Characterization of TiO<sub>2</sub> Nanocrystalline Films for High Performance Dye-Sensitized Solar Cells
Characterization of TiO2 Nanocrystalline Films for High Performance Dye-Sensitized Solar Cells
Transactions on Electrical and Electronic Materials. 2011. Jun, 12(3): 123-126
Copyright ©2011, The Korean Institute of Electrical and Electronic Material Engineers
This is an open-access article distributed under the terms of the Creative Commons Attribution Non-Commercial License( permits unrestricted noncommercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : May 03, 2011
  • Accepted : May 12, 2011
  • Published : June 25, 2011
Export by style
Cited by
About the Authors
Heung-Joe, Jung

Titanium dioxide (TiO 2 ) thin films were deposited by the sol-gel method with a surfactant-assisted mechanism. Its application for dye-sensitized solar cells (DSSCs) was investigated. Brunauer-Emmett-Teller, X-ray diffraction and field emission scanning electron microscopy techniques were used to characterize the surface characteristics of thin films. Photovoltaic-current density measurements were performed to determine the photoelectrochemical properties of the thin films and the performance of DSSCs. Energy conversion efficiency of about 6.1% was achieved for cells with conductive glass under illumination with AM 1.5 (100 mWcm -2 ) simulated sunlight. Investigation showed higher photo-energy conversion efficiency for mesoporous TiO 2 nanocrystalline films used in DSSCs relative to commercially available Degussa P25 films
The dye-sensitized titanium dioxide (TiO 2 ) photoelectrochemical solar cell has attracted much attention due to its low cost, simple fabrication process and reasonably good conversion efficiency [1 - 3] . In general, the porous semiconductor film consists of a large collection of nano-sized particles of a metal oxide interconnected by meso-sized pores, deposited onto the conductive surface of a transparent electrode. This porous metal oxide film acts as a high surface area support for the sensitizer, a pathway for electrical current and a porous membrane for diffusion of the redox couple [4 - 6] . The high surface area of the nanocrystalline TiO 2 film plays a crucial role in increasing the performance of the photoelectrochemical cell in energy conversion.The available surface area for dye absorption can be enormous in highly porous films of a few micrometers thickness, leading to near extinction of incident light.
A suitable degree of porosity is also another important factor.The pore structure must permit the penetration of the electrolyte containing the redox couples, and permit an effective mass transport of electroactive species by diffusion to guarantee the regeneration of the oxidized dye [7] . Furthermore, the porous film must exhibit interconnected particles, to allow the percolation of injected electrons. The crystallinity of the particles (and the extent of defects) also influences the injection of electrons and their transport through the network of particles in the film[8]. Li et al. [3] reported sol-gel-derived TiO 2 thin films for solar cell application, where they showed that nanocrystalline layers of high surface area and a prerequisite for good solar cell performance could be achieved by the sol-gel process. The sol-gel process may also allow more precise control of film thickness,particle size, and porosity by adjusting different parameters,such as sol concentration, and annealing temperature. We have attempted the sol-gel method for the preparation of TiO 2 films using titanium tetra-isopropoxide for dye-sensitized solar cell(DSSC) application. Appropriate control over particle size, morphology and the active surface area plays an important role in the application of TiO 2 thin films.
The aim of the present work is to obtain nano-sized TiO 2 with improved properties that can be used for the development of the photoanode in DSSCs. Special attention is paid to changes in
Lager Image
Field emission scanning electron microscopy images of (a) Degussa P25 powder and (b) synthesized TiO2.
the microstructure and surface area of TiO 2 as a function of the preparation procedure.
TiO 2 powder was synthesized by the sol-gel method. 25 mL of titanium tetraisopropoxide (TTIP) was dropped into 250 mL of 0.1 M HCl aqueous solution while stirring at room temperature.Next, the resulting slurry was sonicated and stirred repeatedly for 24 hours. TTIP was dissolved in Millipore water while stirring continuously at ambient temperature and maintained for 2 hours. Centrifugation was performed with a relatively high 4,000 rpm to remove the ethanol. The resulting particles were washed with deionized water three times and dried by freeze-drying. Finally,the powders were sintered at 450°C for 30 minutes in air for crystallization. TiO 2 colloidal paste that consisted of synthesized TiO 2 powder, polyethylene glycol and triton X-100 was cast onto the pre-cleaned fluorine-doped tin dioxide (FTO, Asahi Glass, 13Ω/cm 2 ) using the squeeze printing method. The coated TiO 2 film was heat-treated at 450°C for 30 minutes with a heating rate of 5°C /min. The printed TiO 2 film thickness was 10 ㎛, and the active area of the photoelectrode was 0.8 × 0.8 cm 2 . Platinized FTO,which is similar to that of the photoelectrode onto the FTO substrate,was fabricated using the squeeze technique of the Pt-Sol(Pt catalyst/SP, Solaronix). The obtained photoelectrode TiO 2 layer was immersed into the ethanol solution of bis(isothiocyanato)bis(2,2’-bipyridyl-4,4’- dicarboxylato)-ruthenium(II)-bis-tetrabutyl ammonium (N719 dye, Ruthenium 535-bis TBA, Solaronix,0.5m mole) for 24 hours. The electrolyte solution consisted of 0.3 M 1,2-dimethyl-3-propylimidazolium iodide, 0.5 M LiI, 0.05 M I2 and 0.5 M 4-t-butylpyridine in 3-methoxypropionitile.
The crystallinity and crystal phase of the TiO 2 film were evaluated by a powder X-ray diffractometry (XRD, Rigaku, RINT2000/PC) using CuKα radiation. The primary crystallite size of TiO 2 was calculated from the full width at half the maximum of the XRD peak at 2θ = 25.4° using Scherrer's equation. Extended X-ray absorption fine structure (EXAFS) was used R-XAS (Rigaku, Japan)with Ti k-edge energy (4966.4 eV). The Brunauer-Emmett-Teller(BET) surface area was determined by a nitrogen adsorptiondesorption apparatus (Quantachrome, Autosorb-1). Pore size distribution, pore volume and porosity were also determined by the Barrett-Joyner-Halenda(BJH) method of nitrogen desorption measurements. The film thickness was measured by a profilometer(Veeco, dektack3). The microstructure of films was studied by field emission scanning electron microscopy (FE-SEM, S-4700;Hitachi, Japan).
The sandwich-type solar cell was assembled by placing a platinum-coated conducting glass (counter electrode) on the N719 dye-sensitized photoelectrode (working electrode), and clipped together as open cells for measurements. Sealed cells were also tested in this study. The two electrodes were separated by a surlyn spacer (25 ㎛ thick) and sealed by heating the polymer frame [9]. The redox electrolyte was introduced into the space of
Lager Image
X-ray diffraction patterns of the synthesized TiO2 (a) without heat-treatment and (b) sintered at 450°C for 30 minutes in air.
inter-electrodes through the two holes pre-drilled on the back of the counter electrode. The two holes were sealed using a surlyn film, on which a glass slide was pressed under heat. The redox electrolyte used was 0.1 M LiI, 0.05 M I 2 , 0.3 M dimethyl propyl imidazolium iodide, and 0.5 M tert-butylpyridine in dried acetonitrile.The current-voltage characteristics of the cells were measured with electrochemical workstation (CHI 660A, USA).An AM1.5 solar simulator (Thermo-Oreal with a 1000-W Xe lamp and an AM 1.5 filter) was employed as a light source. The incident light intensity was calibrated with a standard Si solar cell produced by Japan Quality Assurance Organization (JQA). Four parallel samples for each kind of layer structure were made for J-V measurement, and the reproducibility of TiO 2 photoelectrode was quite good.
Figure 1 displays SEM images of a commercial TiO 2 film deposited on FTO glass and synthesized TiO 2 film. The TiO 2 spherical nanoparticles are well distributed and the film has a porous structure, in which the nanoparticles are all bonded together through a sintering process. Such a porous structure permits the adsorption of a greater number of dye molecules and the formation of networking among the TiO 2 intramoleculars. The synthesized TiO 2 film is smoother than the P25 film and appears to have smaller crystallites.
Figure 2 shows the XRD patterns of the synthesized TiO 2 . Figure 2 (a) is the XRD pattern of the TiO 2 synthesized without heat-treatment. Figure 2 (b) is the XRD data of the sintered TiO 2 particle at 450°C for 30 minutes in air. Figure 2 shows heat-treatment is necessary to improve the crystallinity and the synthesized particles have an anatase structure. The average particle size (Lc = kl/bcos q) for all samples was calculated by Scherrer's equation [10] , where k is related to the shape of the polycrystals,l is the x-ray wavelength, b is the full-width at half maximum(FWHM) of the respective diffraction peak and q is the Bragg angle. The obtained diffraction patterns were fitted by a Gaussian function to obtain the value of the FWHM of a peak from the XRD pattern.
The particle size of TiO 2 synthesized is about 14 nm. These particle sizes are calculated from the FWHM of the (200) peak.Thus, the particle size was decreased. Figure 1 (b) shows the particle size of synthesized TiO 2 is smaller than that of commercial Degussa P25 powder. Figure 2 revokes the XRD pattern,indicating clear peaks of the anatase phase without those of the
EXAFS fit results for P25 and synthesized TiO2powder.EXAFS: extended X-ray absorption fine structure, TiO2: titanium dioxide.
Lager Image
EXAFS fit results for P25 and synthesized TiO2 powder. EXAFS: extended X-ray absorption fine structure, TiO2: titanium dioxide.
Lager Image
Fourier transforms of the Ti k-edge extended X-ray absorption fine structure spectra of (a) P25 powder and (b) TiO2 powders synthesized at 450°C for 30 minutes.
rutile phase, as for the TiO 2 nanoparticles before and after heattreatment at 450°C for 30 minutes. The XRD peaks are intense and well-resolved suggesting that the TiO 2 particles synthesized at 450°C for 30 minutes have high crystallinity.
The EXAFS spectra of TiO 2 powder were obtained to investigate the local environment of the titanium ion, such as the coordination state and geometry that strongly depends on the presence of different molecules around the metal ion. Figure 3 shows the EXAFS spectra of P25 TiO 2 powder and synthesized TiO 2 particles. The experimental data for synthesized TiO 2 particles are represented by the solid line and the fitting data for bulk anatase by the dotted line. Table 1 gives the best-fit parameters for the EXAFS data. Figure 3 (b) shows the EXAFS spectra of the anatase TiO 2 nanoparticles. The Fourier transform similarity
Lager Image
N2 adsorption-desorption isotherms determined at liquid nitrogentemperature on the 450°C calcinations produced. The inset isthe pore-size distribution of synthesized TiO2 film.
of parameters from the change of the phase, so the peak positions are similar to values below those in the original spectrum.The coordination number CN and the nearest Ti-O interatomic distance R were evaluated via the best fit of k3x (k), calculated by inverse Fourier transform of the moduli, to the theoretical one,using a non-linear least squares method.
Table 1 shows the structure parameters of first-shell Ti-O in synthesized TiO 2 nanoparticles are quite different from the standard bulk crystallographic data: Ti-O distance close to 1.96 Åcorresponding to coordination number 2. There are two different nearest-neighbor Ti-O distances in anatase: four Ti-O bonds at 1.93 Å and two at 1.96 Å [11] . The derivation from the standard anatase structure suggests that the larger Ti-O distances result from the surface -Ti-OH. This contrasts the conclusion of Chen et al. [12] and Wu et al. [13] .
Synthesized TiO 2 particles compared to P25 are clearly shown in the difference of the BET surface areas. The synthesized TiO 2 film and the P25 film show remarkable difference in their pore size distribution. Both films have very small pores at 10 nm.However, the synthesized TiO 2 film possesses a large number of mesopores, of around 10 nm. In contrast, the P25 film reveals a very broad pore size distribution, even larger than 20 nm. The synthesized TiO 2 film is characterized by the predominant presence of the mesopores. The smaller particles size and the homogeneous particle size distribution of synthesized TiO 2 film should result in the characteristic pore size distribution of synthesized TiO 2 film.
Lager Image
Photocurrent-voltage characteristics of dye-sensitized solarcells with TiO2 films prepared by (a) Degussa P25 powder and (b) synthesized TiO2 particles.
Figure 5 shows the photovoltaic performances of DSSCs prepared using P25 powder and synthesized. TiO 2 powder has been evaluated using J-V measurements. Figure 5 shows the J-V curves of DSSC prepared by Degussa P25 powder and synthesized TiO 2 particles. The fill factor (ff ) and energy conversion efficiency (η)were calculated using the following equations.
Lager Image
Where, V max is the maximum potential and J max is the current at the maximum power point of the current-voltage (J-V) in the fourth quadrant.
The energy conversion efficiency of a photovoltaic device is given by
Lager Image
Where V OC (mV), J SC (mA/cm 2 ), fill factor (FF), and Pin (mW/cm 2 ) are open circuit voltage, short circuit current, FF, and incident light power, respectively.
A short circuit current density (J sc ) of 12.3 mA/cm 2 , an open circuit voltage (V oc ) 0.64 V, a FF 57% and an overall power conversion efficiency (η) of 4.5% is obtained for the conventional P25 TiO 2 powder. In contrast, the DSSC of the TiO 2 electrode prepared by synthesized TiO 2 powder achieved 6.1% conversion efficiency;J sc = 17.4 mA/cm 2 , V oc = 0.67 V, and FF = 52%. This corresponds to a 135% efficiency increase.
The particle size of TiO 2 synthesized is about 14 nm smaller than that commercially available. The XRD pattern and EXAFS data indicate clear peaks of anantase phase without those of the rutile phase for the TiO 2 nanoparticles. Nanoparticles are essential to increase surface area, and hence, the amount of dye, while large particles are required to enhance absorption of red light through light scattering. It is impossible to increase surface area and light scattering simultaneously, because they oppose each other. Therefore, a balance between them must be maintained.Such a balance is controlled by tuning the layer structure. An energy conversion efficiency of 6.1% is obtained using synthesized TiO 2 powder.
O'Regan B , Gratzel M 1991 Nature 353 737 -    DOI : 10.1038/353737a0
Gratzel M 2005 Chem. Lett 34 8 -    DOI : 10.1246/cl.2005.8
Li Y , Hagen J , Schaffrath W , Otschik P , Haarer D 1999 Sol.Energy Mater. Sol. Cells 56 167 -    DOI : 10.1016/s0927-0248(98)00157-3
Dinh N. N , Oanh N. T. T , Long P. D , Bernard M. C , Hugot-Le Goff A 2003 Thin Solid Films 423 70 -    DOI : 10.1016/s0040-6090(02)00948-3
Park K. H , Hong C. K 2008 Electrochem. Commun 10 1187 -    DOI : 10.1016/j.elecom.2008.05.046
Lee W. J , Lee D. Y , Kim I. S , Jeong S. J , Song J. S 2005 Trans.Electr. Electron. Mater 6 140 -
Scully S. R , Lloyd M. T , Herrera R , Giannelis E. P , Malliaras G.G 2004 Malliaras Synth. Met 144 291 -    DOI : 10.1016/j.synthmet.2004.04.011
Ni M , Leung M. K. H , Leung D. Y. C , Sumathy K 2006 Sol.Energy Mater. Sol. Cells 90 1331 -    DOI : 10.1016/j.solmat.2005.08.006
Koo B. K , Lee D. Y , Kim H. J , Lee W. J , Song J. S , Kim H. J 2006 J.Electroceram 17 79 -    DOI : 10.1007/s10832-006-9941-x
Yang J , Li D , Wang X , Yang X , Lu L 2002 J. Solid State Chem 165 193 -    DOI : 10.1006/jssc.2001.9526
Parrish W , Langford J. I , Prince E 2004 International Tables for Crystallography.Volume C: Mathematical Physical and Chemical Tables 3rd ed Springer 42 -
Chen L. X , Rajh T , Wang Z , Thurnauer M. C 1997 J. Phys.Chem. B 101 10688 -    DOI : 10.1021/jp971930g
Wu Z. Y , Zhang J , Ibrahim K , Xian D. C , Li G , Tao Y , Hu T. D , Bellucci S , Marcelli A , Zhang Q. H , Gao L , Chen Z. Z 2002 Appl.Phys. Lett 80 2973 -    DOI : 10.1063/1.1470699