Effect of an Electric Field on the AC Electrical Treeing in Various Epoxy/Reactive Diluent Systems
Effect of an Electric Field on the AC Electrical Treeing in Various Epoxy/Reactive Diluent Systems
Transactions on Electrical and Electronic Materials. 2013. Dec, 14(6): 308-311
Copyright ©2013, The Korean Institute of Electrical and Electronic Material Engineers
This is an open-access article distributed under the terms of the Creative Commons Attribution Non-CommercialLicense (http://creativecommons.org/licenses/by-nc/3.0) which permits unrestricted noncommercial use,distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : August 08, 2013
  • Accepted : October 10, 2013
  • Published : December 25, 2013
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Jeong- Hwan Bang
Jeong- Hwan Bang Department of Environmental Health, Seonam University, Namwon 590-711, Korea
Jae-Jun Park
Department of Electrical and Electronic Engineering, Joongbu University, Geumsan 312-702, Korea
jjpark@joongbu.ac.kr
Abstract
The effect of an electric field on the ac electrical treeing in various epoxy/reactive diluent systems was studied in a needle-plate electrode geometry. Diglycidyl ether of bisphenol A (DGEBA) type epoxy was used as a base resin, and 1,4-butanediol diglycidyl ether (BDGE) or polyglycol (PG) as a reactive diluent was introduced to the DGEBA system, in order to decrease the viscosity of the DGEBA epoxy system. BDGE was acted as a chain extender, and PG acted as a flexibilizer, after the curing reaction. To measure the treeing initiation time and the propagation rate, three constant alternating currents (ac) of 10, 13 and 15 kV/4.2 mm (60 Hz) were applied to the specimen, in a needle-plate electrode arrangement, at 30℃ of insulating oil bath. When 10 kV/4.2 mm (60 Hz) was applied, the treeing initiation time and the propagation rate in the DGEBA system were 356 min and 1.10 × 10 -3 mm/min, respectively, those in the DGEBA/ BDGE system were 150 min and 1.14 × 10 -3 mm/min, respectively. Those in the DGEBA/PG system were 469 min and 1.05 × 10 -3 mm/min, respectively. As 15 kV/4.2 mm (60 Hz) was applied, the propagation rate in the DGEBA system was 5.41 × 10 -3 mm/min, and that in the DGEBA/PG system was 1.42 × 10 -3 mm/min. These values meant that PG could be used as a reactive diluent in the DGEBA system, without the deterioration of the insulation breakdown property.
Keywords
1. INTRODUCTION
Epoxy resins have good mechanical and thermal properties, as well as excellent electrical properties; thus they have been used as insulation materials in the field of heavy electric equipment, such as mold-type transformers, current transformers (CT), potential transformers (PT), metering out-fit (MOF), gas switching gears, and so on [1 - 3] . In order to achieve these performances, many kinds of inorganic fillers, such as silica (SiO 2 ) [4] , alumina (Al 2 O 3 ) [5] , mica [6] , aluminum nitride (AlN) [7] , titanium dioxide (TiO 2 ) [8] , etc. have been incorporated into the epoxy resins.
However, when inorganic filler was incorporated into an epoxy resin, the viscosity became too high. So it was very difficult, not only to disperse the fillers homogeneously, and to remove bubbles from the epoxy/filler mixture, but also to inject the viscous mixture into a mold, during the curing process. Therefore, in order to decrease the viscosity, plasticizers, organic solvents or reactive diluents were introduced to the epoxy/filler composites, so that bubbles were easily removed from the composites, after injection into a mold.
However, the plasticizers disturbed the cure reaction of the epoxy system, so that the crosslink density decreased. This caused decrease of the electrical, mechanical and thermal properties of the epoxy system. And, when organic solvent was used, it should be removed completely after mixing the epoxy, fillers and organic solvent. If not, it might act as an impurity, so that the electrical, mechanical and thermal properties of the epoxy composite would be negatively affected. Reactive diluents were used, in order to decrease the viscosity during mixing, and the electrical treeing phenomenon was studied, in order to estimate the insulation characteristics of neat epoxies or their nanocomposites, because the treeing phenomenon was often referred to as the most important mechanism for the deterioration of polymeric insulators (e.g. high voltage polymeric cables) [9 - 12] . The treeing growth mechanism was divided into three processes: (1) incubation process, (2) initiation process, and (3) propagation process. If an electrical treeing was initiated, it would be propagated rapidly, and finally the breakdown would occur. Hence, the initiation time should be delayed, and the propagation rate be retarded, in order to get excellent insulation polymeric materials.
In my previous work [13] , the effects of ambient temperature on the electrical treeing phenomenon were studied in needleplate electrodes, and in this study, three epoxy/reactive diluent systems for the insulation materials of heavy electric equipment were prepared, and the effects of electric field on the electrical treeing phenomenon were studied in needle-plate electrodes.
2. EXPERIMENTS
- 2.1 Materials
A commercial DGEBA (diglycidyl ether of bisphenol A) type epoxy resin, trade name YD 128 (Kukdo Chem. Co.), was used. The equivalent weight was 184~190, and the viscosity was 11,500~13,500 cps at 25℃. The curing agent was Me-THPA (3- or 4-methyl-1,2,3,6-tetrahydrophthalic anhydride), whose grade name was HN-2200 (Hitachi Chem. Co.). It is widely used in the field of electric insulation. An accelerator was BDMA (benzyl-dimethyl amine, Kukdo Chem. Co.). A reactive diluent employed as a flexibilizer was a polyglycol (PG), under the trade name DY-040 (Ciba-Geigy Co.). Its molecular weight was about 7,000~10,000, and its viscosity was 60~90 cps at 25℃. Another reactive diluent as an aliphatic epoxy resin was purchased from Kukdo Chem. Co., under the trade name BDGE. Its equivalent weight was 120~140, and its viscosity was 15~30 cps at 25℃.
- 2.2 Specimen preparation for ac treeing test
DGEBA (100 g), THPA (92 g) and reactive diluent (10 g) were well-mixed with a high-speed agitator at 5,000 rpm for 10 min, and BDMA (1 g) was mixed with the agitator for 3 min. The mixture was poured into a mold having a cavity of 15×15 mm 2 with 30 mm height, in which a needle electrode was arranged beforehand, to make the distance of needle-plate electrodes be 4.2 mm. Then it was cured at 120℃ for 2 hr, post-cured at 150℃ for 2 hr, and cooled slowly at a rate of -0.5℃/min until room temperature, to avoid internal stress. Finally, the opposite-side of the needle electrode in the epoxy specimen was coated with conductive silver paste.
- 2.3 AC treeing test
To measure the treeing initiation and propagation rate, three constant alternating currents (ac) of 10, 13, and 15 kV/4.2 mm (60 Hz) were applied to the specimen, in needle-plate electrode arrangement, in insulating oil bath at 30℃. Then, the specimen was inserted into the insulating oil, and maintained sufficiently for 2 hr, until the temperature of the needle tip area reached to 30℃. Then, high voltage (HV) was applied, by using an ac Endurance Voltage Tester (Haefely, Germany) at a rising speed of 1 kV/ s until 10 kV, and the test voltage was kept, until electrical breakdown took place. The treeing morphology was monitored by a video microscope system (ICS-305B, SOMETECH Inc.), and the treeing images were collected every 1 min.
Lager Image
Treeing growth rate in the various epoxy systems, tested in aconstant electric field of 10 kV/4.2 mm (60 Hz) at 30℃.
3. RESULTS AND DISCUSSION
Figure 1 shows the treeing growth rate in DGEBA epoxy systems with BDGE or PG, tested under a constant electric field of 10 kV/4.2 mm (60 Hz) at 30℃. In the DGEBA system, electrical treeing was initiated in 356 min, and propagated at the breakdown speed of 1.10 × 10 -3 mm/min, and finally, breakdown took place in 3,794 min. In the DGEBA/BDGE system, the treeing initiation time in needle-plate electrode geometry was 150 min, which was 2.4 times lower, and the breakdown time was 3,669 min, which was 0.96 times lower, than that of the DGEBA system. The propagation rate of the DGEBA system was 1.10 × 10 -3 mm/ min, and that in the DGEBA/BDGE system was 1.14 × 10 -3 mm/ min, which was slightly faster. In the DGEBA/PG system, the treeing initiation time was 469 min, the breakdown time was 3,996 min, and the propagation rate was 1.05 × 10 -3 mm/min. The breakdown speed of the DGEBA/PG system was 5% slower than that of the DGEBA system.
The morphology of electrical treeing for the DGEBA/PG system was shown in Fig. 2 . Typical behavior of the branch type electrical treeing was obtained from the morphology observation. That is to say, when a constant ac electric field of 10 kV/4.2 mm (60 Hz) was applied, electrons were injected and extracted at the needle tip, so that small electrical treeing was faintly initiated from the needle tip ( Figure 2 (a)). And then, electrons were injected and extracted at the newly generated conductive treeing tip, which had been carbonized, so that several branches newly appeared, and they grew rapidly, became fatter and darker, with many new branches ( Figs. 2 (b)~2(e)); and finally, the penetration breakdown took place, from the needle tip to the silver electrode plate ( Fig. 2 (f )).
To compare the effect of the diluents on the treeing phenomena, the treeing morphologies in the initiation stage and the propagation state in similar time are shown in Fig. 3 . In the initial stage, many more branches were observed in the DGEBA/ BDGE system ( Fig. 3 (c)), than in the DGEBA system, and far fewer branches in the DGEBA/PG system are shown in Fig. 3 (e). In the similar time of the propagation state, the primary branches formed many new secondary branches. That is to say, electrons injected and extracted at the needle tip initiated small electrical treeing from the needle tip, and then electrons were injected and extracted at the newly generated primary treeing tip, which had been carbonized, so that many branches newly appeared ( Figs. 3 (b, d, f )), regardless of the diluents species. They grew, and be-
Lager Image
Electrical treeing morphology of the DGEBA/PG system, testedin a constant electric field of 10 kV/4.2 mm (60 Hz) at 30℃, for (a) 180min, (b) 300 min, (c) 1,050 min, (d) 1,650 min, (e) 3,650 min, and (f )3,996 min.
Lager Image
Electrical treeing morphology of the various epoxy systems,tested in the constant electric field of 10 kV/4.2 mm (60 Hz) at 30℃,for (a) 420 min, and (b) 3,550 min, in the DGEBA system, (c) 115 min,and (d) 3,650 min, in the DGEBA/BDGE system, and (e) 1,050 min,and (f) 3,650 min, in the DGEBA/PG system.
came fatter and darker with new branches, and finally, the penetration breakdown took place.
Many more branches were shown in the DGEBA/BDGE system, as shown in Fig. 3 (d), and far fewer branches were displayed in the DGEBA/PG system. These results meant that PG could be used as a reactive diluent in the DGEBA system, without the deterioration of the insulation breakdown property.
Figs. 4 and 5 show the treeing growth rate in the three epoxy systems tested in the electric field of 13 kV/4.2 mm and 15 kV/4.2 mm at 30℃, respectively. In the DGEBA system at 13 kV/4.2 mm, the treeing propagation rate was 2.62 × 10 -3 mm/min, and that at 15 kV/4.2 mm was 5.41 × 10 -3 mm/min, which was far faster than the value 1.10 × 10 -3 mm/min at 10 kV/4.2 mm, as was expected.
Lager Image
Treeing growth rate in the various epoxy systems, tested in aconstant electric field of 13 kV/4.2 mm (60 Hz) at 30℃.
Lager Image
Treeing growth rate in the various epoxy systems, tested in theconstant electric field of 15 kV/4.2 mm (60 Hz) at 30℃.
Lager Image
Electrical treeing morphology of the DGEBA system, tested in(a) 10 kV/4.2 mm (3,550 min), (b) 13 kV/4.2 mm (720 min), and (c)15 kV/4.2 mm (720 min). All were tested at 30℃, in the electrical frequencyof 60 Hz.
In the DGEBA/PG system at 13 kV/4.2 mm, the treeing propagation rate was 1.63 × 10 -3 mm/min, and that at 15 kV/4.2 mm was 3.62 × 10 -3 mm/min, which was far faster than the value 1.05 × 10 -3 mm/min at 10 kV/4.2 mm. These meant that the tree propagation rate increased with increasing electric field, as was expected.
To study the effect of the applied electric field on the treeing morphology, the electric treeing morphology of the DGEBA system in Fig. 6 was obtained after testing in (a) 10 kV/4.2 mm
Lager Image
Electrical treeing morphology of the (a) DGEBA, (b) DGEBA/BDGE, and (c) DGEBA/PG systems, tested in 15 kV/4.2 mm (60 Hz) at30℃ for 720 min.
(3,550 min), (b) 13 kV/4.2 mm (720 min), and (c) 15 kV/4.2 mm (720 min). Typical branch type treeing was observed, regardless of the electric field. More precisely speaking, as the electric field increased, many more branches were formed. Compared to Fig. 3 , many more branches at the higher electric field were also observed in the other epoxy systems, as shown in Fig. 7 . Far shorter treeing propagation was displayed in the DGEBA/PG system, and it meant that PG could retard the treeing propagation. Therefore, PG could be used as a reactive diluent in the DGEBA system, without the deterioration of the insulation breakdown property.
4. CONCLUSIONS
The effects of an electric field on the ac electrical treeing in DGEBA, DGEBA/BDGE and DGEBA/PG systems were studied, by carrying out the treeing test at constant alternating currents (ac) of 10, 13 and 15 kV/4.2 mm (60 Hz), in needle-plate electrode geometry. When 10 kV/4.2 mm (60 Hz) was applied, the treeing initiation time and the propagation rate in the DGEBA system were 356 min and 1.10 × 10 -3 mm/min, respectively, and those in the DGEBA/BDGE system were 150 min and 1.14 × 10 -3 mm/min, respectively. Those in the DGEBA/PG system were 469 min and 1.05 × 10 -3 mm/min, respectively. When 15 kV/4.2 mm (60 Hz) was applied, the propagation rate in the DGEBA system was 5.41 × 10 -3 mm/min, and that in the DGEBA/PG system was 1.42 × 10 -3 mm/min. These values meant that PG could retard the treeing propagation; therefore, PG could be used as a reactive diluent in the DGEBA system, without the deterioration of the insulation breakdown property.
Acknowledgements
This work was supported by Joongbu University (2013).
References
Lee J. Y. , Shim M. J. , Kim S. W. (1999) Polym. Eng. Sci. 39 1993 -
Cho Y. S. , Shim M. J. , Kim S. W. (2000) Mater. Chem. Phys. 66 70 -
Sarathi R. , Sahu R. K. , Rajeshkumar P. (2007) Mater. Sci. Eng.: A, 445 567 -
Henk P. O. , Kortsen T. W. , Kvarts T. (1999) High Perform. Polym. 11 281 -
Ehsani M. , Farhadinejad Z. , Moemen-bellah S. , Bagher alavi S. M. , Shrazi M. M. S. , Borsi H. (2011) 26th Internal Power System Conference Tehran, Iran 11-E-CAM-2359
Bajaj P. , Jha N. K. , Kumar A. (1995) J. Appl. Polym. Sci. 56 1339 -
Xu Y. , Chung D. D. L. , Mroz C. (2001) Composites: Part A 32 1749 -
Wazzan A. A. , Al-Turaif H. A. , Abdelkader A. F. (2006) Polymer-Plastics Technology and Engineering 45 1155 -
Tanaka T. , Montanari G. C. , Mülhaupt R. (2004) IEEE Trans.Dielectr. Electr. Insul. 11 763 -
Imai T. , Sawa F. , Ozaki T. , Shimizu T. , Kido R. , Kozako M. , Tanaka T. (2005) Intern. Sympos. Electr. Insulating Materials Kitakyushu, Japan 239 -
Park J. J. , Lee J. Y. (2010) IEEE Trans. Dielectr. Electr. Insul. 17 1516 -
Suh D. J. , Park O. O. (2002) J. Appl. Polym. Sci. 83 2143 -
Park J. J. (2013) Trans. Electr. Electron. Mater. 14 221 -