Pore Structure Characterization of Poly(vinylidene chloride)-Derived Nanoporous Carbons
Pore Structure Characterization of Poly(vinylidene chloride)-Derived Nanoporous Carbons
Carbon letters. 2012. Oct, 13(4): 236-242
Copyright ©2012, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : August 08, 2012
  • Accepted : October 10, 2012
  • Published : October 31, 2012
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Hwan Jung Jung
Department of Chemistry, Graduate School of Science, Chiba University, Chiba 263-8522, Japan
Yong-Jung Kim
Research Institute of Industrial Science and Technology, Pohang 790-60, Korea
Dae Ho Lee
Department of Chemistry, Graduate School of Science, Chiba University, Chiba 263-8522, Japan
Jong Hun Han
Deptment of School of Applied Chemical Engineering, Chonnam National University, Gwangju 500-757, Korea
Kap Seung Yang
Department of Polymer & Fiber System Engineering, Chonnam National University, Gwangju 500-757, Korea
Cheol-Min Yang
Institute of Advanced Composite Materials, Korea Institute of Science and Technology, Jeonbuk 565-905, Korea
cmyang1119@kist.re.kr
Abstract
Poly(vinylidene chloride) (PVDC)-derived nanoporous carbons were prepared by various activation methods: heat-treatment under an inert atmosphere, steam activation, and potassium hydroxide (KOH) activation at 873, 1073, and 1273 K. The pore structures of PVDC-derived nanoporous carbons were characterized by the N 2 adsorption technique at 77 K. Heat treatment in an inert atmosphere increased the specific surface area and micropore volume with elevating temperature, while the average micropore width near 0.65 nm was not significantly changed, reflecting the characteristic pore structure of ultramicroporous carbon. Steam activation for PVDC at 873 and 1073 K also yielded ultramicroporosity. On the other hand, the steam activated sample at 1273 K had a wider average micropore width of 1.48 nm, correlating with a supermicropore. The KOH activation increased the micropore volume with elevating temperature, which is accompanied by enlargement of the average micropore width from 0.67 to 1.12 nm. The average pore widths of KOH-activated samples were strongly governed by the activation temperature. We expect that these approaches can be utilized to simply control the porosity of PVDC-derived nanoporous carbons.
Keywords
1. Introduction
Nanoporous carbons have strong potential for application in various fields, including energy and environmental fields in particular [1 , 2] . Extensive research has been carried out to develop efficient storage media of supercritical gases as a clean energy and a realistic alternative to the compression and liquefaction storage techniques of gases. Nanoporous carbons are considered a promising candidate for supercritical gas storage [3 , 4] . As the interaction of a supercritical gas molecule with the pore wall of nanoporous carbon is not strong enough, highly ultramicroporous (pore width < 0.7 nm) carbons are predicted to be efficient adsorption sites for supercritical gases [4] . Supercapacitors, another promising candidate for application of nanoporous carbons, have attracted much attention as energy storage devices for electric vehicles and hybrid electric vehicles [5] . For obtaining high-performance supercapacitors, several parameters of nanoporous carbons are recognized as key factors in terms of their application as electrode materials: specific surface area, pore size, conductivity, and surface chemical state. The selection of an optimal electrolyte has also been demonstrated to be an important factor for maximizing the performance of supercapacitors [6 , 7] . In particular, the relationship between the pore size of the nanoporous carbons and electrolyte ion size is an important parameter in enhancing the specific capacitance of supercapacitors [8] .
Activation conditions of PVDC-derived nanoporous carbonsPVDC: poly(vinylidene chloride), KOH: potassium hydroxide.
Lager Image
Activation conditions of PVDC-derived nanoporous carbons PVDC: poly(vinylidene chloride), KOH: potassium hydroxide.
Pore size and pore geometry of nanoporous carbons are important governing factors in the adsorption behaviors of various guest molecules [9 - 11] . The pores of nanoporous materials are classified according to the pore width w, which is the shortest distance in three-dimensional geometry, as recommended by the International Union of Pure and Applied Chemistry (IUPAC). The micropores have two subgroups of ultramicropores and supermicropores (0.7 nm < pore width < 2 nm). The maximum size of ultramicropores corresponds to the bilayer thickness of the adsorbed N 2 molecules. Although the importance of ultramicropores has been emphasized in molecular sieving and supercritical gas adsorption, an accurate evaluation of the ultramicroporosity is very difficult due to the blocking near the pore entrance. Recently, many researchers have often used the term “nanopores,” which is not recommended by the IUPAC. Nanopores can be defined as having size less than 5 nm, which is convenient owing to the inherent adsorption characteristics according to recent progress in adsorption science and technology.
Poly(vinylidene chloride) (PVDC) has been proposed as a promising precursor material for obtaining nanoporous carbons [8 , 12 - 22] . It is well known that PVDC-derived nanoporous carbons could be prepared by simple heat-treatment without an additional activation process [8 , 12 - 20] . The PVDC-derived nanoporous carbons prepared by heat-treatment alone provide an ultramicroporous structure. In this study, various activation methods for PVDC were performed in order to control the porosity of the PVDC. The effects of the activation conditions on the porosity changes were investigated by the N 2 adsorption technique at 77 K.
2. Experimental
- 2.1. Materials and methods
Homogeneous PVDC (Asahi Kasei Co.) with a crystallite size of 26.7 nm was annealed at 673 K in a N 2 atmosphere for 1 h before the activation process. Activation of PVDC was performed by three methods. First, for the heat-treatment method, the preannealed PVDC samples were further heat-treated at 873, 1073, and 1273 K in a N 2 atmosphere for 1 h, respectively. Second, for the steam activation method, the pre-annealed samples were further heat-treated at the same temperature in a steam atmosphere for 1 h. N 2 was used as a carrier gas. Third, for the KOH activation method, mixtures of pre-annealed PVDC samples and potassium hydroxide (KOH) were further heat-treated at the same temperature in a N 2 atmosphere for 1 h. The weight ratio of KOH to PVDC was 2:1. The N 2 flow rates for all experiments were 100 mL min -1 . The sample names and treatment conditions are summarized in Table 1 .
- 2.2. Characterization
The electrical conductivity of PVDC-derived porous carbons was measured with a powder resistivity measurement system. The powder samples were compressed in a cylinder cavity with a diameter of 21 mm under controlled pressure in a range of 3.6~125.4 MPa at room temperature. The pore structures were determined by N 2 adsorption at 77 K using volumetric equipment (Micromeritics ASAP 2010) after preevacuation at 423 K for 2 h, while maintaining the base pressure at 10 -4 Pa. Pore structure parameters were obtained by the subtracting pore effect (SPE) and Dubinin-Radushkevich (DR) methods. The SPE method was performed by using high-resolution α s -plots, which are constructed using the standard adsorption data for nonporous carbon black [23 , 24] .
3. Results and Discussion
- 3.1. Electrical conductivity of PVDC-derived nanoporous carbons
Fig. 1 shows the powder resistivity of PVDC-derived nanoporous carbons as a function of applied pressure. The electrical conductivities of all samples increased with an increase in applied pressure, suggesting that the contact area between adjacent particles of the nanoporous carbon increases with increasing applied pressure. The relationship between the electrical conductivity of pressed particles and activation temperatures is also
Lager Image
Powder resistivity vs. applied pressure plots for PVDC-derived nanoporous carbons: (a) PVDC pre-annealed at 673 K, (b) PVDC heat-treated in N2 atmosphere, (c) steam-activated PVDC, and (d) KOH-activated PVDC. PVDC: poly(vinylidene chloride), KOH: potassium hydroxide.
shown in Figs. 1 b-d. The electrical conductivity of all samples increases with the activation temperature. Therefore, the electrical conductivity strongly depends on the activation temperature of the PVDC. In general, the electrical conductivity of porous carbons decreases with increasing porosity, which is associated with the formation of isolated conducting pathways. However, thermal decomposition of PVDC eliminates non-carbon atoms and develops a more layered carbon structure by carbonization behavior, resulting in enhanced electrical conductivity. In our results, as heat-treatment at higher temperature accelerates the carbonization as well as the development of a porous structure of the PVDC, the electrical conductivity of the samples should be enhanced. Therefore, to obtain nanoporous carbons with better electrical conductivity, it is important to control the activation temperature for PVDC.
- 3.2. Pore structure of PVDC-derived nanoporous carbons
Fig. 2 a shows N 2 adsorption isotherms (77 K) of PVDCderived nanoporous carbons heat-treated under an inert atmosphere. All adsorption isotherms are of Type I, suggesting the presence of uniform microporosity. The saturated amounts of N 2 adsorption at relative pressure ( P/P0 ) = 1 increase with heat-treatment temperature. The N 2 adsorption isotherms of all samples show steep uptake at low P/P0 due to monolayer adsorption on the micropore walls. Fig. 2 b shows the highresolution α s -plots for N 2 adsorption isotherms at 77 K. The slope of the line passing through the origin and the point at α s = 0.5 leads to the specific surface area. The intercept and slope of the line above α s = 1 with the ordinate gives the micropore volume and the external surface area, respectively [23 , 24] . The average micropore width was obtained by simple geometrical slit pore approximation. Typically, the α s -plot for microporous materials has one or two upward swings below α s = 1.0. The swings at the lower α s region (f-swing) and at the higher α s region (c-swing) are indicated as filling and cooperative swings, respectively. The f-swing originates from monolayer adsorption on the micropore walls. The c-swing is an adsorption process in the residual space after the completion of monolayer adsorption on the micropore walls. Therefore, the c-swing indicates a micropore system with pore width larger than the thickness of trilayer N 2 molecules. All samples show only a f-swing below α s = 0.5, suggesting the presence of only ultramicropores. The α s -plots of heat-treated porous carbons show a typical shape of ultramicroporous carbon. The pore structure parameters of the porous carbons, determined through the α s -plots, are summarized in Table 2 . The total surface area and micropore volume increase with heat-treatment temperature. All samples have a narrow average micropore width of about 0.65 nm, close to an ultramicropore. Table 2 also shows the micropore volume determined from the DR-plots ( V micro-DR ) for comparison with the values from the α s -plots ( V micro-SPE ). Generally, the V micro-DR value corresponds only to ultramicropores, whereas the V micro-SPE value provides information about the total micropores. V micro-SPE and V micro-DR values of all samples are similar, reflecting the ultramicroporosity of the heat-treated samples, in excellent agreement with the average pore width results determined by the SPE method. Therefore, heat-treatment of PVDC is an effective method for the preparation of ul-
Lager Image
(a) N2 adsorption isotherms (77 K) and (b) their high-resolution αs-plots for heat-treated PVDC-derived nanoporous carbons. The open and solid symbols indicate adsorption and desorption branches, respectively: ○ (HT-873K), △ (HT-1073K), □ (HT-1273K). PVDC: poly(vinylidene chloride)
Pore structure parameters of PVDC-derived nanoporous carbons determined by SPE method. Micropore volumes (Vmicro-DR) were determined by the DR methodPVDC: poly(vinylidene chloride), SPE: subtracting pore effect, DR: Dubinin-Radushkevich, KOH: potassium hydroxide, at: total surface area, aext: external surface area, amicro: micropore surface area, Vmicro-SPE: micropore volume determined by SPE method, Vmicro-DR: micropore volume determined by DR method, w: average micropore width.
Lager Image
Pore structure parameters of PVDC-derived nanoporous carbons determined by SPE method. Micropore volumes (Vmicro-DR) were determined by the DR method PVDC: poly(vinylidene chloride), SPE: subtracting pore effect, DR: Dubinin-Radushkevich, KOH: potassium hydroxide, at: total surface area, aext: external surface area, amicro: micropore surface area, Vmicro-SPE: micropore volume determined by SPE method, Vmicro-DR: micropore volume determined by DR method, w: average micropore width.
tramicroporous carbons. The formation of an ultramicroporous structure of the PVDC-derived nanoporous carbon heat-treated in an inert atmosphere is thought to be closely related to complete release of hydrogen and chlorine atoms during thermal decomposition of the PVDC at high temperature [25] .
Fig. 3 a shows N 2 adsorption isotherms of PVDC-derived nanoporous carbons activated under steam. The N 2 adsorption isotherms of activated samples at 673 and 873 K are also Type I, which is due to the presence of uniform microporosity. The saturated amounts of N 2 adsorption at P/P0 = 1 increase with elevated activation temperature. The N 2 adsorption isotherm of the activated sample at 1273 K shows gradual adsorption uptake until P/P0 = 0.4 due to a second layer adsorption on the micropore walls adsorbed by the monolayer. This stems from the presence of supermicropores on porous carbon activated at higher temperature. The N 2 adsorption isotherm for the HT- 1273K sample exhibits a hysteresis loop that can be assigned to type H4. It is well known that type H4 is generally obtained from slit-shaped pores in various activated carbons, but the pore size distribution is mainly in the micropore range. The high-resolution α s -plots for activated samples at 673 and 873 K show only a f-swing below α s = 0.5, suggesting the presence of only ultramicropores ( Fig. 3 b). On the other hand, the α s -plot of the activated sample at 1273 K shows a f-swing and c-swing in the α s region of 0.5 to 1.0, suggesting the presence of both ultramicropores and supermicropores. As shown in Table 2 , the total surface area and micropore volume increase with the steam activation temperature. The steam activated samples at 873 and 1073 K have a narrow average micropore width less than 0.7 nm, close to that of an ultramicropore, and similar to that of heat-treated samples. On the other hand, the steam activated sample at 1273 K has a wider average micropore width of 1.48 nm. The average micropore width increased about two-fold compared to the samples treated at lower temperatures. V micro-SPE and V micro-DR values of samples treated at 873 and 1073 K in steam are similar, indicating ultramicroporosity. On the other hand, the ratio of V micro-DR to V micro-SPE for the sample
Lager Image
(a) N2 adsorption isotherms (77 K) and (b) their high-resolution αs-plots for steam-activated PVDC-derived nanoporous carbons. The open and solid symbols indicate adsorption and desorption branches, respectively: ○ (Steam-873K), △ (Steam-1073K), □ (Steam-1273K). PVDC: poly(vinylidene chloride)
treated at 1273 K dramatically decreases to about 0.7, which is associated with the presence of supermicropores, in good agreement with the average pore width determined by the SPE method. Therefore, steam activation at higher temperature has advantages for creating supermicropores. This should be attributed to pore formation by the elimination of hydrogen and chlorine atoms and to successive pore widening due to the attack of more oxidative steam at higher temperature.
Fig. 4 a presents N 2 adsorption isotherms of PVDC-derived nanoporous carbons chemically activated with KOH. The N 2 adsorption isotherms of all samples are defined as type I. However, the isotherm of the sample treated at 1273 K shows a gradual adsorption uptake until P/P0 = 0.4 due to a second layer adsorption , originating from the presence of supermicropores. The N 2 adsorption isotherm for the KOH-1273K sample also exhibits a hysteresis loop that can be assigned to type H4, which is similar to that for HT-1273K. The N 2 adsorption isotherm of the sample treated at 1073 K shows a steep uptake at a low P/P0 due to monolayer adsorption, resulting in a high specific surface area of 2704 m 2 /g, as shown in Table 2 . The
Lager Image
(a) N2 adsorption isotherms (77 K) and (b) their high-resolution αs-plots for KOH-activated PVDC-derived nanoporous carbons. The open and solid symbols indicate adsorption and desorption branches, respectively: ○ (KOH-873K), △ (KOH-1073K), □ (KOH-1273K). KOH: potassium hydroxide, PVDC: poly(vinylidene chloride).
α s -plot of the sample treated at 1273 K shows a f-swing and c-swing in the α s region of 0.5 to 1.0, suggesting the presence of both ultramicropores and wider micropores, as shown in Fig. 4 b, which reflects more heterogeneous microporosity. The micropore volume increases with activation temperature. In contrast, the specific and micropore surface areas of the sample treated at 1273 K slightly decrease compared to those of the sample treated at 1073 K. The chemical activation at higher temperature also results in widened average micropore width. The average micropore width is linearly proportional to the activation temperature, indicating a strong dependence on the activation temperature of the pore structure. As shown in Table 2 , the ratio of V micro-DR to V micro-SPE decreases with activation temperature, suggesting that porous carbons with higher KOHactivation temperature have more supermicropores. This result should be related to pore widening due to permeation of potassium species into the interlayer space or small pores and the subsequent chemical reactions of KOH, which are accelerated at higher temperature.
4. Conclusions
Nanoporosity control of PVDC-derived porous carbons was successively achieved by various activation methods. Heat-treatment in an inert atmosphere for PVDC provided an ultramicroporous structure. On the contrary, steam activation at 1273 K provided a supermicroporous structure with average micropore width of 1.48 nm. With elevated KOH activation temperature, the average micropore width was gradually enlarged from 0.67 to 1.12 nm. Therefore, the average pore widths of KOH-activated samples were strongly governed by the activation temperature. Consequently, PVDC-derived nanoporous carbons with controllable pore size can find useful applications as electrode materials for energy storage devices.
Acknowledgements
This work was supported by the Korea Institute of Science and Technology (KIST) institutional program.
References
Noguchi D , Hattori Y , Yang CM , Tao Y , Konishi T , Fujikawa T , Ohkubo T , Nobuhara Y , Ohba T , Tanaka H , Kanoh H , Yudasaka M , Iijima S , Sakai H , Abe M , Kim YJ , Kaneko K (2007) Storage function of carbon nanospaces for molecules and ions ECS Trans 11 63 -
Kaneko K , Arai M , Yamamoto M , Ohba T , Miyamoto J , Kim DY , Tao Y , Yang CM , Urita K , Fujimori T , Tanaka H , Ohkubo T , Utsumi S , Hattori Y , Konishi T , Fujikawa T , Kanoh H , Yudasaka M , Hata K , Yumura M , Iijima S , Muramatsu H , Hayashi T , Kim YA , Endo M (2009) Fundamental understanding of nanoporous carbons for energy application potentials Carbon Lett 10 177 -
Miyawaki J , Kanda T , Suzuki T , Okui T , Maeda Y , Kaneko K (1998) Macroscopic evidence of enhanced formation of methane nanohydrates in hydrophobic nanospaces J Phys Chem B 102 2187 -
Yang CM , Noguchi H , Murata K , Yudasaka M , Hashimoto A , Iijima S , Kaneko K (2005) Highly ultramicroporous single-walled carbon nanohorn assemblies Adv Mater 17 866 -
Kim YJ , Yang CM , Park CK , Kaneko K , Kim YA , Noguchi M , Fujino T , Oyama S , Endo M (2012) Edge-enriched, porous carbonbased, high energy density supercapacitors for hybrid electric vehicles ChemSusChem 5 535 -
Yang CM , Kim YJ , Endo M , Kanoh H , Yudasaka M , Iijima S , Kaneko K (2007) Nanowindow-regulated specific capacitance of supercapacitor electrodes of single-wall carbon nanohorns J Am Chem Soc 129 20 -
Chmiola J , Yushin G , Gogotsi Y , Portet C , Simon P , Taberna PL (2006) Anomalous increase in carbon capacitance at pore sizes less than 1 nanometer Science 313 1760 -
Kim YJ , Horie Y , Ozaki S , Matsuzawa Y , Suezaki H , Kim C , Miyashita N , Endo M (2004) Correlation between the pore and solvated ion size on capacitance uptake of PVDC-based carbons Carbon 42 1491 -
Yang CM , Kaneko K (2001) Adsorption properties of nitrogen-alloyed activated carbon fiber Carbon 39 1075 -
Ohkubo T , Iiyama T , Nishikawa K , Suzuki T , Kaneko K (1999) Porewidth dependent ordering of C2H5OH molecules confined in graphitic slit nanospaces J Phys Chem B 103 1859 -
Wang ZM , Kaneko K (1998) Effect of pore width on micropore filling mechanism of SO2in carbon micropores J Phys Chem B 102 2863 -
Endo M , Kim YJ , Takeda T , Maeda T , Hayashi T , Koshiba K , Hara H , Dresselhaus MS (2001) Poly(vinylidene chloride)-based carbon as an electrode materials for high power capacitors with an aqueous electrolyte J Electrochem Soc 148 (10) A1135 -
Kim YJ , Ishii K , Inoue T , Endo M , Dresselhaus MS , Nomura T , Miyashita N (2002) Structure and edlc applications of PVDC based carbons as a function of carbonization time Mol Cryst Liq Cryst 386 (1) 67 -
Endo M , Kim YJ , Ishii K , Inoue T , Takeda T , Maeda T , Nomura T , Miyashita N , Dressselhaus MS (2002) Structure and application of various saran-based carbons to aqueous electric double layer capacitors J Electrochem Soc 149 (11) A1473 -
Endo M , Kim YJ , Ishii K , Inoue T , Nomura T , Miyashita N , Dresselhaus MS (2003) Heat-treatment retention time dependence of polyvinylidenechloride- based carbons on their application to electric double-layer capacitors J Mater Res 18 693 -
Endo M , Kim YJ , Osawa K , Ishii K , Inoue T , Nomura T , Miyashita N , Dresselhaus MS (2003) High capacitance EDLC using a carbon material obtained by carbonization of PVDC: the effect of the crystallite size of the pristine PVDC Electrochem Solid-State Lett 6 A23 -
Eliad L , Poliak E , Levy N , Salitra G , Soffer A , Aurbach D (2006) Assessing optimal pore-to-ion size relations in the design of porous poly(vinylidene chloride)carbons for EDL capacitors App Phys A 82 607 -
Xu B , Wu F , Chen S , Cao G , Zhou Z (2008) A simple method for preparing porous carbon by PVDC pyrolysis Colloids Surf Physicochem Eng Aspects 316 85 -
Xu Bin , Wu Feng , Chen Shi , Zhou Zhiming , Cao Gaoping , Yang Yusheng (2009) High-capacitance carbon electrode prepared by PVDC carbonization for aqueous EDLCs Electrochemical Acta 54 2185 -
Zhang K , Way JD (2011) Optimizing the synthesis of composite polyvinylidene dichloride-based selective surface flow carbon membranes for gas separation J Membr Sci 369 243 -
Kim YJ , Masutzawa Y , Ozaki S , Endo M , Dresselhaus MS (2004) PVDCbased carbon materials by chemical activation and its application to nonaqueous EDLC J Electrochem Soc 151 (6) E199 -
Xu B , Wu F , Mu D , Dai L , Cao G , Zhang H , Chen S , Yang Y (2010) Activated carbon prepared from PVDC by NaOH activation as electrode materials for high performance EDLCs with non-aqueous electrolyte Int J Hydrogen Energy 35 632 -
Setoyama N , Suzuki T , Kaneko K (1998) Simulation study on the relationship between a high resolution α s-plot and the pore size distribution for activated carbon Carbon 36 1459 -
Yang CM , El-Merraoui M , Seki H , Kaneko K (2001) Characterization of nitrogen-alloyed activated carbon fiber Langmuir 17 675 -
Roberge PR , Beaudoin R , Berthiaume JM (1988) Fabrication and characterization of an activated carbon for electrochemical applications Carbon 26 173 -