Improvement of Superhydrophobicity of Multi-Walled Carbon Nanotubes Produced by Fluorination
Improvement of Superhydrophobicity of Multi-Walled Carbon Nanotubes Produced by Fluorination
Carbon letters. 2012. Jul, 13(3): 178-181
Copyright ©2012, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : March 31, 2012
  • Accepted : April 21, 2012
  • Published : July 31, 2012
Export by style
Cited by
About the Authors
Long-Yue, Meng
Soo-Jin, Park

In this work, we synthesized superhydrophobic coatings by chemical surface functionalization of multi-walled carbon nanotubes (MWCNTs). This was accomplished through the radical polymerization of 3-(trimethoxysilyl) propyl methacrylate modified MWCNTs and fluoro acrylate/methyl methacrylate. The chemical compositions and microstructures of the prepared MWCNT surface were investigated using X-ray photoelectron spectroscopy, Fourier transform infrared spectrometry, and scanning electron microscopy, respectively. The wettability of the MWCNTs surface was determined through contact angle assessments in different liquids. The resulting surface exhibited a water contact angle of 157.7°, which is clear evidence of its superhydrophobicity. The 3D MWCNT networks and the low surface energy of the -C-C- and -C-F- groups play important roles in creating the superhydrophobic surface of the MWCNTs.
1. Introduction
Recently, superhydrophobic and conductive materials have attracted attention from researchers due to their importance in fundamental research and potential industrial applications in such areas as electronic devices, transparent films, and structural coatings [1 - 5] . In particular, hydrophobic and conductive films based on multi-walled carbon nanotubes (MWCNTs) have many potential applications due to their novel properties such as high aspect ratio, small radius of curvature, high mechanical strength, thermal/electrical conductivity, and good chemical stability [6 - 9] . However, for typical carbon nanotubes, polar substances such as water cannot wet the nanotube surface easily [10] . A large number of MWCNT applications are hampered by the hydrophobic properties of these types of CNTs. It is desirable to be able to modify the hydration properties of the surfaces of carbon nanotubes so that they become hydrophilic. The wettability of MWCNTs is one of the most important ideas in both theoretical research and practical applications [11] .
Generally, superhydrophobic surfaces have a water contact angle higher than 150° and a water sliding angle of less than 10° [12] . To date, many researchers have endeavored to fabricate superhydrophobic CNTs using aligned-CNTs [11 - 14] . Huang et al. [13] reported a stable superhydrophobic surface composed of aligned carbon nanotubes (CNTs). However, the area of the aligned-CNT films could be limited due to the requirements of the specific preparation methods. Most recently, several studies have reported a means of preparing superhydrophobic surfaces on non-aligned CNTs [5 - 9 , 14 - 16] . For example, Zou et al. [6] fabricated a superhydrophobic surface (154°~160°) with conductivity using a conjugated block copolymer.
In this work, superhydrophobic coatings of multi-walled carbon nanotubes (MWCNTs) were produced by the radical polymerization of 3-(trimethoxysilyl) propyl methacrylate modified MWCNTs and fluoro acrylate/ methyl methacrylate.
Lager Image
Preparation procedure of fluorinated multi-walled carbon nanotubes.
Characteristics of wetting liquids used in the present workγLL: London dispersive component of surface free energy, γSLP: specific component of surface free energy, γL: total surface free energy, η : viscosity, ρ : density.
Lager Image
Characteristics of wetting liquids used in the present work γLL : London dispersive component of surface free energy, γSLP: specific component of surface free energy, γL : total surface free energy, η : viscosity, ρ : density.
2. Material and Methods
- 2.1. Materials and sample preparation
The MWCNTs (Nano Solution Co.) were treated with HNO 3 / H 2 SO 4 mixture solutions [17 , 18] . The oxidized MWCNTs (CNTH) were modified with 3-(trimethoxysilyl) propyl methacrylate (TPM) in toluene at 383 K for 24 h and were then washed thoroughly with toluene several times. The obtained sample is denoted as CNT-Si. Finally, TPM-modified MWCNTs, fluoromonomer (Zonyl ® TM fluoromonomer, average M n of about 534), methyl methacrylate, and AIBN were placed in a vial and dissolved in tetrahydrofuran (THF). The mixture was degassed under a continuous stream of dry argon. A polymerization reaction was carried out at 70℃ for 24 h and this was followed by washing with THF. This sample is denoted as CNT-F ( Fig. 1 ).
- 2.2. Characterization
X-ray photoelectron spectroscopy (XPS) measurements were done on an ESCALAB220i-XL (VG Scientific, UK) spectrometer with monochromatized Al Kα X-ray radiation as the X-ray source for excitation to confirm the surface functional groups of the treated MWCNTs. Fourier transform infrared (FT-IR) spectroscopy on KBr pellets was performed with a Bio-Rad Co. Digilab FTS-165. Corresponding images of the resulting films were obtained by scanning electron microscopy (SEM, HITA-CHI S4200). The contact angle (CA) of the film was determined to be 20 ± 1°C using the sessile drop method (Phoenix Series Contact Angle Analyzer, Phoenix 150/300). Distilled water and diiodomethane were selected for measurement of the contact angle of the films. For each sample, each calculated contact angle was an average of 10 measurements with a standard deviation below 1° [19] . The surface free energy and other characteristics of the three wetting liquids are listed in Table 1 .
3. Results and Discussion
XPS was used to investigate the introduction of elements on the MWCNT surfaces, as shown in Fig. 2 . In the figure, the XPS spectrum of the samples shows carbon peaks (285.08 ev), oxygen peaks (532.08 ev), silicon peaks (835.07 ev), and fluorine peaks (690.08 ev). The XPS spectrum of CNTs-H shows oxygen peaks (533.4) that are attributable to an increase in the number of surface oxygen groups (C-O, O=C-O), which are the result of chemical oxidation [17] . The silicon peak (835.07 ev) and the fluorine peak (690.08 ev) are attributable to silanol groups and fluorine groups (-CF-), respectively [20] . This suggests that the fluoromonomer is grafted onto the surfaces of the CNT-Si via chemical modification.
Figs. 3 a and b shows schematic diagrams illustrating the changes of the contact angle and the surface properties. As shown in Fig. 3 a, the water droplet retains an ellipsoidal shape on the MWCNTs; the droplet has a contact angle of 115.5°, sug-
Lager Image
Wide-scan X-ray photoelectron spectroscopy spectra of pristineMWCNTs, oxidized MWCNTs (CNT-H), silanol group coated MWCNTs (CNTSi),and fluorinated MWCNTs (CNT-F). MWCNTs: multi-walled carbon nanotubes.
Lager Image
Scanning electron microscope image ilustrating the changes ofwater contact angle of multi-walled carbon nanotubes (MWCNTs): (a, c)pristine MWCNTs; (b, d) fluorinated MWCNTs.
gesting that the pristine MWCNTs are hydrophobic [16] . The CA of CNT-F increases to 157.7° after it is polymerized with fluoromonomer because the surface of CNT-Si is grafted with – CF– groups ( Fig. 3 b). This indicates that the wettability of MWCNTs can become superhydrophobic by varying the chemical composition of the MWCNTs [5] . According to Liu et al. [10] , the wettability of CNTs is controlled by the surface energy and surface roughness. The surface roughness of the MWCNTs and CNT-F were examined by SEM, with resulting images shown in Figs. 3 c and d. The pristine MWCNT films showed an assembled bundle structure ( Fig. 3 c). After polymerization, the images revealed that the surface roughness of the MWCNTs contained porous MWCNT networks. The porous CNT-F networks became deeper and larger than those of the pristine MWCNTs, leading to the formation of a hierarchical 3D interpenetrating network. The surface roughness allowed air to become trapped between the solid surface and the water droplet, which decreased the contact
Lager Image
Dispersive (γLS), polar (γSPS), and Surface free energy (γS) componentsof pristine multi-walled carbon nanotubes (MWCNTs), oxidizedMWCNTs (CNT-H), silanol group coated MWCNTs (CNT-Si), and fluorinatedMWCNTs (CNT-F). unit: mJ m−2.
area with water. According to previous research, trapped air is thought to be an important factor that affects the degree of superhydrophobicity [5 , 14 - 16] . Therefore, these results show that the hydrophobic surfaces of films are affected by the -C-F- groups and by the surface roughness.
To obtain more detailed information pertaining to the surface energetics of the CNT-F films, the surface free energy was analyzed based on the method of Fowkes [21] . The total surface free energy can be divided into the London dispersive and specific (or polar) components.
Lager Image
where γS is the total surface free energy, the subscript S represents a solid state, and γLS and γSSP are the London dispersive and specific (Debye, Keesom of van der Waals, H-bonding, π-bonding, and other small polar effects) components of the surface free energy of the constitutive elements. The London dispersive and specific components were determined by measuring the contact angles of two testing liquids with known London dispersive and specific components. The surface free energy of a solid can be determined on the basis of contact angle measurements using the geometric mean, according to Fowkes’ proposition [21] based on a solid (subscript S)–liquid (L) droplet–air system, which can be described by the following equation:
Lager Image
where θ is the contact angle of a liquid droplet in the solid state. The surface free energy components of the samples are shown in Fig. 4 . As reported in our previous work, the specific component, γSSP , is highly dependent on the surface functional groups, and the dispersive component, γLS , is largely dependent on the total electron density in the carbon [19] .
As shown in Fig. 4 , the total surface energy and γSSP value of the MWCNTs increase when the MWCNTs are given an acid treatment. This increase arises due to an increase in the number of hydrophilic functional groups (–OH, C=O, and O=C–O) during the acid oxidation process [22] . After grafting fluoromono-mer onto the CNT-Si surface, a decrease in the surface free energy was observed. Related to the superhydrophobicity, it was reported that the surface free energy decreased in the order –CH 2 > –CH 3 > –CF 2 > –CF 2 H > –CF 3 [10 , 16] . Therefore, the decrease in the values of both γLS and γSSP stems from the substitution of the lower energy -C-F- groups by the grafted -C-F- groups on the MWCNT surfaces [23] .
4. Summary
In conclusion, we successfully prepared superhydrophobic films based on fluoromonomer-grafted MWCNTs. The surface of the films exhibited a high contact angle of 157.7°. The 3D MWCNT networks and the low surface energy of the -CFgroups play important roles in creating the superhydrophobic surface of the MWCNT films. The stable superhydrophobic MWCNT films proposed in this study can be used in many industries and can be extended to control the adhesion properties of a wide variety of superhydrophobic functional materials.
This work was supported by the Korea CCS R& D Center (KCRC) grant funded by the Korea government (Ministry of Education, Science and Technology) (0031985).
Darmanin T , Guittard F , Amigoni S , Tafin de Givenchy E , Noblin X , Kofman R , Celestini F (2011) Superoleophobic behavior of fluorinated conductive polymer films combining electropolymerization and lithography. Soft Matter 7 1053 -    DOI : 10.1039/C0SM00837K
Song W , Zhang J , Xie Y , Cong Q , Zhao B (2009) Large-area unmodified superhydrophobic copper substrate can be prepared by an electroless replacement deposition. J Colloid Interface Sci 329 208 -    DOI : 10.1016/j.jcis.2008.09.059
Zhu Y , Zhang JC , Zhai J , Zheng YM , Feng L , Jiang L (2006) Multifunctional carbon nanofibers with conductive, magnetic and superhydrophobic properties ChemPhysChem 7 336 -    DOI : 10.1002/cphc.200500407
Li M , Zhai J , Liu H , Song Y , Jiang L , Zhu D (2003) Electrochemical deposition of conductive superhydrophobic zinc oxide thin films. J Phys Chem B 107 9954 -    DOI : 10.1021/jp035562u
Han JT , Kim SY , Woo JS , Lee GW (2008) Transparent, conductive, and superhydrophobic films from stabilized carbon nanotube/silane sol mixture solution. Adv Mater 20 3724 -    DOI : 10.1002/adma.200800239
Zou J , Chen H , Chunder A , Yu Y , Huo Q , Zhai L (2008) Preparation of a superhydrophobic and conductive nanocomposite coating from a carbon-nanotube-conjugated block copolymer dispersion. Adv Mater 20 3337 -    DOI : 10.1002/adma.200703094
Sethi S , Dhinojwala A (2009) Superhydrophobic conductive carbon nanotube coatings for steel. Langmuir 25 4311 -    DOI : 10.1021/la9001187
Luo C , Zuo X , Wang L , Wang E , Song S , Wang J , Wang J , Fan C , Cao Y (2008) Flexible carbon nanotube?polymer composite films with high conductivity and superhydrophobicity made by solution process. Nano Lett 8 4454 -    DOI : 10.1021/nl802411d
Tzeng Y , Chen Y , Sathitsuksanoh N , Liu C (2004) Electrochemical behaviors and hydration properties of multi-wall carbon nanotube coated electrodes in water. Diamond Relat Mater 13 1281 -    DOI : 10.1016/j.diamond.2003.11.048
Liu H , Zhai J , Jiang L Wetting and anti-wetting on aligned carbon nanotube films. Soft Matter 2 811 -    DOI : 10.1039/B606654B
Liu H , Feng L , Zhai J , Jiang L , Zhu D. (2004) Reversible wettability of a chemical vapor deposition prepared ZnO film between superhydrophobicity and superhydrophilicity. Langmuir 20 5659 -    DOI : 10.1021/la036280o
Zhu L , Xiu Y , Xu J , Tamirisa PA , Hess DW , Wong C-P (2005) Superhydrophobicity on two-tier rough surfaces fabricated by controlled growth of aligned carbon nanotube arrays coated with fluorocarbon. Langmuir 21 11208 -    DOI : 10.1021/la051410+
Huang L , Lau SP , Yang HY , Leong ESP , Yu SF , Prawer S (2005) Stable superhydrophobic surface via carbon nanotubes coated with a ZnO thin film. J Phys Chem B 109 7746 -    DOI : 10.1021/jp046549s
Men XH , Zhang ZZ , Song HJ , Wang K , Jiang W (2008) Fabrication of superhydrophobic surfaces with poly(furfuryl alcohol)/multiwalled carbon nanotubes composites. Appl Surf Sci 254 2563 -    DOI : 10.1016/j.apsusc.2007.08.084
Shakerzadeh M , Teo HE , Tan C , Tay BK (2009) Superhydrophobic carbon nanotube/amorphous carbon nanosphere hybrid film. Diamond Relat Mater 18 1235 -    DOI : 10.1016/j.diamond.2009.04.010
Meng LY , Park SJ (2010) Effect of fluorination of carbon nanotubes on superhydrophobic properties of fluoro-based films. J Colloid Interface Sci 342 559 -    DOI : 10.1016/j.jcis.2009.10.022
Ham H , Koo C , Kim S , Choi Y , Chung I (2004) Chemical modification of carbon nanotubes and preparation of polystyrene/carbon nanotubes composites. Macromolecular Res 12 384 -    DOI : 10.1007/bf03218416
Kim MS , Lim S , Song MY , Cho H , Choi Y , Yu JS (2010) Acid treatments of carbon nanotubes and their application as Pt-Ru/ CNT anode catalysts for proton exchange membrane fuel cell. Carbon Lett 11 336 -
Park SJ , Hsu JP (1999) Interfacial Forces and Fields: Theory and Applications Marcel Dekker New York 385 -
Jung MJ , Kim JW , Im JS , Park SJ , Lee YS (2009) Nitrogen and hydrogen adsorption of activated carbon fibers modified by fluorination. J Ind Eng Chem 15 410 -    DOI : 10.1016/j.jiec.2008.11.001
Fowkes FM (1964) Attractive forces at interfaces. Ind Eng Chem 56 40 -    DOI : 10.1021/ie50660a008
Nuriel S , Liu L , Barber AH , Wagner HD (2005) Direct measurement of multiwall nanotube surface tension. Chem Phys Lett 404 263 -    DOI : 10.1016/j.cplett.2005.01.072
Hsieh CT , Chen WY , Wu FL , Hung WM (2010) Superhydrophobicity of a three-tier roughened texture of microscale carbon fabrics decorated with silica spheres and carbon nanotubes. Diamond Relat Mater 19 26 -    DOI : 10.1016/j.diamond.2009.10.017