CO<sub>2</sub> adsorption characteristics of slit-pore shaped activated carbon prepared from cokes with high crystallinity
CO2 adsorption characteristics of slit-pore shaped activated carbon prepared from cokes with high crystallinity
Carbon letters. 2015. Jan, 16(1): 45-50
Copyright © 2015, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : September 12, 2014
  • Accepted : December 14, 2014
  • Published : January 31, 2015
Export by style
Cited by
About the Authors
Mi-Seon, Park
Si-Eun, Lee
Min Il, Kim
Young-Seak, Lee

High crystallinity coke-based activated carbon (hc-AC) is prepared using a potassium hydroxide solution to adsorb carbon dioxide (CO 2 ). The CO 2 adsorption characteristics of the prepared hc-AC are investigated at different temperatures. The X-ray diffraction patterns indicate that pitch-based cokes prepared under high temperature and pressure have a high crystal structure. The textural properties of hc-AC indicate that it consists mainly of slit-like pores. Compared to other textural forms of AC that have higher pore volumes, this slit-pore-shaped hc-AC exhibits higher CO 2 adsorption due to the similar shape between its pores and CO 2 molecules. Additionally, in these high-crystallinity cokes, the main factor affecting CO 2 adsorption at lower temperature is the pore structure, whereas the presence of oxygen functional groups on the surface has a greater impact on CO 2 adsorption at higher temperature.
1. Introduction
Carbon dioxide (CO 2 ) emissions into the atmosphere have increased due to the combustion of fossil fuels in the operation of factories and automobiles. CO 2 is a greenhouse gas that gives rise to critical environmental issues, including global warming. Reduction of CO 2 emissions is thus especially urgent [1 , 2] . Among many ways to reduce CO 2 in the atmosphere, using an absorbent is much simpler than other methods such as CO 2 capture and storage technologies involving pre-combustion capture, oxy-fuel combustion, and postcombustion capture [3] .
Porous materials, such as activated carbon, zeolites, and molecular sieves, have been used as CO 2 absorbents due to their highly developed porous structure [4 , 5] . In particular, activated carbon has been widely used because of its low cost, hydrophobicity, and flexibility in terms of its porous texture and surface properties [6] . Activated carbon has been prepared from numerous carbonaceous source materials, such as walnut shells, coconut husk, tar pitch, and petroleum pitch. It has also been prepared from renewable resources, such as aluminum industry waste, bottom ash, peat, steel-plant slag, and beer lees [7 , 8] . In addition, activated carbon may be produced from pitch-based cokes, which may in turn be derived from waste generated during the carbon/carbon composite manufacturing process for highquality brake discs used in F1 automobiles and airplanes. Such cokes have high crystallinity because they are obtained at temperatures lower than 1273 K and extremely high pressure (approximately 700 bar). These cokes can potentially be used as activated carbon and CO 2 adsorbents.
In this study, activated carbon was prepared from high crystallinity cokes using various concentrations of potassium hydroxide (KOH) solution. The CO 2 adsorption characteristics of coke-based activated carbon were evaluated at different temperatures. Additionally, the crystal, textural, and chemical properties of the coke-based activated carbon were investigated.
2. Experimental
- 2.1. Materials
The pitch-based cokes used in this study are obtained from a carbon/carbon composites production process at temperature lower than 1273 K under extremely high pressure (approximately 700 bar). The size of the cokes is controlled below 75 μm using a general pulverizer and a sieve. KOH (95.0%, Samchun, Korea) is used to prepare a KOH solution, which is used as an activation agent in this study.
- 2.2. Preparation of high crystallinity coke based activated carbon
The pulverized cokes are treated with KOH solution to obtain activated carbon. Cokes (2.5 g) are mixed with 18 mL 2, 4, and 8 M KOH solution, respectively. The mixtures of cokes and KOH solution are heated in an electric furnace. Heat treatment is conducted at 1023 K for 3 h under a nitrogen atmosphere. The treated cokes samples are identified as hc-AC-2K, hc-AC-4K, and hc-AC-8K depending on the concentration of KOH solution. The experimental procedure is summarized in Scheme 1 .
PPT Slide
Lager Image
Flow chart of experiment. KOH: potassium hydroxide.
- 2.3. Characterization of prepared samples
The crystal structures of the prepared cokes-based activated carbon are investigated using X-ray diffraction (XRD, D8 DISCOVER, Bruker AXS, Germany). The XRD analysis is conducted using a Cu target. The specific surface area and pore structure of the prepared activated carbon are evaluated using N 2 adsorption at 77 K with an ASAP 2020 device (Micromeritics, Inc., Corp., USA) after each sample is degassed at 423 K for 3 h. The total pore volume is calculated using a t-plot. X-ray photoelectron spectroscopy (XPS, Thermo Electron Cooperation, MultiLab 2000 spectrometer, England) is performed to investigate the elemental composition of the prepared activated carbon.
The textural properties and pore volume of the prepared cokes-based activated carbon are evaluated using an ASAP 2020 device (Micromeritics Inc., Corp.) using CO 2 (3.3 Å) gas because the pore size of activated carbon is extremely small (diameter of N 2 gas is 3.8 Å) [3] . The cumulative pore size distribution (PSD) of the prepared activated carbon is calculated using density functional theory (DFT) using DFT plus software supplied by Micromeritics [9] . The CO 2 adsorption capacity is measured by CO 2 isothermal adsorption at 273 and 298 K at 1 atm.
3. Results and Discussion
- 3.1. Structural properties
The pitch-based cokes have a sharp (0 0 2) peak at 26° and a (1 0 1) peak at 43°, as shown in Fig. 1 . These properties indicate that the pitch-based cokes are high-crystallinity cokes compared to cokes prepared at 1473 K [10] , which may be attributed to the high temperature and pressure treatment used for the pitch. After KOH activation, the height of the (0 0 2) peak decreased considerably with an increase of KOH concentration. This decrease indicates that the high K + (potassium cation) content resulted in attack of the carbon atoms in the crystallite with the (0 0 2) crystal plane, which is the main orientation and then the crystallite with the (0 0 2) orientation decreased [11] . The specific surface area appeared to decrease as the concentration of the KOH solution increased. The height of the (1 0 1) peak changed only slightly. The XRD parameters for L a and interplanar spacing were determined to be 0.161 nm and 0.343 nm, respectively, for cokes; 0.095 nm and 0.345 nm, respectively, for hc-AC-2K; 0.114 nm and 0.361 nm, respectively, for hc-AC-4K; and 0.083 nm and 0.37 nm, respectively, for hc-AC-8K.
PPT Slide
Lager Image
X-ray diffraction patterns of the cokes and the coke-based activated carbon.
- 3.2. Porous properties
Fig. 2a presents the nitrogen adsorption isotherms of the cokes and the coke-based activated carbon. The isothermal curve of the cokes did not increase as P/P 0 increased, indicating non-porous carbon. However, the coke-based activated carbon prepared under different KOH conditions exhibited a significant increase in adsorption, particularly in the region below 0.1 P/P 0 . The observed isotherms of the coke-based activated carbon were type IV according to the International Union of Pure and Applied Chemistry (IUPAC) classification [12 , 13] . In addition, the activated cokes exhibited hysteresis, which is H4 type [12] . These isotherm results indicated that the coke-based activated carbon was porous carbon with slitlike pores. These slit-like pores are favorable for adsorbing CO 2 gas, given its linear molecular structure. The calculated specific surface areas of the prepared activated carbon are shown in Table 1 . The nitrogen adsorption quantity and specific surface area decreased with increased concentration of the KOH solution, which is in accordance with the XRD results presented in Section 3.1.
PPT Slide
Lager Image
(a) Nitrogen adsorption isotherms at 77 K and (b) the cumulative pore size distribution using CO2 for the pitch-based cokes and the coke-based activated carbon.
PPT Slide
Lager Image
The cumulative PSDs of the cokes and activated carbon are shown in Fig. 2b . These PSD results indicate that the KOH-treatment of cokes mainly produced micropores whereas untreated cokes had no pores. The main pore size range that affects CO 2 adsorption is below 8 Å [14] . In this study, hc-AC-2K was found to have the greatest pore volume within 8 Å were introduced in this study. The pore volume decreased with increased concentration of the KOH solution. This relation indicates that hc-AC-2K has the highest CO 2 adsorption capacity in this study. The total pore volume values are also presented in Table 1 . The total pore volumes of the cokes, hc-AC-2K, hc-AC-4K, and hc-AC-8K were 0.015, 0.337, 0.285, and 0.261 cm 3 g -1 , respectively. hc-AC-2K had a higher total pore volume than hc-AC-4K and hc-AC-8K. Considering the cumulative PSD, a high pore volume is attributed to the formation of mesopores, but it is believed that mesopores do not affect CO 2 adsorption.
- 3.3. Surface chemical element composition
To investigate the chemical composition of the activated cokes under different conditions, a XPS analysis was performed to compare the amounts of oxygenated functional groups. Table 2 shows the C1s and O1s elemental content. In the resulting XPS spectra of the activated cokes, the elemental contents of carbon and oxygen atoms were determined to be 94.68% and 5.32%, respectively, for hc-AC-2K; 94.34% and 5.66%, respectively, for hc-AC-4K; and 88.22% and 11.78%, respectively, for hc-AC-8K. The elemental contents of the hc- AC-2K and hc-AC-4K were similar, although the total pore volume of hc-AC-2K was higher than that of hc-AC-4K. In contrast, the oxygen content of hc-AC-8K was considerably higher than that of hc-AC-2K. The oxide group content increased according to the concentration of the KOH solution used, and the corresponding increases in oxide groups are compared in Table 3 . Generally, activated porous carbon materials, activated carbon and activated carbon fiber, have several carbon-oxygen conformations after activation with oxidants [15] . The peak at 284.5 eV is assigned to graphitic C (sp 2 ) [16 , 17] . The values of the cokes and activated cokes in this study are higher than those observed for other activated carbons. Additionally, the contents of the C-O and C=O bonding groups in these samples, indicated by peaks at 286.4 and 287.4 eV, are lower than those in other activated carbons [3] . The amount of C-O and C=O bonds increased with KOH concentration, reaching 6.11% and 5.00%, respectively, for hc-AC-2K; 6.81% and 5.41%, respectively, for hc-AC-4K; and 7.57% and 5.91%, respectively, for hc- AC-8K. The (C=O)OH bonds at 288.8 eV decreased with increased concentration of the KOH solution due to weak bonding. These differences in the surface chemical composition are expected to affect CO 2 adsorption on the cokebased activated carbon.
PPT Slide
Lager Image
PPT Slide
Lager Image
- 3.4. CO2adsorption characteristics
Fig. 3 shows the isothermal CO 2 adsorption characterizations of the cokes and coke-based activated carbon at 273 and 298 K, respectively, at pressure ranging from vacuum to 800 mmHg. The quantity of adsorbed CO 2 on all samples increased with increasing pressure because physical adsorption depends strongly on pressure. The characterization of porous materials with a substantially microporous size distribution can be expected to increase with increasing pressure [18] . As shown in Fig. 3a , the activated cokes with developed ultramicropores (<7 Å) exhibited the highest adsorption capacity. The pore structure in the high crystallinity coke-based activated carbon is slit-like, similar to the molecular structure of CO 2 . This slit-like pore structure contributes to higher CO 2 adsorption that is comparable to that of activated carbon prepared from various carbonaceous sources, as shown in Fig. 4 [19 - 24] . In Fig. 4 , the results for hc-AC-2K indicate that 1) the high-crystallinity coke-based activated carbon has higher CO 2 adsorption than the general CO 2 adsorption trend according to pore volume and 2) high-crystallinity cokebased activated carbon provides higher CO 2 adsorption than that of nut-shell based-activated carbons, although the former/latter had a higher pore volume of 1.16 cm 3 g -1 . In addition, the cokes with few pores have a CO 2 adsorption capacity below 1 mmol g -1 . This phenomenon can be attributed to the ability of the cokes with high crystallinity to interact with CO 2 gas. CO 2 molecules consist of two oxygen groups with two lone pair groups. These lone pairs can interact with graphitic carbon (sp 2 ) by electrostatic attraction. The amount of CO 2 adsorbed on the coke-based activated carbon decreased with increasing temperature due to their weak interaction following increased CO 2 activity. However, the CO 2 adsorption behavior on hc-AC-2K and hc-AC-4K at 298 K was different from the behavior on coke at 273 K. The curves during initial CO 2 adsorption were similar until reaching 200 mmHg, although hc-AC-2K had a larger quantity of ultra-micropores. This difference in the adsorption curves indicates that the CO 2 adsorption capability associated with functional groups formed on the activated carbon was greater at higher temperature [3] . The oxygen groups (C=O, C-O, (C=O)OH) introduced onto the carbon surface by KOH activation were electrophilic, which strongly influences the interaction of the material with CO 2 [25 , 26] . This strong relationship arises because oxygen groups are strong electron-donating groups and the carbon atom of CO 2 has a positive charge due to the high electronegativity of the oxygen atom. These factors are favorable for electrostatic interaction. The C=O and C-O contents of hc-AC-4K were higher than those of hc-AC-2K. These functional groups increased the initial CO 2 adsorption at higher temperature (298 K). Moreover, high-crystallinity cokes can contribute to high CO 2 adsorption if they have more developed pore structures and greater pore size.
PPT Slide
Lager Image
CO2 adsorption characteristics of the cokes and the coke-based activated carbon depending on temperature; (a) 273 K and (b) 298 K.
PPT Slide
Lager Image
Comparison of CO2 adsorption with other adsorbents.
4. Conclusions
Pitch based-cokes were activated by using a KOH solution to obtain activated carbon to absorb CO 2 . The non-activated cokes had a high crystal structure and no pores, as indicated by XRD patterns and nitrogen adsorption isotherms. The coke-based activated carbon had the highest specific surface area and pore volumes within 8 Å when treated with a 2 M KOH solution. Slitshaped pores were formed in the high-crystallinity coke-based activated carbon, which allowed a higher quantity of CO 2 to be adsorbed compared to other activated carbons. In addition, the coke-based activated carbon had the highest CO 2 adsorption at 273 K. However, at 298 K, the curve of coke activated with a 4 M KOH solution during initial CO 2 adsorption was similar to that observed for coke activated with a 2 M KOH solution. This indicates that the oxygen functional groups, i.e., C=O and C-O bonds, are more important than the pore structure at higher temperature.
Bai BC , Cho S , Yu HR , Yi KB , Kim KD , Lee YS 2013 Effects of aminated carbon molecular sieves on breakthrough curve behavior in CO2/CH4 separation J Ind Eng Chem 19 776 -    DOI : 10.1016/j.jiec.2012.10.016
Miyamoto M , Fujioka Y , Yogo K 2012 Pure silica CHA type zeolite for CO2 separation using pressure swing adsorption at high pressure J Mater Chem 22 20186 -    DOI : 10.1039/c2jm34597h
Cho S , Yu HR , Kim KD , Yi KB , Lee YS 2012 Surface characteristics and carbon dioxide capture characteristics of oxyfluorinated carbon molecular sieves Chem Eng J 211-212 89 -    DOI : 10.1016/j.cej.2012.09.047
Xu X , Song C , Andresen JM , Miller BG , Scaroni AW 2002 Novel polyethylenimine- modified mesoporous molecular sieve of MCM-41 type as high-capacity adsorbent for CO2 capture Energy Fuels 16 1463 -    DOI : 10.1021/ef020058u
Siriwardane RV , Shen M-S , Fisher EP , Losch J 2005 Adsorption of CO2 on zeolites at moderate temperatures Energy Fuels 19 1153 -    DOI : 10.1021/ef040059h
Labus K , Gryglewicz S , Machnikowski J 2014 Granular KOH-activated carbons from coal-based cokes and their CO2 adsorption capacity Fuel 118 9 -    DOI : 10.1016/j.fuel.2013.10.042
Lee SG , Park KH , Shim WG , balathanigaimani MS , Moon H 2011 Performance of electrochemical double layer capacitors using highly porous activated carbons prepared from beer lees J Ind Eng Chem 17 450 -    DOI : 10.1016/j.jiec.2010.10.025
Adinaveen T , Kennedy LJ , Vijaya JJ , Sekaran G 2013 Studies on structural, morphological, electrical and electrochemical properties of activated carbon prepared from sugarcane bagasse J Ind Eng Chem 19 1470 -    DOI : 10.1016/j.jiec.2013.01.010
Jagiello J , Tolles ED , Meunier F 1998 Fundamentals of Adsorption Elsevier New York, NY Calculation of pore size distribution of activated carbons based on density functional theory (DFT) data 629 -
Yu L , Kim KJ , Park DY , Kim MS , Kim KI , Lim YS 2008 Preparation and characterization of pitch/cokes composite anode material for high power lithium secondary battery Carbon Lett 9 210 -    DOI : 10.5714/CL.2008.9.3.210
Park MS , Cho S , Jeong E , Lee YS Physico-chemical and electrochemical properties of pitch-based high crystallinity cokes used as electrode material for electric double layer capacitor J Ind Eng Chem in press
Condon JB 2006 Surface Area and Porosity Determinations by Physisorption: Measurements and Theory Elsevier Amsterdam
Yu HR , Cho S , Jung MJ , Lee YS 2013 Electrochemical and structural characteristics of activated carbon-based electrodes modified via phosphoric acid Microporous Mesoporous Mater 172 131 -    DOI : 10.1016/j.micromeso.2013.01.018
An H , Feng B , Su S 2011 CO2 capture by electrothermal swing adsorption with activated carbon fibre materials Int J Greenh Gas Control 5 16 -    DOI : 10.1016/j.ijggc.2010.03.007
Shafeeyan MS , Daud WMAW , Houshmand A , Shamiri A 2010 A review on surface modification of activated carbon for carbon dioxide adsorption J Anal Appl Pyrolysis 89 143 -    DOI : 10.1016/j.jaap.2010.07.006
Tressaud A , Durand E , Labrugère C 2004 Surface modification of several carbon-based materials: comparison between CF4 rf plasma and direct F2-gas fluorination routes J Fluorine Chem 125 1639 -    DOI : 10.1016/j.jfluchem.2004.09.022
Mathur RB , Gupta V , Bahl OP , Tressaud A , Flandrois S 2000 Improvement in the mechanical properties of polyacrylonitrile (PAN)-based carbon fibers after fluorination Synth Met 114 197 -    DOI : 10.1016/S0379-6779(00)00251-4
Cho SH , Bai BC , Yu HR , Lee YS 2011 Carbon capture and CO2/CH4 separation technique using porous carbon materials Appl Chem Eng 22 343 -
Lee CS , Ong YL , Aroua MK , Daud WMAW 2013 Impregnation of palm shell-based activated carbon with sterically hindered amines for CO2 adsorption Chem Eng J 219 558 -    DOI : 10.1016/j.cej.2012.10.064
Shafeeyan MS , Daud WMAW , Houshmand A , Arami-Niya A 2011 Ammonia modification of activated carbon to enhance carbon dioxide adsorption: effect of pre-oxidation Appl Surf Sci 257 3936 -    DOI : 10.1016/j.apsusc.2010.11.127
Pevida C , Plaza MG , Arias B , Fermoso J , Rubiera F , Pis JJ 2008 Surface modification of activated carbons for CO2 capture Appl Surf Sci 254 7165 -    DOI : 10.1016/j.apsusc.2008.05.239
Plaza MG , García S , Rubiera F , Pis JJ , Pevida C 2011 Evaluation of ammonia modified and conventionally activated biomass based carbons as CO2 adsorbents in postcombustion conditions Sep Purif Technol 80 96 -    DOI : 10.1016/j.seppur.2011.04.015
Heidari A , Younesi H , Rashidi A , Ghoreyshi AA 2014 Evaluation of CO2 adsorption with eucalyptus wood based activated carbon modified by ammonia solution through heat treatment Chem Eng J 254 503 -    DOI : 10.1016/j.cej.2014.06.004
Deng S , Wei H , Chen T , Wang B , Huang J , Yu G 2014 Superior CO2 adsorption on pine nut shell-derived activated carbons and the effective micropores at different temperatures Chem Eng J 253 46 -    DOI : 10.1016/j.cej.2014.04.115
Torrisi A , Mellot-Draznieks C , Bell RG 2009 Impact of ligands on CO2 adsorption in metal-organic frameworks: first principles study of the interaction of CO2 with functionalized benzenes. I. Inductive effects on the aromatic ring J Chem Phys 130 194703 -    DOI : 10.1063/1.3120909
Torrisi A , Mellot-Draznieks C , Bell RG 2010 Impact of ligands on CO2 adsorption in metal-organic frameworks: first principles study of the interaction of CO2 with functionalized benzenes. II. Effect of polar and acidic substituents J Chem Phys 132 044705 -    DOI : 10.1063/1.3276105