Effects of pore structures on electrochemical behaviors of polyacrylonitrile-based activated carbon nanofibers by carbon dioxide activation
Effects of pore structures on electrochemical behaviors of polyacrylonitrile-based activated carbon nanofibers by carbon dioxide activation
Carbon letters. 2014. Jan, 15(1): 71-76
Copyright © 2014, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : November 11, 2013
  • Accepted : December 12, 2013
  • Published : January 31, 2014
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Hye-Min Lee
Department of Carbon Fusion Engineering, Jeonju University, Jeonju 520-759, Korea
Hong-Gun Kim
Department of Carbon Fusion Engineering, Jeonju University, Jeonju 520-759, Korea
Kay-Hyeok An
R&D Division, Korea Institute of Carbon Convergence Technology, Jeonju 561-844, Korea
Byung-Joo Kim
R&D Division, Korea Institute of Carbon Convergence Technology, Jeonju 561-844, Korea
kimbj2015@gmail.com
Abstract
Activated carbon nanofibers (ACNF) were prepared from polyacrylonitrile (PAN)-based nanofibers using CO 2 activation methods with varying activation process times. The surface and structural characteristics of the ACNF were observed by scanning electron microscopy and X-ray diffraction, respectively. N 2 adsorption isotherm characteristics at 77 K were confirmed by Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. As experimental results, many holes or cavernous structures were found on the fiber surfaces after the CO 2 activation as confirmed by scanning electron microscopy analysis. Specific surface areas and pore volumes of the prepared ACNFs were enhanced within a range of 10 to 30 min of activation times. Performance of the porous PAN-based nanofibers as an electrode for electrical double layer capacitors was evaluated in terms of the activation conditions.
Keywords
1. Introduction
Electrochemical energy storage and conversion devices play an important role in modern society, with applications in accommodations, portable devices, transportation, the military and space exploration [1 , 2] . A supercapacitor is a kind of novel device that stores electrical energy in an electrode/electrolyte interface [3] . In a supercapacitor, an electrostatic attraction at the electrode/ electrolyte double-layer interface results in the accumulation of charges and stored energy. Supercapacitors are very useful for large-scale portable electronic systems and automotive applications, due to their high power density, excellent reversibility, and long cycle life.
In recent years, efforts to develop better supercapacitor electrode materials have gained considerable attention [4] . Carbon materials are widely used for supercapacitor electrodes because of their relatively low cost, versatile existing forms, large specific surface area, good electric conductivity, and excellent chemical stability [5] . Generally, a highly developed surface area and porosity are necessary for carbon electrodes to obtain high specific capacitance. For this reason, activated carbons (ACs) have been widely adopted as electrode materials for supercapacitors.
ACs have attracted wide interest as the electrode material for energy storage in supercapacitors due to their very high specific surface area, simple processability and low costs. Chemical [5 , 6] and physical [5] methods of carbon activation are well known and allow the production of materials which are well defined in terms of specific surface area and pore size distribution. When fibrous precursors are used, activated carbon fibers are obtained which exhibit high adsorption/desorption rates and narrow pore size distribution [5 , 6] .
Activated carbon nanofibers (ACNFs) are a relatively modern form of porous carbon material with a number of significant advantages over the more traditional powder or granular forms [7] . Advantages include high adsorption and desorption rates, thanks to the smaller fiber diameter and hence very low diffusion limitations, great adsorption capacities at low concentrations of adsorbates, and excellent flexibility [3] . Using fibrous materials is additionally profitable from the construction point of view.
CNFs have been receiving increasing attention because of their high length-to-diameter ratio and their potential applications in composite materials [8] , filters [9] , gas sensors [10] , anode materials for rechargeable batteries [11] , supercapacitors [3] , bottom-up assembly in nanoelectronics, and etc. Among the materials used in the preparation of CNFs, polyacrylonitrile (PAN) and its copolymers are recognized as the most promising precursors [5 , 6 , 10 , 12] . In general, a number of methods are available for the preparation of polymeric nanofibers, though the one most widely used is electrospinning.
Electrospinning of polymers is a very successful method for preparing fibers with nanometer sized diameters. The fibers can be electrospun in the form of yarn, aligned fibrous arrays, or webs. In particular, the electrospinning of PAN, followed by stabilization and carbonization, results in CNFs. PAN is often selected as the precursor because of its advantages, including good spinnability in solution and its relatively high carbon yield [13] .
The production of ACNFs involves spinning of the precursor fiber, stabilization of the precursor chemical structure under an oxidizing atmosphere, carbonization under an inert gas, and finally activation under an activating gas, such as CO 2 or H 2 O vapor (physical activation), or an oxidizing reagent such as KOH or ZnCl 2 (chemical activation) [5 , 6] .
Chemical or physical activation of PAN-based carbon materials has been already reported in the literature. The physical activation method involves carbonization of the raw material and its subsequent activation at high temperature in CO 2 or H 2 O vapor. The chemical activation method involves the carbonization of a raw material previously impregnated with a chemical agent.
In the case of chemical activation by ZnCl 2 or KOH, many by-products remain in the fibers. These activating agents are more expensive, and an additional washing stage is also necessary. Therefore, physical activation with CO 2 or H 2 O is the usual procedure to obtain ACNFs. It is known that physical activation using carbon dioxide results in a more homogeneous development of porosity within the carbon fibers than steam.
In the present study, we tried to develop activated carbons with a large specific surface area and optimal pore structures from PAN-based ACNFs through CO 2 activation. Various analytical techniques were utilized to investigate the morphology and material properties of the precursors and final nanofibers. Finally, an exploration of the properties of the ACNFs demonstrated the increased porosity and total surface area of the CNFs.
2. Experiment Details
- 2.1. CNF preparation
PAN (M w = 150 000) purchased from Sigma Aldrich Chemical Co. was used as the spinnable polymer for all precursor solutions. PAN precursor solutions of 10 wt% were prepared in N,N-dimethylformamide to obtain CNF materials denominated as PAN. After gentle stirring at room temperature for 7 h, these solutions were loaded into a 10 mL polypropylene syringe equipped with a stainless steel needle that was connected to the anode of a high voltage power supply. The conditions employed for electrospinning were 15 kV applied voltage, 15 cm tip-to-collector distance, and a flow rate of 0.5 mL/h. A grounded stainless steel roll wrapped with aluminum foil was employed as the collector. The nanofibers were stabilized in air at 280℃ and carbonized at 1000℃ in N 2 .
- 2.2. CO2activation
Activation of the CNFs was performed using CO 2 as the physical reagent. CO 2 activation was performed in the same quartz tube as the carbonization. The CNFs were heated (5℃/ min) to the required reaction temperature (1000℃) under N 2 (500 mL/min), before the N 2 was switched to CO 2 (500 mL/min) for various activation times, from 10 min to 40 min; the resulting samples were designated ACNF-10 to ACNF-40. The samples were allowed to cool under N 2 (500 mL/min).
- 2.3. Characterizations
The nitrogen adsorption isotherms of the CNFs and ACNFs were measured with BELSORP-max (BEL JAPAN, Japan) at liquid nitrogen temperature. All samples were degassed at 300℃ for 6 h prior to measurement. The specific surface area was calculated in the relative pressure interval of 0.04-0.2 using the Brunauer-Emmett-Teller method [14] . Micropore size was calculated by the Dubinin-Radushkevich equation from adsorption curves [15 , 16] . The d 002 space differences between pure CNFs and ACNFs were determined using a wide-angle X-ray diffractometer (WAXRD), employing a Rigaku SmartLab X-ray diffractor with a customized auto-mount and a Cu Kα radiation source. Diffraction patterns were collected within the diffraction angles from 10° to 90° with a speed of 2°/min. The morphologies of CNF, ACNF-10, ACNF-20, ACNF-30, and ACNF-40 were explored using a field emission scanning electron microscope (JSM 6701-F, JEOL, Japan). To reduce charging during scanning electron microscopy (SEM) imaging, the samples were first placed on a sample holder and coated with platinum.
- 2.4. Electrochemical measurements
Electrodes were prepared by mixing 80 wt% of carbon source, 10 wt% of conductive agents (carbon black), 10 wt% of carboxymethyl cellulose and styrene-butadiene rubber binder dispersed in isopropanol. The slurries were rolled into a membrane and then pressed onto Al mesh current collectors. Thereafter, the electrodes were dried at 120℃ for 24 h in an oven. A two-electrode configuration was used to measure electrochemical performance. Working electrodes were fabricated by pressing the ACNF-coated film between two circular pieces of Al mesh. An organic electrolyte (1 M (C 2 H 5 ) 4 NBF 4 /propylene carbonate) was used.
The fifth cycle of galvanostatic charge/discharge was used to evaluate the electrochemical performance of the samples. The specific capacitance was calculated according to the charge/discharge tests based on the following equation:
PPT Slide
Lager Image
where i is the discharge current (A), Δt is the discharge time (s), m is the mass of the electrode (g), and ΔV is the potential difference (V).
3. Results and Discussion
- 3.1. Surface morphology analysis
The external pore structure of the ACNFs was observed by SEM, and SEM images of all the ACNFs sample types are shown in Fig. 1 , in order by activation process time. Fig. 1 shows SEM images of CNF and its activated forms. The pores and cracks that developed on the surface due to activation can be seen in Figs. 1b - e . The average pore size of ACNF-10, ACNF- 20, ACNF-30, and ACNF-40 was increased by activation. Fig. 2a shows the average diameter of the CNFs, which was around 600-700 nm. The diameter of an ACNF decreased with increasing activation time. It was found that the diameter of the fibers decreased to around 500-700 nm as a result of surface oxidation during the CO 2 activation (40 min).
PPT Slide
Lager Image
Scanning electron microscopy micrographs of activated carbon nanofibers (ACNFs) with various activation times: (a) CNF, (b) ACNF-10, (c) ACNF-20, (d) ACNF-30, (e) ACNF-40.
PPT Slide
Lager Image
Diameter distribution of activated carbon nanofibers (ACNFs) with various activation times: (a) CNF, (b) ACNF-10, (c) ACNF-20, (d) ACNF-30, (e) ACNF-40.
- 3.2. Textural properties and pore structure
The specific surface area and pore structures of the activated carbons nanofibers before and after activation are shown in Table 1 . The specific surface area of the as-received carbon fibers (6 m 2 /g) increased with CO 2 activation (to 1530 m 2 /g). Based on the literature data [5 , 17] for PAN-based CNFs, it was expected that the specific surface area would increase with burn-off. However, when the activation time was 40 min, a significant decrease of specific surface area was observed, dropping to 1150 m 2 /g. The textural properties showed the highest result with ACNF 30 min and then deceased in all highly activated samples. The ACNF-30 sample showed better-developed mesopores than the ACNF-20 and ACNF-40 samples. This means that a moderate activation time results in large pore size.
Textural properties and specific capacitance of ACNFs as a function of activation time
PPT Slide
Lager Image
ACNFs: activated carbon nanofibers.SBET: specific surface area calculated using Brunauer-Emmett-Teller (BET) equation at a relative pressure range of 0.04-0.2.VTotal: total pore volume was estimated at a relative pressure P/P0 = 0.990.VMeso: mesopore volume determined from the subtraction of micropore volume from total pore volume.VMicro: (Dubinin-Radushkevich): DP: average pore diameter. EM: electrode mass.CP: specific capacitance.
Based on the SEM characterization, this trend may be explained as follows.
1) During the initial increase of activation time, micropores and/or mesopores with small pore diameters formed first as a result of the reaction between CO 2 and carbon. With increasing activation time, the quantity of the surface pores increased, leading to increased specific surface areas.
2) However, with further increasing activation time, the pores that developed in the initial stage started to deepen, enlarge, and perhaps merge, resulting in the observed decrease in the specific surface area and the increase in the average pore width.
- 3.3. XRD
ACNFs produced from nanofiber webs using CO 2 activation can be crystallographically characterized by means of XRD. The interlayer spacing, d 002 was determined using the following Bragg equation:
PPT Slide
Lager Image
where λ is the X-ray wavelength, and θ is the scattering angle for the peak position.
The XRD analysis was performed with CuK α with a wavelength of 0.154 nm. The values of d 002 of the prepared ACNFs are given in Fig. 3 . It is well-known that the oxidation behaviors of carbonaceous materials preferably occur in the amorphous region and graphite edges. If carbon atoms in the amorphous regions of the carbonized fibers are removed first, the overall crystallinity of the carbonized fibers can be increased due to the reduction of a portion of the amorphous regions, resulting in a decrease in the d 002 of activated fibers. There will be an expected increase of d 002 , if carbon atoms in graphite edges are removed after the oxidation of the amorphous regions. Therefore, considering that the sample carbonized fibers here were observed to decrease in d 002 at 30 min, it could be expected that the overall crystallinity of the carbonized fibers would increase due to the reduction of a portion of the amorphous region, resulting in the increase in specific surface area of the ACNFs. There was an expected increase of d 002 after 40 min. Consequently, carbon atoms at the edges of graphite had been oxidized as expected. Thus the d 002 values were slightly increased with a decrease in the specific surface area of all samples.
PPT Slide
Lager Image
d002 space difference of activated carbon nanofibers with various activation times.
- 3.4. Electrochemical characterizations
The electrochemical properties of the ACNF electrodes including galvanostatic charge/discharge were studied with an electrolyte of propylene carbonate solution. Fig. 4a shows the typical galvanostatic charge/discharge curves of the specific capacitance in relation to current density for ACNF electrodes prepared with various activation times. At a current density of 2 mA/g, the specific capacitance increased with increasing mesoporosity. Sample ACNF-30, with the highest mesoporosity, had the highest specific capacitance of 12.7 F/g.
PPT Slide
Lager Image
Charge/discharge curves of activated carbon nanofibers (ACNFs) with various activation times.
4. Conclusions
In this work, PAN-based ACNFs were prepared with different activation times in order to produce ACNFs with high specific surface areas and mesopore-rich pore structure. As a function of activation time, the specific surface area increased up to ACNF-30 min and then decreased, and mesopore volume showed a similar trend as well. The ACNF-30 sample showed the highest specific surface area because it had the highest mesoporosity.
Acknowledgements
This research was financially supported by the Jollabuk-do Provincial Government, Jeonbuk Technopark and the Ministry of Trade, Industry &Energy(MOTIE), Korea Institute for Advancement of Technology(KIAT) and Honam Institute for Regional Program Evaluation through the Leading Industry Development for Economic Region.
References
Lu X , Wang G , Zhai T , Yu M , Xie S , Ling Y , Liang C , Tong Y , Li Y 2012 Stabilized TiN nanowire arrays for high-performance and flexible supercapacitors Nano Lett http://dx.doi.org/10.1021/nl302761z 12 5376 -
Nyholm L , Nystrom G , Mihranyan A , Stromme M 2011 Toward flexible polymer and paper-based energy storage devices Adv Mater http://dx.doi.org/10.1002/adma.201004134 23 3751 -
Yu P , Li Y , Yu X , Zhao X , Wu L , Zhang Q 2013 Polyaniline nanowire arrays aligned on nitrogen-doped carbon fabric for high-performance flexible supercapacitors Langmuir http://dx.doi.org/10.1021/la402404a 29 12051 -
Hao L , Li X , Zhi L 2013 Carbonaceous electrode materials for supercapacitors Adv Mater http://dx.doi.org/10.1002/adma.201301204 25 3899 -
Lee HM , Kang HR , An KH , Kim HG , Kim BJ 2013 Comparative studies of porous carbon nanofibers by various activation methods Carbon Lett http://dx.doi.org/10.5714/CL.2013.14.3.180 14 180 -
Lee HM , Bae KM , Kang HR , An KH , Kim HG , Kim BJ 2013 Preparation and characterization of polyacrylonitrile-based porous carbon nanofibers activated by zinc chloride Appl Chem Eng 24 370 -
Kumagai S , Ishizawa H , Toida Y 2010 Influence of solvent type on dibenzothiophene adsorption onto activated carbon fiber and granular coconut-shell activated carbon Fuel http://dx.doi.org/10.1016/j.fuel.2009.08.013 89 365 -
Al-Saleh MH , Saadeh WH , Sundararaj U 2013 EMI shielding effectiveness of carbon based nanostructured polymeric materials: a comparative study Carbon http://dx.doi.org/10.1016/j.carbon.2013.04.008 60 146 -
Lim CS , Guzman M , Schaefer J , Minaie B 2013 Fabrication and properties of dense thin films containing functionalized carbon nanofibers Thin Solid Films http://dx.doi.org/10.1016/j.tsf.2013.02.010 534 111 -
Kim Y , Cho S , Lee S , Lee YS 2012 Fabrication and characterization of porous non-woven carbon based highly sensitive gas sensors derived by magnesium oxide Carbon Lett http://dx.doi.org/10.5714/CL.2012.13.4.254 13 254 -
Chen Y , Li X , Park K , Song J , Hong J , Zhou L , Mai YW , Huang H , Goodenough JB 2013 Hollow carbon-nanotube/carbon-nanofiber hybrid anodes for Li-ion batteries J Am Chem Soc http://dx.doi.org/10.1021/ja408421n 135 16280 -
Jain R , Chae HG , Kumar S 2013 Polyacrylonitrile/carbon nanofiber nanocomposite fibers Composites Sci Technol http://dx.doi.org/10.1016/j.compscitech.2013.08.036 88 134 -
Zhang L , Aboagye A , Kelkar A , Lai C , Fong H 2014 A review: carbon nanofibers from electrospun polyacrylonitrile and their applications J Mater Sci http://dx.doi.org/10.1007/s10853-013-7705-y 49 463 -
Brunauer S , Emmett PH , Teller E 1938 Adsorption of gases in multimolecular layers J Am Chem Soc http://dx.doi.org/10.1021/ja01269a023 60 309 -
Dubinin MM 1985 Generalization of the theory of volume filling of micropores to nonhomogeneous microporous structures Carbon http://dx.doi.org/10.1016/0008-6223(85)90029-6 23 373 -
Dubinin MM 1988 On methods for estimating micropore parameters of carbon adsorbents Carbon http://dx.doi.org/10.1016/0008-6223(88)90014-0 26 97 -
Wang MX , Huang ZH , Shimohara T , Kang F , Liang K 2011 NO removal by electrospun porous carbon nanofibers at room temperature Chem Eng J http://dx.doi.org/10.1016/j.cej.2011.01.017 170 505 -