Electrical Properties of a CuPc Field-Effect Transistor Using a UV/Ozone Treated and Untreated Substrate
Electrical Properties of a CuPc Field-Effect Transistor Using a UV/Ozone Treated and Untreated Substrate
Transactions on Electrical and Electronic Materials. 2011. Feb, 12(1): 40-42
Copyright ©2011, The Korean Institute of Electrical and Electronic Material Engineers
  • Received : January 01, 2011
  • Accepted : January 01, 2011
  • Published : February 28, 2011
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Ho-Shik Lee
Min-Woo Cheon
Yong-Pil Park
yppark@dsu.ac.kr
Abstract
An organic field-effect transistor (OFET) was fabricated using a copper phthalocyanine (CuPc) as the active layer on the silicon substrate. The CuPc FET device was configured as a top-contact type. The substrate temperature was room temperature. The CuPc thickness was 40 nm, and the channel length and channel width were 100 ㎛ 3 mm, respectively. Typical current-voltage (I-V) characteristics of the CuPc FET were observed and subsequently compared to the UV/ozone treatment on substrate surface.
Keywords
1. INTRODUCTION
Organic semiconductors have recently been used as active layers in electronic devices such as field-effect transistors (FETs). In efforts to improve device performance, researchers have allotted great attention to the carrier transport mechanisms of organic semiconductors [1 , 2] . Copper phthalocyanine (CuPc) materials have exhibited excellent semiconductor performance and have been studied for applications as organic FETs (OFETs).
Material choice changes the work function of an electrode. Furthermore, the surface treatment can control a metal surface’s effective work function. Two surface treatments are the UVozone treatment or the plasma treatment of the substrate and electrode surface [3 , 4] .
For both treatments, the devices studied exhibited operation voltage decreases. This clearly shows that the efficiency of the charge injection from metal to organic layer is strongly dependent on the electronic state at the interface.
The effect of the UV/ozone treatment of the source and drain electrode on the CuPc FET characteristics are studied. Understanding the injection behavior of charges at the metal/organic interface is necessary for improving the FET operation. The transistor characteristics of a top contact CuPc FET are discussed based on the carrier accumulation around the electrode, taking into account the current-voltage (I-V) characteristics.
2. EXPERIMENTS
We were the UV/ozone treatment on the SiO 2 layer for the duration of 30 minute. Also, the UV/ozone-treatment carried out with the Au source and drain electrodes before deposited the CuPc material. The UV/ozone-treatment was applied in a UV/ozone-treatment chamber (NL-UV 253S; Nippon Laser & Electronics Laboratory, Tokyo, Japan) filled with oxygen gas. During the UV/ozone-treatment, UV light from a low-pressure mercury lamp was irradiated onto the surface of the SiO 2 layer. The CuPc material was purchased from Tokyo Kasei Kogyo Co. Ltd. (Tokyo, Japan) and was used without purification. The CuPc material was deposited through the thermal evaporation method. The CuPc material deposition rate was 0.5 Å/s and. The vacuum level less was maintained at less than 10 -6 torr. The substrate was kept at a room temperature.
The samples on the pre-patterned top contact FET substrate and the thickness of the CuPc layer was approximately 40 nm. The deposition rate was monitored by a quartz crystal microbalance (QCM).
Figure 1 shows a molecular structure and the device structure of the top-contact CuPc FET. The CuPc FET was fabricated using the silicon substrate. The channel length (L) was 100 ㎛ and channel width was 3 mm and also, the active material thickness was about 40 nm. The I-V characteristics were studied under ambient conditions using a source-meter (Keithley type-2400; Keithley Instruments Inc., Cleveland, OH USA).
Lager Image
Device and molecular structure of the CuPc field-effect transistor (a) molecular structure (b) device structure.
Lager Image
Atomic force microscopy image of the CuPc thin film on SiO2 substrate.
3. RESULTS AND DISCUSSION
Figure 2 shows the atomic force microscopy (AFM) images of the CuPc thin film surface with the SiO 2 substrate. The CuPc materials were layered parallel with the substrate, clearly displaying the CuPc grain.
Figure 3 shows the typical I-V characteristics of a CuPc FET using an untreated substrate with the CuPC FET. Gate voltages between 0 and -80 V were applied with a constant scanning rate. Typical FET characteristics were observed though the V D and V g voltages were very high. V D and V g represent the applied voltages between drain and source electrodes, and gate and source electrodes, respectively. As shown in Fig. 3 , the CuPc FET using an untreated substrate shows enhanced n-channel FET behavior. Interestingly on the other hand, we observed more than faster saturated region of the CuPc FET with a UV/ozone treated sub-
Lager Image
ID-VD characteristics of the CuPc field-effect transistor using untreated substrate.
Lager Image
I-V characteristics of the CuPc field-effect transistor with a UV/ozone treated substrate.
Lager Image
I-V characteristics of the CuPc field-effect transistor using untreated substrate.
strate in Fig. 4 .
Figure 5 shows the transfer characteristics of the CuPC FET using an untreated substrate. Figure 6 shows the CuPc FET with a UV/ozone treated substrate.
According to the transfer characteristics root( I D -V G ) of these FETs shown in Figs. 5 and 6 , the threshold voltage, V th , decreased with a UV/ozone treatment substrate. The threshold voltage was estimated for the UV/ozone-treated and untreated
Lager Image
I-V characteristics of the CuPc field-effect transistor with a UV/ozone treated substrate.
substrate sample about 30 V and 5 V. We also calculated the field-effect mobility of 1.2 × 10 -5 cm 2 /Vs using the untreated substrate of the CuPc FET device and 1.2 × 10 -4 cm 2 /Vs with the UV/ozone treated substrate.
4. SUMMARY
Top-contact CuPc FET devices were fabricated. Subsequently,the I-V characteristics of the devices were measured. The I-V characteristics show the similar FET characteristics as the n-type characteristics.
A significant change in the threshold voltage was observed with the UV/ozone treated substrate. The change manifested as a decrease from 30 V to 5 V. We also calculated the field-effect mobility of 1.2 × 10 -5 cm 2 /Vs an using untreated substrate in the CuPc FET device and 1.2 × 10 -4 cm 2 /Vs with UV/ozone treated substrate.
References
Brown R. J. C , Kucernak A. R , Taylor A. G 2005 Thin Solid Films 476 373 -
Kagan C. R , Andry P 2003 Thin-Film Transistors Marcel Dekker New York
Manaka T , Lim E , Tamura R , Yamada D , Iwamoto M 2006 Appl. Phys. Lett. 89 072113 -
Manaka T , Li C. Q , Cheng X. M , Iwamoto M 2004 J. Chem. Phys. 120 7725 -