Influence of defective sites in Pt/C catalysts on the anode of direct methanol fuel cell and their role in CO poisoning: a first-principles study
Influence of defective sites in Pt/C catalysts on the anode of direct methanol fuel cell and their role in CO poisoning: a first-principles study
Carbon letters. 2015. Jul, 16(3): 198-202
Copyright © 2015, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : March 03, 2015
  • Accepted : May 05, 2015
  • Published : July 31, 2015
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Soonchul Kwon
Department of Civil Engineering, Pusan National University, Busan 609-735, Korea
Seung Geol Lee
Department of Organic Material Science and Engineering, Pusan National University, Busan 609-735, Korea
seunggeol.lee@pusan.ac.kr
Abstract
Carbon-supported Pt catalyst systems containing defect adsorption sites on the anode of direct methanol fuel cells were investigated, to elucidate the mechanisms of H 2 dissociation and carbon monoxide (CO) poisoning. Density functional theory calculations were carried out to determine the effect of defect sites located neighboring to or distant from the Pt catalyst on H 2 and CO adsorption properties, based on electronic properties such as adsorption energy and electronic band gap. Interestingly, the presence of neighboring defect sites led to a reduction of H 2 dissociation and CO poisoning due to atomic Pt filling the defect sites. At distant sites, H 2 dissociation was active on Pt, but CO filled the defect sites to form carbon π-π bonds, thus enhancing the oxidation of the carbon surface. It should be noted that defect sites can cause CO poisoning, thereby deactivating the anode gradually.
Keywords
1. Introduction
Direct alcohol fuel cells (DAFC) have the advantages of high energy density, easy handling of liquid fuel and low operating temperatures, making them a potential candidate system for power generation in portable equipment or devices [1] . Among the various types of DAFCs, direct methanol fuel cells (DMFCs) have been extensively developed as promising devices for the portable power market because of the easy oxidation of methanol [2 , 3] . When Pt is used as a catalyst on a DMFC anode, the electro-oxidation of methanol (<80℃) shows sufficient catalytic activity to produce H 2 . Unfortunately, Pt tends to be readily poisoned by carbon monoxide (CO), a reaction by-product, and thus in time becomes deactivated [4] . For this reason, many studies have focused on enhancing the catalytic activity by inhibiting the CO poisoning effect using carbon-supported binary catalysts including Pt, by means of an electronic effect or an ensemble effect [5 - 13] . Most of this research has focused on the role of the catalyst in maintaining activity. However, it is also possible that the carbon support is not clean enough to maintain sufficient activity.
We investigated the influence of defect sites on the carbon support using density functional theory (DFT) to obtain a fundamental understanding of adsorption characteristics relevant to H 2 dissociation and CO poisoning on Pt/C at the molecular level. We also discuss the effect of the defects of a carbon substrate on catalytic activity due to CO poisoning.
2. Experimental
In this investigation, DFT calculations were performed to evaluate H 2 and CO adsorption on the Pt sites and defect sites of carbon-supported Pt systems, using the three-dimensional periodic slab model. Geometry optimizations were performed using DMol 3 (Dassault Systèmes BIOVIA, San Diego, CA, USA) under the following conditions: 1) the spin-polarized general gradient approximation (GGA)-PBE functional [14 , 15] option, and 2) the DNP basis set, to predict the properties of catalyst and adsorbates (H 2 or CO). GGA-PBE based functions have been extensively used to describe systems including Pt catalysts [16 - 18] and carbon-based materials [19 - 25] .
In the supercell, the surface was exposed as a slab, providing four Pt atoms over three layers of carbon (graphite). For the development of the surface structure, three atomic layers of graphite were cleaved at the (001) plane. The vacuum thickness (size of the unit cell perpendicular to slab-slab thickness) was set to 20 Å to prevent interactions beyond the periodic boundary. The Brillouin zone was sampled using the 4 × 4 × 1 Monkhorst-Pack (MP) k-point mesh [26] . The self-consistent field (SCF) convergence, 1 × 10 −5 Ha, was obtained at the given k-point sampling. Four Pt atoms [27 , 28] were loaded on graphite, and the system was optimized with a constraint of the third layer, as shown in Fig. 1 . We also designed a mono-vacancy carbon substrate to study the effect of defect sites, where Pt is bound to a neighboring site (nbr-Pt/C) or a distant site (dis-Pt/C) on the carbon (001) surface, as shown in Fig. 1b and c .
PPT Slide
Lager Image
Optimized crystal structure of (a) Pt/C, (b) defect site neighboring Pt/C (nbr-Pt/C), and (c) defect site distant to Pt/C (dis-Pt/C). The lattice parameter is (7.38 × 7.38 Å) periodic slab with c = 26.80 Å in the c-axis direction. Red circle denotes the defect site of carbon.
To determine adsorption energies Ead between the adsorbate and the adsorbent surface, three single total energy calculations were performed: for 1) geometry optimization of H 2 /CO, 2) geometry optimization of the catalyst surface slab without H 2 /CO, and 3) geometry optimization of the catalyst surface slab with H 2 /CO. The adsorption energies were determined as below:
PPT Slide
Lager Image
where E ad is the adsorption energy of the adsorbate on the adsorbent; E (catalyst+H2/CO) , the total energy of the catalyst with H 2 /CO; Ecatalyst , the total energy of the catalyst; and E H2/CO , the total energy of H 2 /CO. The calculated values of adsorption energy were used to discuss the adsorption properties of H 2 /CO on Pt/C.
3. Results and Discussion
- 3.1. H2and CO adsorption on Pt/C
We first evaluated the adsorption of H 2 and CO on a “clean” Pt/C surface i.e., a surface with no defect sites. The geometry of H 2 -Pt/C and CO-Pt/C was optimized to identify the preferred molecular conformation, as shown in Fig. 2 . Table 1 shows that H 2 and CO were strongly adsorbed on Pt, with adsorption energies of −1.38 eV and −2.19 eV, respectively. This is in good agreement with the findings of previous theoretical (−1.4 eV and −2.17 eV) and experimental studies [5 , 6 , 29 , 30] . The electron density field also supports the enhanced electronic interaction between Pt and H 2 /CO. H 2 was readily dissociated on Pt clusters to form Pt 1 -H and Pt 2 -H bonds, which is typical for H 2 dissociation on Pt [30] . H 2 splits into two hydrogen atoms, and each bonds to a Pt atom: one with a distance of 1.86 Å, and the other with a distance of 1.95 Å. CO is also favorably bonded in a bidentate fashion because of the highly interactive electron field of CO-Pt, which confirms that CO poisoning is favorable within Pt clusters.
PPT Slide
Lager Image
Geometry configuration of (a) H2 dissociation and (b) carbon monoxide adsorption on clean-Pt/C, with the highest occupied molecular orbital-lowest unoccupied molecular orbital (HOMO-LUMO) band gap.
Adsorption energies of H2/CO on catalyst systems
PPT Slide
Lager Image
a)Carbon monoxide (CO) adsorption on the Pt site of dis-Pt/C. b)CO adsorption on the defect site of dis-Pt/C.
- 3.2. H2and CO adsorption on nbr-Pt/C
Defect surfaces on Pt/C anodes play a notable role in the anode activity, as increased interaction with CO can lead to poisoning and oxidation of the carbon surface. To probe the effect of defect sites, we first investigated H 2 dissociation and CO adsorption on Pt/C, where the defect site is located neighboring to a Pt cluster (nbr-Pt/C), as shown in Fig. 3a . Interestingly, for the adsorption of both H 2 and CO, one Pt atom (Pt 1 ) filled the neighboring defect site, sharing electron density with the defective carbon surface. Meanwhile, the reduced metal content resulted in diminished H 2 dissociation, as shown by the smaller adsorption energy (−1.09 eV) and H-H distance (0.80 Å) compared to those of clean-Pt/C (−1.38 eV and 0.88 Å, respectively).
PPT Slide
Lager Image
Geometry configuration of (a) H2 dissociation and (b) carbon monoxide adsorption on nbr-Pt/C, with the highest occupied molecular orbital-lowest unoccupied molecular orbital (HOMO-LUMO) band gap. Red circle denotes the defect site of carbon.
CO adsorption was expected to be reduced in a similar manner, but the adsorption increased significantly, as shown by the large bond strength (−3.02 eV) and bond length of CO (2.06 Å). The electron density field shows that density is shared between Pt-CO and carbon. Considering the molecular orbitals during the reaction, the degree of electron delocalization of the system leads to a change in the highest occupied molecular orbital-lowest unoccupied molecular orbital (HOMO-LUMO) band gap, which is dependent on the adsorption of the different gas molecules.
Therefore, we investigated the energy trends on the basis of molecular orbitals in order to elucidate the gas binding mechanism. We carried out additional calculations of the electronic energy of the bands and the localization of molecular orbitals for the interaction of H 2 /CO with the Pt atom. The relatively large band gap for H 2 dissociation (0.96 eV) on nbr-Pt/C as compared to that for clean-Pt/C (0.81 eV) suggests that the Pt-H 2 interaction on the system with defects was reduced, which is in line with the reduced adsorption energy. Conversely, the band gap for CO adsorption in nbr-Pt/C narrowed (0.95 eV), because of the strong electronic interaction between CO and Pt, even with one Pt atom filling the defect site. The strength of the interaction between Pt-C and CO contributes to the degree of CO chemisorption. The geometry of the dimer Pt-CO bond is consistent with the orbital sharing conformation, because of the Pt-CO* π-back bond donation [30] . Thus, H 2 dissociation tends to take place on clean-Pt/C rather than on nbr-Pt/C, where CO poisoning occurs.
- 3.3. H2and CO adsorption on dis-Pt/C
Since defect sites on Pt/C are located away from Pt over the carbon surface, we additionally designed a structure containing a mono-vacancy site distant from the Pt clusters, and then optimized the structure with adsorbed H 2 /CO molecules, as shown in Fig. 4 . Both H 2 and CO were strongly adsorbed on Pt with adsorption energies of −1.31 eV and −1.79 eV respectively, which are comparable to the adsorption characteristics on the cleanPt/C surface ( Table 1 ). The electron density field also shows the well-distributed electronic interaction between Pt and H 2 /CO.
PPT Slide
Lager Image
Geometry configuration of (a) H2 dissociation on top of Pt, (b) carbon monoxide (CO) adsorption on Pt, and (c) CO adsorption at a defect site of graphite on dis-Pt/C, with the highest occupied molecular orbital-lowest unoccupied molecular orbital (HOMO-LUMO) band gap. Red circle denotes the defect site of carbon.
Interestingly, CO perfectly filled the defect site on carbon, with a high adsorption energy (−4.24 eV). CO is preferentially bonded to the carbon of graphite via π bond formation, as C CO -C graphite , because of the highly interactive electron sharing of C CO -C graphite , which in turn is attributed to the narrow HOMO-LUMO band gap (0.33 eV). CO adsorption on the Pt cluster (0.95 eV) tends to be similar to that on clean-Pt/C (1.09 eV), which represents the independence of the interaction when the defect site is far from the adsorption site. In addition, the oxygen atom of CO causes electro-oxidation of the carbon surface, suggesting that defect sites lead to further CO poisoning. When filled with CO, the matrix could be saturated with H + to form oxidation side products such as methoxy group products (C x H y O z ). CO poisoning deactivates the catalytic performance on an anode surface having defect sites. From the results of DFT calculations, it is noteworthy that defect sites on carbon significantly increased CO poisoning in the DMFC anode.
4. Conclusion
We investigated carbon-supported Pt catalyst systems as DMFC anodes with defect adsorption sites, in order to elucidate the mechanisms of H 2 dissociation and CO poisoning, using quantum mechanical DFT methods. We found that neighboring Pt/C defect sites suppressed H 2 dissociation and CO poisoning due to Pt atoms filling the defect sites. With distant Pt/C defect sites, H 2 dissociation was still active on Pt, but CO could fill the defect sites to form carbon π-π bonds, thus enhancing the oxidation of the carbon surface. In addition, the oxygen atom of CO caused electro-oxidation of the carbon surface, suggesting that the presence of defect sites can lead to CO poisoning. Therefore, defect sites on the carbon support significantly affect CO poisoning on the DMFC anode.
Acknowledgements
This research was supported by Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT & Future Planning (2014R1A1A1004096).
References
Shao ZG , Zhu FY , Lin WF , Christensen PA , Zhang HM 2006 PtRu/Ti anodes with varying Pt : Ru ratio prepared by electrodeposition for the direct methanol fuel cell Phys Chem Chem Phys http://dx.doi.org/10.1039/B604939g 8 2720 -
Dillon R , Srinivasan S , Arico AS , Antonucci V 2004 International activities in DMFC R&D: status of technologies and potential applications J Power Sources http://dx.doi.org/10.1016/j.jpowsour.2003.09.032 127 112 -
Lamy C , Lima A , LeRhun V , Delime F , Coutanceau C , Leger JM 2002 Recent advances in the development of direct alcohol fuel cells (DAFC) J Power Sources http://dx.doi.org/10.1016/S0378-7753(01)00954-5 105 283 -
Veizaga NS , Rodriguez VI , Rocha TA , Bruno M , Scelza OA , de Miguel SR , Gonzalez ER 2015 Promoting effect of tin in platinum electrocatalysts for direct methanol fuel cells (DMFC) J Electrochem Soc http://dx.doi.org/10.1149/2.0181503jes 162 F243 -
Courtois J , Du WX , Wong E , Teng XW , Deskins NA 2014 Screening iridium-based bimetallic alloys as catalysts for direct ethanol fuel cells Appl Catal A http://dx.doi.org/10.1016/j.apcata.2014.06.029 483 85 -
Parker SF , Frost CD , Telling M , Albers P , Lopez M , Seitz K 2006 Characterisation of the adsorption sites of hydrogen on Pt/C fuel cell catalysts Catal Today http://dx.doi.org/10.1016/j.cattod.2006.02.043 114 418 -
Liu ZL , Ling XY , Su XD , Lee JY 2004 Carbon-supported Pt and PtRu nanoparticles as catalysts for a direct methanol fuel cell J Phys Chem B http://dx.doi.org/10.1021/Jp049422b 108 8234 -
Song SQ , Zhou WJ , Liang ZX , Cai R , Sun GQ , Xin Q , Stergiopoulos V , Tsiakaras P 2005 The effect of methanol and ethanol cross-over on the performance of PtRu/C-based anode DAFCs Appl Catal B http://dx.doi.org/10.1016/j.apcatb.2004.05.017 55 65 -
Lee SA , Park KW , Choi JH , Kwon BK , Sung YE 2002 Nanoparticle synthesis and electrocatalytic activity of Pt alloys for direct methanol fuel cells J Electrochem Soc http://dx.doi.org/10.1149/1.1502685 149 A1299 -
Kim C , Kwon HH , Song IK , Sung YE , Chung WS , Lee HI 2007 Preparation of PtRu nanoparticles on various carbon supports using surfactants and their catalytic activities for methanol electro-oxidation J Power Sources http://dx.doi.org/10.1016/j.jpowsour.2007.05.109 171 404 -
Lim DH , Lee WD , Lee HI 2008 Highly dispersed and nano-sized Ptbased electrocatalysts for low-temperature fuel cells Catal Surv Asia http://dx.doi.org/10.1007/s10563-008-9059-z 12 310 -
Colmati F , Antolini E , Gonzalez ER 2007 Ethanol oxidation on a carbon-supported Pt75Sn25 electrocatalyst prepared by reduction with formic acid: effect of thermal treatment Appl Catal B http://dx.doi.org/10.1016/j.apcatb.2006.06.013 73 106 -
Zeng JH , Lee JY 2007 Ruthenium-free, carbon-supported cobalt and tungsten containing binary & ternary Pt catalysts for the anodes of direct methanol fuel cells Int J Hydrogen Energy http://dx.doi.org/10.1016/j.ijhydene.2007.03.012 32 4389 -
Perdew JP , Burke K , Ernzerhof M 1996 Generalized gradient approximation made simple Phys Rev Lett http://dx.doi.org/10.1103/PhysRevLett.77.3865 77 3865 -
Perdew JP , Burke K , Wang Y 1996 Generalized gradient approximation for the exchange-correlation hole of a many-electron system Phys Rev B http://dx.doi.org/10.1103/PhysRevB.54.16533 54 16533 -
Chen XF , Yan JM , Jiang Q 2014 Single layer of polymeric metal-phthalocyanine: promising substrate to realize single Pt atom catalyst with uniform distribution J Phys Chem C http://dx.doi.org/10.1021/Jp411183h 118 2122 -
Zhang XX , Dai ZQ , Wei L , Liang NF , Wu XQ 2013 Theoretical calculation of the gas-sensing properties of Pt-decorated carbon nanotubes Sensors http://dx.doi.org/10.3390/S131115159 13 15159 -
Gao GP , Wei SH , Gu X , Duan XM 2013 Catalytic role of pre-adsorbed CO in platinum-based catalysts: the reduction of SO2 by CO on PtlAum(CO)n Phys Chem Chem Phys http://dx.doi.org/10.1039/C3cp44712j 15 12846 -
Ko W , Moon HS , Lee SG , Choi JI , Jang SS 2015 A first-principles study of lithium adsorption on a graphene-fullerene nanohybrid system ChemPhysChem 16 789 -
Koh W , Choi JI , Jeong E , Lee SG , Jang SS 2014 Li adsorption on a fullerene-single wall carbon nanotube hybrid system: density functional theory approach Curr Appl Phys 14 1748 -
Koh W , Choi JI , Donaher K , Lee SG , Jang SS 2011 Mechanism of Li adsorption on carbon nanotube-fullerene hybrid system: a first-principles study ACS Appl Mater Interfaces http://dx.doi.org/10.1021/Am200018w 3 1186 -
Koh W , Choi JI , Lee SG , Lee WR , Jang SS 2011 First-principles study of Li adsorption in a carbon nanotube-fullerene hybrid system Carbon http://dx.doi.org/10.1016/j.carbon.2010.09.022 49 286 -
Koh W , Lee JH , Lee SG , Choi JI , Jang SS 2015 Li adsorption on a graphene-fullerene nanobud system: density functional theory approach RSC Adv http://dx.doi.org/10.1039/c4ra15619f 5 32819 -
Moon HS , Lee JH , Kwon S , Kim IT , Lee SG 2015 Mechanisms of Na adsorption on graphene and graphene oxide: density functional theory approach Carbon Lett http://dx.doi.org/10.5714/CL.2015.16.2.116 16 116 -
Lee JH , Kang SG , Moon HS , Park H , Kim IT , Lee SG 2015 Adsorption mechanisms of lithium oxides (LixO2) on a graphene-based electrode: a density functional theory approach Appl Surf Sci http://dx.doi.org/10.1016/j.apsusc.2015.05.119 351 193 -
Monkhorst HJ , Pack JD 1976 Special points for Brillouin-zone integrations Phys Rev B http://dx.doi.org/10.1103/PhysRevB.13.5188 13 5188 -
Balasubramanian K 1991 Potential-energy surfaces for the Pt2+H2 reaction J Chem Phys http://dx.doi.org/10.1063/1.460035 94 1253 -
Dal DG , Liao DW , Balasubramanian K 1995 Potential-energy surfaces for Pt3+H2 and Pd3+H2 systems J Chem Phys http://dx.doi.org/10.1063/1.469084 102 7530 -
Okamoto Y 2006 Comparison of hydrogen atom adsorption on Pt clusters with that on Pt surfaces: a study from density-functional calculations Chem Phys Lett http://dx.doi.org/10.1016/j.cplett.2006.08.013 429 209 -
Mitchell PCH , Wolohan P , Thompsett D , Cooper SJ 1997 Experimental and theoretical studies of fuel cell catalysts: density functional theory calculations of H2 dissociation and CO chemisorption on fuel cell metal dimers J Mol Catal A http://dx.doi.org/10.1016/S1381-1169(96)00486-4 119 223 -