Modifications of mechanical, thermal, and electrical characteristics of epoxy through dispersion of multi-walled carbon nanotubes in supercritical carbon dioxide
Modifications of mechanical, thermal, and electrical characteristics of epoxy through dispersion of multi-walled carbon nanotubes in supercritical carbon dioxide
Carbon letters. 2013. Oct, 14(4): 218-227
Copyright ©2013, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : July 07, 2013
  • Accepted : September 09, 2013
  • Published : October 31, 2013
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
M. G. H. Zaidi
Department of Chemistry, National Institute of Technology, Kurukshetra, 136119, India
mgh_zaidi@yahoo.com
S. K. Joshi
Department of Physics, National Institute of Technology, Kurukshetra, 136119, India
M. Kumar
Department of Mechanical Engineering, G.B. Pant University of Agriculture and Technology, Pantnagar, 263 145, India
D. Sharma
Department of Chemistry, National Institute of Technology, Kurukshetra, 136119, India
A. Kumar
Department of Physics, National Institute of Technology, Kurukshetra, 136119, India
S. Alam
Polymer Division, Defense Materials Stores Research Development and Establishment, G.T. Road, Kanpur, 208 013, India
P. L. Sah
Department of Mechanical Engineering, G.B. Pant University of Agriculture and Technology, Pantnagar, 263 145, India
Abstract
A supercritical carbon dioxide (SCC) process of dispersion of multi-walled carbon nanotubes (MWCNTs) into epoxy resin has been developed to achieve MWCNT/epoxy composites (CECs) with improved mechanical, thermal, and electrical properties. The synthesis of CECs has been executed at a MWCNT (phr) concentration ranging from 0.1 to 0.3 into epoxy resin (0.1 mol) at 1800 psi, 90℃, and 1500 rpm over 1 h followed by curing of the MWCNT/epoxy formulations with triethylene tetramine (15 phr). The effect of SCC treatment on the qualitative dispersion of MWCNTs at various concentrations into the epoxy has been investigated through spectra analyses and microscopy. The developed SCC assisted process provides a good dispersion of MWCNTs into the epoxy up to a MWCNT concentration of 0.2. The effects of SCC assisted dispersion at various concentrations of MWCNTs on modification of mechanical, thermal, dynamic mechanical thermal, and tribological properties and the electrical conductivity of CECs have been investigated.
Keywords
1. Introduction
The importance of supercritical fluids, particularly supercritical carbon dioxide (SCC), as a green friendly alternative to organic solvents for environmentally benign processing of carbon nanomaterials has recently been recognized [1 - 3] .They have been adopted either to develop new technologies or to replace traditional technologies based on the use of organic solvents. The advantages of using SCC over conventional methods for processing of carbon nanomaterials are not only environmental but also chemical and economical. Due to its unique inexpensive, non-toxic, and non-flammable properties and excellent recyclability without energy expenditures, SCC has been used for processing of one dimensional carbon nanostructures [1] , synthesis of carbon nanotubes (CNTs) [2 , 3] , patterning of carbon nanomaterials [4] , growth of CNTs [5] and carbon nanocages [6] , purification of sing-walled CNTs (SWCNTs) [7 , 8] , coating of inorganic nanoparticles [9] and polymers over carbon nanostructured surfaces [10] , non-covalent functionalization of CNTs with molecular anchors [11] , and preparation of endohedral derivatives of CNTs [12] and CNT/polymer composites [13 - 15] .
Synthesis of epoxy based polymer nanocomposites incorporating CNTs is impeded by van der Waals interactions that limit the nanotube dispersion into the polymer matrix [16 , 17] . Remarkable improvements in the physical and barrier properties of these nanocomposites can be achieved by improving the dispersion of CNTs into the polymer matrix, which facilitates better wetting and increased surface contact area between the constituent phases [18 - 24] . In recent decades, efforts have been directed towards the development of physical-mechanical or chemical processes to enhance the dispersion of CNTs in an epoxy matrix [25 - 29] . Physical methods involve breaking up agglomerates through calendaring, grinding, ball milling, high speed shearing, high-pressure homogenization, ultrasonication, a combination thereof [30 , 31] , or chronoamperometry [32] . With regard to chemical methods, the purification procedure involves the removal of metallic catalyst residues, which arise from the synthesis of CNTs and the creation of functional groups on their surface to improve the interfacial interactions between the polymers and CNTs [16 , 31 , 32] . CNTs are seriously damaged, especially when a probe sonicator is employed, suggesting the generation of defects on the CNT surface. In extreme cases, the graphene layers of CNTs are completely destroyed and the nanotubes are converted into amorphous carbon nanofibers. The localized damage to CNTs deteriorates both the electrical and mechanical properties of the multi-walled CNT (MWCNT)/epoxy composites (CECs) [19] . Mechanical dispersion, on the other hand, involves the use of expensive, toxic, and flammable organic solvents and lengthens the manufacturing process. The calendering approach has proved to be an effective method for achieving appropriate nanoreinforcement dispersion in epoxy resins without causing major damage to the nanoreinforcement compared to sonication and high shear mixing techniques, which present limited dispersion effectiveness and may cause damage to the nanoreinforcement when the processing time is lengthened to increase dispersion [31] . With respect to evaluating the dispersion of different types of nanoparticles, depending on the demanded scale, different microscopy methods such as transmission electron microscopy, scanning electron microscopy, and atomic force microscopy are amongst the most widely used techniques. In addition, dispersion of CNTs can be estimated indirectly by UVvis spectra [20] , a disc centrifuge method [29] , and light transmittance and electrical conductivity measurements [33] .
To address the desperate need for effective dispersion of nanotubes into an epoxy matrix together with strong interfacial adhesion to achieve CECs with improved mechanical, thermal, and electrical properties, a SCC assisted process of dispersion of MWCNTs into epoxy has been developed. The influence of the concentration (phr) of MWCNTs, ranging from 0.1 to 0.3, on their qualitative dispersion into epoxy under identical processing conditions of SCC has been investigated to achieve CECs with enhanced mechanical, thermal, and electrical properties.
2. Materials and Methods
Commercially available epoxy diglycidyl ether of bisphenol A (DGEBA) and the curing agent triethylene tetramine were purchased from M/S Huntsman India Limited. Epoxy equivalent of DGEBA (197 g/Eq) was deduced according to the pyridinium chloride method [16] . MWCNTs (diameter 20 nm, 99.5%) were obtained from SES Research, Houston, USA.
- 2.1. Synthesis of CECs through SCC assisted dispersion of MWCNTs
Dispersion of MWCNTs into an epoxy resin assisted with SCC has been conducted in a stainless steel high pressure reactor (100 cm 3 ), manufactured by Pressure Products Industries USA, equipped with a PID temperature controller (±1℃). The reactor was charged with DGEBA (0.1 mol), the requisite concentration of MWCNTs (phr), and carbon dioxide (99.98%). Contents were heated at pressure ranging from 1200 to 1800 psi, 90℃, and 1500 rpm for 1.0 h in SCC. The temperature of the cell was reduced to 40℃ while maintaining mechanical agitation and subsequently CO 2 was vented from the cell @ 50 psi/ min and into dichloromethane. This was followed by subsequent degassing of the contents at 10 mmHg. MWCNT/epoxy formulations were isolated from the reactor cell and investigated in terms of their dispersion through UV-vis spectra [20 , 33] . Supercritical conditions that may provide enhanced dispersion of MWCNTs into the epoxy on the basis of van Hove singularities have been identified and the respective MWCNT/epoxy formulations were degassed at 10 mmHg and subsequently cured with triethylene tetramine (15 phr) to achieve CECs. All the samples were left at room temperature for 24 h and further post-cured for 3 h at 60℃ for 30 min.
- 2.2. Characterizations
- 2.2.1. Dispersion of MWCNTs into epoxy
Prior to curing, preliminary optimization of the dispersions of MWCNT in neat epoxy was achieved by monitoring the UVvis spectra of various supercritically processed MWCNT/epoxy resin formulations [20 , 33] . UV-vis spectra were recorded on a Genesis 10 Spectronic spectrophotometer in toluene at increments of 3 nm. Dispersion of MWCNTs at the surface of CECs was investigated through atomic force microscopy (AFM). AFM images were recorded on a NTEGRA Prima microscope under tapping mode using ultra-sharp Si cantilevers having a force constant of 48 N/m at room temperature. The qualitative extent of dispersion of MWCNTs in the CECs was investigated through scanning electron microscopy (SEM) using gold coated samples on a JEOL 6610 LV.
- 2.2.2. DC electrical conductivity
DC conductivity of the samples was recorded on a Keithley Nanovoltmeter model 2182 A coupled with a 6221 current source and an indigenous sample holder with a PID controlled oven provided by Scientific Instruments, Roorkee, India. Two parallel surfaces of each sample 1 mm apart were polished with silver paint and checked for good electrical conduction. Conductivity of samples was recorded through the four probe method at compliance of 2 V DC at 35 ± 1℃.
- 2.2.3. Fourier transformed infra-red spectra
Fourier transformed infra-red (FT-IR) spectra of the samples were recorded on a Perkin Elmer spectrophotometer in KBr, with a resolution of 4 cm -1 from 4000 to 500 cm -1 in transmission mode.
- 2.2.4. Mechanical characterizations
A plint wear and friction Sr. No. TE 97/7050 fitted with a Muyford super lathe, dead weight tester, transducer with calibration of 0.892 mv/v, microscope, and chart recorder was used in the present work. It consists of a modified lathe carrying a disc-shaped specimen on a mandrel with two pins pressed into contact with opposite surfaces of the disc by means of hydraulic cylinders. Hydraulic end loading was applied by means of a precision dead-weight pressure tester that can be loaded with dead weights to give any pressure up to 15 bar (b) in steps of 0.25 b. A conical hole, having an included angle of 60° and a maximum diameter of about 5 mm, was drilled on the end face of each cylindrical pin. The wear loss was estimated by weighing the mass of the pin after every 60 s by a weighing machine. The rate of rotation of the disc was indicated by a tachometer in the control panel. In addition, elapsed time and cumulative number of revolutions were indicated on a digital counter equipped in the panel. The Rockwell hardness (R scale, RH) of the samples was evaluated over a hardness testing machine using a ball indenter with 1/16” diameter. Tensile strength data of samples with dimensions of 160 × 10 × 5 were recorded at a cross head speed of 1.0 mm/min on a KIPL-PC 2000 computer controlled electronic tesnometer. The load capacity of the machine was 20 KN. This rather low loading rate was selected to consider the brittle character of the composites. The thickness of the samples was assigned at 3 mm ± 0.5 mm. About six to eight specimens were tested for each sample and the average value was obtained from data of these measured specimens. Compressive strength of samples with dimensions of 12.7 × 12.7 × 25.4 mm was measured on a Tinus Olson made universal testing machine (Capacity 35 KN) with a test speed of 5.0 mm/min. Impact strength of samples with dimensions of 64 × 12.7 × 3.2 mm and depth under the notch of 10.2 mm was recorded on a Izod Impact Tester (CEAST). The notch was prepared using a notch cutter with a micrometer screw gauge with 0.001 mm accuracy and a venire calliper (accuracy-0.001 mm). A dynamic mechanical thermal analysis (DMTA) was performed on TA Instrument 2980, operated in three point bending (flexural) mode, with sample dimensions of 60 × 10 × 4 mm, a dual cantilever clamp, and an oscillation frequency of 1 Hz. Data were collected from 20℃ to 180℃ at a scanning rate of 5℃/min in air.
- 2.2.5. Thermal characterizations
Thermo-oxidative stability of the samples was investigated at a sample size (mg) ranging from 8.085-11.020 through a simultaneous thermogravimetric-differential thermogravimetry-differential thermal analysis (TG-DTG-DTA) on a EXSTAR TG/ DTA 6300 instrument in static air at a heating rate of 10℃/min up to 800℃ using alumina powder as a reference. Differential scanning caloriemetry (DSC) of the samples was executed on a Universal V4.2E thermal analyzer at a heating rate of 10℃/min in nitrogen.
3. Results and Discussion
Solubility behavior of oxirane functional molecules under tuned conditions of pressure, density, and temperature in SCC has been well documented but has not been reported in the context of dispersing carbon nanomaterials in SCC [34] . In the present investigation, the dispersion behavior of different concentrations (phr) of MWCNTs ranging from 0.1 to 0.3 into epoxy resin (0.1 /dL mole) has been investigated under the pressure of SCC ranging from 1200 to 1800, at 90℃, and 1500 rpm over 1 h. All the processes involved in dispersion of MWCNTs into epoxy
Lager Image
Effect of pressure of supercritical carbon dioxide on the UV-visspectral absorbance of multi-walled carbon nanotube (MWCNT)/epoxydispersions processed at 90℃, 1 h, 1500 rpm.
have been optimized through UV-vis spectroscopy on the basis of van Hove singularities [20] . Fig. 1 illustrates the effect of pressure on the absorption maxima centered at around 286 nm of the formulations of MWCNT/epoxy resin prepared at various concentrations in SCC. If MWCNTs are dispersed in epoxy resin on a scale of nano-sized particles, the respective formulations should evince higher absorbance at the same concentration of MWCNTs due to absorption on the interfaces between the CNTs and the epoxy resin. With pressure of SCC, the intensity of absorption for each of the formulations was increased irrespective of the concentration of MWCNTs. Dispersion of MWCNTs at 0.1 phr into epoxy (0.1 mole/dL) at 1200 psi showed a peak intensity of 0.346, which has been optimized to 0.544 at 1800 psi. An increase in the concentration of MWCNTs to 0.2 resulted in an increase in the peak intensity to 1.345 at 1200 psi, optimized to 1.431 at 1400 psi. Further increase in the concentration of MWCNTs to 0.3 phr increased the peak intensity of 1.919 at 1400 psi, optimized to 1.973 at 1800 psi. Such optimization of the peak intensity may be attributed to enhanced dispersion of MWCNTs into the epoxy resin at 1800 psi under applied conditions of temperature, stirring rate, and time in SCC. The epoxy formulations prepared at 1800 psi were therefore cured with TETA at 15 phr with the aim of obtaining CECs with comparable physical properties.
The effect of SCC assisted dispersion of various concentrations of MWCNTs into epoxy on the microstructure of respective CECs has been investigated through compositional mapping with AFM ( Fig. 2 ). AFM images at a scan size of 10 μm revealed a biphasic composition of CECs with bright and dark areas. The images show large smooth zones with a bright appearance corresponding to the MWCNTs, and small entities with a grainy aspect identifiable as ordered domains of epoxy resin, forming a dark phase. The inherent properties of the phases are related to their relative phase contrast. Brighter areas of
Lager Image
Atomic force microscopy images (XY = 10 μm) of cured epoxy (a)and multi-walled carbon nanotube (MWCNT)/epoxy composites synthesizedthrough supercritical carbon dioxide assisted dispersion at MWCNTconcentration (phr) of 0.1 (b), 0.2 (c) and 0.3 (d).
AFM images may be attributed to the greater force experienced by the cantilever tip during contact with MWCNTs, whereas dark areas of the image correspond to amorphous phases due to the epoxy matrix. Cured epoxy ( Fig. 2 a) shows relatively more dark areas due to its brittle nature, and these areas become been brighter with higher concentrations of MWCNTs ( Figs. 2 b and d). CECs synthesized up to a MWCNT concentration of 0.2 do not show significant aggregates of MWCNTs, indicating that the interaction between MWCNTs and the epoxy resin helps reduce the possibility of large agglomerations. CECs synthesized at a MWCNT concentration of 0.3 reveal the presence of organized bundles in the epoxy matrix ( Fig. 2 d).
The extent of relative changes of the phase morphology of CECs has further been explored through examination of their average roughness (a r , nm). Cured epoxy shows average roughness (a r , nm) of 6.93 at an indenter height (nm) of 139.46 ( Fig. 2 a). With increasing concentration of MWCNTs, a gradual increase in the ar of the respective CECs has been observed. CECs synthesized at a MWCNT concentration of 0.1 shows an a r of 14.93 at an indenter height of 302.35 ( Fig. 2 b). An increase in a r to 22.52 was observed at an indenter height of 288.32 for CECs synthesized at a MWCNT concentration of 0.2 ( Fig. 2 c). CECs synthesized at a MWCNT concentration of 0.3 showed an increase in a r to 30.95 at an indenter height of 348.45 [29 , 35 , 36] .
A SEM analysis of cured nanocomposites reveals the increasing tendency of reaggregation of MWCNTs in the epoxy with increasing nanotube concentration. Fig. 3 a shows a SEM of CECs at 1 KX, 10 μm, synthesized by dispersing MWCNTs at 0.1 phr in SCC. The micrograph reveals a good dispersion of MWCNTs into the epoxy matrix, likely due to destruction of their entanglement networks. However, this has been associated with some agglomeration, which distinctly appeared at 5 KX, 2 μm ( Fig. 3 b). In order to gain insight into the extent of dispersion of MWCNTs according to their concentration in SCC, the study of microstructure of CECs was further conducted at 5 KX, 2 μm. Upon increasing the concentration of MWCNTs into epoxy to 0.2 while retaining the identical supercritical processing conditions,
Lager Image
Scanning electron microscopy images of multi-walled carbonnanotube (MWCNT)/epoxy composites (CECs) synthesized through supercriticalcarbon dioxide assisted dispersion at MWCNT concentrationof 0.1 phr at 1.0 KX, 10 μm (a), 0.1 phr (b), 0.2 phr (c), 0.3 phr (d), fracturedsurface of CECs at 0.1 phr (e) and 0.3 phr (f ) at 5.5 KX, 2 μm.
a slight increase in the tendency of agglomeration of MWCNTs in the epoxy matrix was observed due to their entanglement in the matrix ( Fig. 3 c). At a MWCNT concentration of 0.3, networks of clusters connected by individual MWCNTs with size (μm) ranging from 1.54 to 3.65 have been formed ( Fig. 3 d) due to their high degree of entanglement in the epoxy matrix, which likely is responsible for their characteristic reagglomeration in the epoxy matrix [17] .
Figs. 3 e and f show different zones of the fractured surface of CECs synthesized at MWCNT concentrations of 0.1 and 0.3. SEM reveals the presence of stress concentration in the matrix of fractured epoxy due to agglomeration of MWCNTs. With increasing concentration of MWCNTs, modification of the roughness of the fractured surface was observed mainly in the areas of the CECs where the crack propagation initiated, which is common in brittle epoxy resin fractures [31 , 35 , 36] . The spectral, microstructure, and electrical conductivity data reveal the capability of SCC to provide well dispersed MWCNT/epoxy formulations up to a filler concentration of 0.2 at applied supercritical processing conditions within 1h without sonication [18 , 29 , 31] .
SCC assisted dispersion of MWCNTs into epoxy has been further substantiated by the increase in their DC electrical conductivity (σ DC , S/cm) with the concentration of MWCNTs. With increasing concentration of MWCNTs up to 0.2, the σ DC of CECs was increased by five orders of magnitude. The σ DC of CECs with the well dispersed MWCNTs is two orders of magnitude higher than that of the CECs with poorly dispersed MWCNTs. For this reason it is easier for the well dispersed MWCNTs to form conductive paths due to their relatively homogeneous dispersion of nanoparticles compared to the case of aggregated MWCNTs [23] . It was confirmed that the percolation threshold for CECs was close to a MWCNT concentration of 0.2 [32 , 35 , 36] . The spectral, microstructure, and σ DC data reveal the capability of SCC to provide well dispersed MWCNT/epoxy formulations up
Lager Image
Fourier transformed infra-red spectra of cured epoxy (a) and amulti-walled carbon nanotube (MWCNT)/epoxy composites synthesizedat MWCNT concentration of 0.3 phr in supercritical carbon dioxide.
to a filler concentration of 0.2 at applied supercritical processing conditions within 1h without procedures of sonication or other related physical methods [18 , 28 , 30] .
The assignments of group frequencies at respective wave numbers (cm -1 ) based on FT-IR spectra reveal the formation of CECs ( Fig. 4 ). Cured epoxy shows wave numbers corresponding to characteristic group frequencies at 3670.25 (ν OH), 1756.23 (ν COOH), 1673.27(δ NH), 1457.09 (δ CH), and 749.88 (oxirane ring). CECs synthesized at a MWCNT concentration of 0.3 shows characteristic absorptions at 3407.05 (ν OH), 3039.73 (Aromatic, ν CH), 2962.47-2925.31 (ν as , CH), 2868.10 (ν sy , CH), 1756.64 (νCOOH), 1608.32 (δNH), 1509.00 (δNH, out of plane), 1460.33-1360.27 (δ CH), 1297.58-1245.22 (ν as ,CN), 1180.78-1033.86 (ν sy ,CN), 828.98 (δCH 2 , twisting/wagging), and 763.68-730.99, corresponding to contraction of the epoxide ring.
- 3.1. Mechanical properties
Fig. 5 represents the effect of MWCNT concentration on control over wear loss (mg/min) of CECs at selected hydraulic end loads (bar) of 2.0 and 4.0 at a constant disc speed of 320 rpm. With increasing concentration of MWCNTs remarkable control over W L of the CECs was observed, and subsequently increased with hydraulic end load ( Fig. 5 a) and time ( Fig. 5 b). At 2b, cured epoxy shows a W L of 3.7 within 2.0 min. With increasing concentration of MWCNTs, respective CECs show W L values ranging from 2.8 to 2.0 within 2.1 to 2.5 min at 2b. An increase in the hydraulic end load from 2.0b to 4.0b induced the observed increase in wear behavior of the cured epoxy and respective CECs. At 4b the cured epoxy shows a W L of 4.0 within 2.3 min, which was gradually controlled to 2.25 within 2.9 min, corresponding to CECs synthesized at a MWCNT concentration of 0.3.
In order to gain further insight into the remarkable control over the wear behavior of the CECs, their RH and impact
Lager Image
Effect of multi-walled carbon nanotube (MWCNT) concentration(phr) on wear loss at 320 rpm and Rockwell hardness of MWCNT/epoxy composites (CECs).
Lager Image
Effect of hydraulic end load on wear time of CECs at 320rpm.
strength (kJ/m 2 ) were investigated. With W L , a simultaneous increase in hardness and impact strength of CECs was observed, and this was further intensified with the concentration of MWCNTs. Cured epoxy shows a RH of 70.5. With increasing concentration of MWCNTs, a gradual increase in the RH of CECs was observed, ranging from 78.5 to 84.3 ( Fig. 5 a). Accordingly, the cured epoxy shows an impact strength of 17.16, whereas with increasing concentration of MWCNTs, the impact strength of respective CECs increased from 21.48 to 31.01.
Cured epoxy shows tensile strength and Young modulus
Lager Image
Dynamic mechanical analysis scans of cured epoxy (a) and multi-walled carbon nanotube (MWCNT)/epoxy composites synthesized at MWCNTconcentration (phr) of 0.1 (b), 0.2 (c) and 0.3 (d) in supercritical carbon dioxide.
(MPa) of 30.36 and 384.89, respectively. At a low concentration of MWCNTs, a marginal increase in the tensile strength of CECs has been observed. With increasing concentration of MWCNTs, a gradual increase in the tensile strength of respective CECs, ranging from 36.44 to 49.36, was observed. This has been accompanied by a simultaneous reduction in the Young moduli of respective CECs ranging from 389.18 to 369.95. The loss in the Young moduli has further been supported with the compressive strength (MPa) data. With increasing concentration of MWCNTs, a gradual loss in the compressive strength of epoxy has been observed, ranging from 131.80 to 110.70. Such modifications in the wear performance, hardness, an impact and tensile strength with the concentration of MWCNTs may be assigned to interfacial bonding and enhanced dispersion of MWCNTs in SCC, their high specific mechanical properties, specific surface area, and good interfacial adhesion between CNTs and the matrix, which plays a role in enhancing the framework. This enhanced dispersion of MWCNTs restricts the mobility of polymer chains under loading and improved the modulus and strength at small loadings ( Table 1 ).
Fig. 6 shows the effects of concentration of MWCNTs on the dynamic mechanical properties of CECs. The respective values of the elastic part of the complex modulus (storage), loss moduli (MPa), and loss factor (tan δ) have been summarized ( Table 1 ). The moduli of the CECs were higher over cured epoxy, due to the high stiffness of the MWCNTs. With increasing concentration of MWCNTs, a regular increase in both moduli of the CECs was observed. This increase in the loss modulus of the resin with the addition of MWNTs may be ascribed to the dispersion of MWCNTs, which led to a significant increase of the moduli both in a glassy and in a rubbery state. This increase in the elastic properties of CECs at elevated temperature may be attributed to interactions between the MWCNTs and the epoxy due to enormous surface area. This interfacial interaction reduces the mobility of the epoxy matrix around the nanotubes and leads to an observed increase in thermal stability.
Tg measurements are highly important as they determine the critical service temperature of materials for engineering applications. If the slope of the storage modulus values in the glass transition zone is used to estimate the Tg of the neat and the CECs, then it can be stated that, similar to the case of the storage modulus, the addition of MWCNTs led to a general increase of the Tg up to 110℃, corresponding to CECs synthesized with a MWCNT concentration of 0.3. The restricted mobility of the polymer chains around the nanotubes and the interfacial bonds between them also explain the increase in Tg. This gain in thermostability can again be interpreted as a reduction of the mobility of the epoxy matrix around the nanotubes by the interfacial interactions. While the increase of the storage modulus at the glassy state with the addition of MWCNTs is a common observation due to the reinforcing effect of MWCNTs and restricted mobility of epoxy chains, CECs synthesized at a MWCNT concentration of 0.2 do not display rubbery modulus enhancements due to the drop in the Tg. With increasing concentration of MWCNTs, a regular increase in the loss modulus of CECs has been observed.
The loss modulus of CECs indicates the energy used to deform the material, which is dissipated into heat and can be used as a measurement of the viscous component or unrecoverable oscillation energy dissipated per cycle. The increase in the loss
Physical characteristics of CECs synthesized through SCC assisted dispersion of MWCNT into epoxyCECs: multi-walled carbon nanotube/epoxy composites, SCC: supercritical carbon dioxide, MWCNT: multi-walled carbon nanotube, DSC: differential scanning caloriemetry, DMTA: dynamic mechanical thermal analysis.aAmerican Society for Testing and Materials (ASTM) D 638,bASTM D 256,cASTM D 695.dWeight residue (%,w/w) from thermogravimetric (TG, temperature of degradation).eHeat of degradation from differential thermal analysis (peak temperature).fRate of degradation from differential thermogravimetry (peak temperature).gCuring enthalpy,hTg,istorage modulus (MPa),jloss modulus (MPa).kDC electrical conductivity.
Lager Image
Physical characteristics of CECs synthesized through SCC assisted dispersion of MWCNT into epoxy CECs: multi-walled carbon nanotube/epoxy composites, SCC: supercritical carbon dioxide, MWCNT: multi-walled carbon nanotube, DSC: differential scanning caloriemetry, DMTA: dynamic mechanical thermal analysis. aAmerican Society for Testing and Materials (ASTM) D 638, bASTM D 256,cASTM D 695. dWeight residue (%,w/w) from thermogravimetric (TG, temperature of degradation). eHeat of degradation from differential thermal analysis (peak temperature). fRate of degradation from differential thermogravimetry (peak temperature). gCuring enthalpy, hTg, istorage modulus (MPa),jloss modulus (MPa). kDC electrical conductivity.
modulus with increasing concentration of MWCNTs can be interpreted by enhanced susceptibility dispersion of MWCNTs into the epoxy, leading to less energy dissipation in the system under visco-elastic deformation. The well dispersed MWCNTs in the CECs must dissipate energy due to resistance against viscoelastic deformation of the surrounding matrix.
Loss factor (tan δ) curves for the neat resin and the CECs can be used to evaluate their damping behaviors. An increase in the height of the tan δ curves of CECs synthesized at a MWCNT concentration 0.1 phr was observed without an appreciable change in the width, suggesting that with the addition of 0.1 phr MWCNTs there was a corresponding change in the energy absorption capability of the resin. However, with an increase in the concentration of MWCNT to 0.2 phr, a marginal increase in the loss factor was observed. This may be attributed to slight modification of the stiffening effect of epoxy due to the dispersion of MWCNTs. However, this is not the only mechanism that influences the way energy is dissipated in the modified systems. Note again that Tg is associated with the temperature where the tan δ peak is observed, in the present study, a clear increase of
Lager Image
Differential scanning caloriemetry scans of cured epoxy (a) andmulti-walled carbon nanotube (MWCNT)/epoxy composites synthesizedat MWCNT concentration (phr) of 0.1 (b), 0.2 (c) and 0.3 (d) in supercriticalcarbon dioxide.
dethe Tg value has been observed with increasing concentration of MWCNTs. This indeed indicates that the MWCNTs, at the investigated concentrations, have a remarkable effect on the relaxation phenomena, leading to the glass transition of the system. This significant increase of the moduli and Tg of CECs may
Lager Image
Simultaneous thermogravimetric-differential thermogravimetry-differential thermal analysis (TG-DTG-DTA) scans of cured epoxy (a) and multi-walled carbonnanotube (MWCNT)/epoxy composites synthesized at MWCNT concentration (phr) of 0.1 (b), 0.2 (c) and 0.3 (d) in supercritical carbon dioxide.
be attributed to improved dispersion and interfacial bonding between the CNTs and the epoxy matrix. The Tg data evaluated through DMA at the loss modulus were further found to be in proximity with DSC ( Table 1 ). Cured epoxy showed a Tg (℃) of 105.19. CECs synthesized at a MWCNT concentration of 0.1 have shown a reduction in Tg to 95.91. A further increase in the concentration of MWCNTs contributed to a remarkable increase in the Tg of CECs up to 107.76. This increase is ascribed to increased density and decreased mobility of the polymer chains. [37] .
- 3.2. Thermal properties
The study of the curing behavior of MWCNT-filled epoxies is of immense importance for designing respective nanocomposites and optimization of their fabrication. The curing behavior of epoxy and respective MWCNT/epoxy formulations synthesized in SCC has been investigated through DSC ( Fig. 7 ). Cured epoxy shows a very weak peak corresponding to curing enthalpy, indicating their complete polymerization. The curing enthalpy (ΔH cure , J/g) of CECs has been increased to 19.41 up to a concentration of MWCNTs of 0.2. CECs synthesized at a MWCNT concentration of 0.1 show an exothermic peak (℃) centered at 62.07 with corresponding curing enthalpy (ΔH cure , J/g) of 2.95. Further increase in the concentration of MWCNTs to 0.2 yielded an exothermic peak centered at 71.47 with a ΔH cure of 19.41. Further increase in the concentration of MWCNTs shifted the exothermic peak to 66.76 with a corresponding reduction in ΔH cure to 11.01. This increase in the ΔH cure value may be attributed to acceleration of the curing process up to a MWCNT concentration of 0.2 ( Table 1 ).
Cured epoxy and respective CECs have shown two-step decomposition with common temperatures corresponding to TG onset (250℃) and endset (550℃). Cured epoxy and the respective CECs retained their respective weights (W r , % w/w) of around 96 at the common TG onset, indicating remarkable heat resistance up to 250℃. With increasing MWCNT concentration, in general, all CECs decomposed at higher rates (mg/min) at the first step of decomposition ranging from 265 to 287℃ compared to the second step of decomposition ranging from 330 to 326℃. At TG endset, all the samples rapidly decomposed with weak heat (J/mg × 10 -3 ) and a rapid rate of decomposition (mg/ min) over TG onset. This has been revealed through a general increase in the heat (J/mg) and rates (mg/min) of decomposition of CECs with increasing peak temperatures corresponding to DTA and DTG, respectively. Prior to TG onset, the weight loss of samples at 100℃ may be assigned to their respective moisture content (%, w/w). Cured epoxy showed moisture content of 1.46. A remarkable reduction in the moisture content to 1.17 was observed for CECs synthesized at a MWCNT concentration of 0.1, which was subsequently increased to 1.49 at a MWCNT concentration of 0.3. However, control of such decomposition rates was observed with an increase in the concentration of MWCNTs up to 0.2 ( Table 1 ). On an individual basis, at the TG onset temperature, cured epoxy decomposed at rates of 0.45 at 281℃ and 0.49 at 330℃ with an integrated DTA peak at 284℃ corresponding to a heat of decomposition of 0.425. At TG endset, cured epoxy rendered relatively fast decomposition at a rate of 0.70 at 486℃ with a weak heat of decomposition (J/mg × 10 -3 ) of 1.09 ( Fig. 8 a). CECs synthesized at a MWCNT concentration of 0.1 decomposed at rates of 0.46 at 287℃ and 0.41 at 331℃ with an integrated DTA peak at 287℃ corresponding to heat of decomposition of 0.56. At TG endset, CECs showed fast decomposition at a rate of 0.63 at 504℃ with a weak heat of decomposition of 1.40 at 504℃ ( Fig. 8 b). At TG onset, CECs synthesized at a MWCNT concentration of 0.2 decomposed at rates of 0.50 at 265℃ and 0.39 at 326℃ with an integrated DTA peak at 287℃ corresponding to a heat of decomposition of 0.63. At TG endset, CECs displayed moderate decomposition at a rate of 0.65 at 501℃ with a weak heat of decomposition of 1.40 at 504℃ ( Fig. 8 c). At TG onset, CECs synthesized at a MWCNT concentration of 0.3 decomposed at a single rate of 0.52 at 282℃ with a monotonous DTA peak corresponding to a heat of decomposition 0.67 at 283℃ At TG endset, CECs showed rapid decomposition at a rate of 0.80 at 515℃ with a weak heat of decomposition of 1.80 at 520℃ ( Fig. 8 d).
4. Conclusions
The authors investigated SCC assisted dispersion of various concentrations (phr) of MWCNTs ranging from 0.1 to 0.3 into epoxy resin (0.1 mol) at various pressures (psi) ranging from 1200 to 1800 at 90℃, an 1500 rpm over 1h. The capability of SCC to enhance the dispersion of MWCNTs into epoxy has been revealed through pressure driven van Hove singularities via UVvisible spectra, microscopy, and DC electrical conductivity. Dispersion of MWCNTs up to a concentration of 0.2 phr has been optimized. Further increase in the concentration of MWCNTs to 0.3 resulted in reaggregation of MWCNTs with size (μm) ranging from 1.54 to 3.65 into the epoxy matrix. The CECs processed up to a MWCNT concentration of 0.2 phr at 1800 psi in SCC rendered enhanced mechanical, thermal, an thermomechanical properties, improved DC electrical conductivity, and reduced wear behavior compared to cured epoxy. The increase in the storage modulus and Tg was indicative of restricted movement of polymer chains, which is ascribed to a strong interaction presented between MWCNTs and epoxy chains, as supported by SEM and AFM analyses. The present study provides an environmentally benign method of dispersing MWCNTs into epoxy assisted with SCC, resulting in CECs with improved dispersion and physical properties.
References
Li L , Zheng X , Wang J , Sun Q , Xu Q (2012) Solvent-exfoliated and functionalizedgraphene with assistance of supercritical carbon dioxide. ACS Sustain Chem Eng 1 144 -
Hao J , Lian Y , Guan L , Yue D , Guo X , Zhao S , Zhao Y , Ibrahim K , Wang J , Qian H , Dong J , Yuan H , Xing G , Sun B (2011) Supercriticalsynthesis and characterization of SWNT-based one dimensionalnanomaterials. Nanoscale 3 3103 -
Ye S , Wu F , Ye XR , Lin Y (2009) Supercritical fluid assisted synthesis andprocessing of carbon nanotubes. J Nanosci Nanotechnol 9 2781 -
Zheng X , Xu Q , Li Z (2010) Supercritical CO2-driven, periodic patterningon one-dimensionals carbon nanomaterials. Sci China Chem 53 1525 -
Li Z , Andzane J , Erts D , Tobin JM , Wang K , Morris MA , Attard G , Holmes JD (2007) A supercritical-fluid method for growing carbon nanotubes. Adv Mater 19 3043 -
Li Z , Jaroniec M , Papakonstantinou P , Tobin JM , Vohrer U , Kumar S , Attard G , Holmes JD (2007) Supercritical fluid growth of porouscarbon nanocages. Chem Mater 19 3349 -
Bertoncini M , Coelho LAF , Maciel IO , Pezzin SH (2011) Purification ofsingle-wall carbon nanotubes by heat treatment and supercriticalextraction. Mater Resh 14 380 -
Wang JS , Wai CM , Shimizu K , Cheng F , Boeckl JJ , Maruyama B , Brown G (2007) Purification of single-walled carbon nanotubes using asupercritical fluid extraction method. J Phys Chem C 111 13007 -
Hiramatsu M , Hori M (2010) Preparation of dispersed platinum nanoparticleson a carbon nanostructured surface using supercritical fluidchemical deposition. Materials 3 1559 -
Wang J , Khlobystov AN , Wang W , Howdle SM , Poliakoff M (2006) Coating carbon nanotubes with polymer in supercritical carbondioxide. Chem Commun 1670 -
Fifield LS , Dalton LR , Addleman RS , Galhotra RA , Engelhard MH , Fryxell GE , Aardahl CL (2004) Noncovalent functionalization ofcarbon nanotubes with molecular anchors using supercritical fluids. J Phys Chem B 108 8737 -
Wang XB , Liu ZM , Hu PA , Liu YQ , Han BX , Zhu DB (2005) Nanofluidsin carbon nanotubes using supercritical CO2: a first step towards ananochemical reaction. Appl Phys A 80 637 -
Nguyen VH , Shim JJ (2013) Supercritical fluid-assisted synthesis ofa carbon nanotubes-grafted biocompatible polymer composite. Compos Interfaces 20 155 -
Liu Z , Han B (2009) Synthesis of carbon-nanotube composites using supercriticalfluids and their potential applications. Adv Mater 21 825 -
Yue B , Wang Y , Huang CY , Pfeffer R , Iqbal Z (2007) Polymeric nanocompositesof functionalized carbon nanotubes synthesized insupercritical CO2. J Nanosci Nanotechnol 7 994 -
Huang YY , Terentjev EM (2012) Dispersion of carbon nanotubes: mixing,sonication, stabilization, and composite properties. Polymers 4 275 -
Ma PC , Mo SY , Tang BZ , Kim JK (2010) Dispersion, interfacial interactionand re-agglomeration of functionalized carbon nanotubesin epoxy composites. Carbon 48 1824 -
Papanicolaou GC , Papaefthymiou KP , Koutsomitopoulou AF , Portan DV , Zaoutsos SP (2012) Effect of dispersion of MWCNTs on the staticand dynamic mechanical behavior of epoxy matrix nanocomposites. J Mater Sci 47 350 -
Gkikas G , Barkoula NM , Paipetis AS (2012) Effect of dispersion conditionson the thermo-mechanical and toughness properties of multiwalled carbon nanotubes-reinforced epoxy. Composites B 43 2697 -
Garg P , Singh B , Kumar G , Gupta T , Pandey I , Seth RK , Tandon RP , Mathur R (2011) Effect of dispersion conditions on the mechanicalproperties of multi-walled carbon nanotubes based epoxyresin composites. J Polym Res 18 1397 -
Prolongo SG , Burón M , Gude MR , Chaos-Morán R , Campo M , Ureña A (2008) Effects of dispersion techniques of carbon nanofibers onthe thermo-physical properties of epoxy nanocomposites. Composites Sci Technol 68 2722 -
Chen H , Jacobs O , Wu W , Rüdiger G (2007) Effect of dispersionmethod on tribological properties of carbon nanotube reinforcedepoxy resin composites. Polym Test 26 351 -
Song YS , Youn JR (2005) Influence of dispersion states of carbon nanotubeson physical properties of epoxy nanocomposites. Carbon 43 1378 -
Guo P , Chen X , Gao X , Song H , Shen H (2007) Fabrication and mechanicalproperties of well-dispersed multiwalled carbon nanotubes/epoxycomposites. Composites Sci Technol 67 3331 -
Hosur M , Barua R , Zainuddin S , Kumar A , Trovillion J , Jeelani S (2013) Effect of processing techniques on the performance of Epoxy/MWCNT nanocomposites. J Appl Polym Sci 127 4211 -
Gupta ML , Sydlik SA , Schnorr JM , Woo DJ , Osswald S , Swager TM , Raghavan D (2013) The effect of mixing methods on the dispersionof carbon nanotubes during the solvent-free processing of multiwalledcarbon nanotube/epoxy composites. J Polym Sci B 51 410 -
Martone A , Formicola C , Piscitelli F , Lavorgna M , Zarrelli M , Antonucci V , Giordano M (2012) Thermo-mechanical characterizationof epoxy nanocomposites with different carbon nanotube distributionsobtained by solvent aided and direct mixing. eXPRESS Polym Lett 6 520 -
Karippal JJ , Murthy HNN , Rai KS , Krishna M , Sreejith M (2010) Theprocessing and characterization of MWCNT/epoxy and CB/epoxynanocomposites using twin screw extrusion. Polym-Plast Technol Eng 49 1207 -
Jin FL , Park SJ (2013) Recent advances in carbon-nanotube-based epoxycomposites. Carbon Lett 14 1 -
Frømyr TR , Hansen FK , Olsen T (2012) The optimum dispersion of carbonnanotubes for epoxy nanocomposites: evolution of the particlesize distribution by ultrasonic treatment. J Nanotechnol 2012 545930 -
Jiménez-Suárez A , Campo M , Gaztelumendi I , Markaide N , Sánchez M , Ureña A (2013) The influence of mechanical dispersion ofMWCNT in epoxy matrix by calendering method: batch methodversus time controlled. Composites B 48 88 -
Prolongo SG , Meliton BG , Del Rosario G , Ureña A (2012) Simultaneousdispersion and alignment of carbon nanotubes in epoxy resinthrough chronoamperometry. Carbon 50 5489 -
Glaskova T , Zarrelli M , Aniskevich A , Giordano M , Trinkler L , Berzina B (2012) Quantitative optical analysis of filler dispersion degreein MWCNT–epoxy nanocomposite. Composites Sci Technol 72 477 -
Foltran S , Cloutet E , Cramail H , Tassaing T (2012) In situ FTIR investigationof the solubility and swelling of model epoxides in supercriticalCO2. J Supercrit Fluids 63 52 -
Guadagno L , De Vivo B , Di Bartolomeo A , Lamberti P , Sorrentino A , Tucci V , Vertuccio L , Vittoria V (2011) Effect of functionalization onthe thermo-mechanical and electrical behavior of multi-wall carbonnanotube/epoxy composites. Carbon 49 1919 -
Guadagno L , Vertuccio L , Sorrentino A , Raimondo M , Naddeo C , Vittoria V , Iannuzzo G , Calvi E , Russo S (2009) Mechanical and barrierproperties of epoxy resin filled with multi-walled carbon nanotubes. Carbon 47 2419 -
Allaoui A , El Bounia N (2009) How carbon nanotubes affect the curekinetics and glass transition temperature of their epoxy composites?A review. eXPRESS Polym Lett 3 588 -