Identifying and quantitating defects on chemical vapor deposition grown graphene layers by selected electrochemical deposition of Au nanoparticles
Identifying and quantitating defects on chemical vapor deposition grown graphene layers by selected electrochemical deposition of Au nanoparticles
Carbon letters. 2012. Jan, 13(1): 56-59
Copyright ©2012, Korean Carbon Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : September 05, 2011
  • Accepted : December 10, 2011
  • Published : January 31, 2012
Export by style
Cited by
About the Authors
Hye-Mi, So
National Nanofab Center, Daejeon 305-806, Korea
Jeong Hun, Mun
Department of Electrical Engineering, Korea Advanced Institute of Science and Technology, Daejeon 305-701, Korea
Gyeong Sook, Bang
National Nanofab Center, Daejeon 305-806, Korea
Taek Yong, Kim
Department of Electrical Engineering, Korea Advanced Institute of Science and Technology, Daejeon 305-701, Korea
Byung Jin, Cho
Department of Electrical Engineering, Korea Advanced Institute of Science and Technology, Daejeon 305-701, Korea
Chi Won, Ahn
National Nanofab Center, Daejeon 305-806, Korea

The defect sites on chemical vapor deposition grown graphene are investigated through the selective electrochemical deposition (SED) of Au nanoparticles. For SED of Au nanoparticles, an engineered potential pulse is applied to the working electrode versus the reference electrode, thereby highlighting the defect sites, which are more reactive relative to the pristine surface. Most defect sites decorated by Au nanoparticles are situated along the Cu grain boundaries, implying that the origin of the defects lies in the synthesis of uneven graphene layers on the rough Cu surface.
1. Introduction
Since mono-layer graphene was isolated by Geim and Novoselov, numerous studies focused on various applications of graphene have been carried out in efforts to realize graphene-based devices. In this regard, the synthesis of large-area, high-quality graphene is a fundamental requirement. To date, epitaxial growth on SiC [1 - 3] , chemical vapor deposition (CVD) methods on catalytic metal substrates [4 - 9] , and chemical reduction of graphite oxide [10 - 13] have been widely studied for large-scale graphene synthesis. Notably, Hong and his colleagues [14] recently showed that the CVD method enables the synthesis of 30-inch wide high quality graphene. However, due to imperfect crystallinity and inherent defects, these synthetic graphene films have lower carrier mobility than mechanically cleaved graphene. For the measuring of the inherent defects in CVD grown graphene layers, Raman spectroscopy, atomic force microscopy (AFM), scanning electron microscopy (SEM), and tunneling electron microscopy are typically utilized. However, these methods are not suitable for the quantitative analysis of defects in graphene over a large area. Selective electrochemical deposition (SED), on the other hand, is a possible solution for efficient and quantitative measurement of the defect densities in synthetic graphene layers. Because the defect sites of graphene are more reactive than the pristine sp 2 bonded graphene lattice, defect sites can be decorated with high selectivity [15 - 21] .
Here, we carried out SED of Au nanoparticles on defect sites on CVD grown graphene layers, and the origin of the defects is suggested on the basis of the results.
2. Experimental
- 2.1. Graphene synthesis and sample preparation
The graphene layer was synthesized on the Cu surface by the CVD process using radio-
Lager Image
(a) Measurement configuration for selective electrochemical deposition of Au nanoparticles. (b) The engineered potential pulse to enhance the selectivity of Au nanoparticle deposition.
frequency (RF) plasma. A 300 nm thick Cu film deposited on top of a Si wafer with a 300 nm thick SiO 2 layer was inserted in an inductively coupled plasma CVD system. After ramping up temperature to 725℃ under Ar ambient at 50 mtorr, the sample was treated by H 2 plasma with a gas flow rate of 40 sccm and RF plasma power of 50 W for 2 min. A gas mixture of Ar and C 2 H 2 (Ar:C 2 H 2 = 40:1 sccm) was then flowed into the chamber with 150 W RF plasma for the graphene synthesis. The graphene layer synthesized on the Cu surface was finally transferred onto the SiO 2 (300 nm)/Si using a poly(methyl methacrylate) supporting layer and wet etching of the metal film.
- 2.2. Au decoration
To selectively decorate Au nanoparticles on graphene, we used electrochemical deposition. Employing a multi-potential system, we controlled both the nanoparticle size and packing density. A droplet of HAuCl 4 in 100 mM KCl (supporting electrolyte) was placed on the device and transferred graphene was used as a working electrode. A reduction potential was then applied with respect to an Ag|AgCl|KCl (3M) reference electrode with current monitoring using a Pt counter-electrode.
- 2.3. SEM and energy dispersive X-ray spectroscopy analysis
The Au particle decorated graphene samples were observed by a field-emission SEM/energy dispersive X-ray spectroscopy
Lager Image
(a) Scanning electron microscopy image, (b) energy dispersive X-ray spectroscopy spectrum, and (c) atomic force microscopy image of graphene surface on SiO2/Si substrate after selective electrochemical deposition of Au nanoparticles.
(EDAX) system (FEI Sirion SEM with an EDAX, The Netherlands). Prior to observation, the samples were placed on a metal stub with double sided carbon adhesive tape. The scanning energy for the EDAX analysis ranged from 0 to 4.75 KeV.
3. Results and Discussion
The measurement configuration and engineered potential pulse are shown in Fig. 1 . A drop of 50 μM HAuCl 4 solution was placed onto the transferred graphene. Deposition of Au nanopar-
Lager Image
(a) Microscope image of Cu surface after graphene synthesis, showing a highly agglomerated and roughened surface. Cross-sectional view of the sample (b) after graphene formation on the Cu substrate and (c) after layer transfer onto the flat SiO2/Si substrate.
ticles entailed three steps: protection, nucleation, and growth. The first step for the protected Au particles was applied at 1 V for 3 s. Following the first step, a pulse with E 2 = -0.6 V for 50 ms initiates nucleation at the prepared sites. Growth was continued at E 3 = 0.6 V for 1 s. We typically obtained roughly 30-nmsize Au nanoparticles using the above method. An SEM image of the Au nanoparticle decorated graphene surface is presented in Fig. 2 a. As reported earlier, wrinkles caused by different coefficients of thermal expansion between graphene and the Cu substrate and mechanical stress induced during layer transfer are observed over the entire graphene surface [8 , 9] . The shape and density of these wrinkles are more clearly shown in the AFM image ( Fig. 2 c). After SED by an engineered potential pulse, Au nanoparticles are situated in specific positions, as shown in Figs. 2 a and c. The EDAX spectrum for a white particle (white arrow) in the SEM image ( Fig. 2 b) exhibits a clear Au peak, implying the nucleation and growth of Au nanoparticles. Even though there are numerous wrinkles over the whole graphene surface, as shown in the SEM and AFM images, most Au nanoparticles are not located on these defects but instead form a specific shape that resembles a grain boundary of the Cu substrate shown in Fig. 3 a. The Cu surface is inevitably agglomerated and roughened during the graphene synthesis because of the high temperature annealing, an essential process for high quality synthesis of high quality graphene layers. Thus, as shown in Fig. 3 b, the graphene layers are synthesized along the highly roughened Cu surface. During the layer transfer of synthetic graphene onto the flat SiO 2 /Si substrate, this uneven graphene layer is folded, and defect sites are formed on the graphene layer ( Fig. 3 c). Consequently, the higher reaction energy of these defects caused by the rough surface of Cu attracts the Au nanoparticles.
4. Conclusions
In this work, we have quantitatively investigated the defects on large size, high quality graphene layers grown by the CVD method via SED of Au nanoparticles. By adjusting the potential applied to the graphene, selective deposition of Au nanoparticles on specific defect sites was achieved. Comparing the positions of defect sites and the Cu grain boundary, it is confirmed that most defect sites are caused by the unevenly synthesized graphene along the rough Cu surface.
This work was supported by the National Research Foundation of Korea (NRF) Research Grant, 2008-2002744, 2010- 0029132, and 2011-0017333.
Berger C , Song Z , Li X , Wu X , Brown N , Naud C , Mayou D , Li T , Hass J , Marchenkov AN , Conrad EH , First PN , De Heer WA (2006) Electronic confinement and coherence in patterned epitaxial graphene. Science 312 1191 -    DOI : 10.1126/science.1125925
Virojanadara C , Syväjarvi M , Yakimova R , Johansson LI , Zakharov AA , Balasubramanian T (2008) Homogeneous large-area graphene layer growth on 6H-SiC(0001). Phys Rev B 78 245403 -    DOI : 10.1103/PhysRevB.78.245403
Emtsev KV , Bostwick A , Horn K , Jobst J , Kellogg GL , Ley L , McChesney JL , Ohta T , Reshanov SA , Rohrl J , Rotenberg E , Schmid AK , Waldmann D , Weber HB , Seyller T (2009) Towards wafer- size graphene layers by atmospheric pressure graphitization of silicon carbide. Nature Mater 8 203 -    DOI : 10.1038/nmat2382
Obraztsov AN , Obraztsova EA , Tyurnina AV , Zolotukhin AA (2007) Chemical vapor deposition of thin graphite films of nanometer thickness. Carbon 45 2017 -    DOI : 10.1016/j.carbon.2007.05.028
Yu Q , Lian J , Siriponglert S , Li H , Chen YP , Pei SS (2008) Graphene segregated on Ni surfaces and transferred to insulators. Appl Phys Lett 93 113103 -    DOI : 10.1063/1.2982585
Reina A , Jia X , Ho J , Nezich D , Son H , Bulovic V , Dresselhaus MS , Jing K (2009) Large area, few-layer graphene films on arbitrary substrates by chemical vapor deposition. Nano Lett 9 30 -    DOI : 10.1021/nl801827v
Kim KS , Zhao Y , Jang H , Lee SY , Kim JM , Ahn JH , Kim P , Choi JY , Hong BH (2009) Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457 706 -    DOI : 10.1038/nature07719
Kang BJ , Mun JH , Hwang CY , Cho BJ (2009) Monolayer graphene growth on sputtered thin film platinum. J Appl Phys 106 104309 -    DOI : 10.1063/1.3254193
Li X , Cai W , An J , Kim S , Nah J , Yang D , Piner R , Velamakanni A , Jung I , Tutuc E , Banerjee SK , Colombo L , Ruoff RS (2009) Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324 1312 -    DOI : 10.1126/science.1171245
Li X , Wang X , Zhang L , Lee S , Dai H (2008) Chemically derived, ultrasmooth graphene nanoribbon semiconductors. Science 319 1229 -    DOI : 10.1126/science.1150878
Li X , Zhang G , Bai X , Sun X , Wang X , Wang E , Dai H (2008) Highly conducting graphene sheets and Langmuir-Blodgett films. Nature Nanotechnol 3 538 -    DOI : 10.1038/nnano.2008.210
Eda G , Fanchini G , Chhowalla M (2008) Large-area ultrathin films of reduced graphene oxide as a transparent and flexible electronic material. Nature Nanotechnol 3 270 -    DOI : 10.1038/nnano.2008.83
Li D , Muller MB , Gilje S , Kaner RB , Wallace GG (2008) Processable aqueous dispersions of graphene nanosheets. Nature Nanotechnol 3 101 -    DOI : 10.1038/nnano.2007.451
Bae S , Kim H , Lee Y , Xu X , Park JS , Zheng Y , Balakrishnan J , Lei T , Ri Kim H , Song YI , Kim YJ , Kim KS , Ozyilmaz B , Ahn JH , Hong BH , Iijima S (2010) Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nature Nanotechnol 5 574 -    DOI : 10.1038/nnano.2010.132
Zach MP , Ng KH , Penner RM (2000) Molybdenum nanowires by electrodeposition. Science 290 2120 -    DOI : 10.1126/science.290.5499.2120
Penner RM (2002) Mesoscopic metal particles and wires by electrodeposition. J Phys Chem B 106 3339 -    DOI : 10.1021/jp013219o
Walter EC , Zach MP , Favier F , Murray BJ , Inazu K , Hemminger JC , Penner RM (2003) Metal nanowire arrays by electrodeposition. Chem Phys Chem 4 131 -    DOI : 10.1002/cphc.200390022
Banks CE , Davies TJ , Wildgoose GG , Compton RG (2005) Electrocatalysisat graphite and carbon nanotube modified electrodes: edgeplanesites and tube ends are the reactive sites. Chem Commun 7 829 -    DOI : 10.1039/b413177k
Fan Y , Goldsmith BR , Collins PG (2005) Identifying and counting pointdefects in carbon nanotubes. Nature Mater 4 906 -    DOI : 10.1038/nmat1516
Mubeen S , Zhang T , Chartuprayoon N , Rheem Y , Mulchandani A , Myung NV , Deshusses MA (2010) Sensitive detection of H2S usinggold nanoparticle decorated single-walled carbon nanotubes. Anal Chem 82 250 -    DOI : 10.1021/ac901871d
Kim YT , Han JH , Hong BH , Kwon YU (2010) Electrochemical Synthesisof CdSe quantum-Dot arrays on a graphene basal plane usingmesoporous silica thin-film templates. Adv Mater 22 515 -    DOI : 10.1002/adma.200902736