Terahertz Wave Transmission Properties of Metallic Periodic Structures Printed on a Photo-paper
Terahertz Wave Transmission Properties of Metallic Periodic Structures Printed on a Photo-paper
Journal of the Optical Society of Korea. 2010. Sep, 14(3): 282-285
Copyright ©2010, Optical Society of Korea
  • Received : June 06, 2010
  • Accepted : July 07, 2010
  • Published : September 25, 2010
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Sung-Ho Lee
Sangyoon Gee
Chul Kang
Chul-Sik Kee
cskee@gist.ac.kr
Abstract
We printed a one-dimensional array of metallic wires and a two-dimensional array of metallic split ring resonators on a photo-paper by using a high-dots-per-inch resolution printer and an ink with silver nano-particles. The printed sample sizes are 1.0 × 1.0 cm 2 . The transmission measured by a terahertz time domain spectroscopy system shows that the arrays of wires and split ring resonators could act as polarizers and band-stop filters, respectively, in a terahertz frequency region.
Keywords
I. INTRODUCTION
Terahertz (THz) waves are electromagnetic radiation with frequencies generally in a range of 0.1 to 10 THz, between the microwaves and the far-infrared [1] . Owing to recent advancements in optical and electrical components, efficient THz sources, detectors, and passive devices have been developed [2] . THz time-domain spectroscopy (THz-TDS) and THz imaging systems still demand suitable THz components for improving their performance.
Artificial periodic structures have been demonstrated to be useful in manipulating electromagnetic waves. The representative example is a photonic crystal which is periodically composed of materials with different dielectric constant [3] . Photonic crystals can improve the performance of optical devices such as waveguides, filters, light emitting diodes, and semiconductor lasers. Metallic periodic structures are also useful in improving radiation efficiency and patterns of antennas in microwave and millimeter wave ranges [4 , 5] . Thus periodic structures are expected to be useful in manipulating THz waves and could act as functional devices in a THz frequency range [6 - 10] .
Usually, planar metallic structures on solid or flexible films have been fabricated by a photolithography technique including nine steps: making a photo-mask, cleaning the substrate, spin-coating the photo-resist, baking, exposure, development, post-baking, metal evaporation (etching) and resist removal. The processes demand a long task time and high cost.
Recently, printing techniques have been widely used in fabricating electronic components on polymer films. The printing method has only 3 steps: cleaning substrate, ink-jet printing, and heating. The last process lets silver nanoparticles be sintered together and thus a printed sample becomes metallic. The printing method reduces processing time and effort for fabrication of planar T y pe metallic structures on films. Walter et al., reported THz transmission of periodic arrays of split ring resonators (SRRs) printed on a polyimide substrate with ink including silver nanoparticles [11] . Hangyo et al., also reported fabrication of wire-grid structures and SRRs on high-resistiviT y Si substrates by using a super-fine ink-jet printer with silver paste ink [12] . The printed structures act a good polarizer and filter. Thus the printing method can be useful in fabricating periodic structures to work in a THz range. It is interesting to print the periodic structures on conventional photo-papers to have no absorption in a THz range. A photo-paper is also flexible as well as cheap. Moreover, surface treatments such as plasma or ultrasonic cleaning are not required, unlike Si-substrates and polymide substrates.
In this paper, we report fabrication of a one-dimensional arrays of metallic wires and two-dimensional arrays of metallic SRRs by using an ink-jet printer and a conductive ink with silver nanoparticles. The structures were printed on a conventional photo-paper. The THz spectral responses are measured by a home-made THz-TDS system. The measured spectra show that the metallic wire array can act as a THz polarizer and the SSR array can act as a THz band-stop filter in a certain THz range.
II. FABRICATION
A high-dpi (dots-per-inch) resolution drop-on-demand printer and a conductive ink were employed to fabricate metallic periodic arrays on a conventional photo-paper. We printed a one-dimensional array of wires on a general-purpose photo paper with an ink containing silver nano-particles (DGP-40LT-15C) by using an ink-jet printer (DMP-2831). The samples were placed on a hot plate at 130℃ during 30 minutes for the sintering of silver nano-particles.
PPT Slide
Lager Image
Microscopic image of a printed one-dimensional array of wires with the period of 300 μm and the width of 140 μm (a) and a two-dimensional array of single split ring resonators (b). The one side length of a SSR is about 150 μm. The line width and the gap size are about 20 μm and 50 μm, respectively. The period of the array is about 230 μm.
The feature resolution of a printed structure depends on a nozzle to jet ink drops and compositions of ink. We have tried to find conditions to give a good feature resolution by varying both the weight percent of Ag in the ink and temperature and bias-voltage of a nozzle. After a lot of trial and error, we achieved 20 μm-feature resolution that is good for printing periodic arrays to work in a THz frequency range under the conditions that temperature and bias-voltage of a nozzle are about 30℃ and 16 V, respectively, and the weight percent of Ag is 32.0. However, printed arrays with 20 μm-feature resolution do not exhibit metallic properties because few Ag nano-particles are sintered in printed 20 μm-lines. To improve probabiliT y of sintering between Ag nano-particles, we iterated printing on the same place maintaining the 20 μm-feature resolution. We have found that four iteration printing is enough to make structures which exhibit metallic properties.
Fig. 1(a) shows the printed one-dimensional array of wires with a period of 300 μm and width of 140 μm. A two-dimensional array of SRRs printed on the photo paper is shown in Fig. 1(b) . The one side length of a SSR is about 150 μm. The line width and the gap size are about 20 μm and 50 μm, respectively. The period of the array is about 230 μm. The printed sample sizes are about 1.0 × 1.0 cm 2 .
III. RESULTS AND DISCUSSION
Fig. 1(a) shows the printed one-dimensional array of wires with a period of 300 μm and width of 140 μm. A two-dimensional array of SRRs printed on the photo paper is shown in Fig. 1(b) . The one side length of a SSR is about 150 μm. The line width and the gap size are about 20 μm and 50 μm, respectively. The period of the array is about 230 μm. The printed sample sizes are about 1.0 × 1.0 cm 2 .
PPT Slide
Lager Image
Schematic view of a home-made terahertz-time domain spectroscopy system employed in experiments.
Fig. 3 shows the transmission spectra of the one-dimensional wire array for THz pulses with polarizations perpendicular ( x -polarized) and parallel ( y -polarized) to the wire when THz pulses are normally incident on the sample. The transmission spectrum of the paper was presented as a reference spectrum. The transmittances of the sample were normalized to that of the paper. One can see that the planar onedimensional wire array prevents the y -polarized THz waves with frequencies below 0.35 THz from transmitting through the sample, while it does not affect the x -polarized THz waves. The y -polarized waves induce currents in the wires and thus the wire array structure acts effectively as a metal for the waves. However, for the x-polarized waves, the structure does not act as a metal but, in effect, as a lossy dielectric because currents are not induced by the x-polarized waves. In fact, due to the polarization dependent properT y , a one-dimensional metallic wire array has been used as a polarizer for waves with wavelengths much longer than the period of the array [14 , 15] .
To test the abiliT y of our sample as a THz polarizer, we calculated the ratio of transmittances of x - and y -polarized THz waves, P xy = T x / T y , shown in Fig. 4 . P xy calculated from transmittance data is depicted in Fig. 3 . The dashed line indicates P xy = 3. T x is larger than three times T y in a frequency range between 0.1 and 0.4 THz. Thus the printed wire array could be a polarizer in that range.
Fig. 5 shows the transmission spectra of a two-dimensional array of SRRs for the x - and y -polarized THz waves. The dashed line presents the transmission spectrum of a paper used as a substrate. One can see that the SRR array exhibits a transmission dip around 0.325 THz, for the y-polarized wave. It has been demonstrated that the y -polarized wave induces a current circulating along a SRR, and a magnetic properT y with negative permeabiliT y . Thus, a SRR array strongly reflects an electromagnetic wave in a frequency range where permeabiliT y is negative. Our printed sample has negative permeabiliT y around 0.325 THz [16] .
PPT Slide
Lager Image
Transmission spectra of the one-dimensional wire array for the x- and the y-polarized THz waves when THz waves are normally incident on the sample. The transmission spectrum of the paper was presented as a reference spectrum.
The SRR structure has been also modeled to be a LC resonant circuit because the metallic line of a SRR gives rise to an inductance and the gap of a SRR gives rise to a capacitance [17] . A LC resonant circuit exhibits high impedance at the resonant frequency and thus electromagnetic waves are highly reflected from the SRR array structure around the resonant frequency which corresponds to a frequency range with negative permeabiliT y . The resonant characteristic of a SRR could make the SRR array a THz band stop filter.
PPT Slide
Lager Image
The ratio of transmittances of x- and y-polarized THz waves, Pxy = Tx /Ty, of the printed one-dimensional array of wires.
PPT Slide
Lager Image
Transmission spectra of a two-dimensional array of SRRs for the x- and y-polarized THz waves. The dotted line presents the transmission spectrum of a substrate paper.
IV. CONCLUSION
A one-dimensional array of wires and a two-dimensional array of split ring resonators were printed on a photo-paper with an ink including silver nano-particles. The printed sample sizes are about 1.0 × 1.0 cm 2 . The transmission measured by a THs system shows that the arrays of wires and split ring resonators could act as a polarizer and a band-stop filter in a THz region, respectively. The printing method could be a tool to realize various structures for functional THz devices.
Acknowledgements
This work was supported by the National Research Foundation Grant funded by the Korea Government (2010- 0014291) and Photonics 2020 research project through a grant provided by GIST in 2010.
References
Dexheimer S 2007 Terahertz Spectroscopy: Principles and Applications Taylor & Francis London UK
Lee Y.S 2008 Principles of Terahertz Science and Technology Springer New York USA
Joannopoulos J , Johnson S , Meade R , Winn J 1995 Photonic Crystals: Molding the Flow of Light Princeton University Press Princeton NJ USA
Brown E.R , Parker C.D , Yablonovitch E 1993 Radiation properties of a planar antenna on a photonic crystal substrate J Opt Soc Am B 10 404 - 407
Gonzalo R , de Maagt P , Sorolla M 1999 Enhanced patch-antenna performance by suppressing surface waves using photonic-bandgap substrate IEEE Trans Microw Theory Tech 47 2131 - 2138
Zhao Y , Grischkowsky D 2006 Terahertz demonstrations of effectively two-dimensional photonic bandgap structures Opt Lett 31 1534 - 1536
Prasad T , Colvin V.L , Jian Z , Mittleman D.M 2007 Superprism effect in a metal-clad terahertz photonic crystal slab Opt Lett 32 683 - 685
Zhao Y , Grischkowsky D 2007 2-D terahertz metallic photonic crystals in parallel-plate waveguides IEEE Trans Microw Theory Tech 55 656 - 663
Han H , Park H , Cho M , Kim J 2002 Terahertz pulse propagation in a plastic photonic crystal fiber Appl Phys Lett 80 2634 - 2636
Kim S , Kee C.S , Lee J 2007 Single-mode condition and dispersion of terahertz photonic crystal fiber J Opt Soc Korea 11 97 - 100
Walther M , Ortner A , Meier H , Loffelmann U , Smith P.J , Korvink J.G 2009 Terahertz metamaterials fabricated by inkjet printing Appl Phys Lett 95 251107 - 251107
Takano K , Kawabata T , Hsieh C.F , Akiyama K , Miyamaru F , Abe Y , Tokuda Y , Pan R.P , Pan C.L , Hangyo M 2010 Fabrication of terahertz planar metamaterials using a super-fine ink-jet printer Appl Phys Exp 3 016701 - 016701
Kang C , Kee C.S , Sohn I.B , Lee J 2008 Spectral properties of THz-periodic metallic structures J Opt Soc Korea 12 196 - 199
Costley A.E , Hursey K.H , Neill G.F , Wald J.M 1977 Free-standing fine-wire grids: their manufacture performance and use at millimeter and submillimeter wavelengths J Opt Soc Am 67 979 - 981
Mok C.L , Chambers W.G , Parker T.J , Costley A.E 1979 Far-infrared performance and application of freestanding grids wound from 5μm diameter tungsten wire Infrared Phys 19 437 - 442
Yen T.J , Padilla W.J , Fang N , Vier D.C , Smith D.R , Pendry J.B , Basov D.N , Zhang X 2004 Terahertz magnetic response from artificial materials Science 303 1494 - 1496
Marques F , Mesa J , Martel F , Medina 2003 Comparative analysis of edge- and broadside- coupled split ring resonators for metamaterial design - theory and experiments IEEE Transactions on Antennas and Propagation 51 2572 - 2581