Electrochemical Performance of Lithium Iron Phosphate by Adding Graphite Nanofiber for Lithium Ion Batteries
Electrochemical Performance of Lithium Iron Phosphate by Adding Graphite Nanofiber for Lithium Ion Batteries
Transactions on Electrical and Electronic Materials. 2012. Jun, 13(3): 121-124
Copyright ©2012, The Korean Institute of Electrical and Electronic Material Engineers
This is an open-access article distributed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted noncommercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : March 06, 2012
  • Accepted : May 29, 2012
  • Published : June 25, 2012
Export by style
Cited by
About the Authors
Wan Lin, Wang
En Mei, Jin
Hal-Bon, Gu

Olivine type LiFePO 4 cathode material was synthesized by solid-state reaction method including one-step heat treatment. To improve the electrochemical characteristics, graphite nanofiber (GNF) was added into LiFePO 4 cathode material. The structure and morphological performance of LiFePO 4 were investigated by X-ray diffraction (XRD); and a field emission-scanning electron microscope (FE-SEM). The synthesized LiFePO 4 has an olivine structure with no impurity, and the average particle size of LiFePO 4 is about 200~300 nm. With graphite nanofiber added, the discharge capacity increased from 113.43 mAh/g to 155.63 mAh/g at a current density of 0.1 mA/cm 2 . The resistance was also significantly decreased by the added graphite nanofiber.
Lithium ion batteries are widely used in mobile phones, notebook computers, electronic equipment, electric vehicles and other applications. The cathode material plays a decisive role in determining the capacity and life time of the battery. Among cathode materials of lithium ion batteries, LiFePO 4 with olivine structure has attracted extensive attention due to a high theoretical specific capacity (~170 mAh/g), environmental friendliness, excellent thermal stability, and low cost. However, its weakness in diffusion limitation and poor electrical conductivity lead to poor electrochemical performance and makes it difficult to be used as a cathode material for commercial lithium ion batteries [1] .
In recent years, many researchers have improved the electrochemical performance by coating with carbon [2 - 4] or preparing suitable procedures to minimize the particle size of the material [5 - 8] , or doping supervalent metal ions to Li sites [9] or Fe sites [10 , 11] . As an active additive, graphite nanofiber (GNF) can be added to LiFePO 4 cathode material. As a carbon source, it can possibly improve the electrochemical characteristics of LiFePO 4 through increasing the electronic conductivity [12 , 13] . Furthermore, various synthesis methods have been developed to prepare LiFePO 4 materials. Among these methods, olivine-type LiFePO 4 can be synthesized by a solid-state reaction method. The solid-state reaction is widely adopted for synthesis of pure crystalline olivine phase LiFePO 4 [14] .
In this study, LiFePO 4 cathode material was synthesized by solid-state reaction method followed by one-step heat treatment. To improve the electrochemical characteristics, graphite nanofiber (GNF) was added to the LiFePO 4 cathode material. The electrochemical characteristics of LiFePO 4 /Li cells were analyzed by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and galvanostatic charge/discharge performance at 25℃.
LiFePO 4 was prepared from starting materials of Li 2 CO 3 (Aldrich, 99.0%), FeC 2 O 4 ·2H 2 O (Aldrich, 99.0%), and NH 4 H 2 PO 4 (Aldrich, 99.999%). The starting materials were mixed in a molar ratio for Li/Fe/P=1:1:1 by ball-milling with N-methyl-2-pyrrolidone (NMP) solvent at 300 rpm for 24 h. After that, the obtained LiFePO 4 slurry was dried at 90℃ for 12 h in air. The prepared
Lager Image
XRD pattern for LiFePO4 and LiFePO4-GNF.
The unit cell parameters of LiFePO4and LiFePO4-GNF.
Lager Image
The unit cell parameters of LiFePO4 and LiFePO4-GNF.
LiFePO 4 was pelletized then calcined at 650℃ for 5 h in a nitrogen atmosphere, then ground and ball-milled with NMP at 300 rpm for 6 h. Lastly, it was dried at 90℃ for 24 h in air and ground into powder.
In order to improve the low electronic conductivity of LiFePO 4 , 3 wt.%, 5 wt.%, and 7 wt.%, amounts of graphite nanofiber (GNF) (Diameter: ~300 nm, Length: ~30 um, purity: 90%) were respectively added to different samples.
The cathode electrode was fabricated onto Al foil using a homogeneous slurry. The slurry was prepared with 70 wt.% of the synthesized LiFePO 4 (LFP) or LiFePO 4 -GNF (LFPG), 25 wt.% carbon black (SP-270), and 5 wt.% polyvinylidene di-fluoride (PVDF) binder, which was dissolved in NMP solvent. The slurry was spread onto the Al foil. After drying at 90℃ and being roll pressed, the area of the coated cathode electrode was cut to 2×2 cm 2 . The electrodes were dried in a vacuum oven under a vacuum pressure of 760 Torr at 110℃ for 24 h.
The LFP/Li cell and LFPG/Li cells were assembled in an argon filled glove box using lithium metal foil as the anode electrode. Polypropylene film (Celgard 2500) was used as the separator and a solution of 1M LiPF 6 in ethylene carbonate (EC) and dimethyl carbonate (DMC) (1:1 in volume) was used as the electrolyte.
The samples were charged and discharged over a voltage range of 2.5-4.0 V using a current density of 0.1 mA/cm 2 for both processes by WBCS-3000 8ch substation. Cyclic voltammetry (CV) measurements were performed using an IM6 instrument at a 0.1 mV/s scanning rate. AC impedance measurement was performed over the frequency range of 2 MHz to 10 mHz.
Figure 1 shows the XRD pattern of the LiFePO 4 and LiFePO 4 - GNF samples. All the patterns can be indexed to a single-phase material having an orthorhombic olivine-type structure with a space group of Pnma , which is almost the same as the one that is listed in the X-ray diffraction data file (JCPDS card). No impurities such as Fe 2 O 3 , Li 3 Fe 2 (PO 4 ) 3 or Li 3 PO 4 were found in the LiFe- PO 4 or LiFePO 4 -GNF powders, as indicated by the lack of other peaks found in the main peaks of the LiFePO 4 . There was also no
Lager Image
FE-SEM image of LiFePO4 (a) and LiFePO4-GNF (b).
Lager Image
50th Cyclic voltammogram of LFP/Li cell and LFPG/Li cells at a scan rate of 0.1 mV/s.
evidence for crystalline carbon, nor were there any amorphous peaks present. This is undoubtedly due to the small amount of carbon present and the thinness of the layer on the LiFePO 4 and LiFePO 4 -GNF.
The unit cell parameters of the prepared samples are given in Table 1 , which was calculated in the XRD analysis. The cell parameters for the LiFePO 4 sample are a =0.6036 nm, b =1.0313 nm, c =0.4708 nm, and the unit cell volume is V =0.2931 nm 3 . The unit cell parameters of LiFePO 4 -GNF(5 wt.%) are a =0.5963 nm, b =1.0329 nm, c =0.4722 nm, and V =0.2908 nm 3 . From Table 1 , it can be seen that the lattice parameter changes slightly with added GNF. Meanwhile, we can clearly see from the phenomenon in Fig. 1 that the diffraction peaks (311) of the samples gradually shift right when GNF is added, which means the unit cell volume minimizes gradually according to the Prague equation. The volume contraction of the added samples might be due to the coexistence of lithium ion vacancies caused by added GNF [1] .
FE-SEM was tested to confirm the particle size and image of LiFePO 4 and LiFePO 4 -GNF samples. Figure 2 show the FE-SEM images of LiFePO 4 and LiFePO 4 -GNF. The figure shows that the particle size of all the samples is about 200~300 nm. For LiFePO 4 , small particle size is important for enhancing the electrochemical properties [15] . In particles with a small diameter, the lithium ions may diffuse over smaller distances between the surfaces and center during lithium intercalation and de-intercalation. And as
Lager Image
Discharge capacity of the LFP/Li cell and LFPG/Li cells.
Lager Image
10th impedance spectra of LFP/Li cell and LFPG/Li cells at 25℃ (a) and Equivalent circuit of the impedance spectra (b).
shown in Fig. 2 (b), the typical morphology of tubular graphite nanofiber was observed (the image of the graphite nanofiber is shown in the inset, which is on the left). It can be seen that the LiFePO 4 particles are homogenously adhered to the surface of the graphite nanofiber. The bridging graphite nanofiber can form an effective conducting network. At the same time, a porous structure between LiFePO 4 and graphite nanofiber was formed by the random hybrid composite, which can facilitate the penetration of the electrolyte to the surface of active materials. As a result, LiFePO 4 -GNF has a superior rate capability and higher reversible capacities in comparison with the LiFePO 4 [13] .
Figure 3 shows cyclic voltammograms of the LFP/Li cell and LFPG/Li cells taken at a scan rate of 0.1 mV/s, between 2.3~4.5 V at the 50th cycle. As for CV, the voltage difference between the oxidation peak and reduction peak is an important parameter to evaluate the electrochemical reaction reversibility [16] . All of the cells’ oxidation and reduction peaks appear at about 3.6 V and 3.3 V. The voltage difference between the oxidation and reduction peak is 0.3 V. Furthermore, the CV of the LFPG/Li cells shows more symmetry and a sharper shape of oxidation and reduction peaks, which indicates better electrochemical activity [17] . Particular, the intensity of the LFPG (5 wt.%) cell peak is highest. The well-defined peaks and smaller potential peak separation
Lager Image
Bode diagram of LFP/Li cell and LFPG/Li cells at 25℃
indicate higher electrochemical reactivity and lower ohmic resistance for the LFPG(5 wt.%)/Li cell.
Figure 4 shows the discharge curves of the LFP/Li cell and LFPG/Li cells at a current density of 0.1 mA/cm 2 . The initial discharge capacity of the LFP/Li cell is 106.03 mAh/g. The highest capacity, which appears in the 3rd cycle, is 113.43 mAh/g. After 50 cycles, the discharge capacity is retained 106.32 mAh/g. To improve the capacity of LiFePO 4 , graphite nanofiber was added in amounts of 3 wt.%, 5 wt.%, 7 wt.% to LiFePO 4 . The initial discharge capacity of LFPG(5 wt.%)/Li cell is 151.73 mAh/g. The highest capacity is achieved in the 4th cycle at 155.63 mAh/g. After 50 cycles, the discharge capacity is retained at 139.45 mAh/ g. These results are the same as the FE-SEM and CV test results, which were analyzed above. In addition, compared to the LFP/Li cell, the discharge capacity of the LFPG(5 wt.%)/Li cell increased by 37.20%.
Figure 5 (a) shows the impedance performance of the LFP/ Li and LFPG/Li cells at 25℃. The frequency range was from 2 MHz to 10 mHz, and amplitude was 5 mV. The AC impedance response of the cells consisted of a broad semicircle in the highmiddle frequency region and a sloping line in the low frequency region. The impedance spectra can be interpreted on the basis of an equivalent circuit with ohmic resistance (Rs), charge-transfer resistance (Rct), capacitance of the double layer (Cd), and Warburg impedance (Zw), as indicated in Fig. 5 (b). It has been recognized that the high-middle frequency semicircles might correspond to the charge-transfer impedance that resulted from the electrochemical reaction at the electrode and electrolyte interface. The sloping line in the low frequency region is attributed to the Warburg impedance, which is associated with lithium ion diffusion in the LiFePO 4 electrode. In the 10th cycle, the resistance of the LFP/Li cell is 280 Ω, and the resistance of the LFPG(5 wt.%)/Li cell is 100 Ω, which are shown in figure 3 . 6 . It is obvious that the resistance decreased after adding the graphite nanofibers.
In this research, LiFePO 4 cathode material with olivine structure was synthesized by solid-state method followed by one-step heat treatment. To improve the electrochemical characteristics of LiFePO 4 , graphite nanofiber was added, and the morphology properties were analyzed. During the lithium-ion intercalation and de-intercalation processes, the lithium-ion diffusion coefficient was boosted after adding GNF. Impedance results show that the conductivity was enhanced by the added GNF, because the charge-transfer resistance was significantly reduced. Cyclic voltammetry results indicated that the electrode redox reaction reversibility was excellent due to adding GNF. The LFPG(5 wt.%)/ Li cell exhibited superior high discharge capacity and cycling stability at 25℃. The results demonstrate that a feasible route of adding GNF by solid-state reaction has been offered.
The following are results of a study on the “Human Resource Development Center for Economic Region Leading Industry” Project, supported by the Ministry of Education, Science & Technology (MEST) and the National Research Foundation of Korea (NRF).
Hu Guo-rong , GAO Xu-guang , PENG Zhong-dong , DU Ke , TAN Xian-yan , LIU Yan-jun (2007) Trans Nonferrous Met Soc. China. 17 296 - 300    DOI : 10.1016/S1003-6326(07)60088-0
HU G R , GAO X G , PENG Z D , CHEN Z Y , TAN X Y , YU X Y (2005) Trans Nonferrous Met Soc. China. 15 (4) 795 - 798
MYUNG S T , KOMABA S , HIROSAKI N , YASHIRO H , KUMAGAI N. 2004 Electrochimica Acta 49 (24) 4213 - 4222    DOI : 10.1016/j.electacta.2004.04.016
BAKER J , SAIDI M Y , SWOYER J . 2003 Electrochem Solid-State Lett 6 (3) A53 - A55    DOI : 10.1201/9780203913321.ch15
YANG S F , ZAVALIJ P Y , WHITTINGGHAM M S. 2001 Electrochem Commun 3 (9) 505 - 508    DOI : 10.1016/S1388-2481(01)00200-4
PARK K S , KANG K T , LEE S B , KIM G Y , PARK Y J , KIM H G. 2004 Ma-terials Research Bulletin 39 (12) 1803 - 1810    DOI : 10.1016/j.materresbull.2004.07.003
YAMADA A , CHUNG S C , HINOKUMA K. 2001 J Electrochem Soc 148 (3) A224 - A229    DOI : 10.1149/1.1348257
CHO T H , CHUNG H. 2004 J Power Sources 133 (2) 272 - 276    DOI : 10.1016/j.jpowsour.2004.02.015
CHUNG S Y , BLOCKING J T , CHIANG Y M. 2002 Nature Mater 2 123 - 128    DOI : 10.1038/nmat732
MI C H , ZHANG X G , ZHAO X B , LI H L. 2006 Materials Science & Engineering 129 8 - 13    DOI : 10.1016/j.mseb.2005.11.015
SLI G H , KUDO Y , LIU K Y , AZUMA H , TOHDA M. 2002 J Electrochem Soc 149 (11) A1414 - A1418    DOI : 10.1149/1.1510768
Xinlu Li , Feiyu Kang , Xinde Bai , Wanci Shen (2007) Electrochemistry Communications 9 663 - 666    DOI : 10.1016/j.elecom.2006.10.050
Li Wang , Haibo Wang , Zhihong Liu , Chen Xiao , Shanmu Dong , Pengxian Han , Zhongyi Zhang , Xiaoying Zhang , Caifeng Bi , Guanglei Cui. (2010) Solid State Ionics 181 1685 - 1689    DOI : 10.1016/j.elecom.2006.10.050
Kang Hee-Cheol , Jun Dae-Kyoo , Jin Bo , Jin En Mei , Park Kyung-Hee , Gu Hal-Bon , Kim Ki-Won (2008) Journal of Power Sources 179 340 - 346    DOI : 10.1016/j.jpowsour.2007.12.093
Padhi A. K. , Nanjundaswamy K. S. , Goodenough J. B. (1997) J. Electrochem. Soc. 144 1188 -    DOI : 10.1149/1.1837571
Ni J. F. , Zhou H. H. , Chen J. T. , Zhang X. X. (2005) Mater. Lett. 59 2361 -    DOI : 10.1002/chin.200544013
Shenouda Atef Y. , Liu. Hua K. (2009) Journal of Alloys and Compounds 477 498 - 503    DOI : 10.1016/j.jallcom.2008.10.077