were prepared by varying the ratios of monomers, the amount of crosslinking agent, and the different amount of drug. The pure PNIPA hydrogel without APA was also fabricated under the same condition. All formulations used in this work were given in 1 .
PPT Slide
Lager Image
Synthetic scheme of poly(NIPA-co-APA) hydrogel.
Formulation of hydrogels with KT and their encapsulation efficiencies
PPT Slide
Lager Image
Formulation of hydrogels with KT and their encapsulation efficiencies
- Swelling Studies
Dynamic swelling of the copolymeric hydrogels prepared with three different crosslink densities as well as three different drug loadings was studied at pH 1.2 and 7.4 by mass measurements at 37 ℃. To perform the swelling experiments, hydrogels were soaked in water and then removed from the swelling bottles at different time intervals. The hydrogels were wiped carefully with tissue paper (without pressing hard) to remove the surface-adhered water. Swelling experiments were repeated thrice for each sample and the average values were used in data analysis. The standard deviations (SD) in all cases were < 5%. The percentage of swelling ratio (% SR) was calculated by the following equation (1).
PPT Slide
Lager Image
where, Ws is the weight of the swollen gel at time t and Wd is the dry weight of the gel.
- Release Dynamics of the Model Drug
Standard curve of Ketorolac Tromethamine
In this procedure, the absorbance of a number of standard solutions with the reference substance encompassing the sample concentrations were measured by using the UV-vis Spectrophotometer (Agilent 8453 UV spectrophotometer) at λ max 324 nm. The calibration graph was constructed and the concentration of the drug in sample solution was determined from the absorbance of solution. Two calibration graphs were made in pH 1.2 and 7.4 dissolution media, to determine the amount of drug release from the drug-loaded hydrogels.
Loading of the drug in copolymeric networks
The loading of the drug onto poly(NIPA-co-APA) hydrogels was carried out by the swelling equilibrium method. The poly(NIPA-co-APA) hydrogels were allowed to swell in the drug solution of known concentration for 24 h at 37 ℃ and then dried to obtain the release device. 27
Estimation of drug loading and encapsulation
The loading efficiency of KT in the copolymeric hydrogel was examined spectrophotometrically. About 10 mg of the drug-loaded hydrogels were placed in 10 mL of buffer solution and stirred vigorously for 48 h to extract drug from the hydrogels. The solution was filtered and assayed by using the UV spectrophotometer at 324 nm. The percentage (%) drug loading and encapsulation efficiency were calculated by Eqs. (2) and (3), respectively, and the data were compiled in 1 .
PPT Slide
Lager Image
PPT Slide
Lager Image
In vitro release studies
The KT release from the poly(NIPA-co-APA) copolymeric hydrogels was investigated in dissolution media at pH 1.2 and 7.4 with different percentage of KT loading and different extent of crosslinking. In vitro release experiments were performed by using the digital tablet dissolution test apparatus (Model: VDA-8D, Mumbai, India) at a stirring speed of 100 rpm. The weighed quantities of the samples equivalent to 10 mg of the drug were placed in the basket, which was then immersed in 900 mL dissolution medium maintained at 37 ℃. A 5 mL of sample aliquot was withdrawn at different time intervals and filtered through a 0.25 μm filter. The dissolution media were then replaced with 5 mL of fresh dissolution media. The KT concentration was determined spectrophotometrically at 324 nm. These measurements were carried out in triplicate for each sample, but average values were considered in data analysis and graphical presentations.
- Characterization
Differential scanning calorimetric analysis
Differential scanning calorimetry (DSC) was performed on placebo poly(NIPA-co-APA) hydrogel, drug-loaded poly(NIPA-co-APA) hydrogel, and pristine KT. The thermal properties of poly(NIPA-co-APA) copolymeric hydrogels were evaluated by using TA 5000/SDT 2960 DSC Q10 thermal system (Zurich, Switzerland). About 1−4 mg of sample was heated from 25 to 250 ℃ at the heating rate of 10 ℃/min under nitrogen atmosphere with keeping the flow rate at 20 mL/min.
X-ray diffractometry (XRD)
The crystallinity of KT after encapsulation was evaluated for placebo poly(NIPA-co-APA) hydrogel, drug-loaded poly (NIPA-co-APA) hydrogel, and pristine KT by using the X-ray diffractometer (X’pert MPD 3040). The uniform size of dried poly(NIPA-co-APA) hydrogel was mounted on a sample holder and XRD patterns were recorded in the angle range of 5−45° at the speed of 5°/min.
Scanning Electron Microscopy (SEM)
SEM images of the poly(NIPA-co-APA) hydrogels were recorded using a MIRA LMH, H.S. scanning electron microscope (SEM), equipped with Phoenix energy dispersive analysis of X-rays (EDAX) at the required magnification. The micrographs were obtained at 15 kV as operating voltage.
RESULTS AND DISCUSSION
- Differential Scanning Calorimetric Study
The DSC thermograms of (a) placebo poly(NIPA-co-APA) hydrogels, (b) drug-loaded poly(NIPA-co-APA) hydrogels, and (c) pristine KT are presented in . 1 . The crystallinity of drug and the melting temperature ( Tm ) of polymer were determined. The placebo poly(NIPA-co-APA) hydrogels have shown an endothermic peak at 96 ℃, indicating the melting temperature, whereas the drug-loaded poly(NIPA-co-APA) hydrogels showed an endothermic peak at 85 ℃. However, a strong exothermic decomposition peak was observed around 172 ℃ for KT, which designates the melting and the decomposition of the drug. It should be noted that this exothermic peak did not appeared in all the drug-loaded hydrogels comfirming an amorphous dispersion of the drug into the polymer matrix.
PPT Slide
Lager Image
DSC thermograms of (a) placebo poly(NIPA-co-APA) hydrogels, (b) drug-loaded poly(NIPA-co-APA)hydrogels, and (c) pristine KT.
- X-ray Diffraction Studies
To investigate the crystallinity of the drug in the crosslinked poly(NIPA-co-APA) hydrogels, x-ray diffraction patterns of Placebo poly(NIPA-co-APA) hydrogels, drug-loaded poly(NIPA-co-APA) hydrogels and pristine KT were recorded ( . 2a−c ). Characteristic intense peaks were observed between 8, 14, 18, and 20° due to crystalline nature of KT ( . 2c ). However, these peaks were disappeared when KT was loaded in poly(NIPA-co-APA) hydrogels and only placebo polymer matrix peaks were observed ( . 2a , b ). This result revealed that the KT dispersed well at the molecular level in the polymer matrix and crystallinity was not found in the drug-loaded matrices. Moreover, it is very difficult to measure the detection limit due to the amorphous nature of the loaded drug.
PPT Slide
Lager Image
X-ray diffraction patterns of (a) placebo poly(NIPAco- APA) hydrogels, (b) drug-loaded poly(NIPA-co-APA) hydrogels, and (c) pristine KT.
- Scanning Electron Microscopy Studies
The SEM micrographs of poly(NIPA-co-APA) hydrogels indicate smooth surface with partial holes which helps the drug release as well as swelling capacity of the hydrogels ( . 3 ).
PPT Slide
Lager Image
Scanning Electron Microscope image of a pure poly (NIPA-co-APA) hydrogel.
- Swelling Studies
Hydrogels are composed of hydrophilic homopolymer or copolymer networks, which can swell in the presence of water or physiological fluids. Swelling parameters are the most important factors for hydrogel characterization because of fundamental relationship exists between the swelling of a polymer and the nature of the swelling medium. 28 29 Chemical crosslinks (covalent bonds) or physical junctions (e.g., secondary forces, crystallite formation, chain entanglements) provide the hydrogels unique swelling behavior and three-dimensional structure. 30 32 In order to evaluate the optimum reaction parameters for the synthesis of hydrogels, we took the swelling of the hydrogels and the structural integrity maintained by the hydrogels after swelling for 24 h as the criteria. The swelling of the poly(NIPA-co-APA) hydrogels was studied as a function of APA content, in pH value of 1.2 and 7.4, amount of KT and amount of MBA in the polymer matrix.
Effect of N-acryloyl-L-phenylalanine (APA) contents
The effect of monomer concentration on the swelling of crosslinked polymers was investigated as a function of APA contents and the results are presented in . 4(a) . The extent of APA is related largely to the swelling equilibrium. It was observed that the % swelling ratios of the hydrogels were increased from 44 to 1652 with increasing the amount of APA from 0 to 300 mg. This is attributed to increase the hydrophilicity of matrix due to the presence of carboxylic as well as amide groups in APA.
PPT Slide
Lager Image
Effect of (a) N-acryloyl-L-phenylalanine (APA), (b) drug loading, (c) crosslinking agent in distilled water, and (d) pH in different buffer medium, on swelling kinetics of poly(NIPA-co-APA) hydrogels at 37 ℃.
Effect of drug loading
The hydrogels were prepared with different KT contents from 0 to 150 mg in order to study the entrapment of KT on the polymer network. The swelling was taken in pH 7.4 dissolution media at 37 ℃. As can be seen in . 4(b) , the swelling was increased with increasing KT contents in the composition of hydrogel matrix. Such an increase in swelling of the matrix is mainly due to the incorporation of the acidic nature of KT and formation of matrix between hydrophilic APA and NIPA chains.
Effect of crosslinking agent
The effect of crosslinking agent (MBA) on the swelling of the hydrogel at 37 ℃ was investigated by preparing polymers with different concentration of crosslinking agent ( . 4(c) ). The extent of crosslinking is dependent upon the amount of crosslinking agent (MBA) used and the swelling equilibrium. For instance, % swelling ratio decreased from 1415 to 897 with increasing the amount of MBA from 10 to 30 mg. The denser crosslinking produced by increasing the crosslinker concentration leading to decreased void size in the polymer matrix and thereafter decreases the swelling in the polymer.
Effect of pH
To investigate the effect of pH and ionic strength of the external medium on the swelling of poly(NIPA-co-APA) hydrogels, the swelling experiments were carried out in pH 1.2 and 7.4 ( . 4(d) ). The % swelling ratio values were found to be much higher at pH 7.4 than at1.2 due to the swelling ratio of the hydrogel was limited at pH 1.2 owing to the formation of intermolecular hydrogen bonds. At pH 7.4, the carboxylic acid groups on the hydrogel become ionized (−COO−) progressively. In this case, a large swelling force created by the electrostatic repulsion between the ionized acid groups make the hydrogel to be swelled more significantly. The electrostatic attraction between opposite charged molecules is an adjustable driving force for structured material construction.
- Encapsulation Efficiency (EE %)
In order to explore the percentage of encapsulation efficiency (EE %), three different concentrations of KT (1, 2, and 3 wt%) were loaded in the hydrogels. The results reveal that the percentage of encapsulation efficiency increases by increasing the drug concentration ( 1 ). It should be noticed that EE % was enhanced with increasing the amount of APA in the copolymeric hydrogels. The copolymeric hydrogels containing 0, 0.1, 0.2, and 0.3 g of APA, and 1 wt% of KT with 1 wt% of MBA, the EE % were 46.5, 50.5 55.2 and 62.3%, respectively. For hydrogels crosslinked with 1, 2, and 3 wt% of MBA, the EE % are 55.2, 46.7, and 41.1%, respectively. Such a decreasing trend in encapsulation efficiency is resulted from reducing the free volume spaces within the polymer matrix associated with an increase in crosslinking density and the ridgidty of the copolymeric hydrogels.
- In vitro cumulative drug release studies
Drug release kinetics was analyzed by plotting the cumulative release values, (M t /M ) versus time, where, M t /M is a fraction of drug released at time ‘t’.
The poly(NIPA-co-APA) copolymeric hydrogels were used to study the release behavior of KT in pH 1.2 and 7.4.
Effect of N-acryloyl-L-phenylalanine (APA) content
Effect of APA content in the hydrogel polymers was studied at constant loading of 1 wt% KT. The hydrogels prepared with different amounts of APA showed release trends up to >80% of cumulative release within ~10 h ( . 5(a) ). A systematic increase in the % cumulative release was observed with increasing the composition of APA. The three-dimensional networks in the hydrogel polymers swelled systematically more with increasing amount of APA, probably due to the ionization of crosslinked chains. Therefore, the relaxation responses of the polymer chains made an increase of dimension of the polymer coil, and further a significant increase in molecular volume of the overall hydrated polymer matrix. Noteworthy, the nature of release profiles remains almost identical for all the matrices containing different amount of APA indicating that swelling of APA has a linear relationship with their release profiles.
PPT Slide
Lager Image
Percentage of cumulative drug release of poly(NIPA-co-APA) hydrogels containing (a) different amount of APA, (b) different amount of KT, and (c) different amount of crosslinking agent in pH 7.4 and (d) in pH 1.2 at 37 ℃.
Effect of drug loading
. 5(b) displays the drug release profiles of drug-loaded hydrogels with different amounts of drug loadings (50, 100, and 150 mg). The effect of drug loading on the release rates was investigated for three formulations, NAD 2, 6, and 7 ( 1 ).
It was observed that the drug release rates were slower for the formulations containing lower amount of the drug and vice versa
The drug in the hydrogels might act as inert filler by occupying the free volume of the swollen hydrogel. This could have created a twisted path for water molecules to permeate, however, the degree of twisting depends upon the volume fraction of the filler. 27
Effect of crosslinking agent
Typical plots between % cumulative release data versus time are illustrated in . 5(c) by varying the amounts of MBA (i.e., 1, 2, and 3 wt%) at constant drug loading. The % cumulative release was relatively large at the lower amount of MBA (1 wt%), compared with those at higher amount of MBA (3 wt%), probably due to the polymeric chains become rigid at higher concentration of MBA owing to the contraction of microvoids.
Effect of pH
The cumulative drug release experiments of poly(NIPA-co- APA) hydrogels were performed in pH 1.2 and 7.4 dissolution media at 37 ℃. . 5 indicates a considerable increase in the cumulative drug release for all the hydrogels when pH was increased from 1.2 to 7.4. It can be seen that the poly(NIPA-co-APA) hydrogels have shown extensive drug release rates than the pure NIPA hydrogels. However, it should be remarked that there is a drastic difference in the drug release rates of the formulated blend hydrogels in pH 1.2 and 7.4, implying the drug release of the poly(NIPAco- APA) hydrogels depends upon the nature of the polymer matrix as well as pH of the media. For instance, in 24 h, only 70% of drug was released in pH 1.2 ( . 5(d) ) and 90% was released in pH 7.4. In the case of the hydrolyzed blend polymer, it is likely that there is a complexation of carboxylic acid groups of APA, but there could be a deformation of the complex (NH-COO-) formed in pH 1.2.
CONCLUSION
Copolymeric hydrogels, poly(NIPA-co-APA), based on NIPA and APA were prepared by redox polymerization method and characterized by differential scanning calo-rimetry, X-ray diffractometry, and scanning electron microscopy. All hydrogels swelled slowly in pH 1.2 and 7.4 at 37 ℃ and reached the equilibria within 24 h. The percentage of swelling ratio of the hydrogels was increased from 44 to 1652 with increasing the amount of APA (from 0 to 300 mg) and the KT contents. Effect of pH on swelling kinetic studies revealed that percentage of swelling ratio decreases by decreasing the pH due to the formation of intermolecular hydrogen bonds. The drug KT was dispersed at the molecular level in the polymer matrix and no crystals were found in the drug-loaded matrices. The amounts of matrix crosslinking agent, drug-loading, and APA content of the matrix influenced the release of KT. The drug release profile was varied (up to 10 h) depending upon the nature of the matrix in gastro intestinal tract (GIT) disease conditions.
Acknowledgements
This work was supported by the research project of Changwon National University (2012-2014).
References
Raman K. , Ramamoorthy R. , Reddy B. S. R. 2005 React. Funct. Polym. 62 215 -    DOI : 10.1016/j.reactfunctpolym.2004.06.013
Vaidya A. A. , Lele B. S. , Kulkarni M. G. , Mashelkar R. A. 1999 Biotechnol. Bioeng. 64 418 -    DOI : 10.1002/(SICI)1097-0290(19990820)64:4<418::AID-BIT4>3.0.CO;2-Y
Deshmukh M. V. , Vaidya A. A. , Kulkarni M. G. , Rajamohanan P. R. , Ganapathy S. 2000 Polymer 41 7951 -    DOI : 10.1016/S0032-3861(00)00174-9
Puskas J. E. , Chen Y. , Dahman Y. , Padavan D. 2004 J. Polym. Sci. Part A: Polym. Chem. 42 3091 -    DOI : 10.1002/pola.20114
Vyavahare N. , Kohn J. 1994 J. Polym. Sci. Part A: Polym. Chem. 32 1271 -
Nathan A. , Zalipsky S. , Kohn J. 1994 J. Bioact. Compat. Polym. 9 239 -
Lin H. B. , Sun W. , Mosher D. F. , Garcia-Echeverria C. , Schaufelberger K. , Lelkes P. I. , Cooper S. L. 1994 J. Biomed. Mater. Res. 28 329 -    DOI : 10.1002/jbm.820280307
Salhi F. , Lam J. W. Y. , Cheuk K. K. L. , Cha J. A. K. , Tan B. Z. 2000 Polymer Preprint 41 1185 -
Song H. , Chu C. C. 2012 J. Appl. Poly. Sci. 124 3840 -    DOI : 10.1002/app.35512
Sato M. , Mutsumi Inata M. , Yamaguchi I. 2012 J. Appl. Poly. Sci. 126 E298 -    DOI : 10.1002/app.36956
Angiolini L. , Caretti D. , Giorgini L. , Salatelli E. , Altomare A. , Carlini C. , Solaro R. 1998 Polymer 39 6621 -    DOI : 10.1016/S0032-3861(98)00161-X
Ramesh Babu V. , Kim C. , Kim S. , Ahn, C. Lee Y. I. 2010 Carbohyd. Polym. 81 196 -    DOI : 10.1016/j.carbpol.2010.02.050
Erbil C. , Aras S. , Uyanik N. 1999 J. Polym. Sci. Part A: Polym. Chem. 37 1847 -    DOI : 10.1002/(SICI)1099-0518(19990615)37:12<1847::AID-POLA14>3.0.CO;2-G
Vesterinen E. , Dobrodumov A. , Tenhu H. 1997 Macromolecules 30 1311 -    DOI : 10.1021/ma960685g
Chen G. , Hoffman A. S. 1995 Nature 373 49 -    DOI : 10.1038/373049a0
Serizawa T. , Uemura M. , Kaneko T. , Akashi M. 2002 J. Polym. Sci. Part A: Polym. Chem. 40 3542 -    DOI : 10.1002/pola.10415
Wang M. , Fang Y. , Hu D. 2001 React. Funct. Polym. 48 215 -    DOI : 10.1016/S1381-5148(01)00057-8
Yan L. , Zhu Q. , Kenkare P. U. 2000 J. Appl. Poly. Sci. 78 1971 -    DOI : 10.1002/1097-4628(20001209)78:11<1971::AID-APP170>3.0.CO;2-P
Krishna Rao K. S. V. , Vijaya Kumar N. B. , Subha M. C. S. , Sairam M. , Aminabhavi T. M. 2006 Carbohyd. Polym. 66 333 -    DOI : 10.1016/j.carbpol.2006.03.025
Cui Z. F. , Guan Y. X. , Chen J. L. , Yao S. J. 2005 J. Appl. Poly. Sci. 96 1734 -    DOI : 10.1002/app.21640
Grøttum J. A. , Erikson U. , Grasdalen H. , Staurnes M. 1998 Comparative Biochemistry and Physiology Part A: Molecular & Integrative Physiology 120 469 -    DOI : 10.1016/S1095-6433(98)10047-8
Shin B. C. , Jhon M. S. , Lee H. B. , Yuk S. H. 1998 Eur. Polym. J. 34 171 -    DOI : 10.1016/S0014-3057(97)00104-3
Soppimath K. S. , Aminabhavi T. M. , Kulkarni A. R. , Rudzinski W. E. 2001 J. Controlled Release 70 1 -    DOI : 10.1016/S0168-3659(00)00339-4
Casolaro M. , Paccagnini E. , Mendichi R. , Ito Y. 2005 Macromolecules 38 2460 -    DOI : 10.1021/ma047652i
Baljit S. 2007 Int. J. Pharm. 334 1 -    DOI : 10.1016/j.ijpharm.2007.01.028
Peppas N. A. 1980 Bioavailability and the Pharmacokinetic Control of Drug Response Wiley New York
1985 Pharmacopoeia of India Controller of publications Delhi, India
Dogu Y. , Okay O. 2006 J. Appl. Poly. Sci. 99 37 -    DOI : 10.1002/app.22140
Gundogan N. , Melekaslan D. , Okay O. 2012 J. Appl. Poly. Sci. 94 135 -
Peppas N. A. , Mikos A. G. 1986 Preparation Methods and Structure of Hydrogels. In Hydrogels in Medicine and Pharmacy; Peppas, N. A., Ed CRC Press Boca Raton, Florida
Allan S. H. 2002 Adv. Drug Delivery Rev. 54 3 -    DOI : 10.1016/S0169-409X(01)00239-3
Peppas N. A. , Bures P. , Leobandung W. , Ichikawa H. 2000 Eur. J. Pharm. Biopharm. 50 27 -    DOI : 10.1016/S0939-6411(00)00090-4