Preparation and application of reduced graphene oxide as the conductive material for capacitive deionization
Preparation and application of reduced graphene oxide as the conductive material for capacitive deionization
Carbon letters. 2014. Jan, 15(1): 38-44
Copyright © 2014, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : November 08, 2013
  • Accepted : December 07, 2013
  • Published : January 31, 2014
Export by style
Cited by
About the Authors
Ayu Tyas Utami, Nugrahenny
Fuel Cell Research Center, Korea Institute of Energy Research, Daejeon 305-343, Korea
Jiyoung, Kim
Fuel Cell Research Center, Korea Institute of Energy Research, Daejeon 305-343, Korea
Sang-Kyung, Kim
Fuel Cell Research Center, Korea Institute of Energy Research, Daejeon 305-343, Korea
Dong-Hyun, Peck
Fuel Cell Research Center, Korea Institute of Energy Research, Daejeon 305-343, Korea
Seong-Ho, Yoon
Institute for Materials Chemistry and Engineering, Kyushu University, Kasuga, Fukuoka 816-8580, Japan
Doo-Hwan, Jung
Fuel Cell Research Center, Korea Institute of Energy Research, Daejeon 305-343, Korea

This paper reports the effect of adding reduced graphene oxide (RGO) as a conductive material to the composition of an electrode for capacitive deionization (CDI), a process to remove salt from water using ionic adsorption and desorption driven by external applied voltage. RGO can be synthesized in an inexpensive way by the reduction and exfoliation of GO, and removing the oxygen-containing groups and recovering a conjugated structure. GO powder can be obtained from the modification of Hummers method and reduced into RGO using a thermal method. The physical and electrochemical characteristics of RGO material were evaluated and its desalination performance was tested with a CDI unit cell with a potentiostat and conductivity meter, by varying the applied voltage and feed rate of the salt solution. The performance of RGO was compared to graphite as a conductive material in a CDI electrode. The result showed RGO can increase the capacitance, reduce the equivalent series resistance, and improve the electrosorption capacity of CDI electrode.
1. Introduction
Water recovery research has attracted great attention due to the existing global water crises. One of the key tools to resolve a future global water crises is continued research into methods that will provide low-cost and high efficiency desalination. Most existing desalination technologies such as reverse osmosis and distillation require a great deal of energy, so it is imperative to find more energy efficient methods to desalinate water [1] .
Electrosorption has been shown to be the most promising method for potential future application, for desalinating solutions of low-to-moderate ionic strength [2] . The basic concept of electrosorption is to use an external applied potential to force charged ions in an electrolyte solution toward oppositely charged electrodes, making an electrical double layer (EDL) region. This salt removal technology has been known as capacitive deionization (CDI). The ability of the CDI process to operate at low voltage and without chemical waste has made it a promising technology for overcoming the drawbacks of other desalination technologies.
The CDI unit cell mainly consists of electrodes, current collectors, and a spacer. The correct choice of electrode material is important because its ability to adsorb ions affects the performance of the salt removal process. Carbon, with its wide variety of available forms and porosity, has been found to be the electrode material of choice for CDI and other electrosorption processes [3] . Many studies have been carried to investigate the electrochemical behavior of many kinds of carbons for application as electrosorption electrodes [4 - 8] .
Among the various forms of carbon materials, activated carbon (AC) has been widely used as the main electrode material for CDI, due to its high surface area (>1000 m 2 g -1 ) and extensive micropores (pore size <2 nm) [9 , 10] . The main problems of AC electrodes have been their the low electrode conductivity due to the low accessibility of micropores to the aqueous solution [11] and the weak physical bonding of AC [12] .
To manufacture CDI electrodes with good particle-to-particle contact between the small carbon grains, AC powder is combined with a polymeric binder, such as polytetrafluoroethylene or polyvinylidene fluoride (PVdF). However, the amount of polymeric binder used must be limited (5-10%) because the use of polymeric binder increases internal resistance and may block some of the carbon pores, resulting in diminished capacitance [9 , 11] . For this reason, some CDI unit cells add a conductive material to the composition of the CDI electrode, such as carbon black or graphite [12 - 14] .
In this present study we prepared a reduced graphene oxide (RGO) and used it as a conductive material to improve the performance of electrodes made from AC powder and polymer binder for CDI application. The salt removal performance of RGO was compared with graphite, which is a common conductive material for CDI.
2. Experimental
- 2.1. Synthesis of RGO
GO was prepared using a modification of Hummers method [15] . Graphite flakes (Timrex, Timcal Ltd.) were added and stirred in a mixture of 2:1 HNO 3 (Junsei Chemical Ltd.) and H 2 SO 4 (Junsei Chemical Ltd.). After that, the mixture was diluted with water at room temperature and left overnight. The mixture was filtered and dried in ambient conditions for 24 h. Later, KMnO 4 (Junsei Chemical Ltd.) was added slowly to a reaction vessel with concentrated H 2 SO 4 in an ice bath and the mixture was stirred for 2 h. After dilution with water, H 2 O 2 (Dongwoo Fine-Chem) was added to the mixture in an ice bath. Finally the mixture was centrifuged and washed with HCl aqueous solution (Junsei Chemical Ltd.) to remove residual ions and then washed with water until its pH reached 7. GO was reduced by heat treatment to 400℃, followed by a rapid heating process for graphene exfoliation to 900℃. Constant heating at 900℃ was maintained for 2 h and the RGO sample was obtained.
- 2.2. Characterization
The morphology of samples was characterized by using scanning electron microscope (SEM, S-4700, Hitachi). The specific surface areas and pore parameters were obtained by analyzing nitrogen adsorption-desorption isotherms, recorded at 77 K using a surface area analyzer (BELSORP-mini, BEL Japan Inc.). Prior to this measurement, the samples were degassed at 250℃ for 2 h. The specific surface area and the pore size were analyzed using the Brunauer-Emmett- Teller (BET) method and the Barrett-Joyner-Halenda (BJH) method, respectively. X-ray diffraction (XRD, RINT2000, Rigaku) was carried out to investigate the graphitic structure of graphite, GO, and RGO. Scans were done for 2θ values between 5 and 80° at 0.02°/min.
- 2.3. Fabrication of CDI electrodes
The carbon slurry for the electrodes was prepared by mixing AC (P-60 Kuraray Co., Ltd.) with PVdF (Sigma-Aldrich Co., Ltd.) which was dissolved in dimethylacetamide (DMAc, Sigma-Aldrich Co., Ltd.), and RGO as the conductive material, with the composition of 85%:10%:5%, respectively. The mixture was stirred for 12 h. The obtained carbon slurry was cast into a graphite sheet using a doctor blade, for use as a current collector. The total thickness of the electrode was 400 μm. The cast electrode was dried in a vacuum oven at 70℃ for two hours. The AC-RGO electrode was obtained by cutting the cast electrode into a piece 10 × 10 cm 2 with an additional area (3 × 5 cm 2 ) left for a connectivity space. A hole with a diameter of 8 mm was made for electrolyte flow in the middle of the electrode. For comparison, we also made an electrode with graphite as the conductive material (AC-Gr) with the same composition as ACRGO. An electrode with no added conductive material (AC) was also made, with the composition of AC and PVdF of 85% and 15 % respectively. The morphologies of the fabricated electrodes were observed with a SEM (S-4700, Hitachi).
- 2.4. Electrochemical characterization
Cyclic voltammetry (CV) using a three electrode system was conducted to measure the capacitance behavior of the carbon electrodes. CV was performed with an AutoLab PGST30 potentiostat. A polarized electrode with the same composition as the CDI electrode was used as a working electrode. A platinum electrode and Ag/AgCl electrode were used as the counter and reference electrode, respectively. The electrolyte solution was 0.5 M NaCl, and all tests were performed at 35℃ in a water bath. The measurements were performed in the potential range of -0.2 to 0.8 V and measured at the sweep rate of 5, 10, 20, 50, and 100 mV/s.
Electric impedance spectroscopy (EIS) using a two electrode system was conducted to determine the internal resistance of the electrodes. The impedance measurement was conducted using the IM6ex spectroscope (Zahner Messtechnnik). A given potential of 0.0 V was applied to the electrode with AC potential amplitude of 10 mV for a short time until the system stabilized. After giving 10 mA applied current to the electrodes with 10 mV potential amplitude, the changes in resistance of the electrodes were measured in the frequency range of 0.1 Hz-100 kHz.
- 2.5. Desalination performance test
The desalination test of the CDI unit cell was performed in a continuous flow-through system as shown in Fig. 1 . NaCl solution was pumped by a peristaltic pump and passed through the unit cell. A given potential was applied to the cell using a potentiostat (WPG100, WonATech Co., Ltd.). The conductivity of the effluent was measured using a pH-conductivity meter (Sevenmulti, Mettler Toledo) and was converted to the concentration (mg/L).
PPT Slide
Lager Image
Scheme of desalination performance test. CDI: capacitive deionization.
The desalination comparison tests between AC-RGO, AC-Gr, and AC electrodes were conducted with the following conditions. The applied voltage was 1.0 and 1.5 V for adsorption and 0.0 V for desorption, where both were performed for 3 min and repeated for 5 cycles. NaCl 250 mg/L was used as the feed solution with a feed rate of 20 and 30 mL/min.
3. Results and Discussion
- 3.1. Characterization of RGO
The morphologies of the obtained RGO were observed and compared with the graphite and GO by SEM, and these SEM images of graphite, GO, and RGO material are shown in Figs. 2a - c respectively. GO can be obtained by modification of Hummers method [15] which changes the highly crystalline layered graphite structure shown in Fig. 2a into an exfoliated structure ( Fig. 2b ). The surfaces of GO sheets have a soft morphology which may be due to the hydroxyl and carboxyl functional group that are attached to GO. The reduction of GO that was performed to 400℃ removes these functional groups from the GO structure and the following rapid heating process up to 900℃ exfoliated the GO into single layers of graphite. As shown in Fig. 2c , wrinkle morphology is observed in the RGO structure which is probably due to the removal of carbon atoms in the form of carbon dioxide, which leads to lattice defects throughout the sheets [16] . The single layer of graphite has been known to have high electric conductivity [16 , 17] , thus its addition to the carbon electrode compositions will improve the electrode’s conductivity and ability to adsorb the charged ions for CDI.
PPT Slide
Lager Image
Scanning electron microscope images of materials: (a) graphite (b) graphite oxide (GO) (c) reduced GO.
The structural changes of graphite, GO, and RGO were investigated by XRD measurement, and the patterns are shown in Fig. 3 . The XRD pattern of graphite shows one strong and sharp peak at 2θ = 26.4° which corresponds to an interlayer distance (d 002 ) of 3.38 Å. After thermal treatment, this peak was markedly shifted to a point of 2θ = 10.24° and the interlayer distance expanded to 8.64 Å. The larger interlayer distance is due to the oxidation of graphite into GO with the formation of hydroxyl and carboxyl groups. The reduction process was expected to contract the interlayer of the GO and remove the functional groups, leading to the exfoliation of the GO layer to produce a single layer of graphite. After the thermal treatment of GO, the peak was similar to that of graphite, which is at the point of 2θ = 26.76° and the interlayer distance was reduced to 3.33 Å. This re-shifted peak shows that the functional groups in the GO interlayer were removed and the layers were exfoliated. The calculation of the RGO peak using the Debye-Scherrer equation gives about 12-13 layers in a single sheet.
PPT Slide
Lager Image
X-ray diffraction patterns of graphite, graphite oxide (GO), and reduced GO (RGO).
Table 1 summarizes the BET surface areas, total pore volumes, and average pore sizes of synthesized RGO and graphite for comparison. The N 2 adsorption-desorption isotherm as well as pore size distribution is shown in Fig. 4 . The BET surface area and total pore volume of RGO are slightly larger than graphite due to the thermal exfoliation. However, the surface area of the synthesized RGO in this experiment is still below the theoretical value of the fully exfoliated pristine graphene, which might be due to the incomplete exfoliation of GO. Based on pore width, the RGO and graphite consist of mesopores with pore diameters of 3-4 nm, which was suitable for access by ions.
BET properties of RGO and graphite
PPT Slide
Lager Image
BET: Brunauer-Emmett-Teller, RGO: reduced graphene oxide.
PPT Slide
Lager Image
(a) Nitrogen adsorption-desorption isotherms for reduced graphite oxide (RGO) and graphite (b) Barrett-Joyner-Halenda pore-size distribution curves.
- 3.2. Characterization of AC-RGO electrode
Fig. 5 shows SEM images of the AC and AC-RGO electrodes. The AC electrodes provide a large number of micropores ( Fig. 5a ) to accommodate the charged ions to be adsorbed, yet strong aggregation between AC particles resulted in poor conductivity. For the AC-RGO electrode ( Fig. 5b ), RGO can act as a flexible bridge to form a “plane-to-point” (RGO to AC) conducting network, which is beneficial for decreasing the aggregation of AC particles and therefore enhances the pore availability [18] .
PPT Slide
Lager Image
Scanning electron microscope images of electrodes: (a) activated carbon (AC) (b) AC- reduced graphite oxide.
Table 2 shows the BET surface area, total pore volume, and average pore diameter of the AC-RGO electrode compared with the AC electrode. The AC material provides high surface area as the main active material for electrosorption. With the addition of RGO in the electrode composition, the surface area and pore volume decrease as the RGO particles fill the path of the ions to be adsorbed. However, compared to the AC, which mainly consists of micropores, RGO can decrease the overlapping effect caused by micropores, which is beneficial to electrosorption. Hence, despite the decrease in surface area, the conductivity of electrode is also an important factor for the electrosorption capacity, and helps determine the flow of charged ions in the electrode pore. The movement of ions is more difficult in the smaller pores than in the large pores, so that RGO can provide micropores’ accessibility to the salt solution [11] .
BET properties of the AC, AC-RGO, and AC-Gr electrodes
PPT Slide
Lager Image
BET: Brunauer-Emmett-Teller, AC: activated carbon, RGO: reduced graphene oxide.
- 3.3. Electrochemical characterization
CV measurements were carried out within the potential range of -0.2 to 0.8 V to analyze the electrochemical behavior of the CDI electrodes. Fig. 6a shows the cyclic voltammograms of ACRGO, AC-Gr and AC electrodes at a scan rate of 20 mV/s. It can be seen that the samples show a typical rectangular curve within the potential ranges, indicating high electrosorption capacitive behavior. However, small distortions were also observed in the voltammogram, a delay of potential when reversing the potential sweep. This means that the electrochemical behavior of the CDI electrodes depends not only on the charging current in the electric double layer, but also on faradaic currents [19] .
PPT Slide
Lager Image
(a) Cyclic voltammograms of activated carbon (AC), AC-reduced graphite oxide (RGO), and AC-Gr electrodes. (b) The specific capacitance of AC, AC-RGO, and AC-Gr electrodes at different sweep rates.
The electrodes’ specific capacitances were calculated by using the following equation [20] :
PPT Slide
Lager Image
where t s is the total one-way scan time (s), r s is the scan rate (V/s), S c is the area of the total charge i, V is the potential (V), and m is the mass of carbon (g). The specific capacitance of each electrode at the varying scan rate is shown in Fig 6b . AC-RGO has the largest specific capacitance of about 110-125 F/g, while for the AC and AC-Gr it was 73-81 and 63-70 F/g respectively, depending on the potential scan rate. The specific capacitance of AC-RGO was increased compared with the AC electrode, indicating that the aggregation of AC particles can be decreased by adding a conductive material such as RGO. However, the addition of graphite reduced the specific capacitance of the electrode, perhaps due to the bulk filling of graphite in the AC electrode pores. This result shows that after the oxidation and thermal treatment of graphite, RGO can be used to increase the specific capacitance of AC electrodes.
EIS was also used to observe the electrochemical behavior of the CDI electrodes. The Nyquist plots and their enlarged sections (high frequency, inset) of the AC-RGO, AC-Gr, and AC electrodes are shown in Fig. 7 . These plots show typical EDL capacitor behavior. The region with the 45° slope at high frequencies (10 kHz-1 Hz) can be assigned to the behavior of the porous structure and is often called the distributed resistance. For low frequencies (<1 Hz), the spectrum approaches a vertical line and behaves like an ideal capacitor, with R and C being no longer frequency-dependent [21] .
PPT Slide
Lager Image
Nyquist plots for the impedance response of the activated carbon (AC), AC-reduced graphite oxide (RGO), and AC-Gr electrodes in terms of (a) cation (Na+) adsorption (b) anion (Cl-) adsorption.
The impedance performance from the high-frequency range, which is referred to as equivalent series resistance (ESR), is discussed here, as it is related to the electrode conductivity. By comparing the three samples in a single plot as in Fig. 7 , it can be seen that the AC-RGO and AC-Gr electrodes have lower ESR than the AC electrode. This shows that the addition of a conductive material to the AC electrode reduces the electrode/electrolyte interface resistance, thus increasing the ability of the electrolyte solution to penetrate into the micropores of the AC particles.
Two kinds of Nyquist plot are shown in Figs. 7a and b , comparing the difference of the electrodes adsorption for cation (Na + ) and anion (Cl - ), respectively. There is not much difference between them, just the ESR for the Na + adsorption is slightly lower than the ESR for the Cl - , due to the difference in ion size.
- 3.4. Desalination performance test
The desalination performance test was carried out with adsorption (1.5 V for 3 min) and desorption (0.0 V for 3 min) processes with a NaCl feed rate of 20 mL/min, repeated for five cycles. The results of conductivity change per unit time at the 5th cycle for AC-RGO, AC-Gr, and AC are shown in Fig. 8a. The initial conductivity was 512 μS/cm based on the conductivity of the 250 mg/L NaCl solution. When the potential was applied to the electrode, Na + and Cl - were attracted onto the surface of the oppositely charged electrodes, which can be observed from the decreasing conductivity of the NaCl solution. The AC-RGO electrode reduced the conductivity of the NaCl solution more than the AC-Gr and AC electrodes, which means relatively more ions were being adsorbed in the AC-RGO electrodes’ pores. The conductivity of NaCl was also reduced using the AC-Gr electrode. However after it reached the lowest point, the conductivity increased gradually. This can be explained because the capacitance of the AC-Gr electrode was the lowest.
PPT Slide
Lager Image
(a) Conductivity changes per time of activated carbon (AC), AC-reduced graphite oxide (RGO), and AC-Gr electrodes at 5th cycle using 1.5 V applied voltage and 20 mL/min feed rate. (b) The comparison of electrosorption capacity of AC, AC-RGO, and AC-Gr electrodes for various conditions.
The electrosorption capacity of the electrodes was calculated using the following equation:
electrosorption capacity
PPT Slide
Lager Image
where C i is the influent concentration of the salt solution (mg/L), V is the total volume of feed solution (L), t is the adsorption time (s), C eff is the effluent concentration from the 5th cycle (mg/L), and m is the amount of carbon used (g). The concentration of the solution was determined by converting the conductivity. Comparisons of the electrosorption capacity of the AC-RGO, AC-Gr, and AC electrodes at various conditions is shown in Fig. 8b . The AC-RGO electrode shows the greatest improvement of electrosorption capacity from the AC electrode in every condition of the performance test. In comparison, the AC-Gr electrode shows improvement only at the higher voltage and lower solution feed rate. These results show that RGO can be effectively used as the conductive material for CDI electrodes rather than graphite.
4. Conclusions
RGO was synthesized and added as a conductive material in the composition of a carbon electrode for application in CDI. The electrochemical behavior of the AC-RGO electrode showed that it can increase the specific capacitance and reduce the ESR of an AC electrode, and indicated that RGO reduced the aggregation of AC particles, thus improving the penetration of electrolyte solution into the micropores of AC particles. The salt removal efficiency and the electrosorption capacity of the AC-RGO electrode was higher than the AC-Gr in every condition performed in this experiment, which proves that RGO is preferred over graphite as a conductive material addition for CDI applications.
This work was supported by the Innopolis Commercialization of Technology Development Project (Establishment of KIERKyushu University R&D Center and Development of Nano-Carbon Composite Electrode for CDI) funded by the INNOPOLIS Foundation in the Republic of Korea.
Welgemoed TJ , Schutte CF 2005 Capacitive Deionization TechnologyTM: an alternative desalination solution Desalination 183 327 -
Zou L , Morris G , Qi D 2008 Using activated carbon electrode in electrosorptive deionisation of brackish water Desalination 225 329 -
Oren Y 2008 Capacitive deionization (CDI) for desalination and water treatment--past, present and future (a review) Desalination 228 10 -
Farmer JC , Fix DV , Mack GV , Pekala RW , Poco JF 1996 Capacitive deionization of NaCl and NaNO3solutions with carbon aerogel electrodes J Electrochem Soc 143 159 -
Hou CH , Huang CY 2013 A comparative study of electrosorption selectivity of ions by activated carbon electrodes in capacitive deionization Desalination 314 124 -
Oh HJ , Lee JH , Ahn HJ , Jeong Y , Kim YJ , Chi CS 2006 Nanoporous activated carbon cloth for capacitive deionization of aqueous solution Thin Solid Films 515 220 -
Yang J , Zou L , Choudhury NR 2013 Ion-selective carbon nanotube electrodes in capacitive deionisation Electrochim Acta 91 11 -
Zhan Y , Nie C , Li H , Pan L , Sun Z 2011 Enhancement of electrosorption capacity of activated carbon fibers by grafting with carbon nanofibers Electrochim Acta 56 3164 -
Kurzweil P 2009 Electrochemical double-layer capacitors: Carbon material. In: Batteries and supercapacitors Elsevier 821 -
Qu D , Shi H 1998 Studies of activated carbons used in double-layer capacitors J Power Sources 74 99 -
Frackowiak E , Beguin F 2001 Carbon materials for the electrochemical storage of energy in capacitors Carbon 39 937 -
Nadakatti S , Tendulkar M , Kadam M 2001 Use of mesoporous conductive carbon black to enhance performance of activated carbon electrodes in capacitive deionization technology Desalination 268 182 -
Li H , Zou L , Pan L , Sun Z 2010 Novel graphene-like electrodes for capacitive deionization Environ Sci Technol 44 8692 -
Park KK , Lee JB , Park PY , Yoon SW , Moon JS , Eum HM , Lee CW 2007 Development of a carbon sheet electrode for electrosorption desalination Desalination 206 86 -
Hummers WS , Offeman RE 1958 Preparation of graphitic oxide J Am Chem Soc 80 1339 -
Pei S , Cheng HM 2012 The reduction of graphene oxide Carbon 50 3210 -
Shin HJ , Kim KK , Benayad A , Yoon SM , Park HK , Jung IS , Jin MH , Jeong HK , Kim JM , Choi JY , Lee YH 2009 Efficient reduction of graphite oxide by sodium borohydride and its effect on electrical conductance Adv Funct Mater 19 1987 -
Li H , Pan L , Nie C , Liu Y , Sun Z 2012 Reduced graphene oxide and activated carbon composites for capacitive deionization J Mater Chem 22 15556 -
Choi JY , Choi JH 2010 A carbon electrode fabricated using a poly(vinylidene fluoride) binder controlled the Faradaic reaction of carbon powder J Ind Eng Chem 16 401 -
Tashima D , Yoshitama H , Otsubo M , Maeno S , Nagasawa Y 2011 Evaluation of electric double layer capacitor using Ketjenblack as conductive nanofiller Electrochim Acta 56 8941 -
Kotz R , Hahn M , Gallay R 2006 Temperature behavior and impedance fundamentals of supercapacitors J Power Sources 154 550 -