Simulation Study of Injection-Molded Light Guide Plates for Improving Luminance Uniformity Based on the Measured Replication Quality of Micro-Patterns for LED TV Backlight
Simulation Study of Injection-Molded Light Guide Plates for Improving Luminance Uniformity Based on the Measured Replication Quality of Micro-Patterns for LED TV Backlight
Journal of the Optical Society of Korea. 2015. Apr, 19(2): 159-164
Copyright © 2015, Optical Society of Korea
  • Received : January 01, 2015
  • Accepted : February 02, 2015
  • Published : April 25, 2015
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Byung-Yun Joo
Department of Mechanical Engineering, Korea University of Technology and Education, Cheonan 330-708, Korea
Jae-Hyeon Ko
Department of Physics, Hallym University, Chuncheon 200-702, Korea
hwangko@hallym.ac.kr
Abstract
In the injection-molded light guide plate the replication quality, i.e. the reproduction accuracy, of micro-patterns should be high and uniform over the entire surface area. However technical difficulty in meeting the necessary replication quality arises as the plate size becomes large for TV applications. We propose a simulation technique to optimize the distribution of micro-patterns on a 55-inch injection molded light guide plate considering non-ideal replication quality of micro-patterns. The luminance uniformity could be improved by more than 16% by optimizing the pattern distribution in spite of the same replication quality.
Keywords
I. INTRODUCTION
Successful development of efficient backlight units has made it possible to expand the application of liquid crystal displays (LCD) to various fields including mobile devices and large-size TVs [1 - 11] . The light guide plate (LGP) is the most important optical component in the edge-lit backlight for LCD applications. Light-emitting diodes (LEDs) are usually used as light sources in the backlight. Edge-lit backlight technology has traditionally been applied to small- and medium-size LCDs, but recent development of large-size LGP has made it possible to fabricate very thin, efficient LCD TVs, which are commercially called “LED TVs”. Because of increase in the emitting power and efficiency of LEDs, the number of LEDs adopted in one edge-lit backlight has decreased continuously. In addition, many studies on the optimization of micro-patterns formed on LGPs have been reported, where the authors suggested various designs to improve the light-utilization efficiency and the luminance uniformity.
An extrusion or injection molding process has been used to fabricate plate-type LGPs. One of the important methods for fabricating large-size light guide for LED TV applications is the injection molding process. Recently, injection molding technology has attracted attention for improving the luminance property of large-size LGPs for LCD TV applications [12] . This is due to the fact that micro-patterns, such as micro-prisms, can be formed on LGPs by injection molding. Various shapes of micro-prismatic pattern geometry have been applied to the light guide plate for achieving high luminance. When the injection molding is used to fabricate micro-patterned LGPs, it is desirable to reproduce the accurate shape of the mold on the LGP having the high “replication quality” because poor micro-patterns can seriously deteriorate the on-axis luminance distribution on the LGP. Several groups have studied to design new injection molding processes in order to improve the replication quality of LGPs.
Several injection molding technologies have been used to fabricate patterned LGPs, for example, general injection molding (IM), injection compression molding (ICM), and rapid heat compression molding (RHCM) technologies. Figure 1 shows the measured replication quality of a small-size LGP with dimensions of 120 × 200 × 4 mm 3 , which was fabricated via the three injection molding processes by using a micro-cavity type mold. The numerical value for the degree of replication, denoted as R Replication , can be defined by the formed pattern height of the molded part divided by the stamper depth expressed in Eq.(1). The total area of the LGP was divided into nine regions, and the R Replication of each region was measured. As Fig. 1(c) shows, R Replication depends significantly on the injection molding technique. R Replication becomes significantly lower as the injection molding technique changes from RHCM → ICM → IM. Moreover, R Replication decreases with increasing distance from the molding gate. This kind of non-uniformity problem may become much worse for large-size LGPs.
PPT Slide
Lager Image
(a) Dimensions of the injection-molded light guide plate with respect to the injection gate: (b) Replication shape at position 5 of the light guide plate fabricated by three different molding technology with respect to the mold shape. (c) Replication results of injection-molded specimen as a function of position from the injection gate.
PPT Slide
Lager Image
In previous optical designs of backlights, the ideal micro-patterns were usually assumed over the whole area of the LGP. The arrangement of the micro-patterns, such as density and/or size, formed on the backside of the LGP was adjusted to meet the uniformity quality. In the case of the fabricated LGP, the replication quality is not ideal, which is the main reason for the difference in the optical properties between the prediction by optical simulation and the measurement from the real LGP. This suggests that the replication quality on the LGP should be considered and reflected in the optimization process of the optical design of LGPs for large-size backlights. In this study, we will suggest a design method for optical patterns on large-size LGPs considering the replication quality depending on the detailed micro-shape of the pattern and the injection molding process. For this purpose, positional dependence of the replication quality Rreplication was measured from the fabricated LGP, which was reflected in the optical simulation to improve the optical performances of large-size LGPs.
II. MEASUREMENT OF REPLICATION QUALITY
In this section, the measurement method for the replication quality of micro-patterns is introduced. Figure 2 shows a schematic figure of the 55-inch light guide plate investigated in this study. The dimensions are 1245 × 698 × 3 mm 3 , and total 120 LEDs were attached on two edges. A lenticular lens array with a pitch of 50 μm was formed on the upper surface pitch, while one-dimensional prism patterns were engraved on the bottom surface. The width and the inclination angle were 10 μm and 50°, respectively, and the pitch was adjusted to satisfy the uniformity requirement.
PPT Slide
Lager Image
A schematic view of a 55-inch light guide plate along with the cross-sectional shapes of lenticular and prism arrays.
Based on the cross-sectional view of micro-patterns, we defined shape parameters of micro-patterns as shown in Fig. 3 . The cross-section of lenticular lenses was assumed to be part of a semicircle. The radius of the semicircle R 1 can be calculated by using the pitch p , the height H and the interval G between two patterns. The result is shown by Eq.(2). For the case of micro-prisms, two radii of curvature R 2 and R 3 in addition to the inclination angle θ and the width W were defined according to Fig. 3 .
PPT Slide
Lager Image
Geometrical shape parameters of micro-patterns.
PPT Slide
Lager Image
We carried out optical simulation for the LGP under various conditions to monitor the 9-point luminance uniformity. The inset of Table 1 shows the luminance measurement points on the LGP. Table 1 shows the simulation condition (initial value and the range of variation) and the difference between the maximum and the minimum luminance values obtained from the 9-point measurements. We can easily know that the height H of the lenticular lens, the radius of curvature R 3 , the inclination angle θ and the width W of prism patterns have substantial effects on the luminance uniformity. Accordingly, these four parameters will be monitored and analyzed for the fabricated LGP as described below.
Simulation conditions (initial value and the range of variation) of each shape parameter and the difference between the maximum and the minimum luminance values obtained from the 9 points. Sensitivity indicates the degree of effect of each shape parameter on the luminance uniformity. The inset figure shows the measurement points of luminance
PPT Slide
Lager Image
Simulation conditions (initial value and the range of variation) of each shape parameter and the difference between the maximum and the minimum luminance values obtained from the 9 points. Sensitivity indicates the degree of effect of each shape parameter on the luminance uniformity. The inset figure shows the measurement points of luminance
Figure 4 shows the measurement method of shape parameters of micro-patterns. Room-temperature-vulcanized silicone rubber (Repliset F5, Struers corp.) was used to cut out the pattern on a certain region on the 55-inch LGP. The replication error caused by using the silicon rubber is usually less than 1 μm. The vulcanized silicon gum was sliced and observed under the optical microscope. The shape parameters were determined by using shape-measurement software which was combined with the optical microscope.
PPT Slide
Lager Image
Measurement procedure of shape parameters of micro-patterns formed on the light guide plate by injection molding technology.
Table 2 shows the measurement results of the shape parameters H , W , R 3 , and θ , that is, the average, the standard deviation, the maximum and the minimum values of each parameter are shown in Table 2 . The replication map of each parameter was obtained by using the equations (3) ~ (6). Figure 5 shows the four replication map of the shape parameters obtained from the LGP fabricated by using RHCM method. These replication maps show the regions where the replication quality becomes worse over the whole LGP area when the LGP was fabricated by the RHCM method. This nonuniform replication quality is expected to induce the problem of luminance nonuniformity.
Measurement results of the shape parametersH,W,R3, andθ, that is, the average, the standard deviation, the maximum and the minimum values of each parameter
PPT Slide
Lager Image
Measurement results of the shape parameters H, W, R3, and θ, that is, the average, the standard deviation, the maximum and the minimum values of each parameter
PPT Slide
Lager Image
Replication maps of the four shape parameters obtained from the procedure shown in Fig. 4. (a) Replication map for H, (b) Replication map for W, (c) Replication map for R3, (d) Replication map for θ.
PPT Slide
Lager Image
PPT Slide
Lager Image
PPT Slide
Lager Image
PPT Slide
Lager Image
III. SIMULATION OF LIGHT GUIDE PLATE CONSIDERING REPLICATION MAP OF MICRO-PATTERNS
A 55-inch backlight model was constructed and used in the simulation to search for the right approach toward optimized optical design of light guide plates. Figures 6 (a) and (b) show the geometrical model of lenticular and prism array, respectively. The one-dimensional lenticular or prism lens was assumed to consist of unit pattern segments in the simulation. The unit pattern segment was defined according to the right figures of Fig. 6(a) and (b) . The total number of segments is shown on the left side. At first, we assumed that the micro-patterns were ideal, that is, the replication quality was perfect, and carried out the optical simulation under this assumption. The 55-inch backlight model consisted of one LGP shown in Fig. 2 , one reflection film (E6SV, Toray), one diffusion film (SD743, Shinhwa), and one prism film. The pitch variation of micro-prisms was optimized in the simulation by monitoring the 9-point luminance uniformity. The optimized pitch distribution is shown as a dark blue line denoted as (A) in Fig. 7 . The simulated luminance distribution is shown in Table 3 , and the calculated luminance uniformity is 81.2 %. As a next step, we included the measured, real replication quality, shown in Table 2 , into the optical simulation under the same pitch distribution (A). In this case, the luminance uniformity decreased substantially down to 68.1 %. This degradation in luminance uniformity suggests that the simulation result obtained under the perfect replication quality cannot be used for optimization of micropatterns and that the replication quality should be considered in the optimization process of pattern distribution of large-size LGPs. In order to reflect the replication quality in the simulation, the shape parameters of the unit segment shown in Fig. 7 ( H , W , R 3 , and θ ) were fixed by considering the values of the replication maps. That is, the shape parameter of each unit segment was fixed to the product of the value in the map and the average value in Table 2 , which was divided by 100. The luminance uniformity was monitored during the optical simulation under this condition, and the optimized pitch distribution, denoted as (B), of micro-prisms is shown in Fig. 7 as a red line. The obtained luminance uniformity is 84.4%, which is comparable to that obtained under the ideal replication quality combined with the distribution (A). This result clearly shows that the luminance uniformity can be improved significantly by considering the real replication quality of the LGP even though the replication quality is far from perfect.
PPT Slide
Lager Image
Geometrical model of (a) lenticular and (b) prism array along with the unit pattern segment comprising each model.
PPT Slide
Lager Image
Optimized pitch distribution of the prism array under the ideal and the real replication quality. See the text for details.
Simulation conditions and the obtained luminance uniformity. See the text for details
PPT Slide
Lager Image
Simulation conditions and the obtained luminance uniformity. See the text for details
The prism pattern used in this study is one-dimensional. In this case, the design degree of freedom is only the pattern pitch. Therefore, it is difficult to improve the luminance uniformity along the direction parallel to the prism grooves. If the prism pattern is divided into many segments and if the pitch between the segments is optimized, better luminance uniformity will be achieved based on the proposed design approach.
IV. CONCLUSION
We proposed an optical design method where the replication quality of large-size light guide plates could be implemented for improving luminance uniformity. Micro-lenticular and micro-prism arrays were formed on the top and the bottom surfaces of 55-inch light guide plate, respectively. The replication quality of the light guide plate fabricated by injection molding technology was measured by using silicone resin and an optical microscope, and replication maps were constructed for important shape parameters of lenticular and prism arrays. The prism pitch was optimized by optical simulation under the condition of perfect replication quality in order to maximize the luminance uniformity, which, however, decreased significantly once the measured replication quality was reflected in the optical modeling. The degraded luminance uniformity could be increased substantially by considering the measure replication map in the optical simulation. This study showed that the optical performances of large-size backlight could be improved by measuring and reflecting real replication quality of LGP into the optical modeling even though the replication quality is far from perfect.
Acknowledgements
This research was partially supported by the “Sensitivity touch platform development and new industrialization support program” through the Ministry of Knowledge Economy (MKE) and Korea Institute for Advancement of Technology (KIAT).
References
Tjahjadi M. , Hay G. , Coyle D. J. , Olczak E. G. 2006 “Advances in LCD backlight film and plate technology,” Information Display 10 (6) 22 - 27
Lee J.-H. , Lee H.-S. , Lee B.-K. , Choi W.-S. , Choi H.-Y. , Yoon J.-B. 2007 “Simple liquid crystal display backlight unit comprising only a single-sheet micropatterned polydimethylsiloxane (PDMS) light-guide plate,“ Opt. Lett. 32 2665 - 2667
Park G.-J. , Kim Y.-G. , Yi J.-H. , Kwon J.-H. , Park J.-H. , Kim S.-H. , Kim B.-K. , Shin J.-K. , Soh H.-S. 2009 “Enhancement of the optical performance by optimization of optical films in direct-illumination LCD backlight,” J. Opt. Soc. Korea 13 152 - 157
Choi E. S. , Choi Y. H. , Shin Y. J. 2009 “Light manipulation in a transparent medium with laser-patterned three-dimensional and surface scatterers,” J. Korean Phys. Soc. 55 2646 - 2649
Hur S.-T. , Choi S.-W. , Lee M. 2011 “An edge-lit backlight unit for small portable liquid crystal displays with a newly designed single pyramid sheet,” J. Korean Phys. Soc. 58 392 - 395
Park S. H. , Lee S. S. , Ma H. J. , Choi E. S. , Shin Y. J. 2010 “Simulation of luminance and uniformity of LGP according to the laser scattering pattern,” Korean J. Opt. Photon. 21 225 - 229
Hur S. T. , Choi S.-W. , Lee M. 2011 “An edge-lit backlight unit for small portable liquid crystal displays with a newly designed single pyramid sheet,” J. Korean Phys. Soc. 58 392 - 395
Seo J. S. , Yeom T. E. , Ko J.-H. 2012 “Experimental and simulation study of the optical performances of a wide grid polarizer as a luminance enhancement film for LCD backlight applications,” J. Opt. Soc. Korea 16 151 - 156
Kwon J. H. , Jun H. J. , Gwag J. S. , Lee H. S. 2013 “Effect of wavelength-dependent scattering on the color chromaticity of the LCD backlight,” J. Opt. Soc. Korea 17 275 - 278
Joo B.-Y. , Ko J.-H. 2013 “Analysis of color uniformity of white LED lens packages for direct-lit LCD backlight applications,” J. Opt. Soc. Korea 17 506 - 512
Yoon G.-W. , Kim H.-D. , Yeon J. , Yoon J.-B. 2014 “Novel buried inverse-trapezoidal micropattern for dual-sided light extracting backlight unit,” Opt. Express 22 32440 -
Kim T. H. , Kim J. Y. , Kim J. S. , Kang J. J. , Kim J. S. , Noh S. H. 2009 “A study on the large area rapid-injection compression molding for mold optimum design,” Proc. Kor. Soc. Tech. Plasticity Wonju, Korea 99 - 102