Vector Passive Harmonic Mode-locking Fiber Laser Based on Topological Insulator Bi2Se3 Interacting with Fiber Taper
Vector Passive Harmonic Mode-locking Fiber Laser Based on Topological Insulator Bi2Se3 Interacting with Fiber Taper
Journal of the Optical Society of Korea. 2016. Feb, 20(1): 135-139
Copyright © 2016, Optical Society of Korea
  • Received : August 18, 2015
  • Accepted : December 05, 2015
  • Published : February 25, 2016
Export by style
Cited by
About the Authors
Jian Ping, Li

I propose a vector passive harmonic mode-locked fiber laser based on topological insulator Bi 2 Se 3 interacting with a fiber taper with a diameter of 7 μm. The particles of topological insulator are deposited uniformly onto the fiber taper with light pressure effect. By incorporating the fabricated saturable absorber into an Er-doped fiber laser cavity, stable mode-locked fiber is obtained. Due to the intense evanescent field of the fiber taper, strong confinement of light enhances the nonlinearity of the laser cavity, and passive harmonic mode-locking is performed. I observe a maximum harmonic mode-locking of 356th, corresponding to a frequency of 3.57 GHz. The pulse duration is 824 fs, and the full width at half maximum of the spectrum is about 8.2 nm. The polarization dependent loss of the saturable absorber is ~ 2.5 dB in the wavelength range of the C band. As the cavity contains no other polarization dependent device, the mode-locked laser is functioning in the vector state. The harmonic order vs pump power is investigated. To the best of our knowledge, this report is the highest frequency mode-locked fiber laser based on Bi 2 Se 3 . Experimental results indicate that the topological insulator Bi 2 Se 3 functioning with a thin fiber taper is effective for vector harmonic mode-locking.
Passively mode-locked fiber (ML) has drawn significant attention for its potential applications in nonlinear optics, micro-machining, communication, sensing, etc. [1 - 8] . Specifically, ML with sufficient high frequency is a hot topic. This high frequency is possible to achieve via dissipative four-wave-mixing [3 - 5] , or passive harmonic mode-locking (HML) based on high nonlinearity [6 - 12] . The former technique utilizes an additional optical interferometer with high finesses, such as a Fabry–Pérot interferometer, which increases the cost of the laser system [4] . In contrast, high frequency pulsed laser based on HML is shown to be a potential solution for a low-cost laser system that could be used for a high speed communication, optical microwave source [8] . The physical origin of the HML is that a fundamental soliton laser splits into high order solitons when experiencing significant nonlinear shift, and operation with stable multiple pulses can be maintained when all the effects, such as dispersion, gain and loss, and Kerr effect reach a balance. Nowadays, lots of efforts have been made to generate HML, and several articles have been published. For example, high frequency ML based on nonlinear polarization rotation has been proposed [9] . Also, HML based on nonlinear materials such as graphene and reduced graphene oxide with saturable absorption effect have been reported [10 - 15] . Those 2-dimensional materials possess excellent saturation absorption advantages due to the unique bandgap structure. Conventionally, the HML is mainly achieved via intense evanescent field, through which pulses accumulate significant nonlinear phase shift due to the strong confinement of light. This phase shift destabilizes the fundamental mode-locking, and leads to break up of those pulses. For example, there are several reports about MLs functioning with HML [6 - 9] . Recently, new materials, topological insulators (TI), such as, Bi 2 Se 3 , Bi 2 Te 3 , and Sb 2 Te 3 , have shown excellent saturation absorption effect [13 - 22] . They exhibit a linear dispersion Dirac-like electronic band structure like that of graphene, and saturable absorption is induced by Pauli blocking. Luo et al . report a 2 GHz passively harmonic mode-locked fiber laser based on Bi 2 Te 3 [15] . Recently, researchers have shown that the bandgap of Bi 2 Se 3 could be ~0.3 eV, and the absolute modulation depth of Bi 2 Se 3 can be as high as 98% [13] . Although various kinds of lasers have been demonstrated based on Bi 2 Se 3 [12 - 26] , its full characteristic has not been fully explored.
Here, I propose a high frequency mode-locked fiber laser based on Bi 2 Se 3 interacting intensely with a fiber taper. HML is formed when the pump power is larger than 18 mW. I produce the saturable absorber (SA) by depositing Bi 2 Se 3 nanoparticles onto the fiber taper surface with light pressure. I measure the polarization dependent loss of the SA. By incorporating the SA into a fiber ring cavity, stable HML is observed, and the vector nature is experimentally explored with a polarization beam splitter (PBS).
Figure 1 depicts schematically the fiber ring cavity. As shown, it contains 2 m erbium-doped fiber with a peak absorption of 80 dB/m at 1530 nm, and additional 18.4 m SMF. Other devices include a 980 nm laser for pumping the gain fiber, a wavelength division multiplexer (WDM), a polarization independent isolator for unidirectional operation, a polarization controller (PC) for optimizing the polarization state of the cavity, an optical fiber coupler with 10% output, and an SA based on Bi 2 Se 3 . The group velocity dispersion of EDF and SMF are 15.7 ps/nm/km and 18 ps/nm/km, respectively, so the net anomalous dispersion is −0.467 ps 2 . The length of the ring cavity is about 20.4 m, so the fundamental frequency is ~10.03 MHz. The bandwidth of the temporal detecting equipment is 5 GHz (detector: DET08CFC/M, Thorlabs Co., Ltd.; oscilloscope: Pulsecheck, APE) The resolution bandwidth of the radio-frequency (RF) frequency analyzer (Agilent, PSAE4447A) is 1 kHz, and the optical frequency information is analyzed by an optical spectrum analyzer (AQ6370, Yokogawa) with a resolution of 0.05 nm. To investigate the polarization characteristics, I use a fiber-based PBS.
PPT Slide
Lager Image
Schematic setup of the fiber ring laser.
The SA is produced by depositing the Bi 2 Se 3 particles onto the taper with light pressure as in [19] . The fiber taper shown in Fig. 2(a) possesses a waist diameter of 7 μm, and the length of the uniform section is larger than 15 mm. It was produced from a standard single mode fiber (SMF, Corning SMF-28)) with hydrogen flame as shown in Fig. 2(b) . Based on a strong evanescent-interaction with Be 2 Se 3 , this taper would provide sufficient high nonlinearity for HML. The taper loss is about 0.5 dB at C bands, and no modulation is shown in the transmission spectrum. The Bi 2 Se 3 flakes are produced by exfoliating Bi 2 Se 3 crystal produced from bismuth oxide powder and selenium powder [26] , then the crystal is sonicated in N-methy1-2-pyrrolidone solution to get few-layer Bi 2 Se 3 solution. Its corresponding Raman spectrum in Fig. 2(c) contains three typical Raman peaks, A 11 g , E 2 g , and A 21 g , locating at 72 cm −1 , 129 cm −1 , and 173 cm −1 , respectively. I immerse the taper into the Bi 2 Se 3 solution, and inject 10 mW continuous 980 nm laser into one port of the taper and monitor the output power from the other port. 20 seconds later, the deposition loss drops to ~4 dB. I pick up the taper and dry it for further experiment. I measure the polarization dependent losses (PDLs) of the pure taper and the SA at 1560 nm as 0.5 dB and 2.5 dB, respectively. The relative large PDL of the SA is originated because the nanoparticles have not been deposited uniformly on the taper. For example, gravity would make the deposition asymmetric, and the different sizes of the particles may also contribute to the relative PDL. However, the following experiment indicates that although the saturable absorption materials may possess significant PDL, the fiber taper deposition method would be an excellent choice for fabricating SA for vector ML.
PPT Slide
Lager Image
(a) Micro photograph of fiber taper, where a waist diameter of 7 μm is shown. (b) Fabrication process of the fiber taper. (c) Raman spectrum of the Bi2Se3. (d) Nonlinear transmission of the SA with respect to average power.
I measure the nonlinear transmission of the fabricated SA based on a balance two-detectors method as in Ref. 26 . The detailed parameters of the optical source are as follow: center wavelength (1560 nm); pulse duration (540 fs); repetition rate (13 MHz). Figure 2(d) depicts the nonlinear optical response, and the modulation depth is 2.3%.
Due to the stochastic birefringence induced by twisting of the fiber, polarization adjusting with a PC is needed. In our experiment, stable ML with fundamental frequency is observed for pump power larger than 18 mW. This low threshold is mainly induced by relatively small saturation intensity. Figure 3 shows the typical output for pump power at 20 mW. The oscilloscope trace contains a period of 99.7 ns, corresponding to the fundamental frequency of 10.03 MHz. The optical spectrum contains significant Kelly sidebands, and the full width at half maximum (FWHM) of the spectrum is about 7.3 nm. The autocorrelation trace shows a pulse duration of 958 fs. The RF spectrum contains a contrast ratio of 70 dB at the fundamental frequency.
PPT Slide
Lager Image
Output characteristics for pump power at 20 mW. (a) temporal trains; (b) optical spectrum; (c) autocorrelation trace; (d) RF spectrum.
When the pump power is increased, different orders of harmonic mode-locking can be observed. Figure 4 depicts the order of HML with respect to pump power. In our experiment, a maximum order of 356th, namely 3.57 GHz, is obtained, and pump power larger than 600 mW will destroy the SA. The average output power is 11.5 mW for pump power at 600 mW. Figure 5 depicts the typical temporal trains, optical spectra, the single pulse widths, and the RF spectra of this HML. As shown in Fig. 5(a) , the pulse train in HML seems broad. This is because that the pulse period is comparable to the bandwidth of the oscilloscope. However, the contrast ratio larger than 60 dB at harmonic fundamental frequency shown in Fig. 5(d) indicates that this HML is also very stable. The FWHM of the total optical spectrum is 8.2 nm, which is slightly larger than that of the fundamental mode-locking. The autocorrelation trace in Fig. 5(c) shows a pulse duration of 824 fs after fitted by sech 2 shape. The time-bandwidth product (TBP) of this laser is 0.571, which is larger than the 0.315 for a standard transform limited pulse.
PPT Slide
Lager Image
Number of harmonic order and pulse duration versus pump power.
PPT Slide
Lager Image
Output characteristics for pump power at 600 mW. (a) temporal trains; (b) optical spectrum; (c) autocorrelation trace; (d) RF spectrum, the inset is the frequency within 15 MHz.
I examine the vector nature of soliton laser with a PBS. Clearly, the system generates pulses within both polarization directions. As shown in Fig. 6 , optical spectra in the two ports of the PBS differ from each other, and cross couplings are found at several frequencies. The pulse durations and contrast ratios of the two polarization directions are found to be the same. This may be induced by the relative large resolution of the autocorrelator. In our experiment, all devices are polarization independent, and the PDL of SA is also relative small. This laser cavity always supports two orthogonal polarization modes. The small random birefringence in the cavity can be tuned by the PC, and I observed stable polarization fixed vector laser. I record the output of the two ports of the PBS, and the detected signals keep the same intensities. This result indicates that the vector laser is polarization locked rather than rotated. Generally, harmonic ML and fundamental ML share similar vector characteristics.
PPT Slide
Lager Image
Optical spectra of the HML when splitted by a PBS.
I propose a vector harmonic mode-locked fiber laser based on fiber taper interacting strongly with topological insulator Bi 2 Se 3 . The strong confinement of fiber taper enhances the nonlinearity of the cavity, and a maximum harmonic mode-locking of 356th is obtained. A pulse train with a duration of 824 fs, and a spectrum width of 8.2 nm is observed. As the particles of topological insulator are deposited uniformly onto the taper surface, the polarization dependent loss is small enough to get a vector functioning state. This kind of vector high frequency pulse laser would find potential applications in nonlinear optics, communication, sensing etc.
Color versions of one or more of the figures in this paper are available online.
Fermann M. E. , Hartl I. (2013) “Ultrafast fibre lasers,” Nature Photon. 7 868 - 874    DOI : 10.1038/nphoton.2013.280
Bonaccorso F. , Sun Z. , Hasan T. , Ferrari A. C. (2010) “Gaphene photonics and optoelectronics,” Nature Photon. 4 611 - 622    DOI : 10.1038/nphoton.2010.186
Yoshida E. , Nakazawa M. (1997) “Low-threshold 115-GHz continuous-wave modulational-instability erbium-doped fiber laser,” Opt. Lett. 22 1409 - 1411    DOI : 10.1364/OL.22.001409
Zhang S. , Lu F. , Dong X. , Shum P. , Yang X. , Zhou X. , Gong Y. , Lu C. (2005) “Passive mode locking at harmonics of the free spectral range of the intracavity filter in a fiber ring laser,” Opt. Lett. 30 2852 - 2854    DOI : 10.1364/OL.30.002852
Peccianti M. , Pasquazi A. , Park Y. , Little B. E. , Chu S. T. , Moss D. J. , Morandotti R. (2012) “Demonstration of a stable ultrafast laser based on a nonlinear microcavity,” Nature Commun. 3 765 -    DOI : 10.1038/ncomms1762
Zhu P. F. , Lin Z. B. , Ning Q. Y. , Cai Z. R. , Xing X. B. , Liu J. , Chen W. C. , Luo Z. C. , Luo A. P. , Xu W. C. (2013) “Passive harmonic mode-locking in a fiber laser by using a microfiber-based graphene saturable absorber,” Laser. Phys. Lett. 10 105107 -    DOI : 10.1088/1612-2011/10/10/105107
Zhang Z. , Wang L. , Wang Y. (2013) “Sub-100 fs and passive harmonic mode-locking of dispersion-managed dissipative fiber laser with carbon nanotubes,” IEEE J. Lightwave Technol. 31 3719 - 3725    DOI : 10.1109/JLT.2013.2287632
Grudinin A. B. , Gray S. (1997) “Passive harmonic mode locking in soliton fiber lasers,” J. Opt. Soc. Am. B 14 144 - 154    DOI : 10.1364/JOSAB.14.000144
Sobon G. , Krzempek K. , Kaczmarek P. , Abramski K. M. , Nikodem M. (2011) “10 GHz passive harmonic mode-locking in Er-Yb double-clad fiber laser,” Opt. Commun. 284 4203 - 4206    DOI : 10.1016/j.optcom.2011.04.050
Bao Q. L. , Zhang H. , Wang Y. , Ni Z. H. , Yan Y. L. , Shen Z. X. , Loh K. P. , Tang D. Y. (2009) “Atomic-layer graphene as a saturable absorber for ultrafast pulsed lasers,” Adv. Funct. Mater. 19 3077 - 3083    DOI : 10.1002/adfm.200901007
Sotor J. , Sobon G. , Krzempek K. , Abramski K. M. (2012) “Fundamental and harmonic mode-locking in erbium-doped fiber laser based on grapheme saturable absorber,” Opt. Commun. 285 3174 - 3178    DOI : 10.1016/j.optcom.2012.03.002
Song Y. W. , Jang S. Y. , Han W. S. , Bae M. K. (2010) “Graphene mode-lockers for fiber lasers functioned with evanescent field interaction,” Appl. Phys. Lett. 96 051122 -    DOI : 10.1063/1.3309669
Bonaccorso F. , Sun Z. (2013) “Solution processing of graphene, topological insulators and other 2d crystals for ultrafast photonics,” Opt. Mater. Express 4 63 - 78
Zhao C. , Zhang H. , Qi X. , Chen Y. , Wang Z. , Wen S. , Tang D. (2012) “Ultra-short pulse generation by a topological insulator based saturable absorber,” Appl. Phys. Lett. 101 211106 -    DOI : 10.1063/1.4767919
Luo Z. C. , Liu M. , Liu H. , Zheng X. W. , Luo A. P. , Zhao C. J. , Zhang H. , Wen S. C. , Xu W. C. (2013) “2 GHz passively harmonic mode-locked fiber laser by a microfiber-based topological insulator saturable absorber,” Opt. Lett. 38 5212 - 5215    DOI : 10.1364/OL.38.005212
Jun C. S. , Choi S. Y. , Rotermund F. , Kim B. Y. , Yeom D. (2012) “Toward higher-order passive harmonic mode-locking of a soliton fiber laser,” Opt. Lett. 37 1862 - 1864    DOI : 10.1364/OL.37.001862
Sobon G. , Sotor J. , Abramski K. M. (2012) “Passive harmonic mode-locking in Er-doped fiber laser based on graphene saturable absorber with repetition rates scalable to 2.22 GHz,” Appl. Phys. Lett. 100 161109 -    DOI : 10.1063/1.4704913
Jun C. S. , Im J. H. , Yoo S. H. , Choi S. Y. , Rotermund F. , Yeom D. , Kim B. Y. (2011) “Low noise GHz passive harmonic mode-locking of soliton fiber laser using evanescent wave interaction with carbon nanotubes,” Opt. Express 19 19775 - 19780    DOI : 10.1364/OE.19.019775
Gao L. , Huang W. , Zhang J. D. , Zhu T. , Zhang H. , Zhao C. J. , Zhang W. , Zhang H. (2014) “Q-switched mode-locked erbium-doped fiber laser based on topological insulator Bi2Se3 deposited fiber taper,” Appl. Opt. 53 5117 - 5122    DOI : 10.1364/AO.53.005117
Sotor J. , Sobon G. , Macherzynski W. , Paletko P. , Grodecki K. , Abramski K. M. (2014) “Mode locking in Er doped fiber laser based on mechanically exfoliated Sb2Te3 saturable absorber,” Opt. Mat. Express 4 1 - 6
Lee J. , Koo J. , Jhon Y. M. , Lee J. H. (2015) “Femtosecond harmonic mode‐locking of a fiber laser based on a bulk-structured Bi2Te3 topological insulator,” Opt. Express 23 6359 - 6369    DOI : 10.1364/OE.23.006359
Zhao C. , Zou Y. , Chen Y. , Wang Z. , Lu S. , Zhang H. , Wen S. , Tang D. (2012) “Wavelength-tunable picosecond soliton fiber laser with topological insulator: Bi2Se3 as a mode locker,” Opt. Express 20 27888 - 27895    DOI : 10.1364/OE.20.027888
Luo Z. , Liu C. , Hang Y. , Wu D. , Wu J. , Xu H. , Cai Z. , Lin Z. , Sun L. , Weng J. (2014) “Topological-insulator passively Q-switched double-clad fiber laser at 2 μm wavelength,” IEEE J. Select. Topics Quantum Electron. 20 0902708 -
Lee J. , Koo J. , Jhon Y. M. , Lee J. H. (2014) “A femtosecond pulse erbium fiber laser incorporating a saturable absorber based on bulk-structured Bi2Se3 topological insulator,” Opt. Express 22 6165 - 6173    DOI : 10.1364/OE.22.006165
Gao L. , Zhu T. , Huang W. , Luo Z. (2015) “Stable, ultrafast pulse mode-locked by topological insulator Bi2Se3 nanosheets interacting with photonic crystal fiber: from anomalous dispersion to normal dispersion,” IEEE Photon. J. 7 3300108 -
Chen Y. , Zhao C. , Chen S. , Du J. , Tang P. , Jiang G. , Zhang H. , Wen S. , Tang D. (2014) “Large energy, wavelength widely tunable, topological insulator Q-switched erbium-doped fiber laser,” IEEE J. Select. Topics Quantum Electron. 20 0900508 -