A study on elemental mercury adsorption behaviors of nanoporous carbons with carbon dioxide activation
A study on elemental mercury adsorption behaviors of nanoporous carbons with carbon dioxide activation
Carbon letters. 2014. Oct, 15(4): 295-298
Copyright © 2014, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : September 02, 2014
  • Accepted : October 05, 2014
  • Published : October 31, 2014
Export by style
Cited by
About the Authors
Kyong-Min, Bae
Soo-Jin, Park

In this work, nanoporous carbons (NPCs) were prepared by the self-assembly of polymeric carbon precursors and block copolymer template in the presence of tetraethyl orthosilicate and colloidal silica. The NPCs’ pore structures and total pore volumes were analyzed by reference to N 2 /77 K adsorption isotherms. The porosity and elemental mercury adsorption of NPCs were increased by activation with carbon dioxide. It could be resulted that elemental mercury adsorption ability of NPCs depended on their specific surface area and micropore fraction.
1. Introduction
Coal-fired power plants are one of the primary sources of mercury emissions. In the United States, nearly one third of the 150 tons of mercury emitted comes from coal-fired power plants. Coal is a major energy resource which is mainly burnt to produce electricity. As is known, it is not a clean fuel. Various types of pollutants, such as SO x , NO x and mercury, are released into the atmosphere during the burning of coal. Concerns over mercury emissions have increased due to the high toxicity, volatility, and bioaccumulation of mercury in the environment and due to the neurological health impact of mercury. According to the Global Mercury Assessment Report, coal-fired power plants are the primary source of the anthropogenic emissions of mercury into the atmosphere [1 - 8] .
Porous carbon materials have gained much attention due to their high specific surface area, good thermal stability, tunable porosity, chemical inertness, and biocompatibility. These features contribute to their high performance in various applications, such as the adsorption of dye molecules, which have become one of the most serious air/water pollutants [9 - 14] . Activated carbon, owing to its large specific surface area and high pore volume, is frequently used as an adsorbent [15 - 21] . However, its widespread use is restricted due to the micropore size, which limits the transfer of bulky dye molecules from the surface of active carbon into the pores [11 , 22 , 23] . Therefore, ordered mesoporous carbons (OMCs) with uniformly large pores and a high surface area are in great demand.
The versatility of carbon-based nanomaterials makes them very appealing for a number of applications, including catalysis, adsorption, separation, and energy storage. Many of these applications require carbons with well-developed micro- and mesoporosity. While microporosity can be easily created by the carbonization of certain natural materials or through the use of CO 2 , steam or KOH as an activating agent [24 , 25] , the formation of mesopores is more challenging.
There have been extensive developments related to the synthesis of OMCs [26] over the last decade. Initial reports were based on the hard-templating method, in which the pore geometry and size of the mesopore structure can be tuned by the choice of template materials. However, a major drawback of this synthesis route is the large number of preparation steps correand, in some cases, the fairly limited control of the mesopore diameters. The recently reported soft-templating approach [26] greatly simplified the preparation of OMCs. The use of triblock copolymers and thermosetting carbon precursors permits the direct formation of polymer–polymer composites, which, when subjected to a controlled thermal treatment, can be converted into mesoporous polymers and finally to mesoporous carbons. This synthesis route allows more freedom in the design of the symmetry and size of mesopores through simple changes in the synthesis conditions and/or the triblock copolymers used as soft templates. Though several synthetic pathways have been reported to date for the synthesis of mesoporous materials, a general one-step synthetic strategy to prepare crystalline nanoporous materials is still desired [27 , 28] .
In this study, a direct, one-step synthetic protocol which can be used to synthesize nanoporous carbons (NPCs) is reported. The essence of this method is its direct use of the self-assembly of block copolymers as templates for the generation of porous metal-carbon structures, without the extra step of generating templating silica structures. Mesoporous carbons were synthesized using a tri-block copolymer (structure-directing agent), a mixture of resorcinol and formaldehyde (carbon source) under a mild acidic condition, after which the efficiency of elemental mercury adsorption given the activation condition was evaluated.
2. Materials and Methods
- 2.1. Sample preparation
Approximately 1.25 g of resorcinol (Aldrich, USA) and 1.25 g of Pluronic F127 (Aldrich) were dissolved in deionized water and ethanol. The weight ratio of water to ethanol was fixed at 5.5:10. After stirring for about 10-15 min, the reaction mixture was supplied with 1.1 mL of 37% HCl with continual stirring for an additional 30 min. Next, 1.25 mL of formaldehyde and 1.87 mL of tetraethyl orthosilicate were added to the synthesis mixture. The resulting solution turned milky after 2-3 h, and after an additional 30 min of stirring, the aqueous and solid phases were allowed to separate. The polymer-containing bottom layer was spread on a Petri dish and left under the fume hood overnight. Then, the sample was aged at 100℃ for 24 h. A thermal treatment was performed in a nitrogen atmosphere in a tube furnace using a heating rate of 2℃/min up to 180℃. The sample was kept at this temperature for 5 h and then heated at a rate of 2℃/ min up to 400℃, and then at a rate of 5℃/min up to 850℃. Finally, the sample was kept at 850℃ for 2 h.
For activation, the samples were heated in a tube furnace in a nitrogen atmosphere at a heating rate of 5℃/min up to the activation temperature. After reaching this temperature, an activating gas was introduced into the tube furnace (80 cm 3 /min) for 1 h, with switching back to nitrogen to prevent further activation during the cool-down process. The activation temperature was varied at 600℃, 700℃, 800℃, and 900℃.
- 2.2. Textural properties
The N 2 adsorption isotherms were measured using a Belsorp Max (BEL Japan) at 77 K. The samples were degassed at 573 K for 12 h to obtain a residual pressure of less than 10 -6 torr. The amount of N 2 adsorbed onto the samples was used to calculate the specific surface area by means of the Brunauer-Emmett-Teller (BET) equation [29] . The total pore volume was estimated to be the liquid volume of the N 2 at a relative pressure of approximately 0.995. The micropore volume was calculated using the Dubinin-Radushkevitch (D-R) equation [30] .
- 2.3. Elemental mercury removal efficiency
The reactor, with a 12.7 mm diameter and made of quartz, was placed inside a temperature-controllable tubular furnace which was heated to a temperature of 70℃. For every experiment, 1.0 g of sample materials were loaded and packed inside a quartz tube. A carrier gas was fed into the adsorption apparatus at a flow rate of 100 mL/min. Elemental mercury gas was generated from elemental mercury permeation tubes (Dynacalibrator ® Model 150; VICI Metronics Inc., USA), and the concentration of the elemental mercury gas was maintained at 700 ppm during the experimental process. Measurements of both the inlet and outlet concentrations of the elemental mercury were done using a mercury analyzer (VM-3000; Mercury Instruments, Germany), and sulfur was used to capture the elemental mercury from the effluent gas.
3. Results and Discussion
Fig. 1 shows high-resolution scanning electron microscope images of the NPCs as a function of the activation temperature. An obvious hexagonal arrangement of the mesopores is observed for all samples, suggesting that an ordered mesostructure is maintained.
PPT Slide
Lager Image
Scanning electron microscope images of the nanoporous carbons (NPCs) as a function of the activation temperature: (a) NPCs, (b) NPCs-900.
Good understanding of the porosity and the specific surface area of an adsorbent can be achieved by constructing an adsorption isotherm of N 2 . Fig. 2 shows the N 2 adsorption isotherms of the NPCs as a function of the activation temperature. All carbons show type IV adsorption isotherms, indicating the presence of a well-developed mesoporous structure. The capillary condensation steps are nearly perpendicular to the relative pressure axis, suggesting high uniformity of the mesopores. The isotherm has a sharp slope at a relative pressure of 0 to 0.1, which can be attributed to the presence of micropores, and a small slope at a relative pressure of 0.4 to 0.8, which indicates a broad pore-size distribution in the mesopore range. This is identified as a slow rate of increase in N 2 uptake at a low relative pressure, correand sponding to monolayer-multilayer adsorption on the pore walls. Additionally, the capillary condensation step became slightly broader, implying some minor deterioration of the mesopore structure.
PPT Slide
Lager Image
Adsorption isotherms of N2/77 K on the nanoporous carbons (NPCs) as a function of the activation temperature.
Table 1 lists detailed information of the textural properties of the samples from the N 2 /77 K adsorption isotherms. The NPC sample had a specific surface area of 589 m 2 /g, a total pore volume of 0.510 cm 2 /g and a micropore volume of 0.328 cm 2 /g. The activated samples manifested an increasing specific surface area and increasing total and micropore volumes as the activation temperature increased. This suggests that higher CO 2 activation temperatures definitely alter both types of pores, as reflected by the high surface area and total pore volume.
Textural properties of the NPCs as a function of the activation temperature
PPT Slide
Lager Image
NPCs: nanoporous carbons.
Fig. 3 shows the elemental mercury removal efficiency of the ordered NPCs. All tests were conducted at 70℃ for 90 min in an elemental mercury adsorption apparatus. Normally, gas adsorption depends strongly on the specific surface area and pore volume of the adsorbents. The NPCs showed only a low elemental mercury adsorption rate of 8 ppm at 90 min. Meanwhile, the elemental mercury removal efficiency of the CO 2 -activated NPCs was higher than that of the NPCs due to the clearly higher specific surface area and micro-/mesopore ratio. In conclusion, the optimal materials for mercury vapor adsorption possess the following attributes: 1) a high-specific surface area, and 2) a high-micropore fraction.
PPT Slide
Lager Image
Elemental mercury removal of the nanoporous carbons (NPCs) as a function of the activation temperature.
In this work, we investigated the synthesis of phenolic resin- based carbons by a combination of templating followed by post-synthesis activation in an effort to enhance the elemental mercury adsorption behaviors. The results of this study indicate that CO 2 activation offers high elemental mercury removal efficiency of ordered NPCs. We can conclude this work by stating that mercury vapor adsorptions rates can be optimized in terms of the specific surface area and micropore fraction.
This work is supported by the Carbon Valley Project of the Ministry of Knowledge Economy, Korea.
Darbha GK , Singh AK , Rai US , Yu E , Yu H , Chandra Ray P 2008 Selective detection of mercury (II) ion using nonlinear optical properties of gold nanoparticles J Am Chem Soc 130 8038 -    DOI : 10.1021/ja801412b
An J , Shang K , Lu N , Jiang Y , Wang T , Li J , Wu Y 2014 Performance evaluation of non-thermal plasma injection for elemental mercury oxidation in a simulated flue gas J Hazard Mater 268 237 -    DOI : 10.1016/j.jhazmat.2014.01.022
Kim BJ , Bae KM , Park SJ 2012 Elemental mercury vapor adsorption of copper-coated porous carbonaceous materials Microporous Mesoporous Mater 163 270 -    DOI : 10.1016/j.micromeso.2012.05.038
Du W , Yin L , Zhuo Y , Xu Q , Zhang L , Chen C 2014 Catalytic oxidation and adsorption of elemental mercury over CuCl2-impregnated sorbents Ind Eng Chem Res 53 582 -    DOI : 10.1021/ie4016073
Bae KM , Kim BJ , Rhee KY , Park SJ 2014 Roles of metal/activated carbon hybridization on elemental mercury adsorption J Nanosci Nanotechnol 14 5811 -    DOI : 10.1166/jnn.2014.8459
Hou W , Zhou J , Yu C , You S , Gao X , Luo Z 2014 Pd/Al2O3 Sorbents for elemental mercury capture at high temperatures in syngas Ind Eng Chem Res 53 9909 -    DOI : 10.1021/ie501292a
Im JS , Park SJ , Lee YS 2007 Preparation and characteristics of electrospun activated carbon materials having meso- and macropores J Colloid Interface Sci 314 32 -    DOI : 10.1016/j.jcis.2007.05.033
Horowitz HM , Jacob DJ , Amos HM , Streets DG , Sunderland EM 2014 Historical mercury releases from commercial products: global environmental implications Environ Sci Technol. 48 10242 -    DOI : 10.1021/es501337j
Hu Y , Wen Z , Wu X , Jin J 2012 Low-cost shape-control synthesis of porous carbon film on β″-alumina ceramics for Na-based battery application J Power Sources 219 1 -    DOI : 10.1016/j.jpowsour.2012.07.025
Kim BJ , Lee YS , Park SJ 2008 A study on the hydrogen storage capacity of Ni-plated porous carbon nanofibers Int J Hydrogen Energy 33 4112 -    DOI : 10.1016/j.ijhydene.2008.05.077
Kim S , Park SJ 2006 Effects of chemical treatment of carbon supports on electrochemical behaviors for platinum catalysts of fuel cells J Power Sources 159 42 -    DOI : 10.1016/j.jpowsour.2006.04.041
Fu Y , Ming H , Zhou Q , Jin L , Li X , Zheng J 2014 Nitrogen-doped carbon coating inside porous TiO2 using small nitrogen-containing molecules for improving performance of lithium-ion batteries Electrochim Acta 134 478 -    DOI : 10.1016/j.electacta.2014.04.130
Park SJ , Jang YS , Shim JW , Ryu SK 2003 Studies on pore structures and surface functional groups of pitch-based activated carbon fibers J Colloid Interface Sci 260 259 -    DOI : 10.1016/S0021-9797(02)00081-4
Park SJ , Kim BJ 2005 Ammonia removal of activated carbon fibers produced by oxyfluorination J Colloid Interface Sci 291 597 -    DOI : 10.1016/j.jcis.2005.05.012
Belhachemi M , Jeguirim M , Limousy L , Addoun F 2014 Comparison of NO2 removal using date pits activated carbon and modified commercialized activated carbon via different preparation methods: effect of porosity and surface chemistry Chem Eng J 253 121 -    DOI : 10.1016/j.cej.2014.05.004
Park SJ , Kim KD 1999 Adsorption behaviors of CO2 and NH3 on chemically surface-treated activated carbons J Colloid Interface Sci 212 186 -    DOI : 10.1006/jcis.1998.6058
Lee HM , Kim HG , An KH , Kim BJ 2014 Effects of pore structures on electrochemical behaviors of polyacrylonitrile-based activated carbon nanofibers by carbon dioxide activation Carbon Lett 15 71 -    DOI : 10.5714/CL.2014.15.1.071
Park SJ , Kim KD 2001 Influence of activation temperature on adsorption characteristics of activated carbon fiber composites Carbon 39 1741 -    DOI : 10.1016/S0008-6223(00)00305-5
Kim BJ , Lee YS , Park SJ 2008 Novel porous carbons synthesized from polymeric precursors for hydrogen storage Int J Hydrogen Energy 33 2254 -    DOI : 10.1016/j.ijhydene.2008.02.019
Park SJ , Kim BJ 2004 Influence of oxygen plasma treatment on hydrogen chloride removal of activated carbon fibers J Colloid Interface Sci 275 590 -    DOI : 10.1016/j.jcis.2004.03.011
Im JS , Kwon O , Kim YH , Park SJ , Lee YS 2008 The effect of embedded vanadium catalyst on activated electrospun CFs for hydrogen storage Microporous Mesoporous Mater 115 514 -    DOI : 10.1016/j.micromeso.2008.02.027
Adelodun AA , Lim YH , Jo YM 2014 Surface oxidation of activated carbon pellets by hydrogen peroxide for preparation of CO2 adsorbent J Ind Eng Chem 20 2130 -    DOI : 10.1016/j.jiec.2013.09.042
Babel K , Janasiak D , Jurewicz K 2012 Electrochemical hydrogen storagein activated carbons with different pore structures derived from certain lignocellulose materials Carbon 50 5017 -    DOI : 10.1016/j.carbon.2012.06.030
Park SJ , Park BJ , Ryu SK 1999 Electrochemical treatment on activated carbon fibers for increasing the amount and rate of Cr(VI) adsorption Carbon 37 1223 -    DOI : 10.1016/S0008-6223(98)00318-2
Kubota M , Hata A , Matsuda H 2009 Preparation of activated carbon from phenolic resin by KOH chemical activation under microwave heating Carbon 47 2805 -    DOI : 10.1016/j.carbon.2009.06.024
Bansal RC , Goyal M 2005 Activated Carbon Adsorption Taylor & Francis Boca Raton, FL
Tang L , Yang GD , Zeng GM , Cai Y , Li SS , Zhou YY , Pang Y , Liu YY , Zhang Y , Luna B 2014 Synergistic effect of iron doped ordered mesoporous carbon on adsorption-coupled reduction of hexavalent chromium and the relative mechanism study Chem Eng J 239 114 -    DOI : 10.1016/j.cej.2013.10.104
Peng X , Hu X , Fu D , Lam FLY 2014 Adsorption removal of acid black 1 from aqueous solution using ordered mesoporous carbon Appl Surf Sci 294 71 -    DOI : 10.1016/j.apsusc.2013.11.157
Brunauer S , Emmett PH , Teller E 1938 Adsorption of gases in multimolecular layers J Am Chem Soc 60 309 -    DOI : 10.1021/ja01269a023
Dubinin MM , Plavnik GM 1968 Microporous structures of carbonaceous adsorbents Carbon 6 183 -    DOI : 10.1016/0008-6223(68)90302-3