Effect of SiO2 and Nb2O5 Buffer Layer on Optical Characteristics of ITO Thin Film
Effect of SiO2 and Nb2O5 Buffer Layer on Optical Characteristics of ITO Thin Film
Transactions on Electrical and Electronic Materials. 2015. Feb, 16(1): 29-33
Copyright © 2015, The Korean Institute of Electrical and Electronic Material Engineers
This is an open-access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0) which permits unrestricted noncommercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : October 10, 2014
  • Accepted : December 12, 2014
  • Published : February 25, 2015
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Yong-Han Kwon
Gun-Eik Jang
gejang@chungbuk.ac.kr
Abstract
This paper presents the results of the optical characteristics of ITO thin film with different buffer layer thicknesses of SiO 2 and Nb 2 O 5 for touch sensor application. SiO 2 and Nb 2 O 5 buffer layers were deposited using RF magnetron sputtering equipment. The buffer layers were inserted between glass and ITO layers. In order to compare with the experimental results, the Essential Macleod Program (EMP) was adopted. Based on EMP simulation, the [Nb 2 O 5 |SiO 2 |ITO] multi-layered thin film exhibited high transmittance of more than 85% in the visible region. The actual experimental results also showed transmittance of more than 85% in the visible region, indicating that the simulated results were well matched with the experimental results. The sheet resistance of ITO based film was about 340 Ω/sq. The surface roughness maintained a relatively small value within the range of 0.1~0.4 nm when using the Nb 2 O 5 and SiO 2 buffer layers.
Keywords
1. INTRODUCTION
Transparent conducting oxides (TCOs) are special semiconductors that possess three physical properties: high optical transparency, low reflectivity, and high electrical conductivity [1-4]. They are used as transparent conducting coatings, and have been widely used in a variety of electronic and optoelectronic device applications [5 - 11] such as organic light emitting diodes (OLED), liquid crystal displays (LCD), solar cells [12 - 17] , and anti-reflection casting. To date, a number of research projects have been successfully carried out in the area of TCO materials. Important TCO semiconductors include impurity-doped ZnO, In 2 O 3 , SnO 2 , and CdO, ternary compounds including Zn2SnO4, ZnSnO 3 , Zn 2 In 2 O 5 , Zn3In 2 O6, In 2 SnO4, and CdSnO 3 , as well as multi-component oxides consisting of combinations of ZnO, In 2 O 3 , and SnO 2 . However, among many TCO materials, Sn doped In 2 O 3 (ITO) is still the preferred material for most present applications. ITO has a multitude of properties, including degenerated semiconductor (n-type) behavior with a controllable resistivity and high optical gap (3.6eV) [18 , 19] . The low resistivity of ITO film is believed to be due to the large free carrier density, which is within the range of 10 20 /cm 3 to 10 21 /cm 3 [20 , 21] .
To date, many investigators have conducted research to determine how to further increase the transmittance of ITO film while reducing the resistivity and processing temperature using buffer layers. Another issue that still needs to be resolved is how to minimize the visibility problem when ITO film is used. Some researchers have considered the effect of introducing a buffer layer such as SiO 2 , ZnO [22] , Al 2 O 3 , or Nb 2 O 5 , while suggesting that the optical and electrical properties of TCO film coated on the soda lime glass can be improved by introducing such buffer layers because these oxide films effectively prevent the diffusion of Na atoms into ITO films and improve the surface roughness of films. Also, the buffer layer can be effective to reduce the visual problem due to the anti-reflection effect.
The overall objective of this research is to evaluate the transmittance change of ITO based film using buffer layers with high and low refractive index material. In this study, SiO 2 and Nb 2 O 5 were selected as suitable buffer layers among the buffer layer materials. SiO 2 was selected due to its low refractive index material (n = 1.4) and its additional advantages in ITO films. Also, niobium oxide (Nb 2 O 5 ) is a representative high refractive index material (n = 2.3) with outstanding thermal stability.
2. EXPERIMENTS
- 2.1 Sample preparation
[Nb 2 O 5 |SiO 2 | ITO] multi-layer films were prepared using a radio-frequency (RF) magnetron sputtering system. A series of [Nb 2 O 5 |SiO 2 |ITO] multi-layer thin films with different Nb 2 O 5 and SiO 2 thicknesses were deposited on the soda lime glass substrates. The Nb 2 O 5 and SiO 2 thicknesses varied from 10 to 20 nm and 45 to 55 nm, respectively. In addition, the ITO thickness was kept constant at 40 nm. The sputtering gas was pure Ar(99.99%) at a pressure of 2.5 × 10 -5 torr. The RF powers for the Nb 2 O 5 (purity 99.99%), SiO 2 (purity 99.99%) and ITO targets were fixed as 100 W. The ITO target (purity 99.99%) was a commercially available hot-pressed pallet composed of 90 wt.% In 2 O 3 with 10 wt.% SnO 2 . Table 1 lists all the sputtering conditions for films such as Nb 2 O 5 , SiO 2 , and ITO.
Deposition conditions of Nb2O5, SiO2, and ITO films by RF magnetron sputtering.
PPT Slide
Lager Image
Deposition conditions of Nb2O5, SiO2, and ITO films by RF magnetron sputtering.
- 2.2 Characterizations
In order to select the Nb 2 O 5 and SiO 2 buffer layer thicknesses, the Essential Macleod Program (EMP) was adopted. The simulation was designed with variable parameters such as wavelength (400~700 nm) and thickness of layers [Nb 2 O 5 (5~30 nm)|SiO 2 (40~65 nm)|ITO (40 nm)]. The surface morphology of the films was investigated by Atomic Force Microscope (AFM) measurements in contact mode. The transmittance and reflectance of the films were measured using a UV-VIS-NIR spectrophotometer (KONICA-MINOLTA CM-3600d) in the 400~700 nm wavelength range. The sheet resistance and the resistivity of the samples were calculated using the four-point probe method (KEITHLEY 2700 multimeter/data acquisition system). In addition, the interfacial properties of the optimized [Nb 2 O 5 (20 nm)|SiO 2 (45 nm)|ITO (40 nm)] electrodes were analyzed using (AES) depth profiling.
3. RESULTS AND DISCUSSION
An Essential Macleod Program (EMP) was adopted to optimize the Nb 2 O 5 and SiO 2 buffer layer thicknesses. Figure 1 shows the transmittance of [Nb 2 O 5 (5, 10, 15, 20, 25, 30 nm)|SiO 2 (40, 45, 50, 55, 60, 65 nm)|ITO (40 nm)] multi-layer films from 400 to 700 nm wavelength using the EMP method. Based on EMP simulation, the [Nb 2 O 5 (10, 15, 20 nm)|SiO 2 (45, 50, 55 nm)|ITO (40 nm)] multi-layered thin film exhibited a high average transmittance of more than 85% in the visible region (400~700 nm).
PPT Slide
Lager Image
Simulated optical transmittance spectra of ITO films with Nb2O5 and SiO2 buffer layers of different thicknesses; (a) [Nb2O5(5-30 nm)|SiO2(50 nm)|ITO(40 nm)] and (b) [Nb2O5(15 nm)|SiO2(40-65 nm)|ITO(40 nm)].
Figure 2 presents the typical simulated optical transmittance of the [Nb 2 O 5 (15 nm)|SiO 2 (50 nm)|ITO (40 nm)] film using the EMP program and the measured optical transmittance of the [Nb 2 O 5 (15 nm)|SiO 2 (50 nm)|ITO (40 nm)] multi-layer film, respectively for comparison. The transmission spectra were measured with a UV-VIS-NIR spectrophotometer in the 400~700 nm wavelength range. Compared with the EMP simulation result, the experimental results matched relatively well with the simulated results, showing a similar tendency in terms of different wavelengths. The simulated and measured transmittances of the [Nb 2 O 5 (15 nm)|SiO 2 (50 nm)|ITO (40 nm)] film were in the range of about 87% ~ 92% at 550 nm wavelength.
PPT Slide
Lager Image
Simulated optical transmittance of the [Nb2O5(15 nm)|SiO2(50 nm)|ITO(40 nm)] film using the EMP program and the measured optical transmittance of the [Nb2O5(15 nm)|SiO2 (50 nm)|ITO(40 nm)] multi-layer film for comparison.
Figure 3 shows the transmittance of the ITO films with different [Nb 2 O 5 |SiO 2 ] buffer layers in the wavelength range of 400-700 nm, with the ITO single layer as the reference. The glass substrate has a 95% transmittance at 550 nm, whereas the ITO films with Nb 2 O 5 and SiO 2 buffer layers deposited on glass have a transmittance of about 85%~88% at 550 nm. As seen in Fig. 3 , the film transmittance decreased slightly in the 400~500 wavelength range when the Nb 2 O 5 and SiO 2 buffer layer thicknesses increased, possibly due to the increase in absorption of the buffer layers. As a result of using the buffer layer, the transmittance of the multi-layer films was 5% higher than that of the ITO single layer.
PPT Slide
Lager Image
Transmittance spectra of ITO films with Nb2O5 and SiO2 buffer layers of different thicknesses.
The morphology of the deposited films was investigated using AFM. Fig. 4 shows AFM images of the ITO single layer and [Nb 2 O 5 |SiO 2 |ITO] multi-layer films. The thickness of the ITO films was kept at about 40 nm. It can be seen that the surface roughness of the ITO films was related to that of the underlying buffer layer. A relatively large RMS value appeared for the ITO film deposited directly on the glass substrate. The pre-deposition of the Nb 2 O 5 and SiO 2 buffer layer decreased the surface roughness of the glass substrate, resulting in a decrease of the RMS value of the ITO films. Atoms grow preferably in sunken regions on the substrate. Surface roughness maintained a relatively small value in the range of 0.1~0.4 nm, using Nb 2 O 5 and SiO 2 buffer layers. The net effect is that the ITO film with the Nb 2 O 5 and SiO 2 buffer layers has the smoothest surface.
PPT Slide
Lager Image
AFM images of the ITO (40 nm) films with Nb2O5 and SiO2 buffer layers of different thicknesses; (a) ITO single layer; (b) Nb2O5(10 nm) | SiO2(45 nm); (c) Nb2O5(10 nm) | SiO2(50 nm); (d) Nb2O5(10 nm) | SiO2(55 nm); (e) Nb2O5(15 nm) | SiO2(45 nm); (f) Nb2O5(15 nm) | SiO2(50 nm); (g) Nb2O5(15 nm) | SiO2(55 nm); (h) Nb2O5(20 nm) | SiO2(45 nm); (i) Nb2O5(20 nm) | SiO2(50 nm); (j) Nb2O5(20 nm) | SiO2(55 nm).
Figure 5 shows the effect of Nb 2 O 5 and SiO 2 buffer layer thicknesses on the sheet resistivity of the ITO films. Table 2 presents the sample numbers in terms of Nb 2 O 5 and SiO 2 film thicknesses. The ITO single layer has a 391 Ω/sq. sheet resistance, and the ITO films with Nb 2 O 5 and SiO 2 buffer layers deposited on glass show a sheet resistivity of about 330~343 Ω/sq. A comparison of the RMS in Fig. 4(h) shows that ITO films with Nb 2 O 5 (20 nm) and SiO 2 (45 nm) buffer layers have the smoothest surface. We assume the decrease of sheet resistance in the ITO film with an optimized buffer layer is related to the change of ITO surface morphology. It was known that a smoother surface has a positive effect on decreasing resistivity [23] . Fig. 6 shows the AES depth profiles of the optimized [Nb 2 O 5 (20 nm)|SiO 2 (45 nm)|ITO (40 nm)] electrodes on the glass substrate. Based on AES data, each Nb 2 O 5 and SiO 2 ITO region is relatively well defined and no typical and distinguishable interfacial diffusion is observed between each layer.
PPT Slide
Lager Image
Dependence of the sheet resistance for ITO films on the [Nb2O5|SiO2] buffer layer thickness ; (a) ITO single layer; (b) Nb2O5(10 nm) | SiO2(45 nm); (c) Nb2O5(10 nm) | SiO2( 50 nm); (d) Nb2O5(10 nm) | SiO2(55 nm); (e) Nb2O5(15 nm) | SiO2(45 nm); (f) Nb2O5(15 nm) | SiO2(50 nm); (g) Nb2O5(15 nm) | SiO2(50 nm); (h) Nb2O5(20 nm) | SiO2(45 nm); (i) Nb2O5(20 nm) | SiO2(50 nm); (j) Nb2O5(20 nm) | SiO2(55 nm).
Sample number in terms of Nb2O5and SiO2film thickness.
PPT Slide
Lager Image
Sample number in terms of Nb2O5 and SiO2 film thickness.
PPT Slide
Lager Image
AES depth profiles of [Nb2O5|SiO2|ITO] multi-layer film grown on a glass substrate under an optimized condition.
4. CONCLUSIONS
The effects of the thickness of the Nb 2 O 5 and SiO 2 buf fer layer on the optical, structural, and electrical properties of ITO films on glass substrates were investigated. An improvement in the electrical resistivity of ITO film was achieved by applying a [Nb 2 O 5 |SiO 2 ] buffer layer between the ITO film and the glass substrate. The resistivity of the films decreased from 391 Ω /sq. to 320 Ω /sq. when the [Nb 2 O 5 |SiO 2 ] buffer layer produced at a deposition thickness of 20 nm and 45 nm was applied. ITO films with 20 nm thick Nb 2 O 5 and 45 nm thick SiO 2 buffer layers have the lowest sheet resistance (320 Ohm/sq.). During the degree of crystallization, the decrease in surface roughness was beneficial to the enhancement of electrical properties. The [Nb 2 O 5 |SiO 2 ] buffer layers have little effect on the optical transmittance of all the ITO films. Compared with the transmittance of an ITO single layer film, the transmittance of [Nb 2 O 5 |SiO 2 |ITO] multi-layer films increased slightly in the visible range of 400~700 nm. We can conclude that the structural, optical, and electrical studies reveal that [Nb 2 O 5 |SiO 2 ] buffer layers play a key role in increasing the transmittance of ITO thin films.
References
Yang C. H. , Lee S. C. , Lin T. C. , Chen S.C. 2008 Thin Solid Films 516 1984 -
Chen C. M. , Hsu T. C. , Cherng S. J. 2011 J. Alloy. Compd. 509 872 -
Dagkaldiran U. , Gordijn A. , Finger F. , Yates H. M. , Evans P. , Sheel D. W. , Remes Z. , Vanecek M. 2009 Mater. Sci. Eng. B 159 6 -
Seong C. H. , Shin Y. J. , Jang G. E. 2012 Trans. Electr. Electron. Mater. 13 2 -
Ramamoorthya K. , Kumara K. , Chandramohan R. , Sankaranarayanan K. 2006 Mater. Sci. Eng. B 126 -
Houng B. , Lin S. L. , Chen S. W. , Wang A. 2011 Ceramics International 37 3397 -
Guillen C. , Herrero J. 2006 Vaccum 80 615 -
Kim D. H. , Park M. R. , Lee C. H. 2006 Surf. Coat. Technol. 201 927 -
Sun X. W. , Wang L. D. , Kwok H. S. 2000 Thin Solid Films 360 75 -
Kim S. I. , Cho S. H. , Choi S. R. , Yoon H. H. , Song P. K. 2009 Current Appl. Phys. 9 S262 -
Paeng S. H. , Park M. W. , Sung Y. M. 2010 Surf. Coat. Technol. 205 S210 -
Selvan J.A.A. , Delahoy A. E. , Li Y. M. 2006 Sol. Energ. Mat. Sol. C. 90 3371 -
Abreu Fernandes S. , Schoeps B. , Kowalick K. , Nett R. , Esen C. , Pickshaus M. , Ostendorf A. 2013 Physics Procedia 41 795 -
Choi K. H. , Kim J. H. , Noh Y. J. , Na S. I. , Kim H. K. 2013 Sol. Energ. Mat. Sol. C. 110 147 -
Lim J. W. , Na S. I. , Kim H. K. 2012 Sol. Energ. Mat. Sol. C. 98 409 -
Lachaume R. , Favre W. , Scheiblin P. , Garros X. , Nguyen N. , Coignus J. , Munoz D. , Reimbold G. 2013 Energy Procedia 38 770 -
Meng L. J. , Santos M.P.D. 1997 Thin Solid Films 303 151 -
Ambrosini A. , Duarte A. , Poeppelmeier K. R. , Lane M. , Kannewurf C. R. , Mason T. O. 2000 Journal of Solid State Chemistry 154 41 -
Brewer S. H. , Franzen S. 2004 Chemical Physics 300 285 -
Hamberg I. , Granqvist C. G. 1986 J. Appl. Phys. 60 R123 -
Ellmer K. , Mientus R. 2008 Thin Solid Films 516 5829 -
Hsu C. Y. , Ko T. F. , Huang Y. M. 2008 Journal of the European Ceramic Society 28 3065 -
Ri K. H. , Wang Y. B. , Zhou W. L. , Gao J. X. , Wang X. J. , Yu J. 2011 Appl. Surf. Sci. 257 5471 -