Performance-determining factors in flexible transparent conducting single-wall carbon nanotube film
Performance-determining factors in flexible transparent conducting single-wall carbon nanotube film
Carbon letters. 2013. Oct, 14(4): 255-258
Copyright ©2013, Korean Carbon Society
This is an Open Access article distributedunder the terms of the Creative CommonsAttribution Non-Commercial License(http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestrictednon-commercial use, distribution, andreproduction in any medium, providedthe original work is properly cited.
  • Received : August 08, 2013
  • Accepted : October 10, 2013
  • Published : October 31, 2013
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Young Il Song
Advanced Materials and Process Research Center, Sungkyunkwan University, Suwon, Gyeonggi-do 440-746, Korea
Jung Woo Lee
Advanced Materials and Process Research Center, Sungkyunkwan University, Suwon, Gyeonggi-do 440-746, Korea
Tae Yoo Kim
Advanced Materials and Process Research Center, Sungkyunkwan University, Suwon, Gyeonggi-do 440-746, Korea
Hwan Jung Jung
Institute of Advanced Composites Materials, Korea Institute of Science and Technology, Jeonbuk 565-905, Korea
Yong Chae Jung
Institute of Advanced Composites Materials, Korea Institute of Science and Technology, Jeonbuk 565-905, Korea
Su Jeung Suh
Advanced Materials and Process Research Center, Sungkyunkwan University, Suwon, Gyeonggi-do 440-746, Korea
suhsj@skku.edu
Cheol-Min Yang
Institute of Advanced Composites Materials, Korea Institute of Science and Technology, Jeonbuk 565-905, Korea
cmyang1119@kist.re.kr
Abstract
Flexible transparent conducting films (TCFs) were fabricated by dip-coating single-wall carbon nanotubes (SWCNTs) onto a flexible polyethylene terephthalate (PET) film. The amount of coated SWCNTs was controlled simply by dipping number. Because the performance of SWCNT-based TCFs is influenced by both electrical conductance and optical transmittance, we evaluated the film performance by introducing a film property factor using both the number of interconnected SWCNT bundles at intersection points, and the coverage of SWCNTs on the PET substrate, in field emission scanning electron microscopic images. The microscopic film property factor was in an excellent agreement with the macroscopic one determined from electrical conductance and optical transmittance measurements, especially for a small number of dippings. Therefore, the most crucial factor governing the performance of the SWCNT-based TCFs is a SWCNT-network structure with a large number of intersection points for a minimum amount of deposited SWCNTs.
Keywords
1. Introduction
Flexible transparent conducting films (TCF) are technologically important for future wearable displays. Although present indium-tin-oxide thin films have excellent electrical properties and high optical transmittance, their flexibility upon bending is extremely poor. Therefore, development of an alternative material with high mechanical flexibility is highly desired. Carbon nanotubes (CNTs) have been recently proposed as a promising candidate to satisfy the desired flexibility, owing to their high aspect ratio and excellent elastic property, in addition to high electrical conductivity [1 - 3] . Consequently, the fabrication of flexible TCFs with CNTs has recently been carried out. These recent studies have shown that the electrical conductivity and optical transmittance of CNT films varies, depending on the coating methods and the intrinsic properties of the CNTs [4 - 14] . In general, the performance of CNT-based TCFs are typically governed by the inherent properties of the CNTs, such as purity, defect concentration, and electrical conductivity. Efforts have been made to associate material-induced factors with better TCF performance [1 , 15] . However, the characteristics of CNT-based TCFs are still not clear due to a lack of systematic studies on the relationship between preparation conditions and film properties. The performance of CNT-based TCFs depends strongly on the higher order structure of the CNTs, such as entangled and bundle structures. This feature could be evaluated while investigating the performance-determining factors for designing better TCFs.
We assume that the performance of CNT-based TCFs directly depends on the number of intersecting, interconnected CNT bundles, and the coverage of SWCNTs on the substrate. In this study, we microscopically and macroscopically evaluated the performance of TCFs to elucidate performance-determining factors, by using experimental results of single-wall CNTs (SWCNTs)-coated TCFs on flexible polyethylene terephthalate (PET) film prepared by dip-coating process [14] .
2. Experimental Details
Highly pure SWCNTs synthesized by arc discharge process were purchased from Iljin Nanotech. The SWCNT diameters were in the range of 1.4 to 1.5 nm with a length of 5 to 20 μm. Thermogravimetric analysis profile gave 1.3 wt% of metal catalyst.
The purified SWCNTs were well dispersed in 1,2-dichloroethane (DCE) solvent without additives [14 , 16 , 17] . The low vaporization temperature of DCE (83.5℃) allows more SWCNT to be deposited on the substrate. Ten milligram of SWCNTs were immersed in 100 mL of DCE solvent. These were then sonicated in a bath type sonicator for 500 min at room temperature, followed by centrifugation at a speed of 6800 rpm for 10 min. The supernatant was decanted and sonicated prior to film formation. The PET substrate was sonicated in acetone for 10 min and then washed with deionized water to clean the substrate surface. The PET substrate was vertically positioned above a container of the SWCNT-dispersed DCE solution and then immersed into the SWCNT solution for 2 s, and withdrawn upward, with a continuous speed of 50 mm/min. Then, the PET substrate was dried for 5 s. This procedure was repeated between 100 to 400 times. The dip-coating was conducted in a glove box in Ar atmosphere in order to avoid moisture adsorption into the DCE solvent.
Field emission scanning electron microscopic (FE-SEM) images of the SWCNT-based TCFs were obtained with a JSM-63301 (JEOL). Their electrical conductance was measured using a four-point probe method. Optical transmittance was measured using UV-visible spectrometry (Carry 5000) in the range of 400 to 800 nm.
3. Results and Discussion
Fig. 1 presents the FE-SEM images of SWCNT network films on the PET substrate as a function of the different number of dippings. With increasing number of dippings, the amount of coated SWCNTs increases considerably. However, the coating of the PET substrate is not enough after a dipping treatment of 100 times, although the DCE completely wets the PET substrate.
The DCE solvent is easily evaporated from the substrate, depositing the SWCNTs film on it. The SWCNT film consists of a network having many intersection points. The intersection points in the TCF film are a crucial factor for good electrical conductivity of the film. The FE-SEM images of SWCNTcoated TCFs according to dipping treatment number show that the number of intersection points increases significantly with the number of dippings. The percolation threshold should reach a minimum amount of SWCNT deposits to maximize optical transmittance [18 - 20] .
Fig. 2 shows a schematic representation for estimating the performance-determining factors of the TCFs using the observed FE-SEM images. Figs. 2 a and b show an optical image and an
Lager Image
Field emission scanning electron microscopic images of singlewalledcarbon nanotube network film coated with different dippingnumber; (a) 100, (b) 200, (c) 300, and (d) 400 times.
Lager Image
(a) Optical image, (b) field emission scanning electron microscopicimage after 100 dipping times, and schematic representations fordetermining (c) conductance factor (fG) and (d) absorbance factor (fA) in B1of (b).
FE-SEM image after 100 dippings. We defined two factors that govern the SWCNT-TCF performance. First, the electrical conductance of the film is closely related to the intersection points in the SWCNT network; the electrical conductance of the SWCNT network film should be simply proportional to the number of intersection points of SWCNT bundles, and the number of SWCNT bundles that are interconnected at each intersection point. Therefore, we first define the conductance factor fG as follows.
Lager Image
Lager Image
(a) Electrical conductance (G) and optical transmittance (T) and(b) the conductance (fG) and absorbance (fA) factors of single-walled carbonnanotube-transparent conducting films as a function of the numberof dipping.
where Bi is the number of interconnected SWCNT bundles ( j ) at each intersection point ( i ), as illustrated in Fig. 2 c. Therefore, fG is the sum of Bi at the intersection point ( i ). Second, the absorbance of the film is proportional to the coverage of SWCNTs on the substrate. Therefore, we also define the absorbance factor fA , which is given by Eq. (2).
Lager Image
where lj and dj are the length and diameter of the j -th SWCNT bundle in the FE-SEM image, respectively, as illustrated in Fig. 2 d, and S is the total area of the FE-SEM image.
Fig. 3 a shows the changes of electrical conductance ( G ) and optical transmittance ( T ) of dip-coated SWCNT-TCFs with the number of dippings. With the increasing number of dippings, the electrical conductance of the SWCNT-TCFs increases, accompanied by a reduction of the optical transmittance; this is ascribed to the increase in the number of SWCNT intersection points and the coverage of SWCNTs on the substrate. The conductance ( fG ) and absorbance ( fA factors determined by Eqs. (1) and (2) are shown in Fig. 3 b. Since the optical transmittance is inversely proportional to the absorbance, the change of fA value with the number of dippings has an opposite tendency to that of the T value. Both higher conductance and transmittance are simultaneously desired for better film performance. We need a film property factor including both properties. Thus, we define the microscopic film property factor (Q Mic ), as given by Eq. (3).
Lager Image
Comparison of the microscopic film property factor (QMic) withmacroscopic film property factor (QMac) as a function of the number ofdipping.
Lager Image
QMic can be compared with the macroscopic film property factor ( QMac ) expressed with the measured electrical conductance ( G ) and optical transmittance ( T ), as given by Eq. (4).
Lager Image
Fig. 4 presents the comparison of QMic with QMac as a function of the number of dippings. QMac shows a sharp increase up to 200 dipping times and then decreases at 300 dipping times. Although the electrical conductance was increased, the optical transmittance decreased rapidly at a large number of dippings. As a consequence, the film performance is degraded. The QMic resembled the QMac in a similar way up to 300 dipping times. It should be noted, at a large number of dippings, counting the number of intersection points in the SWCNT network becomes ambiguous because these numbers increase very rapidly, as shown in Fig. 1 . Thus the errors in counting these numbers dominate, making the data point uncertain.
4. Conclusions
In summary, SWCNT-TCFs were fabricated by dip-coating method. Our dip-coating approach provided reasonable quality SWCNT-TCF films. The film’s microscopic property factor was defined by the number of interconnected SWCNT bundles at intersection points, and the coverage of SWCNTs on the substrate, in FE-SEM images. The microscopically extracted film property factors are in good agreement with macroscopically obtained values, especially for a small number of dippings. Our results clearly revealed that a sparsely entangled random network structure with a sufficient number of intersection points and a minimum SWCNT coverage is a key factor for improving SWCNT-TCF performance. However, the dispersion of SWCNTs is also an important factor influencing SWCNT-TCF performance. Therefore, dispersing SWCNT bundles into individual SWCNTs, or into a smaller bundle size, is desired to improve TCF electrical conductance and optical transmittance.
Acknowledgements
This work was supported by the Korea Institute of Scienceand Technology (KIST) Institutional Program (2M32790,2Z03870) and Nano-Convergence Foundation [Development ofhigh heat dissipative nanocarbon-polymer composites for 25 W/mK and its commercialization] funded by the Ministry of Science,ICT and Future Planning(MSIP, Korea) & the Ministry ofTrade, Industry and Energy (MOTIE, Korea). We thank Prof. K.Kaneko (Chiba University, Japan) and Prof. Y. H. Lee (SungkyunkwanUniversity, Korea) for their very useful commentsand discussions in preparing the manuscript.
References
Wu Z , Chen Z , Du X , Logan JM , Sippel J , Nikolou M , Kamaras K , Reynolds JR , Tanner DB , Hebard AF , Rinzler AG. (2004) Transparent,conductive carbon nanotube films. Science 305 1273 -
Cao Q , Hur SH , Zhu ZT , Sun YG , Wang CJ , Meitl MA , Shim M , Rogers JA. (2006) Highly bendable, transparent thin-film transistors thatuse carbon-nanotube-based conductors and semiconductors withelastomeric dielectrics. Adv Mater 18 304 -
Fanchini G , Unalan HE , Chhowalla M. (2006) Optoelectronic propertiesof transparent and conducting single-wall carbon nanotubethin films. Appl Phys Lett 88 191919 -
De Volder MFL , Tawfick SH , Baughman RH , Hart AJ. (2013) Carbonnanotubes: present and future commercial applications. Science 339 535 -
Park HG , Lee MJ , Kim K , Seo DS. (2012) Transparent conductivesingle wall carbon nanotube network films for liquid crystaldisplays. ECS Solid State Lett 1 R31 -
Yang Y , Jeong S , Hu L , Wu H , Lee SW , Cui Y. (2011) Transparent lithiumionbatteries. Proc Natl Acad Sci U S A 108 13013 -
Zhang M , Fang S , Zakhidov AA , Lee SB , Aliev AE , Williams CD , Atkinson KR , Baughman RH. (2005) Strong, transparent, multifunctional,carbon nanotube sheets. Science 309 1215 -
Lee SH , Teng CC , Ma CCM , Wang I. (2011) Highly transparent and conductivethin films fabricated with nano-silver/double-walled carbonnanotube composites. J Colloid Interface Sci 364 1 -
Kim MJ , Shin DW , Kim JY , Park SH , Han It , Yoo JB. (2009) The productionof a flexible electroluminescent device on polyethyleneterephthalate films using transparent conducting carbon nanotubeelectrode. Carbon 47 3461 -
Shin EC , Jeong GH. (2011) Fabrication of transparent, flexible andconductive films using as-grown few-walled carbon nanotubes. Curr Appl Phys 11 S73 -
Meitl MA , Zhou Y , Gaur A , Jeon S , Usrey ML , Strano MS , Rogers JA. (2004) Solution casting and transfer printing single-walled carbonnanotube films. Nano Lett 4 1643 -
Saran N , Parikh K , Suh DS , Munoz E , Kolla H , Manohar SK. (2004) Fabricationand characterization of thin films of single-walled carbonnanotube bundles on flexible plastic substrates. J Am Chem Soc 126 4462 -
Shimoda H , Oh SJ , Geng HZ , Walker RJ , Zhang XB , McNeil LE , Zhou O. (2002) Self-assembly of carbon nanotubes. Adv Mater 14 899 -
Song YI , Yang CM , Kim DY , Kanoh H , Kaneko K. (2008) Flexible transparentconducting single-wall carbon nanotube film with networkbridging method. J Colloid Interface Sci 318 365 -
Pasquier AD , Unalan HE , Kanwal A , Miller S , Chhowalla M. (2005) Conductingand transparent single-wall carbon nanotube electrodes forpolymer-fullerene solar cells. Appl Phys Lett 87 203511 -
Kim KK , Bae DJ , Yang CM , An KH , Lee JY , Lee YH. (2005) Nanodispersionof single-walled carbon nanotubes using dichloroethane. J Nanosci Nanotechnol 5 1055 -
Song YI , Kim GY , Choi HK , Jeong HJ , Kim KK , Yang CM , Lim SC , An KH , Jung KT , Lee YH. (2006) Fabrication of carbon nanotubefield emitters using a dip-coating method. Chem Vap Depos 12 375 -
Hu L , Hecht DS , Grüner G. (2004) Percolation in transparent and conductingcarbon nanotube networks. Nano Lett 4 2513 -
Unalan HE , Fanchini G , Kanwal A , Du Pasquier A , Chhowalla M. (2006) Design criteria for transparent single-wall carbon nanotubethin-film transistors. Nano Lett 6 677 -
Darhuber AA , Troian SM , Davis JM , Miller SM , Wagner S. (2000) Selectivedip-coating of chemically micropatterned surfaces. J Appl Phys 88 5119 -