A novel drying process for oil adsorption of expanded graphite
A novel drying process for oil adsorption of expanded graphite
Carbon letters. 2013. Jul, 14(3): 193-195
Copyright ©2013, Korean Carbon Society
This is an Open Access article distributedunder the terms of the Creative CommonsAttribution Non-Commercial License( which permits unrestrictednon-commercial use, distribution, andreproduction in any medium, providedthe original work is properly cited.
  • Received : May 03, 2013
  • Accepted : June 27, 2013
  • Published : July 31, 2013
Export by style
Cited by
About the Authors
Soo-Jin, Park
Department of Chemistry, Inha University, Incheon 402-751, Korea
Seul-Yi, Lee
Department of Chemistry, Inha University, Incheon 402-751, Korea
Ki-Seok, Kim
Department of Chemistry, Inha University, Incheon 402-751, Korea
Fan-Long, Jin
Department of Polymer Materials, Jilin Institute of Chemical Technology, Jilin City 132022, People’s Republic of China

Expanded graphite (EG) was prepared using a drying process for application as an oiladsorbent: the morphology, expansion volume, and oil absorption capacity of the EG were investigated. The expanded volume of the EG increased with an increasing reaction time and heat treatment temperature. The oil adsorption capacity of the EG was 45 g of n-dodecane per 1 g of EG. It is noted that the drying process of EG is a useful technique for a new oiladsorbent.
1. Introduction
Expanded graphite (EG) is a well-known carbon material that is usually produced from various graphite intercalation compounds (GICs). The process of GIC exfoliation may be undertaken using chemical, electrochemical, and thermal methods. EG maintains layered structures similar to natural flake graphite, but it has differences in the distances between the graphite layers. As a new carbon material, EG has been used in many fields, such as gaskets, seals, batteries, substratum for adsorption, etc. Among these applications, its potential as an adsorbent for heavy oil has attracted significant attention due to the surprisingly high adsorption capacity of EG for various oils [1 - 7] .
Toyoda and Inagaki [8] studied the adsorption behaviors of exfoliated graphites using four types of heavy oils. The results indicated that the maximum adsorption capacity of 1 g of exfoliated graphite was as high as 86 g of A-grade heavy oil or 76 g of crude oil. Zheng et al. [9] investigated the adsorption capacity of exfoliated graphite for oil-sorption in and among worm-like particles. Their results demonstrated that the adsorption capacities of the pores in and among the worm-like particles increased with increases in the exfoliation volume.
In this study, EG was prepared using a new drying process for oil-adsorbent materials, and its morphology, expansion volume, and oil absorption capacity are investigated.
2. Experimental
- 2.1. Materials
The graphite used in this study was supplied by GRAF Guard™ (>297 μm, flake graphite). Oleum (25% SO 3 ) was used as an intercalant, and n-dodecane was purchased from Sigma (Korea).
- 2.2. EG preparation
The GICs were prepared using the direct reaction of graphite with oleum gas in atmospheric conditions. In order to intercalate SO 3 in the graphite layers, SO 3 gas was vaporized through heating the oleum at 120℃ and passing it through an upper flask filled with graphites. The GICs were dried at 90℃ for 8 h in order to remove the SO 3 molecules condensed on the graphite surfaces. The EG was obtained through heat treatment of the dried graphite particles at 900℃ for 1 min.
- 2.3. Characterization and measurements
The morphology of the EG was examined using a scanning electron microscopy (SEM; JXA 840A, JEOL, Japan). The expansion volume was calculated from the EG volumes before and after the heat treatment. The oil adsorption tests were conducted via direct addition of the graphite to the oil. The EG was added to a mixture of water and oil. It was then dried on an 80 μm sieve in order to remove the non-aborted oil and moisture. The oil adsorption was calculated using the following equation:
PPT Slide
Lager Image
where m0 and m are the weight of EG before and after the adsorption, respectively.
3. Results and Discussion
Fig. 1 presents a SEM image of the EG. As seen from this image, there were numerous carbon layers with large interlayer distances, which were formed as a result of the heat treatment of the GICs at a sufficiently high temperature. Furthermore, the EG had a loose and porous vermicular structure. The structure of the EG appeared to have parallel boards and it exhibited many pores with different sizes [10 , 11] .
Fig. 2 presents the expanded volume of the EG as a function of the reaction time. The expanded volume of the EG increased significantly with an increasing reaction time up to 10 h. When the reaction time was increased, the graphite layers opened gradually due to the oxidizing agent, and the molecules of the inserting reagent entered the graphite layers, which resulted in the formation of a large amount of GICs. Thus, the expansion volume of the EG increased rapidly [12] .
PPT Slide
Lager Image
Expanded graphite morphology.
Fig. 3 presents the expanded volume of the EG as a function of the heat treatment temperature. When the heat treatment temperature increased, the expanded volume increased gradually with the maximum expanded volume being achieved at 900℃ and the expanded volume decreasing over 900℃. This can be attributed to the expanded GIC needing energy; however, some carbon began to combust over 900℃ [12] .
Fig. 4 shows the oil adsorption capacity of natural graphite and EG for n-dodecane. The oil adsorption tests indicated that the n-dodecane was absorbed rapidly by the EG. The oil adsorption capacity of EG (45 g of n-dodecane per 1 g of EG) was significantly higher than that of natural graphite. These results can be attributed to the EG having surface characteristics that consist of micropores and macropores, which induce the capillary phenomenon between the particles and pores on the surface of the EG and result in an increasing oil adsorption capacity [13 , 14] .
In this work, EG was prepared using a drying process for potential application as an oil-adsorbent. The morphology,
PPT Slide
Lager Image
Expanded volume of the expanded graphite as a function of thereaction time.
PPT Slide
Lager Image
Expanded volume of the expanded graphite as a function of theheat treatment temperature.
PPT Slide
Lager Image
Oil adsorption capacities of natural graphite and expandedgraphite for n-dodecane.
expansion volume, and oil adsorption capacity of EG were investigated. As expected, the expanded volume of the EG increased with an increasing heat treatment temperature up to 900℃. The oil adsorption capacity of EG was 45 g of n-dodecane per 1 g of EG. The data reported in this study suggests that EG has excellent properties and is a promising candidate for oiladsorbent applications.
This work was supported by the Korea CCS R&D Center(KCRC) grant funded by the Korea government (Ministry ofScience, ICT and Future Planning) (grant No. 0031985).
Balima F , Pischedda V , Le Floch S , Brulet A , Lindner P , Duclaux L , San-Miguel A (2013) An in situ small angle neutron scattering study of expanded graphite under a uniaxial stress. Carbon 57 460 -    DOI : 10.1016/j.carbon.2013.02.019
Dittrich B , Wartig KA , Hofmann D , Mulhaupt R , Schartel B (2013) Flame retardancy through carbon nanomaterials: carbon black,multiwall nanotubes, expanded graphite, multi-layer graphene andgraphene in polypropylene. Polym Degrad Stab 98 1495 -    DOI : 10.1016/j.polymdegradstab.2013.04.009.
Park SJ , Kim KS (2004) A study on oil adsorption of expanded graphites. Korean Chem Eng Res 42 362 -
Park SJ , Kim KS , Hong SK (2003) Preparation and characterization ofexpanded graphites by wet process. Hwahak Konghak 41 802 -
Ajalesh Balachandran N , Philip K , Rani J (2013) Effect of expandedgraphite on thermal, mechanical and dielectric properties of ethylene–propylene–diene terpolymer/hexa fluoropropylene–vinylidinefluoridedipolymer rubber blends. Eur Polym J 49 247 -    DOI : 10.1016/j.eurpolymj.2012.08.014
Sever K , Tavman IH , Seki Y , Turgut A , Omastova M , Ozdemir I (2013) Electrical and mechanical properties of expanded graphite/highdensity polyethylene nanocomposites. Composites B 53 226 -    DOI : 10.1016/j.compositesb.2013.04.069
Piana F , Pionteck J (2013) Effect of the melt processing conditions onthe conductive paths formation in thermoplastic polyurethane/expandedgraphite (TPU/EG) composites. Compos Sci Technol 80 39 -    DOI : 10.1016/j.compscitech.2013.03.002
Toyoda M , Inagaki M (2000) Heavy oil sorption using exfoliated graphite:new application of exfoliated graphite to protect heavy oil pollution. Carbon 38 199 -    DOI : 10.1016/S0008-6223(99)00174-8
Zheng YP , Wang HN , Kang FY , Wang LN , Inagaki M (2004) Sorption capacityof exfoliated graphite for oils-sorption in and among wormlikeparticles. Carbon 42 2603 -    DOI : 10.1016/j.carbon.2004.05.041
Wang LW , Tamainot-Telto Z , Metcalf SJ , Critoph RE , Wang RZ (2010) Anisotropic thermal conductivity and permeability of compactedexpanded natural graphite. Appl Therm Eng 30 1805 -    DOI : 10.1016/j.applthermaleng.2010.04.014
Krawczyk P (2011) Effect of ozone treatment on properties of expandedgraphite. Chem Eng J 172 1096 -    DOI : 10.1016/j.cej.2011.06.005
Jihui L , Huifang D , Qian L , Shufen L (2010) Preparation of sulfur-freeexpanded graphite with 320 μm mesh of flake graphite. Mater Lett 60 3927 -    DOI : 10.1016/j.matlet.2006.06.066
Li S , Tian S , Du C , He C , Cen C , Xiong Y (2010) Vaseline-loaded expanded graphite as a new adsorbent for toluene. Chem Eng J 162 546 -    DOI : 10.1016/j.cej.2010.05.059
Li S , Tian S , Feng Y , Lei J , Wang P , Xiong Y (2010) A comparative investigationon absorption performances of three expanded graphitebasedcomplex materials for toluene. J Hazard Mater 183 506 -    DOI : 10.1016/j.jhazmat.2010.07.052