Improvement in ammonia gas sensing behavior by polypyrrole/multi-walled carbon nanotubes composites
Improvement in ammonia gas sensing behavior by polypyrrole/multi-walled carbon nanotubes composites
Carbon letters. 2012. Apr, 13(2): 88-93
Copyright ©2012, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : January 12, 2012
  • Accepted : April 05, 2012
  • Published : April 30, 2012
Export by style
Cited by
About the Authors
Woo Kyung, Jang
Jumi, Yun
Hyung-Il, Kim
Young-Seak, Lee

Polypyrrole (PPy)/multi-walled carbon nanotubes (MWCNTs) composites were prepared by in situ polymerization of pyrrole on the surface of MWCNTs templates to improve the ammonia gas sensing properties. PPy morphologies, formed on the surface of MWCNTs, were investigated by field emission scanning electron microscopy. The thermal stabilities of the PPy/MWCNTs composites were improved as the content of MWCNTs increased due to the higher thermal stability of the MWCNTs. PPy/MWCNTs composites showed synergistic effects in improving the ammonia gas sensing properties, attributed to the combination of efficient electron transfer between PPy/MWCNTs composites and ammonia gas, and the reproducible electrical resistance variation on PPy during the gas sensing process.
1. Introduction
Ammonia (NH 3 ) is a kind of gas with high toxicity. The detection of NH 3 is necessary and important for environmental monitoring and chemical control in industrial, agricultural, and medical fields. For example, the maximum NH 3 concentration allowed at the industrial working place is 25 ppm for 8 h exposure, and 35 ppm over a 10 min period [1] . However, the olfactory limit of detection of NH 3 is 55 ppm [2] . Therefore, a sensitive NH 3 gas sensor must be developed for the detection of lower NH 3 concentration below these limits.
NH 3 gas sensors based on conventional materials such as SnO 2 [3] , TiO 2 [4] , In 2 O 3 [5] , WO 3 [6] , and ZnO [7] have been developed with good responsiveness and selectivity, and fast response-recovery, that can be used in detecting the lower level presence of NH 3 gas. However, these NH 3 gas sensors are fabricated using metal oxides which operate effectively at temperature ranges between 150 and 400℃, resulting in both high power consumption and complexities in integration. Thus, there is a great need to develop a new class of materials for gas sensors that have good performance at room temperature.
Carbon nanotubes' (CNTs) special geometry and their outstanding feature of surface reactivity, offer great potential for application in gas sensor devices working at room temperature [8] . However, CNTs still have certain limitations for gas sensor application, such as long recovery time, limited gas detection, and vulnerability to humidity and other gases. These limitations can be resolved effectively by forming composites with conducting polymers.
Conducting polymers such as polypyrrole (PPy) and polythiophene and their composites have been widely investigated as effective materials for chemical sensors [9 - 11] . Among the conducting polymers, PPy has attracted considerable attention because it varies its electrical conductivity using the redox reactions and has a good stability in both air and aqueous media [12] . Fig. 1 demonstrates the oxidation process of PPy. Some electrons are removed from PPy backbones by chemical or electrochemical oxidations, leaving positive charges on them. The resulting cation radicals are called polarons, acting as the charge carriers. Counter ions, X-, are also induced close to the polymer chains to balance the positive charges. Doped conducting
Lager Image
Oxidation doping of polypyrrole.
polymers are semiconductors or conductors (10 0 -10 5 S cm -1 ). PPy and other conductive polymers have, therefore, also been classified as organic metals. There exists a wide range of applications suitable for organic metals use, such as cell culture substrates [13] , field effect transistors [14] , light-emitting diodes [15] , solar cells [16 , 17] , electrochromic devices [18] , electronic circuits [19] , elastic textile composites [20] , supercapacitors for energy storage and secondary batteries [21] , protection of metals [22] , ion exchange membranes responding to external stimulations [23] , and sensors and biosensors [24 , 25] .
Preparation of PPy/multi-walled CNTs (MWCNTs) composites by electropolymerization on an oxidisable surface such as a Cu electrode have been reported, using MWCNTs as an appropriate substrate to induce the preferential deposition of PPy [26] . In our study, PPy/MWCNTs composites were prepared conveniently by in situ chemical oxidative polymerization resulting in the uniform deposition of PPy on MWCNTs without using any electrode.
Gas sensors were fabricated by spin-coating the PPy/MWCNTs composites having various compositions. The NH 3 sensing properties of PPy/MWCNTs composites were investigated based on the variation of electrical resistance upon gas adsorption. This study aims to investigate the synergistic effects in improving the gas sensing properties based on the combination of electrical properties of MWCNTs and PPy.
2. Experimental
- 2.1. Materials
Pyrrole monomer (99%), ammonium persulfate (APS), and MWCNTs were obtained from Sigma Aldrich. The diameter of the MWCNTs was between 110 and 170 nm, and purity of the MWCNTs was over 90%. Sodium dodecyl sulfate as surfactant was obtained from ICN Biomedicals. Hydrogen peroxide (H 2 O 2 ) was purchased from Kanto chemical.
- 2.2. Synthesis of PPy and PPy/MWCNTs composites
PPy was synthesized by free radical chemical oxidative polymerization through the direct route using H 2 O 2 as oxidant. Three gram of pyrrole monomer was dropped into distilled water and stirred continuously for 10 min. Then 4.5 mL of H 2 O 2 was added to the pyrrole solution. 0.8 g of APS dissolved in 10 mL distilled water was slowly added to the pyrrole solution and the reactant solution was polymerized for 4 h at 0℃ with constant stirring. The synthesized PPy was filtered and rinsed several times with distilled water, methanol, and acetone, respectively. The PPy powder was dried under vacuum at 40℃ for 24 h.
PPy/MWCNTs composites were synthesized using in situ chemical oxidative polymerization on the MWCNT template. The polymerization of pyrrole was carried out in distilled water using H 2 O 2 as oxidant for pyrrole and APS as initiator. Various contents of MWCNTs (0, 0.5, 1.0, 3.0, and 5.0 wt%) were dispersed in the surfactant solution and ultrasonicated over 1 h. Three gram of pyrrole monomer was added into the MWCNTs dispersed mixture and stirred continuously for 10 min. Then 4.5 mL of H 2 O 2 was added to the reactant solution followed by the slow addition of 0.8 g of APS, dissolved in 10 mL distilled water, to the reactant solution. The template polymerization was carried out for 4 h at 0℃ with constant stirring. The synthesized PPy/MWCNTs composites were filtered and rinsed several times with distilled water, methanol, and acetone, respectively. The composite powders were dried under vacuum at 40℃ for 24 h. Five different composite samples, such as PPy/0 wt%-MWCNTs, PPy/0.5 wt%-MWCNTs, PPy/1 wt%-MWCNTs, PPy/3 wt%-MWCNTs, and PPy/5 wt%-MWCNTs, were named as PPy, 0.5-PPC, 1-PPC, 3-PPC, and 5-PPC, respectively.
- 2.3. Preparation of the gas sensor
The PPy/MWCNTs composites (0.1 g) were dispersed in acetone (5 g) and ultrasonicated for 30 min to disperse the samples uniformly in the acetone. Then the dispersion (0.01 g) was dropped onto a silicon wafer by using a micro-pipette (Ovation pipette, Vistalab) and spin-coated (spin coater, ACE-200) at 900 rpm for 4 min. The coated wafer was heated to remove the solvent at 40℃ for 10 min. The thickness of the coating layer was 15 ± 1 μm .
- 2.4. Measurement of gas sensing properties
In order to evaluate the gas sensing properties of composites, their electrical resistance was measured using a programmable electrometer (Keithley 6514). The setup of the gas sensor system is depicted in Fig. 2 . The gas sensing device was prepared by using two Pt electrodes and a SiO 2 plate, as shown in previous work [27 , 28] . This measurement was performed in a stainless steel chamber with a volume of 1500 cm 3 . The chamber was connected to gas cylinders (NH 3 and air). The prepared sample gas sensor was placed in a sealed chamber under vacuum at a pressure of 1 × 10 ?3 torr. Air was injected into the chamber to stabilize the electrical resistance of the gas sensor. The air was used as the carrier gas for the control of gas concentrations. The mixture of two different gases was then prepared with a concentration of 33.2 ppm NH 3 in air and injected into the chamber. The gas feeding rate was kept constant at 500 sccm in all cases. The change in electrical resistance was measured at 298 ± 1 K. When the electrical resistance was stable under the NH 3 gas in-
Lager Image
Schematic diagram of the gas sensing property measurement.
jection, the injection of NH 3 gas was turned off and the recovery of electrical resistance was observed. The adsorbed gases on the gas sensors were removed by heating the sensors to 373 K at a pressure of 1 × 10 -3 torr for 5 min [27 , 28] . Recovery testing was carried out four times.
The gas sensitivity (S) is expressed by the following equation [29 , 30] :
Lager Image
where R 0 is the resistance due to the air and R g is the resistance measured upon exposure to NH 3 gas.
- 2.5. Characterization
Field emission scanning electron microscopy (FE-SEM, Hitachi, S-5500) was used to investigate the surface morphology of the prepared gas sensors. FE-SEM measurements were conducted at 5 kV. SEM images were taken without prior treatment
Lager Image
Field emission scanning electron microscopy images of (a) polypyrrole, (b) 0.5-PPC, (c) 1-PPC (d) 3-PPC, and (e) 5-PPC.
in order to ensure the acquisition of accurate images. Thermogravimetric analysis (TGA) was performed under nitrogen flow (50 cm 3 min -1 ) at a heating rate of 10℃ min -1 to 800℃ by using Perkin Elmer TGA5OH thermogravimetric analyzer.
3. Results and Discussion
- 3.1. Morphology
FE-SEM images of PPy and PPy/MWCNTs composites (0.5- PPC, 1-PPC, 3-PPC, 5-PPC) are presented in Fig. 3 . The granular structure of PPy is seen in Fig. 3 a. PPy was coated uniformly on the MWCNTs templates while maintaining the granular structure as shown in Figs. 3 b-e.
The layer structures of PPy were formed successfully on the outer surface of MWCNTs. In addition, the size reduction of PPy clusters was observed as MWCNTs content increased. These morphological characteristics were expected to play an important role in the NH 3 sensing performance of the PPy/MWCNTs composites.
- 3.2. Thermal stability
The thermal stabilities of PPy and PPy/MWCNTs composites were investigated by TGA as shown in Fig. 4 . The PPy/MWCNTs composites showed improved thermal stability compared with the PPy alone. MWCNTs are well known scavengers of free radicals [31] . MWCNTs, which were dispersed uniformly in the PPy matrices, retarded the thermal decomposition of the composites effectively. Although the PPy showed poor thermal stability, with an initial decomposition temperature of 250℃ [32] , the thermal properties of the PPy/MWCNTs composites were improved by incorporating the MWCNTs.
Lager Image
Thermogravimetric analysis thermograms of (a) polypyrrole (b) 0.5-PPC, (c) 1-PPC, (d) 3-PPC, and (e) 5-PPC.
Lager Image
Ammonia gas sensibility of (a) polypyrrole, (b) 0.5-PPC, (c) 1-PPC, (d) 3-PPC, and (e) 5-PPC.
- 3.3. Gas sensitivity by resistive response
Fig. 5 presents the NH 3 gas sensitivity of various PPy/MWCNTs composites as measured by changes in the electrical resistance. The gas sensitivity of PPy and various PPy/MWCNTs composites was investigated based on two different factors, namely, the response time and the sensing intensity. PPy/ MWCNTs composites usually exhibited a change in electrical resistance in accordance with the typical characteristics of a ptype semiconductor. When this occurs with a p-type conducting polymer, the doping level as well as the electric conductance of the conducting polymer is enhanced. Generally, the electrons travel from CNTs to the NH 3 gas (reducing gas), resulting in the increase of electrical resistance [33] . The following reactions are possibly involved in the NH 3 gas sensing process [34 , 35] :
  • PPy++ NH3→ PPy0+ NH3+Adsorption
  • PPy0+ NH3+→ PPy++ NH3Desorption
Based on this mechanism, all p-type conducting polymers are
Lager Image
Reproducibility of resistive response to the repeated exposures to ammonia gas for 5-PPC.
expected to de-dope under an NH 3 gas atmosphere. It was found that a resistance increase occurred upon reaction with NH 3 gas.
In this study, the gas sensitivity of various PPy/MWCNTs composites was evaluated to investigate the synergistic effects of PPy and MWCNTs. The variation in electrical resistance is attributed to the electron charge transfer between NH 3 gas and the surface of PPy/MWCNTs composites. The PPy sample showed continuously increased resistivity during the initial 25 min, with the slow response to NH 3 gas showing the lack of sensitivity in gas sensing properties. This drawback was overcome by forming a composite with MWCNTs.
The sensitivity for NH 3 gas was improved significantly as MWCNTs content was increased in the PPy/MWCNTs composites. The 5-PPC sample showed not only the highest sensitivity change of 65% but also the fastest response time of less than 10 min for NH 3 gas among the prepared PPy/MWCNTs composite samples. 5-PPC showed about 15 times higher sensitivity for NH 3 gas compared with PPy due to the synergistic effect of PPy and MWCNTs based on the combination of electrical properties of the MWCNTs and PPy. The conducting polymer-coated MWCNTs showed the unique combination of effects on both the efficiency of adsorption of gas and the resistive response, resulting in the improvement in gas sensing properties. The improved sensitivity for NH 3 gas seems to be attributable to the effective electron charge transfer in the interface between PPy/MWCNTs composites and NH 3 gas, and the resulting change in electrical resistance by the uniformly dispersed MWCNTs. The reproducibility of the gas sensor performance was also investigated every 10 min by evacuating the gas in the chamber at a pressure of 1× 10 -3 torr. The gas sensing behavior of the 5-PPC in the cyclic exposures to NH 3 gas is shown in Fig. 6 . Excellent reproducibility was observed for the 5-PPC sample, showing over 90% recovery.
4. Conclusions
The composites of PPy and MWCNTs were prepared by in situ chemical oxidative template polymerization on the surface of MWCNTs, as effective NH 3 gas sensing materials. PPy was formed uniformly on the surface of the MWCNTs as confirmed by FE-SEM images. The grain size of the PPy decreased as MWCNTs content increased. The thermal stability of the PPy coating on MWCNTs was improved by the effect of oxygen radical scavenger of the MWCNTs. The improved gas sensitivity for NH 3 was attributed to the effective electron charge transfer at the interface between PPy/MWCNTs composites and NH 3 gas, and the efficient electron transfer by MWCNTs. PPy/MWCNTs composites showed the synergistic combination effects of efficient adsorption and conduction resulting in the improvement of gas sensing properties by dispersing MWCNTs uniformly in PPy. The reproducibility of gas sensing behavior was also investigated every 10 min by evacuating the gas in the chamber at a pressure of 1 × 10 -3 torr. Excellent reproducibility was observed for the PPy/MWCNTs composites showing over 90% recovery. The high-performance NH 3 gas sensor could be prepared based on the composites of PPy and MWCNTs.
Christie S , Scorsone E , Persaud K , Kvasnik F (2003) Remote detection of gaseous ammonia using the near infrared transmission properties of polyaniline. Sensors Actuators B: Chem 90 163 -    DOI : 10.1016/S0925-4005(03)00036-4
Bendahan M , Lauque P , Lambert-Mauriat C , Carchano H , Seguin JL (2002) Sputtered thin films of CuBr for ammonia microsensors: morphology, composition and ageing. Sensors Actuators B: Chem 84 6 -    DOI : 10.1016/S0925-4005(02)00004-7
Wang YD , Wu XH , Su Q , Li YF , Zhou ZL (2001) Ammonia-sensing characteristics of Pt and SiO2doped SnO2materials. Solid State Electron 45 347 -    DOI : 10.1016/S0038-1101(00)00231-8
Hayakawa I , Iwamoto Y , Kikuta K , Hirano S (2000) Gas sensing properties of platinum dispersed-TiO2 thin film derived from precursor. Sensors Actuators B: Chem 62 55 -    DOI : 10.1016/s0925-4005(99)00303-2
Mbarek H , Saadoun M , Bessaïs B (2006) Screen-printed Tin-doped indium oxide (ITO) films for NH3gas sensing. Mater Sci Eng C 26 500 -    DOI : 10.1016/j.msec.2005.10.037
Wang X , Miura N , Yamazoe N (2000) Study of WO3-based sensing materials for NH3and NO detection Sensors Actuators B: Chem 66 74 -    DOI : 10.1016/S0925-4005(99)00410-4
Patil DR , Patil LA , Patil PP (2007) Cr2O3-activated ZnO thick film resistors for ammonia gas sensing operable at room temperature. Sensors Actuators B: Chem 126 368 -    DOI : 10.1016/j.snb.2007.03.028
Tran TH , Kwon JH , Lee KS , Lee JW , Ju BK (2006) pH sensor using carbon nanotubes as sensing material. First International Conference on Communications and Electronics, Hanoi Vietnam 490    DOI : 10.1109/CCE.2006.350876
Lange U , Roznyatovskaya NV , Mirsky VM (2008) Conducting polymers in chemical sensors and arrays. Anal Chim Acta 614 1 -    DOI : 10.1016/j.aca.2008.02.068
de Souza JEG , dos Santos FL , Barros-Neto B , dos Santos CG , de Melo CP (2001) Polypyrrole thin films gas sensors. Synth Met 119 383 -    DOI : 10.1016/s0379-6779(00)01051-1
Ram MK , Yavuz O , Lahsangah V , Aldissi M (2005) CO gas sensing from ultrathin nano-composite conducting polymer film. Sensors Actuators B: Chem 106 750 -    DOI : 10.1016/j.snb.2004.09.027.
Albuquerque JE , Mattoso LHC , Balogh DT , Faria RM , Masters JG , MacDiarmid AG (2000) A simple method to estimate the oxidation state of polyanilines. Synth Met 113 19 -    DOI : 10.1016/s0379-6779(99)00299-4
Song HK , Toste B , Ahmann K , Hoffman-Kim D , Palmore GTR (2006) Micropatterns of positive guidance cues anchored to polypyrrole doped with polyglutamic acid: a new platform for characterizing neurite extension in complex environments. Biomaterials 27 473 -    DOI : 10.1016/j.biomaterials.2005.06.030
Dimitrakopoulos CD , Malenfant PRL (2002) Organic thin film transistors for large area electronics. Adv Mater 14 99 -    DOI : 10.1002/1521-4095(20020116)14:2<99::aidadma99>;2-9.
Kraft A , Grimsdale AC , Holmes AB (1998) Electroluminescent conjugated polymers?seeing polymers in a new light. Angew Chem Int Ed 37 402 -    DOI : 10.1002/(sici)1521-3773(19980302)37:4<402::aid-anie402>;2-9.
Huynh WU , Dittmer JJ , Alivisatos AP (2002) Hybrid nanorod-polymer solar cells. Science 295 2425 -    DOI : 10.1126/science.1069156.
Sun B , Marx E , Greenham NC (2003) Photovoltaic devices using blends of branched CdSe nanoparticles and conjugated polymers. Nano Lett 3 961 -    DOI : 10.1021/nl0342895
Argun AA , Cirpan A , Reynolds JR (2003) The first truly all-polymer electrochromic devices. Adv Mater 15 1338 -    DOI : 10.1002/adma.200305038
Crone B , Dodabalapur A , Lin YY , Filas RW , Bao Z , LaDuca A , Sarpeshkar R , Katz HE , Li W (2000) Large-scale complementary integrated circuits based on organic transistors. Nature 403 521 -    DOI : 10.1038/35000530
Kim HK , Kim MS , Chun SY , Park YH , Jeon BS , Lee JY , Hong YK , Joo J , Kim SH (2003) Characteristics of electrically conducting polymercoated textiles. Mol Cryst Liq Cryst 405 161 -    DOI : 10.1080/15421400390263550
Hughes M , Shaffer MSP , Renouf AC , Singh C , Chen GZ , Fray DJ , Windle AH (2002) Electrochemical capacitance of nanocomposite films formed by coating aligned arrays of carbon nanotubes with polypyrrole. Adv Mater 14 382 -    DOI : 10.1002/1521-4095(20020304)14:5<382::aid-adma382>;2-y.
Rahman SU , Abul-Hamayel MA , Aleem BJA (2006) Electrochemically synthesized polypyrrole films as primer for protective coatings on carbon steel. Surf Coat Technol 200 2948 -    DOI : 10.1016/j.surfcoat.2005.04.012
Gardner JW , Bartlett PN (1995) Application of conducting polymer technology in microsystems. Sensors Actuators A: Physical 51 57 -    DOI : 10.1016/0924-4247(95)85004-x
Mazzoldi A , Della Santa A , De Rossi D (2000) Conducting polymer actuators: properties and modeling. In: Osada Y, De Rossi DE, eds. Polymer Sensors and Actuators Springer Berlin, Germany 207 -
Hagleitner C , Hierlemann A , Lange D , Kummer A , Kerness N , Brand O , Baltes H (2001) Smart single-chip gas sensor microsystem. Nature 414 293 -    DOI : 10.1038/35104535
Arami H , Mazloumi M , Khalifehzadeh R , Emami SH (2007) Sadrnezhaad SK. Polypyrrole/multiwall carbon nanotube nanocomposites electropolymerized on copper substrate. Mater Lett 61 4412 -    DOI : 10.1016/j.matlet.2007.02.015
Kauffman DR , Star A (2008) Carbon nanotube gas and vapor sensors. Angew Chem Int Ed 47 6550 -    DOI : 10.1002/anie.200704488
Im JS , Kim JG , Lee YS (2009) Fluorination effects of carbon black additives for electrical properties and EMI shielding efficiency by improved dispersion and adhesion. Carbon 47 2640 -    DOI : 10.1016/j.carbon.2009.05.017
Makeiff DA , Huber T (2006) Microwave absorption by polyaniline? carbon nanotube composites. Synth Met 156 497 -    DOI : 10.1016/j.synthmet.2005.05.019
Singh V , Mohan S , Singh G , Pandey PC , Prakash R (2008) Synthesis and characterization of polyaniline?carboxylated PVC composites: application in development of ammonia sensor. Sensors Actuators B: Chem 132 99 -    DOI : 10.1016/j.snb.2008.01.007.
Kodjie SL , Li L , Li B , Cai W , Li CY , Keating M (2006) Morphology and crystallization behavior of HDPE/CNT nanocomposite. J Macromol Sci B 45 231 -    DOI : 10.1080/00222340500522299
Mohammad F , Calvert P , Billingham N (1995) Thermal stability of electrochemically prepared polythiophene and polypyrrole. Bull Mater Sci 18 255 -    DOI : 10.1007/bf02749663
Wang SG , Zhang Q , Yang DJ , Sellin PJ , Zhong GF (2004) Multi-walled carbon nanotube-based gas sensors for NH3detection. Diamond Relat Mater 13 1327 -    DOI : 10.1016/j.diamond.2003.11.070.
Bhat NV , Gadre AP , Bambole VA (2001) Structural, mechanical, and electrical properties of electropolymerized polypyrrole composite films. J Appl Polym Sci 80 2511 -    DOI : 10.1002/app.1359
Yoon H , Chang M , Jang J (2006) Sensing behaviors of polypyrrole nanotubes prepared in reverse microemulsions: effects of transducer size and transduction mechanism. J Phys Chem B 110 14074 -    DOI : 10.1021/jp061423b