Improvement in the Stabilities of White Organic Light Emitting Diodes Using a Partially Doped Emission Layer
Improvement in the Stabilities of White Organic Light Emitting Diodes Using a Partially Doped Emission Layer
Transactions on Electrical and Electronic Materials. 2010. Jun, 11(3): 145-148
Copyright ©2010, The Korean Institute of Electrical and Electronic Material Engineers
  • Received : March 03, 2009
  • Published : June 25, 2010
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Hyeon-Sung Jeon
Hwansool Oh
Seok-Beom Yoon
Abstract
White organic light emitting devices were fabricated to improve the stability through a structural change using the two peak emission method. The fabricated devices were composed of indium tin oxide (100 nm)/ α-NPD (30 nm)/4,40- bis(2,20-diphenylvinyl)-1,10-biphenyl (DPVBi, d : variable)/DPVBi: Rubrene (40 nm)/2,9-dimethyl-4,7-diphenyl- 1,10-phenanthroline(5 nm)/ Alq 3 (5 nm)/ Al (100 nm). A DPVBi for blue emissions was used as the host material in the emitters. The doping concentration of the Rubrene was fixed at 2.0% (by weight). The white emission with Commission Internationale De L'Eclairage coordinates of (0.3342, 0.3439) occurred at 14 V with a thickness d of 1 nm. It was insensitive to the drive voltage, and the devices had a maximum luminance of 211 cd/cm 2 . At 19 V, the current density and maximum external quantum efficiency were 173 mA/cm 2 and 0.478%, respectively.
Keywords
1. INTRODUCTION
One of the flat panel displays, the organic light emitting device (OLED), is a spontaneous photon emission device. It offers a higher quality display than those of existing displays. Thanks to its simple manufacturing process, it is very competitive in price. Also, various advantages such as its wide viewing angle, good response speed, and thinness have highlighted the OLED as a next generation display that is superior to the liquid crystal display (LCD) and plasma display panel (PDP) [1 , 2] .
The OLED is a new type of light source known as a surface light source. The applications of OLEDs will be enlarged in the lighting market and the new e-paper market, as well as in the display market [3] . Tang and VanSlyke [4] studied a multi-layer OLED composed of an emission layer and a hole transport layer, which had been studied previously [5] . However, OLEDs have not yet achieved the long lifespans, high efficiency, high brightness, and high purity necessary for full-color realization [6] .
There are various methods for realizing full-color OLEDs. The three-color separate emission method (driving separate pixels by separate emissions using three colors of red, green, and blue) and the white emission method (using white emission and color filters) have been researched [7 , 8] . The white emission method can use the current LCD process lines and can be applied diversely in light sources, except in displays [9 , 10] . The three peak white emission method mixes the three primary colors, and the two peaks white emission method mixes the blue (or bluishgreen) and red (or orange) colors [11] . The excellent performances of the two peak white emission method with regard to stability, efficiency, and process have been highlighted recently [12 , 13] because it also has low color interference and easily controlled colors. Moreover, the manufacturing costs may be reduced as the control factors decrease [13] .
Consequently, we improve the stabilities of white OLEDs through a structural change using the two peak emission method.
Device structure thicknesses.
Lager Image
Device structure thicknesses.
Lager Image
The energy-band diagram of the fabricated devices.
Lager Image
The normalized electro-luminescence (EL) spectra of devices at various distances (d).
2. EXPERIMENTS
White OLEDs were fabricated on transparent indium tin oxide (ITO), which had a surface resistance of 10 Ω/□ and was coated onto a glass substrate. The patterned ITO substrate was cut into 1 inch 1 inch sections to be used as test pieces, which were essentially composed of ITO (100 nm)/ α-NPD (30 nm)/ 4,40-bis(2,20-diphenylvinyl)-1,10-biphenyl (DPVBi, d : variable)/ DPVBi: Rubrene (40 nm)/ 2,9-dimethyl-4,7-diphenyl-1,10- phenanthroline (BCP, 5 nm)/ Alq 3 (5 nm)/ Al (100 nm). α-NPD with low ionization energy was used for the hole transport layer (HTL), and DPVBi was used as a host material in which the blue emitting layer (EML) had variable thicknesses d of 0 nm, 1 nm, 2 nm, and 3 nm (Table 1) .
An orange light-emitting Rubrene was used as a dopant material, and the doping concentration was fixed at 2.0% (by weight). Alq 3 was used to inject electrons easily into the EML. To bind the holes to the EML and restrict the electron-hole recombination zone to the EML, BCP was injected between the EML and the HTL to function as a hole blocking layer. Aluminum was used for the cathode electrode since it has a low work function and a strong anti-oxidation property in air. Each layer was vacuum evaporated at 5-10 nm/sec in the vacuum condition of 10 -7 torr. The luminous properties of the fabricated devices were characterized, and their electrical properties were obtained. Figure 1 shows the energy-band diagram of the fabricated devices.
Lager Image
(a) The normalized electro-luminescence (EL) spectra of deviceI, (b) The Commission Internationale De L Eclairage coordinatesof device I.
3. RESULTS AND DISCUSSION
We focused on fabricating new white OLEDs using partially doped EMLs, which operate stably and can thus be used for lighting in the future. We obtained white color in two peak emission using the blue and orange EMLs.
Figure 2 shows the electro-luminescence (EL) spectra for the different DPVBi thicknesses from the interface.
The applied voltage for each device was 14 V. The maximum values of the blue and orange EL spectra were normalized. In the case of device I ( d = 0 nm), the yellow EL intensity was stronger than that of the blue. Device II ( d = 1 nm) also indicated a strong yellow EL intensity.
Lager Image
(a) The normalized electro-luminescence (EL) spectra of deviceII, (b) The Commission Internationale De L Eclairage coordinatesof device II
As the thickness was increased from d = 2 nm (device III) to d = 3 nm (device IV), the blue EL intensity increased to be greater than those for devices I and II, but the yellow intensity diminished rapidly. In the case of d = 3 nm, there was no yellow emission. Therefore in the cases of device III and device IV, we observed only a blue emission. As a result, it was determined that the Commission Internationale De L'Eclairage (CIE) coordinates move from the white light area to the blue light area, because the EL intensity of the orange emission area of the Rubrene was rapidly reduced. This is why the emission site of the white OLED is said to be activated at a thickness of 3 nm from the interface. Therefore, from now on, we discuss only device I and device II.
Figures 3(a) and (b) show the EL spectra and CIE coordinates of device I with a change in the applied voltage ( d = 0 nm).
As shown in Fig. 3(a) , in the case of increased voltage from 10 V to 16 V, yellow EL intensity was unchanged, but blue EL intensity increased. In Fig. 3(b) , the transition of the CIE coordinates was shifted as well as the increased voltage. When the doping concentration was fixed at 2.0% (by weight) and a voltage of 12 V, a white emission with CIE coordinates of (0.3219, 0.3383) was close to that of pure white light (0.3333, 0.3333). Though it was revealed to have closer CIE coordinates to those of pure white light at 12 V-14 V, it shifted from a white light area to a blue light area at voltages greater than 16 V. At 19 V, the current density and the maximum external quantum efficiency were 128 mA/cm 2 and 0.43%, respectively, and it had a maximum luminance of 184 cd/m 2 .
Figures 4(a) and (b) show the EL spectra and CIE coordinates of device II with a change in the applied voltage ( d = 1 nm).
Lager Image
The Commission Internationale De L Eclairage coordinates ofdevice I (d = 0 nm) and device II (d = 100 nm).
Lager Image
The current density-voltage-light intensity characteristics ofdevice I.
As shown in Fig. 4(a) , in the case of a voltage increase from 10 V to 16 V, the yellow EL intensity was unchanged and the blue EL intensity was increased in the same manner as for device I in Fig. 3(a) . However, the change in the blue EL intensity was not much greater than that in the case of Fig. 3(a) .
As in Fig. 4(b) , a white emission with CIE coordinates of (0.3342, 0.3439) was the closest to pure white light with CIE coordinates at 14 V. Judging from the CIE coordinates, it seemed that pure white light would be produced in the voltage range of 10 V-16 V.
Lager Image
The current density-voltage-light intensity characteristics of device II.
Figure 5 compares the white emissions of device I ( d = 0 nm) and device II ( d = 1 nm) according to the CIE coordinates.
In the case of device II, the white emission area seemed totally insensitive to the drive voltages at 10 V-16 V compared to those of device I.
When the orange emitting Rubrene material was doped onto the emitting layer, the emission zone due to the energy transition was limited to within ~5 nm from the interface. The function of the Rubrene is to shallowly capture holes at a constant position away from the interface, and this position becomes a hopping site for the easy transmission of electrons. The Rubrene also improves the mobility of the electrons and captures electrons while maintaining a proper distance from the interface. As a result, early saturation of the recombination site is prevented so that the site can be stably recombined. Therefore, it was identified that the EL spectra and CIE coordinates were insensitive to the drive voltage.
Figure 6 shows the current-voltage-light intensity characteristics of device 1.
In Fig. 6 , the operating and emission states were 2 V and 4 V, respectively. As the voltage increased, the light intensity increased rapidly, starting at 5 V. This is because energy was transmitted from the Rubrene at less than 12 V, and orange emission appeared predominately.
This is the same reason that, in the CIE coordinates, the orange emission predominately appeared at low voltages and the blue emission predominately appeared at high voltages, with a maximum luminance of 184 cd/m 2 . At 19 V, the current density and the maximum external quantum efficiency were 128 mA/cm 2 and 0.43% respectively. The external quantum efficiency slowed incrementally from 15 V and decreased from 19 V, explaining why, as the voltage increased, the number of excitons disappearing without emission due to the saturation of the photons increased. Thus, the light intensity increases more slowly than does the current density.
Figure 7 shows the current-voltage-light intensity characteristics of device II, in which the operating and emission state voltages were 4.5 V and 5.5 V, respectively. The light intensity was slightly higher than in the case of device I. On this account, the initial orange emission by the Rubrene on the interface is weak. This shows that the light intensity was steadily increased without rapid increase or decrease to the drive voltage. This also was identified in the CIE coordinates and EL spectra, in which there was insensitivity to the drive voltage. Device II had a maximum luminance of 211 cd/m 2 , and, at 19 V, the current density and the maximum external quantum efficiency were 173 mA/cm 2 and 0.478% respectively. The maximum luminance and the external quantum efficiency were greater than in the case of device I.
4. CONCLUSIONS
White OLEDs utilizing the two peak white emission method using blue EML and orange EML were fabricated. The fabricated devices are composed of ITO (100 nm)/ α-NPD (30 nm)/ DPVBi ( d : variable)/ DPVBi: Rubrene (40 nm)/ BCP (5 nm)/ Alq 3 (5 nm)/ Al (100 nm). By varying the thickness of the DPVBi, we verified that white OLED was relatively stable at d = 10 nm from the drive voltages. The white emission was close to that of pure white light with CIE coordinates of (0.3342, 0.3439) at 14 V, and the white emission area seemed totally insensitive to the drive voltages at 10 V-16 V. We also obtained a greater maximum luminance and external quantum efficiency of 211 cd/m 2 and 0.478%, respectively, at 19 V. In conclusion, we improved the stability of white OLEDs through imparting insensitivity to the drive voltages.
Acknowledgements
This work was supported by Konkuk University in 2007.
References
Charton C , Schiller N , Fahland M , Hollander A , Wedel A , Noller K 2006 Thin Solid Films 502 99 -
Morimoto M , Watanabe H 1996 NEC Tech J 49 82 -
Holton W. C 1997 Solid State Tech 40 163 -
Tang C. W , VanSlyke S. A 1987 Appl Phys Lett 51 913 -
Tokito S , Tsuzuki T , Sato F , Iijima T 2005 Curr Appl Phys 5 331 -
Feng J , Li F , Gao W , Liu S , Liu Y , Wang Y 2001 Appl Phys Lett 78 3947 -
Mattoussi H , Murata H , Merritt C. D , Iizumi Y , Kido J , Kafafi Z. H 1999 J Appl Phys 86 2642 -
Vincett P. S , Barlow W. A , Hanu R. A , Roberts G. G 1982 Thin Solid Films 94 171 -
O Brien D. F , Baldo M. A , Thompson M. E , Forrest S. R 1999 Appl Phys Lett 74 442 -
Oh H. S , Cho J. Y , Yoon S. B 2004 J Korean Phys Soc 45 460 -
Oh H. S , Cho J. Y , Yoon S. B , Kang M. K 2004 J Korean Phys Soc 44 1490 -
Ko C. W , Tao Y. T 2001 Appl Phys Lett 79 4234 -
Deshpande R. S , Bulovic V , Forrest S. R 1999 Appl Phys Lett 75 888 -