Advanced
Water-Soluble Distyrylbenzene Fluorophore and Fluorescence Behavior in a Polymeric Vesicle
Water-Soluble Distyrylbenzene Fluorophore and Fluorescence Behavior in a Polymeric Vesicle
Journal of the Korean Chemical Society. 2007. Dec, 51(6): 513-519
Copyright © 2007, The Korean Chemical Society
  • Received : November 16, 2007
  • Published : December 20, 2007
Download
PDF
e-PUB
PubReader
PPT
Export by style
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Rati Ranjan Nayak
한영 우

Abstract
A vesicle forming polymer, poly(sodium acrylamidoundecanoate) ( PSAU ) and a water-soluble distyrylbenzene-based fluorophore, TPADSB-C were synthesized and characterized by using UV-vis and photoluminescence (PL) spectroscopy. An inter-chain vesicle formation of PSAU was observed at ~0.01 g/L from N-phenyl naphthylamine fluorescence measurement with changing PSAU concentration in water. Above critical aggregation concentration of PSAU , optical properties of TPADSB-C were investigated to study the microenvironment modulation through dye incorporation in the polymeric vesicle. The emission of TPADSB-C in the presence of PSAU vesicles was blue-shifted and the PL quantum efficiency was increased to 90% due to the microenvironment (e.g. polarity) change in aqueous solution. This study shows that the polymeric vesicle containing molecular fluorophores has a great potential as an efficient, stable and biocompatible labeling tag in biological cell imaging.
Keywords
INTRODUCTION
Among the various microstructures formed by the amphiphilic molecules, a vesicle is an especially interesting structure as it has two distinct domains, the lipophilic membrane and the interior aqueous cavity. It can entrap large quantities of chemicals (or molecules) either in the lipophilic membrane or in the aqueous cavity. Therefore, vesicles formed by synthetic surfactants have attracted tremendous attention because of their potential uses as agents for encapsulation and eventual release of drugs, flavors, and fragrances, and also as microreactors for the synthesis of monodispersed nanosized semiconductor particles. 1 - 6 The microstructures formed by the amphiphiles are in dynamic equilibrium with the surfactant monomers in solution. One way to obtain structural stabilization of the molecular self-assemblies is chemically tethering the surfactant monomers through polymerization. Polymerization prevents the surfactant reorganization necessary for the formation of reversed micelles and flip-flop. The vesicles formed by polysoaps are reported to be more stable and less permeable than respective monomeric ones. 7 Therefore, polymerized vesicles are expected to act as an excellent micro-container for chemicals such as cosmetic substances and pharmaceutical drugs. The polymerized vesicles are well known structures as a biomimetic system which is capable of carrying out celllike functions. 8
In this contribution, we report the synthesis and optical characterizations of a vesicle-forming amphiphilic polymer, poly(sodium acrylamidoundecanoate) ( PSAU ) and a water-soluble distyrylbenzene-based fluorophore, TPADSB-C ( . 1 ). Inter-chain vesicle formation of PSAU , the chromophore inclusion in the vesicle and its optical properties with/without the vesicles were studied by using UV-vis and photoluminescence (PL) spectroscopy. The microenvironment modulation around the fluorophores using the vesicles is discussed in terms of utilizing them as optical tags in biological cell imaging.
PPT Slide
Lager Image
Chemical structures of PSAU and TPADSB-C.
EXPERIMENTAL
All chemicals except acryloyl chloride (TCI) were purchased from Aldrich Chemical Co. and used without further purification. All solvents used were of reagent - grade and whenever necessary purified, dried, and distilled before use. 1 H NMR spectra were recorded on a JEOL (JNM-AL300) FT NMR system. UV-visible spectra were measured with a Jasco (model V-630) spectrophotometer. The steady-state fluorescence spectra were measured on a Jasco FP-6500 spectrofluorometer. A saturated solution of the probe, N-phenyl naphthylamine (NPN) was prepared by adding an excess compound to deionized water with stirring at 40 ℃ for 24 h. After equilibration at room temperature, the remaining undissolved molecules were removed by filtration through Millipore syringe filter (0.22 mm). A polymer stock solution (2 g/L) was prepared in the above probe solution. Appropriate volume of the saturated probe solution was used to make various dilutions of the polymer stock solution. All fluorescence spectra were measured at equilibration (after 24 hrs) after sample preparation.
Synthesis of PSAU. PSAU was obtained by free radical polymerization of sodium acrylamidoundecanoate (SAU) in water using K 2 S 2 O 8 as a radical initiator at 60 ℃ under a N 2 atmosphere according to the procedures reported elsewhere. 9 The polymer solution was dialyzed for 72 h using 12 kDa molecular weight cut off dialysis bag against alkaline water (pH=10) and lyophilized to get dry PSAU . 1 H-NMR for SAU (300 MHz, CDCl 3 ): δ 6.29 (d, 1H), 6.06 (dd, 1H), 5.59 (d, 1H), 3.27 (qt, 2H), 2.3 (t, 2H), 1.5 (br, 4H), 1.21 (br, 12H). The polymerization was confirmed by the disappearance of the vinyl proton peaks at δ=5~7 ppm in the 1 H NMR spectrum of PSAU in D 2 O.
N,N-Bis[4’-(6’’-bromohexyl)phenyl]-4-aminobenzaldehyde (1). A 100 mL round-bottom flask containing 30 mL of dry DMF was cooled down to 0 ℃. Phosphorous oxybromide (1.2 g, 4.2 mmol) was added maintaining the temperature below 5 ℃. The reaction mixture was stirred for 30 min. A white solid was observed to be precipitated. Bis[4-(6’-bromohexyl)phenyl]phenylamine (0.8 g, 1.4 mmol) in 10 mL of dry DMF was added to the above solution and the temperature was slowly increased to 90 ℃. After the solution was heated overnight, it was cooled down to room temperature and poured into cold water. The pH of the solution was adjusted to around 7 with aqueous NaOH solution. The product was extracted with dichloromethane, dried over magnesium sulfate, and purified by silica gel column chromatography (ethyl acetate/hexane (v/v) = 1/10). The product yield was 0.67 g (80%). 1 H-NMR (300 MHz, CDCl 3 ): δ 9.79 (s, 1H, - CHO ), 7.66 (d, 2H, J = 8.8 Hz), 7.15 (d, 4H, J = 8.4 Hz), 7.09 (d, 4H, J = 8.4 Hz), 6.96 (d, 2H, J = 8.8 Hz), 3.42 (t, 4H, - CH2 Br, J = 6.8 Hz), 2.61 (t, 4H, Ar CH2 -, J = 7.8 Hz), 1.88 (m, 4H), 1.66 (m, 4H), 1.50 (m, 4H), 1.40 (m, 4H). 13 C-NMR (100 MHz, CDCl 3 ): δ 190.6, 153.8, 143.8, 139.9, 131.5, 129.8, 128.6, 126.6, 118.5, 35.5, 34.2, 32.9, 31.4, 28.6, 28.2. HRMS (EI): m/z = 597.1268 (M + ), Δ = 4.3 ppm.
1,4-Bis[N,N-bis(4’’-(6’’’-bromohexyl)phenyl)-4’-aminostyryl]benzene (TPADSB-N). A 50 mL twonecked flask charged with 1,4-bis(diethylphosphonatemethyl) benzene (0.14 g, 0.37 mmol) and 2.2 eq. of aldehyde 1 (0.5 g, 0.83 mmol) in 20 mL of dry THF was cooled down to 0 ℃ with an ice bath. To the above solution, 0.83 mL (2.2 eq.) of potassium tert-butoxide (in THF, 1M) was added dropwise at 0 ℃. The reaction mixture was stirred for 6 hrs at 0 ℃ and then quenched with water. The solvent was removed under reduced pressure and the resulting mixture was diluted with dichloromethane, washed with water and brine, and dried over magnesium sulfate. The crude compound was purified by silica gel column chromatography (dichloromethane/hexane = 1/5).The product yield was 0.38 g (80%). 1 H-NMR (300 MHz, CDCl 3 ): δ 7.47 (s, 4H), 7.38 (d, 4H, J = 8.8 Hz), 7.09~7.01 (m, 22H), 6.98 (d, 2H, J = 16 Hz), 3.43 (t, 8H, - CH2 Br, J = 6.8 Hz), 2.59 (t, 8H, Ar CH2 -, J = 7.6 Hz), 1.89 (m, 8H), 1.65 (m, 8H), 1.50 (m, 8H), 1.40 (m, 8H). 13 C-NMR (100 MHz, CDCl 3 ): δ 147.9, 145.5, 137.6, 136.9, 131.0, 129.4, 128.1, 127.4, 126.8, 126.4, 124.8, 122.8, 35.5, 34,3, 33.0, 31.5, 28.7, 28.3. MS (FAB): m/z = 1264 (M + ).
1, 4-Bis[N,N-bis(4’’-(6’’’-(N,N,N-trimethylammonium)hexyl)phenyl)-4’-aminostyryl]benzene tetrabromide (TPADSB-C). To a solution of TPADSB-N (0.15 g, 0.12 mmol) in THF (20 mL), was added an excess of condensed trimethylamine (2 mL) using a dry ice/acetone filled gas condenser at -78 ℃. The reaction mixture was allowed to warm to room temperature slowly and stirred for 12 hrs. A small amount of water was added to the above solution to dissolve the precipitated compounds and the reaction solution was cooled down to -78 ℃ with a dry ice/acetone bath. An excess of condensed trimethylamine (2 mL) was added again and the resulting solution was allowed to reach room temperature and stirred for additional 12 hrs. After the reaction was completed, the remaining trimethylamine and solvent were removed under reduced pressure. A crude product was dissolved in a minimum amount of hot methanol and precipitated into diethyl ether several times. The yield was 0.15 g (85 %). 1 H-NMR (300 MHz, DMSO): δ 7.55 (s, 4H), 7.48 (d, 4H, J = 8.8 Hz), 7.20 (d, 2H, J = 16.4 Hz), 7.15 (d, 8H, J = 8.4 Hz), 7.08 (d, 2H, J = 16.4 Hz), 6.96 (d, 8H, J = 8.4 Hz), 6.88 (d, 4H, J = 8.8 Hz), 3. 28 (m, 8H), 3.05 (s, 36H), 2.55 (t, 8H, Ar CH2 -, J = 7.6 Hz), 1.68 (m, 8H), 1.60 (m, 8H), 1.36 (m, 16H). MS (ESI): m/z = 671 (M-2Br) 2+ , 421 (M-3Br) 3+ , 296 (M-4Br) 4+ .
RESULTS AND DISCUSSION
PPT Slide
Lager Image
Synthetic routes to TPADSB-N and TPADSB-C.
PSAU was obtained by free radical polymerization of sodium acrylamidoundecanoate in water using K 2 S 2 O 8 as a radical initiator. 9 The final polymer was purified by dialysis using 12 kDa molecular weight cut off bag against alkaline water (pH=10). For the synthesis of compound 1 ( 1 ), triphenylamine was brominated with N-bromosuccinimide in dichloromethane and the successive lithiation/alkylation with t-BuLi and excess 1,6-dibromohexane yielded bis[4-(6’-bromohexyl)phenyl]phenylamine in 63% yield. To prevent intermolecular coupling reactions, a large excess (10 eq.) of 1,6-dibromohexane was added. Aldehyde functionality was easily introduced by Vilsmeier formylation to give the structure 1 in 78% yield. Horner-Emmons Wittig coupling between 1,4-bis(diethylphosphonatemethyl)benzene and 2 eq. of compound 1 using potassium tert-butoxide in THF at 0 ℃ gave TPADSB-N . The reaction temperature was kept around 0 ℃ in order to remove the possibility of halide elimination during the reaction. Formation of the final water-soluble TPADSB-C was easily achieved via quaternization with a large excess of trimethylamine in the mixed solvent of THF and water. After addition of trimethylamine, the insoluble solid forms gradually as the reaction proceeds, which means the ionic units are formed via quaternization. To ensure that complete quaternization is achieved, it is recommended to re-dissolve the precipitated compounds by adding water and to add excess trimethylamine for a further reaction. Removal of unreacted trimethylamine does not impose any problem because of its low boiling point.S
The surfactant units in the polymer chain can assemble in a way to form unimolecular micelles in aqueous solution. This process is expected to be independent on the polymer concentration [ PSAU ]. On the other hand, the polymer chains can also undergo self-organization to form inter-chain aggregates at higher concentrations. In order to examine hydrophobic domain formation, we have performed fluorescence probe studies using NPN as a probe molecule. Though NPN is weakly fluorescent in aqueous solution, its fluorescence spectrum in the presence of PSAU shows 8 times intensity increase accompanied by a 52 nm blue-shift ( . 2 ). This suggests that the probe molecules are solubilized in nonpolar environments within the polymer aggregates. 10 - 11
The change of relative fluorescence intensity ( I/Io , where I and Io are the fluorescence intensities of NPN in the presence and absence of polymer, respectively) with increasing polymer concentration is shown in . 3 . Large enhancement of I/Io at higher polymer concentrations indicates the formation of inter-chain aggregates. The corresponding shift of the emission maximum of NPN (Δλ = λ in water - λ in PSAU solution ) is also plotted as a function of polymer concentration (Inset . 3 ). Although spectral shift shows saturation after complete solubilization of the probe within the hydrophobic domains of polymer aggregates, the emission intensity keeps increasing. The plot shows that the onset of interchain aggregation occurs at polymer concentration of ~0.01 gL -1 . In analogy with the critical micelle concentration (cmc) of monomeric surfactants, the concentration corresponding to the inflection point can be referred as a critical aggregation concentration (cac). Thus, cac of PSAU obtained from the plot is about 0.01 gL -1 . The absence of any concentration-independent region at low [ PSAU ] (inset . 3 ) suggests that single polymer chain has also hydrophobic domains that can bind the probes in dilute aqueous solutions.
PPT Slide
Lager Image
Fluorescence spectra of NPN with increasing [PSAU].
PPT Slide
Lager Image
Plot of relative PL intensity (I/Io) of NPN as a function of [PSAU]. Inset) plot of the shift of emission maximum of NPN as a function of [PSAU].
. 4 shows absorption and PL spectra of TPADSB-N in toluene and TPADSB-C in water. Both TPADSB-N and TPADSB-C have same electronic conjugation. The charged ionic units only adjust the solubility in different solvents due to break-up of π-conjugation with the main chromophore backbone. The emission spectrum in water is red-shifted (λ PL = 520 nm), structureless and broad relative to that in toluene (λ PL = 457 nm). The absorption spectra in toluene (λ abs = 415 nm) and in water (λ abs = 408 nm) show a negligible difference and a slight blue-shift in water is originated from conformational distortion due to poor solubility and/or hydrogen bonding interaction with water.
PPT Slide
Lager Image
UV-vis absorption and fluorescence spectra of TPADSB-N in toluene (dotted line) and TPADSB-C in water (solid line).
PPT Slide
Lager Image
Absorption and fluorescence spectra of TPADSB-C in water (solid line) and in PSAU vesicle solution (dotted line).
The steady-state PL and UV-vis spectra of TPADSB-C ([ TPADSB-C ] = 1×10 -6 M) in the presence and absence of PSAU in water are presented in . 5 . The PSAU concentration (3 g/L) was adjusted to exceed its cac (~0.01 g/L) for complete formation of inter-chain vesicles. The emission of TPADSB-C is blue-shifted (λ PL =520 nm→510 nm) in PSAU solution due to incorporation of the chromophores inside of the vesicles. The PL quantum efficiency (Φ PL ) of the chromophore was measured relative to fluorescein in water (pH=10). The Φ PL of TPADSB-C in water is 73% in the absence of PSAU and 90% in the presence of PSAU vesicle. The enhancement in the quantum efficiency is caused by the nonpolar microenvironment around the chromophores due to inclusion inside the PSAU vesicle. The inside of bilayers of the vesicle is hydrophobic and nonpolar relative to water, which is similar to organic solvents. TPADSB-C is water-soluble with charged ionic groups but the main conjugated backbone is still hydrophobic. The chromphores are expected to exist in the bilayers through hydrophobic interactions. Molar absorptivity of the chromophore is also increased with the PSAU vesicles ( . 5 ).
It is interesting to mention that the fluorescence spectrum with PSAU shows a blue-shifted emission with enhanced Φ PL (90%) but it is different from the spectra in toluene and in water. However same UV-vis and PL spectra of TPADSB-C in a sodium dodecylsulfate (SDS) micelle were reported with regard to those of TPADSB-N in toluene. 12 It is expected that the microenvironment inside the SDS micelle is very similar to nonpolar organic solvents such as toluene, which is not the same case with the PSAU vesicle. There are two different micro domains inside the vesicle, the aqueous core and the hydrophobic bilayer. TPADSB-C can exist in both of the core and the bilayer. The measured absorption and PL spectra of TPADSB-C in PSAU vesicles are intermediate between those in toluene and water. The chromophores in two different micro domains probably contribute together to the resulting spectra. The polymeric vesicle is a very interesting microcontainer which modulates the microenvironment (such as polarity) around the molecular fluorophores in bulk aqueous solution. The encapsulated fluorophores inside the vesicle have a great potential as efficient molecular labels with biocompatibility in biological imaging using confocal microscopy and two-photon induced fluorescence microscopy.
In summary, an inter-chain vesicle formation of poly(sodium acrylamidoundecanoate) ( PSAU ) was studied using NPN fluorescence measurement with changing PSAU concentration in water. PSAU shows a critical aggregation concentration at ~0.01 g/L. Above cac, UV-vis and fluorescence spectroscopy of the water-soluble fluorophore ( TPADSB-C ) was investigated to study the microenvironment modulation through dye incorporation in the polymeric vesicle. The emission of TPADSB-C in the presence of PSAU vesicles was blue-shifted and the PL quantum efficiency was increased to 90% due to the microenvironment (e.g. polarity) change in aqueous solution. This study shows that the polymeric vesicle containing molecular fluorophores has a great potential as efficient, stable and biocompatible labeling tags in biological cell imaging.
Acknowledgements
This work was supported for two years by Pusan National University Research Grant.
References
Kishimura A. , Koide A. , Osada K. , Yamasaki Y. , Kataoka K. 2007 Angew. Chem. Int. Ed. 46 6085 -    DOI : 10.1002/anie.200701776
Holowka E. , Sun V. Z. , Kamei D. T. , Deming T. J. 2007 Nat. Mater. 6 52 -    DOI : 10.1038/nmat1794
Ma Y. , Dong W.-F. , Hempenius M. A. , Mohwald H. , Vancso G. J. 2006 Nat. Mater. 5 724 -    DOI : 10.1038/nmat1716
Ranquin A. , VersLes W. , Meier W. , Steyaert J. , Gelder P. V. 2005 Nano Lett. 5 2220 -    DOI : 10.1021/nl051523d
Bellomo E. G. , Wyrsta M. D. , Pakstis L. , Pochan D. J. , Deming T. J. 2004 Nat. Mater. 3 244 -    DOI : 10.1038/nmat1093
Sumida Y. , Masuyama A. , Takasu M. , Kida T. , Nakatsuji Y. , Ikeda I. 2001 Langmuir 17 609 -    DOI : 10.1021/la0008939
Lasic D. D. , Needham D. 1995 Chem. Rev. 95 2601 -    DOI : 10.1021/cr00040a001
Kusumi A. , Singh M. , Tirrell D. A. , Oehme G. , Singh A. , Samuel N.K.P. , Hyde J. S. , Regen S. L. 1983 J. Am. Chem. Soc. 105 2975 -    DOI : 10.1021/ja00348a009
Nayak R. R. , Roy S. , Dey J. 2006 Colloid Polym. Sci. 285 219 -    DOI : 10.1007/s00396-006-1554-z
Gan L. M. , Chew C. H. 1992 In Surfactant Science Series; Friberg, S. E.; Lindman, B., Ed. Marcel Dekker, Inc. New York 44 327 -
Tohru S. , Keita T. , Masataka H. 2002 Anal. Chim. Acta. 454 203 -    DOI : 10.1016/S0003-2670(01)01575-6
Woo H. Y. , Korystov D. , Mikhailovsky A. , Nguyen T.-Q. , Bazan G. C. 2005 J. Am. Chem. Soc. 127 13794 -    DOI : 10.1021/ja054911q