Facile preparation of self-assembled wool-based graphene hydrogels by electron beam irradiation
Facile preparation of self-assembled wool-based graphene hydrogels by electron beam irradiation
Carbon letters. 2014. Apr, 15(2): 136-141
Copyright © 2014, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : March 03, 2014
  • Accepted : March 03, 2014
  • Published : April 30, 2014
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Mira Park
Department of Organic Materials and Fiber Engineering, Chonbuk National University, Jeonju 561-756, Korea
Bishweshwar Pant
Department of BIN Fusion Technology, Chonbuk National University, Jeonju 561-756, Korea
Jawun Choi
Department of BIN Fusion Technology, Chonbuk National University, Jeonju 561-756, Korea
Yong Wan Park
Korea Institute for Knit Industry, Iksan 570-330, Korea
Chohye Lee
Department of BIN Fusion Technology, Chonbuk National University, Jeonju 561-756, Korea
Hye Kyoung Shin
Department of Chemistry, Inha University, Incheon 402-751, Korea
Soo-Jin Park
Department of Chemistry, Inha University, Incheon 402-751, Korea
khy@jbnu.ac.kr
Hak-Yong Kim
Department of BIN Fusion Technology, Chonbuk National University, Jeonju 561-756, Korea
khy@jbnu.ac.kr
Abstract
Three dimensional self-assembled graphene hydrogels were easily fabricated by electron beam irradiation (EBI) using an aqueous solution of wool/poly(vinyl alcohol) and graphene oxide (GO). After exposure to various levels of EBI radiation, the highly porous, self-assembled, wool-based graphene hydrogels were characterized using scanning electron microscopy and Fourier-transform infrared spectroscopy; to determine the gel fraction, degree of swelling, gel strength, kinetics-of-swelling analyses and removal of hexavalent chromium (Cr(VI)) from the aqueous solution. X-ray diffraction results confirmed that EBI played a significantly important role in reducing GO to graphene. The adsorption equilibrium of Cr(VI) was reached within 80 min and the adsorption capacity was dramatically increased as the acidity of the initial solution was decreased from pH 5 to 2. Changes in ionic strength did not exert much effect on the adsorption behavior.
Keywords
1. Introduction
Graphene is a two-dimensional, one-atom-thick honeycomb lattice sheet of sp 2 carbon atoms. Since the discovery and subsequent development of graphene [1 , 2] , tremendous research has been focused on it due to its large theoretical specific-surface area, strong mechanical properties, excellent thermal and electrical conductivity, and relatively low density [3] . Furthermore, self-assembly is a promising strategy for fabricating graphene-based carbon materials for sensors and catalysis, as well as for energy storage and conversion. Two dimensional (2D) self-assembly of functionalized graphene has been accomplished by means of flow-directed self-assembly [4] , evaporation-induced self-assembly [5] , the Langmuir-Blodgett technique [6] , and layer-by-layer deposition [7] . Recently, 3D carbon aerogels have been obtained by simple assembly of graphene oxide (GO) sheets [8 , 9] . Compared to traditional carbon aerogels, graphene-based aerogels exhibit ultralow density, high surface area and a very highly porous structure. Typical graphene/carbon composite aerogels were obtained by pyrolysis at 900℃ for 2 h after typical synthesis of polymer solution at 180℃ for 24 h and freeze-drying of the resulting hydrogels [8 , 9] . Making such freeze-dried, pyrolyzed products is time-consuming and requires an expensive process. Of unusual interest is a report of a process using electron beam irradiation (EBI) techniques that provided products that were nontoxic (without post-processing), used an environmentally friendly procedure, and exhibited the combined effects of cross-linking and sterilization [10] . Moreover, the EBI technique is also useful for modifying the physico-chemical properties of carbon materials. For instance, Park et al. [11] reported that the EBI exposures (50 kGy) resulted in the D to G band intensity ratio of 1.01 (I D /I G ) due to the transformation of graphene from the nanocrystalline to the amorphous form. Finally, although reports on poly(vinyl alcohol)-blended hydrogels are numerous, to date, there are only a few reports on wasted-wool-based hydrogels.
Here we report the preparation of self-assembled, wool-based graphene hydrogels as a 3D structure for graphene-based materials. We also report the results of our study of the corresponding mechanical properties, gel fraction, swelling behavior, and hexavalent chromium (Cr(VI)) removal from aqueous solution. We attempted to save time and costs in producing hydrogels using EBI. Properties of self-assembled graphene hydrogels are rarely studied, so this information is of great interest for developing preparations of promising, environmentally friendly, lowcost graphene hydrogels.
2. Experimental
- 2.1. Materials
Urea, sodium disulfite (Na 2 S 2 O 5 ), sodium dodecyl sulfate (SDS), acetone (CH 3 COCH 3 ), ethanol (C 2 H 5 OH), poly(ethylene imine) (PEI, branched, average M n ~10 000 by gel permeation chromatography, average M w ~25 000 g/mol by light scattering), PVA (Mw = 85 000-124 000 g/mol, 87-89% hydrolyzed) and potassium dichromate (K 2 Cr 2 O 7 ) were purchased from the Sigma Aldrich, Co. (St. Louis, MO, USA). Wasted wool (Merino) was obtained from local bedding factories for free. Disposable sterilized polystyrene square dishes (125 × 125 × 20 mm) were purchased from SPL Life Sciences Co., Republic of Korea.
- 2.2. Keratin extraction method (S-sulfo keratin)
The wool was vigorously washed with water containing 0.5% SDS, rinsed and then air-dried. Keratin was extracted by sulfitolysis [12 , 13] . The wasted wool was then extracted using a Soxhlet apparatus and the dried-wool samples (150 g each) were cut into snippets of a few millimeters each, and then placed into 1.5 liters of an aqueous solution containing 8 M urea, 75 g of SDS and 150 g of Na 2 S 2 O 5 . The mixture was heated to 100℃, shaken for 30 min and then filtered through a stainless-steel mesh with pore sizes of 75 μm. The filtrate (molecular-weight cutoff of 12 000 Da) was dialyzed using 15 liters of water that contained 0.1 wt% Na 2 S 2 O 5 , using cellulose tubing, for 3 days at 25℃.
- 2.3. Synthesis of GO
GO was synthesized by a modified Hummers method [14] . Four grams of graphite flakes were added to a 250 mL flask containing 120 mL of H 2 SO 4 , which was then stirred for 1 h. Fifteen grams of KMnO 4 was gradually added to the mixture at intervals of 20 min (nine times). The mixture was slowly heated to 40℃, and then maintained for 5 h in order to oxidize the graphite. Next, 150 mL of deionized (DI) water was added to the system. Finally, 15 mL of H 2 O 2 solution was added to the mixture, stirred for 30 min, and then left in this condition for 24 h, after which it was centrifuged.
- 2.4. Preparation of wool-based graphene hydrogels
Hydrogels that contained the prepared keratin protein (5 wt%), PVA (5 wt%), GO (3 wt%), and DI water were produced in the form of a sheet (125 × 125 × 5 mm). To improve the gelation, 0.01 wt% PEI was included in the wool-PVAGO solution. Afterwards, the polymer solution was poured into the square dishes, and the dishes were irradiated with an electron-beam at a dose of 10-60 kGy. The irradiation of the samples was performed using an electron beam accelerator (beam energy 2.5 MeV, beam current 8.5 mA, irradiation width 110 cm, conveyor velocity 10 m/min, dose rate 6.67 kGy/s, and roller type handling system, EBTECH Co., Ltd., Korea) at room temperature, in air. The specific energy (SE) requirement in kilojoules per kilogram (kJ/kg) was equal to the dose in kilogray, as follows:
PPT Slide
Lager Image
- 2.5. Gel strength
The tensile-strength-at-rupture and elongation-at-break were measured using a universal test machine (Lloyd, US/LRIOK) according to the ASTM D882 standard method. The data were transferred to a computer to evaluate the stress-strain curve. The gel strength was calculated using Eq. (2) [13] .
PPT Slide
Lager Image
- 2.6. Gel fraction
The sample was dried at 60℃ for 48 h to reach a constant weight (A) and then boiled in double-distilled water for 5 min before being dried again to a constant weight (B). The % gel fraction was calculated using Eq. (3).
PPT Slide
Lager Image
- 2.7. Degree of swelling
The sample was weighed (w 1 ), and placed in distilled water for 72 h, weighed (w 2 ), dried, and weighed (w 3 ) again. The % water uptake was calculated using Eq. (4).
PPT Slide
Lager Image
- 2.8. Cr(VI) adsorption experiments
K 2 Cr 2 O 7 was used as the source of Cr(VI). Hydrogel (300 mg) was put into a vial containing 30 mL 200 ppm Cr(VI) solution, varying the pH for 12 h. Adjustment of the pH of the Cr(VI) solutions was done using 0.2 M HCl or 0.2 M NaOH. The removal percentage of Cr(VI) was calculated using Eq. (5), where C 0 is the initial concentration of Cr(VI) in solution (mg/L), and C e is the equilibrium concentration (mg/L).
PPT Slide
Lager Image
The kinetic adsorption was determined by taking out 0.1- mL samples of the Cr(VI) solution at different times, for each of which the adsorption capacity was calculated using Eq. (6); where Q t is the adsorption capacity at time t, C 0 is the initial concentration of Cr(VI) in solution (mg/L), C t is the concentration at time t (mg/L), m is mass of adsorbent (g), and V is the volume of solution (L). All experiments were performed at 25℃.
PPT Slide
Lager Image
- 2.8. Characterization
The changes in the functional groups of the hydrogels were evaluated using Fourier-transform infrared spectroscopy (FTIR, Varian 1000 FT-IR Scimitar series; PIKE Technologies, USA) on freeze-dried samples. Freeze-dried hydrogel samples were coated with platinum (ion-sputter, Hitachi E-1010, Japan) under vacuum, and were used to investigate the morphology of the keratin protein hydrogels using a Jeol JSM-5900 scanning electron microscopy (SEM). The crystal structure of the hydrogels was estimated using X-ray diffraction (XRD, Rigaku D/ max-2500) with Cu K α radiation (40 kV, 250 mA). The removal of Cr(VI) was performed by atomic absorption spectrometry (AAS, Perkin-Elmer 3110).
3. Results and Discussion
- 3.1. FT-IR study of the hydrogels
Fig. 1 presents the FT-IR spectra of GO, wool, PVA, wool/ PVA hydrogels and wool/PVA/GO hydrogels. GO has hydroxyl (at 1049 and 3386 cm −1 ) and ether groups on both sides, with carboxyl groups (at 1736 cm −1 ) on the edge. At 1624 cm −1 , the peak indicated unoxidized graphitic domains in GO, or the stretching vibrations of the C=C bond. Typical, characteristic peaks of keratin proteins were observed, including those indicating the elastic vibration of the C=O bond at 1625 cm −1 and the bending deformation of the C-N-H bond at 1520 cm −1 [15] . A broad band that appeared at 2900-3700 cm −1 belonged to OH groups, and bands of carboxyl and carbonyl groups were also observed at 1736 cm −1 and 1,616 cm −1 , respectively [16] . Comparison of wool/PVA and wool/PVA/GO hydrogels, revealed that the locations of peaks for C–H stretching (2920 cm −1 ), –OH and –NH 2 (3700-3000 cm −1 ), and C=O stretching (1637 cm −1 ) in NHCO– were similar, and that most of the peaks compared were not significantly different. After adding GO to the polymer solution, the peaks for the oxygen functional groups did not increase and the peak at 1414 cm −1 , corresponding to carboxy C–O, was almost eliminated by the EBI treatment. Furthermore, the peak at 1736 cm −1 for the wool/PVA/GO hydrogels decreased. These findings suggested that the functional groups of GO reacted with protein chains and played an important role in reducing GO to graphene when subjected to EBI.
PPT Slide
Lager Image
Fourier-transform infrared spectra of graphene oxide (GO), poly(vinyl alcohol) (PVA), wool, wool/PVA and wool/PVA/GO hydrogels prepared at a dose of 30 kGy in the presence of poly(ethylene imine).
- 3.2. Characterization of the hydrogels
The mechanical properties, gel fraction, and degree-of-swelling of the wool-based graphene hydrogels, and wool-based hydrogels, are shown in Table 1 . The mechanical properties and water-absorption ratio of the hydrogels are normally influenced by the degree of cross-linking. The wool-based graphene hydrogels exhibited higher gel strength compared to wool-based hydrogels, when subjected to EBI doses of 20 kGy, with the highest gel strength of 689 g·cm observed at an EBI dose of 30 kGy. The gel strength of the wool/PVA/ GO hydrogels decreased as the EBI dose was increased from 30 to 60 kGy. The gel strength of the wool/PVA hydrogels decreased starting at a lower EBI dose (20 to 60 kGy). In our previous work [13] , we observed that keratin-based/PVA hydrogels prepared using EBI exhibited a superior degree of swelling behavior, not only due to the considerable number of hydrophilic components produced upon irradiation (chemical water absorption), but also due to the highly porous structures (physical water absorption). Covalent cross-linking and physical cross-linking probably occurred coincidentally among the S-sulfo keratin main chains, oxygen groups in the PVA aqueous solution, GO, and amine groups of the PEI. Between the polymer chains, radicals were formed via direct or indirect reactions to the radiation, and to solvent-derived radicals. The gel fraction of the wool/PVA/GO hydrogels increased as the EBI dose was increased to 40 kGy, indicating a constant degree of cross-linking. The wool/PVA hydrogels presented probable predominating scission reactions, over cross-linking reactions, at EBI doses above 40 kGy.
Characterization of wool-based graphene hydrogels and wool-based hydrogels prepared using EBI at various radiation doses
PPT Slide
Lager Image
EBI: electron beam irradiation. a)One kilogray (kGy) = 1 kilojoule (kJ)/kilogram (kg). b)Gel strength (g·cm) = tensile strength at rupture × elongation at break. c)% gel fraction = (B/A) × 100. d)% degree of swelling = {(w2-w3)/w1} × 100.
- 3.3. Surface morphology and structural analysis of hydrogels
SEM images of the freeze-dried hydrogels produced from wool solutions blended with PVA and GO, in the presence of PEI, and at a dose of 30 kGy; were exhibited in Fig. 2 . As seen in Fig. 2a , the freeze-dried wool/PVA/GO hydrogels clearly exhibited a more porous structure than the wool/PVA hydrogels. Furthermore, the wool/PVA/GO hydrogels also exhibited a considerably larger pore size than that of the wool/PVA hydrogels. A number of the physico-chemical properties (e.g., the gel fraction, degree of swelling, gel strength, and swelling kinetics) of the resulting hydrogels can be influenced by pore size [13] . The types and amounts of protein have probably influenced the morphological properties of the resulting hydrogels. Higher swelling capacities and higher swelling rates are required in practical applications. The swelling kinetics in water of wool/ PVA/GO and wool/PVA hydrogels is represented in Fig. 2c . The freeze-dried wool/PVA/GO hydrogels absorbed distilled water rapidly (more than 28 g/g within 2000 min) and then reached a plateau, whereas wool/PVA hydrogels absorbed approximately 25 g/g in the same time. The swelling kinetics of superabsorbent polymers is influenced by the smaller pore size of the absorbents. However, the swelling behavior of the wool/PVA/GO and wool/PVA hydrogels was dominated by larger pore size after 30 min. This finding suggests that wool/PVA/GO hydrogels have the potential for practical applications because of their excellent swelling capacity and swelling kinetics. To further explore the structural changes of the distance of layers, a series of XRD analyses were carried out and the results presented in Fig. 2d . For the GO sample, an intense and sharp diffraction peak shows at 2θ = 10.6°, corresponding to the (001) reflection [17] . Wool has a broad peak at 2θ = 20.2°, and typical PVA at 2θ = 19.5°. The XRD pattern of wool/PVA/GO hydrogels was similar to those of wool/PVA hydrogels, while the peaks characteristic of GO completely disappeared. A broad diffraction peak at around 2θ = 21°, and a very weak peak at 2θ = 44° corresponding to the (100), suggested significant changes in the crystal structure of GO and confirmed again the reduction of GO. This is in accordance with the above FT-IR results for self-assembled, woolbased graphene hydrogels.
PPT Slide
Lager Image
Scanning electron microscopy micrographs of freeze-dried hydrogels produced from: (a) wool, and (b) wool/graphene oxide (GO) solutions blended with poly(vinyl alcohol) (PVA, keratin/PVA = 50/50, w/w) at a dose of 30 kGy, in the presence of poly(ethylene imine) (0.01 wt%); (c) swelling kinetics in water of wool/PVA and wool/PVA/GO hydrogels; and (d) X-ray diffraction patterns of samples. The inset shows photographs of hydrogels.
- 3.4. Removal of Cr(VI) by self-assembled, wool-based graphene hydrogels
A hypothetical schematic is presented in Fig. 3a . Wool comprises a three-dimensional mesh structure of keratin, which is composed of polypeptides with different amino acids, with inter- molecular bonding by disulfide cystine amino acids. Sulfur side-chains on the cysteine molecules after sulfitolysis of wool were bonded to another cysteine by the EBI. A slight shift of the typical absorption peaks for the C=O and C-N-H bonds showed in the FT-IR spectra of the self-assembled, wool-based graphene hydrogels, due to intermolecular interactions and cross-linking reactions [13] . In Fig. 3b , the effect of pH on the adsorption of Cr(VI) is significant, and is possibly due to the amine groups in self-assembled, wool-based graphene hydrogels [18] . At pH 2.0-6.0, the predominant Cr(VI) species initially exists in the monovalent (HCrO 4 ) form; then is gradually converted to the divalent (CrO 4 2− ) form by the increased pH. As the pH increased, the uptake of Cr(VI) ions decreased because the higher concentration of OH- ions present in the aqueous solution competed with the Cr(VI) species (CrO 4 2− ) for the adsorption sites [18] . By adjusting the initial pH to 2.0 before adsorption, and by varying the concentration of NaCl, the effect of ionic strength on the adsorption of Cr(VI) by self-assembled, wool-based graphene hydrogels was studied. The results are presented in Fig. 3c . The adsorption capacity remained approximately 82%, whether with no NaCl or with 0.1 mol/L NaCl. That is to say, the effect of ionic strength was not very great. The Cr(VI) adsorption kinetics, of hydrogels at pH 2.0, are shown in Fig. 3d . The adsorption capacity of Cr(VI) increased according to the adsorption time and concentrations of Cr(VI) solution. The equilibrium capacity was 29, 41, and 49 mg/g for 100, 200, and 300 mg/L of initial Cr(VI) solution, respectively. After 12 h, the color of the Cr(VI) aqueous solution changed from yellow to colorless.
PPT Slide
Lager Image
Role and effects of Cr(VI): (a) schematic representation of its adsorption, (b) effect of pH on its removal, (c) effect of ionic strength on its removal performance, and (d) effect of contact time and initial concentration on its adsorption (at 25℃, pH 2) of self-assembled graphene hydrogels.
4. Conclusions
Here, we reported the preparation of self-assembled, woolbased graphene hydrogels to save time and costs in producing hydrogels. Promising, environmentally friendly, low-cost graphene hydrogels were successfully prepared by means of EBI and then used as an adsorbent for Cr(VI) ions from aqueous solution. The resulting self-assembled graphene hydrogels exhibit fibrous and highly porous morphologies and graphene structures, qualities confirmed by SEM and XRD analyses. These findings are in good agreement with the results of the FT-IR analysis. Such an EBI-induced self-assembly process for producing graphene offers a more convenient, more environmentally friendly and less expensive technique for large-scale applications.
Acknowledgements
This work was supported by a National Research Foundation of Korea (NRF) grant funded by the Korea government (Ministry of Education, Science and Technology, MEST, No. 2012R1A2A2A01046086). This work was also financially supported by MEST and NRF through the Human Resource Training Project for Regional Innovation (No. 201210A0404613010100).
References
Novoselov KS , Geim AK , Morozov SV , Jiang D , Zhang Y , Dubonos SV , Grigorieva IV , Firsov AA 2004 Electric field effect in atomically thin carbon films Science http://dx.doi.org/10.1126/science.1102896 306 666 -
Geim AK , Novoselov KS 2007 The rise of graphene Nat Mater http://dx.doi.org/10.1038/nmat1849 6 183 -
Geim AK 2009 Graphene: status and prospects Science http://dx.doi.org/10.1126/science.1158877 324 1530 -
Chen H , Muller MB , Gilmore KJ , Wallace GG , Li D 2008 Mechanically strong, electrically conductive, and biocompatible graphene paper Adv Mater http://dx.doi.org/10.1002/adma.200800757 20 3557 -
Chen C , Yang QH , Yang Y , Lv W , Wen Y , Hou PX , Wang M , Cheng HM 2009 Self-assembled free-standing graphite oxide membrane Adv Mater http://dx.doi.org/10.1002/adma.200803726 21 3007 -
Li X , Zhang G , Bai X , Sun X , Wang X , Wang E , Dai H 2009 Highly conducting graphene sheets and Langmuir-Blodgett films Nat Nanotechnol http://dx.doi.org/10.1038/nnano.2008.210 3 538 -
Shen JF , Hu YZ , Li C , Qin C , Shi M , Ye MX 2009 Layer-by-layer self-assembly of graphene nanoplatelets Langmuir http://dx.doi.org/10.1021/la900126g 25 6122 -
Hu H , Zhao Z , Wan W , Gogotsi Y , Qiu J 2013 Ultralight and highly compressible graphene aerogels Adv Mater http://dx.doi.org/10.1002/adma.201204530 25 2219 -
Qian Y , Ismail IM , Stein A 2014 Ultralight, high-surface-area, multifunctional graphene-based aerogels from self-assembly of graphene oxide and resol Carbon http://dx.doi.org/10.1016/j.carbon.2013.10.082 68 221 -
Abad LV , Relleve LS , Aranilla CT , Dela Rosa AM 2003 Properties of radiation synthesized PVP-kappa carrageenan hydrogel blends Radiat Phys Chem http://dx.doi.org/10.1016/S0969-806X(03)00164-6 68 901 -
Park M , Shin HK , Kim BS , Pant B , Barakat NAM , Kim HY 2013 Facile preparation of graphene induced from electron-beam irradiated graphite Mater Lett http://dx.doi.org/10.1016/j.matlet.2013.04.027 105 236 -
Aluigi A , Vineis C , Varesano A , Mazzuchetti G , Ferrero F , Tonin C 2008 Structure and properties of keratin/PEO blend nanofibres Eur Polym J http://dx.doi.org/10.1016/j.eurpolymj.2008.06.004 44 2465 -
Park M , Kim BS , Shin HK , Park SJ , Kim HY 2013 Preparation and characterization of keratin-based biocomposite hydrogels prepared by electron beam irradiation Mater Sci Eng C http://dx.doi.org/10.1016/j.msec.2013.08.032 33 5051 -
Hummers WS, Jr. , Offeman RE 1958 Preparation of graphitic oxide J Am Chem Soc http://dx.doi.org/10.1021/ja01539a017 80 1339 -
Cardamone JM 2010 Investigating the microstructure of keratin extracted from wool: peptide sequence (MALDI-TOF/TOF) and protein conformation (FTIR) J Mol Struct http://dx.doi.org/10.1016/j.molstruc.2010.01.048 969 97 -
Li R , Liu C , Ma J 2011 Studies on the properties of graphene oxide-reinforced starch biocomposites Carbohydr Polym http://dx.doi.org/10.1016/j.carbpol.2010.12.041 84 631 -
Zhang K , Zhang LL , Zhao XS , Wu J 2010 Graphene/polyaniline nanofiber composites as supercapacitor electrodes Chem Mater http://dx.doi.org/10.1021/cm902876u 22 1392 -
Hu J , Chen G , Lo IM 2005 Removal and recovery of Cr(VI) from wastewater by maghemite nanoparticles Water Res http://dx.doi.org/10.1016/j.watres.2005.05.051 39 4528 -