Observation of Peptide-Ion Generation by Laser-Induced Surface Heating from Tungsten Silicide Surfaces
Observation of Peptide-Ion Generation by Laser-Induced Surface Heating from Tungsten Silicide Surfaces
Mass Spectrometry Letters. 2012. Mar, 3(1): 18-20
Copyright ©2012, Korean Society Mass Spectrometry
  • Received : February 27, 2012
  • Accepted : March 06, 2012
  • Published : March 15, 2012
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Shin Hye Kim
Center for Nano-Bio Technology, Korea Research Institute of Standards and Science, Daejeon 305-340, Republic of Korea, Department of Chemistry, Chung-Nam National University, Daejeon 305-764, Republic of Korea
Sun Hwa Park
Center for Nanocharacterization, Korea Research Institute of Standards and Science, Daejeon 305-340, Republic of Korea, Department of Nanomaterials Science and Engineering, University of Science and Technology, Daejeon 305-350, Republic of Korea
Jae Yong Song
Center for Nanocharacterization, Korea Research Institute of Standards and Science, Daejeon 305-340, Republic of Korea
Sang Yun Han
Center for Nano-Bio Technology, Korea Research Institute of Standards and Science, Daejeon 305-340, Republic of Korea
sanghan@kriss.re.kr

Abstract
We report observation of laser desorption/ionization (LDI) of peptides from flat surfaces of tungsten silicide (WSi 2 ). In contrast to MALDI (matrix-assisted laser desorption/ionization) and SALDI (surface-assisted laser desorption/ionization) mass spectrometry, this study did not utilize any matrices and surface nanostructures. In this work, LDI on WSi 2 surfaces is demonstrated to cover a mass range up to 1,600 Da (somatostatin; monoisotopic mass = 1637.9 Da). In addition, it exhibited a high sensitivity, which could detect peptides, which could detect peptides of low femtomole levels (20 fmol for angiotensin II). The observed LDI process was discussed to be largely thermal, more specifically, due to laser-induced surface heating that is most likely promoted by the low thermal diffusivity (κ) of WSi 2 substrate.
Keywords
Introduction
Matrix-assisted laser desorption/ionization (MALDI) is a powerful means of soft ionization for mass spectrometry of thermally labile biomolecules. However, the use of organic crystals as matrix creates certain limitations on applications. It includes interference of matrix peaks in the small mass region (< 500 Da) and sweet spots. Careful matrix selection for given analytes is also important for successful mass analysis. To address such issues, extensive efforts were made to develop matrix-free laser desorption/ionization (LDI) in recent years, which can be an alternative method of soft ionization to the MALDI method. 1
DIOS (desorption/ionization on porous silicon) mass spectrometry was the first demonstration of LDI, which utilized specially prepared Si surfaces. 2 In DIOS mass spectrometry, LDI of small molecules was found to occur on the nanoporous surfaces of crystalline Si (c-Si) formed by photo-electrochemical etching. However, without such surface nanostructures of a sub-micrometer dimension, the DIOS process was hardly observed to take place. Since the advent of DIOS mass spectrometry, surfaces possessing various nanostructures have been examined for their LDI capabilities. In the researches, Si-based nanostructures were most popularly investigated, the examples of which include porous Si surfaces fabricated by etching, 3 clathrate-structured Si surfaces, 4 Si nanowires, 5 Si microcolumn and nanoposts arrays. 6 , 7 In addition to Si, nanostructured surfaces made of other materials, such as nanostructured Au thin film, 8 selfassembled germanium nanodots, 9 and zinc oxide nanowires, 10 also exhibited a promising level of sensitivity and mass range for mass spectrometry. Likewise, utilization of surface nanostructures has been a key component in the previous developments of high-efficiency LDI surfaces.
On the other hand, few cases of LDI occurring on flat surfaces are known, i . e . surfaces without nanostructures, which include amorphous Si (a-Si) and commercial Al foils. 11 , 12 Obviously, flat surfaces for LDI have certain advantages. As it does not require fabrication of complex nanostructures on surfaces, it is easier to prepare in a large scale and even often commercilly available. By avoiding sweet spots caused by uneven matrix crystals and surface nanostructures, flat surfaces may offer an opportunity for quantitative measurement as well. In addition, lack of complexity from surface nanostructures provides a further opportunity to look into the LDI mechanism more closely. In this letter, we report LDI of peptides from flat surfaces of tungsten silicide (WSi 2 ).
Experimental
- Preparation of WSi2surfaces
WSi 2 on Si(001) substrates were prepared by the Ar + magnetron sputtering method. During the sputtering process, the flow of Ar gas was maintained at 50 mTorr and the working pressure was 1.7 mTorr. Various thicknesses of WSi 2 were examined, including 65 nm, 260 nm, and 400 nm. For additional heat treatment, the samples were heated at 873 K in vacuum (2 × 10 −6 Torr) for 1 hr. The prepared WSi 2 surfaces were then characterized using a fieldemission scanning electron microscope (FESEM, S-4800, Hitachi), an X-ray diffractometer (θ-2θ, Cu-Kα, Bruker D8), and an atomic force microscopy (AFM, XE-150, PSIA). The AFM ( r.m.s. ) roughness of WSi 2 surfaces as prepared was measured to be about 0.07 nm, and it slightly increased to be 0.2 nm after heat treatment. In the XRD study, WSi 2 used in this work was characterized to carry a polymorphism with tetragonal and hexagonal crystal structures.
- LDI mass spectrometry
LDI mass spectrometry was performed using a MALDI-TOF mass spectrometer (Autoflex III; Bruker-Daltonics, Leipzig, Germany) in reflectron mode. Before experiments, WSi 2 chips were sonicated in isopropyl alcohol for 30s, washed in deionized water, and then dried under a gentle flow of nitrogen. A peptide solution was prepared in 10% methyl alcohol to a concentration of 10 pmol/μL. It consisted of bradykinin 1-5 (monoisotopic mass: 572.7 Da), bradykinin 1-7 (756.9 Da), angiotensin II (1046.2 Da), substance P (1347.6 Da), and somatostatin (1637.9 Da). The chemicals were commercially obtained from Sigma-Aldrich and used without purification. For LDI experiments, a 0.2 μl drop of the peptide solution (2 pmol) was taken and pipetted onto WSi 2 surfaces, and then dried in ambient conditions. The WSi 2 surfaces were moderately hydrophilic, so the sample drop somewhat spread on the surfaces. Thus, the actual sample consumption used to obtain a LDI mass spectrum was much lower than the applied quantity of 2 pmol.
Results and Discussion
Although efficient LDI from various nanostructured
PPT Slide
Lager Image
SEM (cross-section) and AFM images of WSi2 surfaces; (a) 260 nm, (b) 400 nm, and (c) 400 nm thick.
surfaces is known, understanding of the LDI mechanism has been very limited. However, some of previous investigations recognized a possible contribution of laser-induced surface heating to the LDI process. 3 , 10 It was viewed that the physical existence of surface nanostructures might provide heat conduction barriers for absorbed laser energy; thus, the absorbed energy is momentarily trapped in surface nanostructures, which gives rise to a rapid surface heating. Such a rapid increase in surface temperature is known to promote thermal desorption of thermally labile molecules, which thus can contribute to LDI of biomolecules. 13
A recent work on a-Si demonstrated that a rapid surface heating for LDI could be achieved even without employing surface nanostructures by selecting appropriate surface materials. 11 Because of the low thermal conductivity (K = 5.5W m −1 K −1 ), the thermal diffusivity (κ = K/C p ) of a-Si is very small (0.03 cm 2 s −1 ; heat capacity (C p ) for a-Si = 1.65 J cm −3 K −1 ). During the period of laser irradiation (t~7 ns), the absorbed energy can diffuse only for about 90 nm (D) into the bulk substrate (depth of conductive heating: (D) = (κt/π) 1/2 ). As the heat energy is localized near the surface due to the low thermal diffusivity, the surface temperature on a-Si can drastically increase to higher than 1000 K within 10 nsec. On the other hand, because of the higher thermal conductivity (150 W m −1 K −1 ) of c-Si, the transient increase in surface temperature is predicted to be only about 300 K,
PPT Slide
Lager Image
LDI mass spectra of a peptide mixture (bradykinin 1-5, bradykinin 1-7, angiotensin II, substance P, somatostatin (2 pmol each) from WSi2 surfaces (65 nm thick) (a) as prepared and (b) after high-temperature heat treatment.
PPT Slide
Lager Image
LDI mass spectra of angiotension II; (a) 200 fmol and (b) 20 fmol.
much lower than on a-Si, which may explain that LDI of biomolecules on flat c-Si surfaces has not been successful before.
In this study, we examined WSi 2 surfaces for flat LDI substrates. WSi 2 possesses a moderate thermal conductivity of 18.3Wm -1 K −1 . However, as typical in metal silicides, it has a very large heat capacity (309.3 J cm −3 K −1 ), which gives a much low thermal diffusivity of 0.0006 cm 2 s −1 that predicts a conduction depth (D) of 11 nm. Thereby, it can be suggested that the heat capacity of WSi 2 surfaces might give us an opportunity for LDI of thermally labile molecules. In order to corroborate the idea, we examined LDI of peptides from WSi 2 surfaces. Figure 1 displays SEM and AFM images for WSi 2 surfaces used in this study. As shown in the AFM image, the surfaces do not possess any noticeable surface nanostructures, which would otherwise contribute to promoting the LDI process, possibly. We examined the LDI capability of WSi 2 surfaces prepared in different conditions using a mixture of 5 peptides. For example, we examined 65 nm, 260 nm, and 400 nm thick WSi 2 surfaces before and after high-temperature heat treatment. However, within the conditions we varied, the results on LDI performance were not quite different. Figure 2 shows the LDI mass spectra of peptides obtained from 65 nm thick WSi 2 surfaces with and without heat treatment. The results shown in Figure 2 clearly exhibit pronounced production of peptide ions from the flat surfaces of WSi 2 . It supports our postulation that the thermal mechanism is indeed a main driving force for LDI of thermally labile molecules from surfaces, where selecting surface materials with a large heat capacity can be a way to develop efficient LDI plates. As shown in Figure 3 , the LDI-on-WSi 2 method also offers a good sensitivity of low femtomole levels (20 fmol for angiotensin II), which is acceptable for peptide mass spectrometry as well.
Conclusion
We report that LDI on tungsten silicide (WSi 2 ) surfaces exhibits pronounced production of peptide ions. It covers a mass range up to 1600 Da. It is sensitive, which can ionize low femtomole levels of peptide molecules without assistance of matrices or surface nanostructures. The mechanism for LDI is viewed to be thermal, i . e . driven by laser-induced surface heating. It is most likely promoted by the thermal properties of WSi 2 such as very large heat capacity, causing a rapid surface heating that favors intact desorption of thermally labile molecules like peptides. By demonstrating efficient LDI from flat surfaces of a material with a large heat capacity (C p ), thus with a small heat diffusivity (κ), we suggest that the thermal mechanism indeed plays a key role in LDI, which provides an important point of consideration in the future development of matrix-free LDI method.
Acknowledgements
The authors acknowledge support for this research from the Converging Research Center Program through the NRF, funded by MEST (2011K000887).
References
Peterson D. S. 2007 Mass Spectrom. Rev. 26 19 -    DOI : 10.1002/mas.20104
Wei J. , Buriak J. M. , Siuzdak G. 1999 Nature 399 243 -    DOI : 10.1038/20400
Alimpiev S. , Nikiforov S. , Karavanskii V. , Minton T. , Sunner J. 2001 J. Chem. Phys. 115 1891 -    DOI : 10.1063/1.1381531
Northen T. R. , Yanes O. , Northen M. T. , Marrinucci D. , Uritboonthai W. , Apon J. , Golledge S. L. , Nordstrom A. , Siuzdak G. 2007 Nature 449 1033 -    DOI : 10.1038/nature06195
Go E. P. , Apon J. V. , Luo G. , Saghatelian A. , Daniels R. H. , Sahi V. , Dubrow R. , Cravatt B. F. , Vertes A. , Siuzdak G. 2005 Anal. Chem. 77 1641 -    DOI : 10.1021/ac048460o
Walker B. N. , Razunguzwa T. , Powell M. , Knochenmuss R. , Vertes A. 2009 Angew. Chem. Int. Ed. 48 1669 -    DOI : 10.1002/anie.200805114
Walker B. N. , Stolee J. A. , Pickel D. L. , Retterer S. T. , Vertes A. 2010 J. Phys. Chem. C. 114 4835 -    DOI : 10.1021/jp9110103
Nayak R. , Knapp D. R. 2010 Anal. Chem. 82 7772 -    DOI : 10.1021/ac1017277
Seino T. , Sato H. , Yamamoto A. , Nemoto A. , Torimura M. , Tao H. 2007 Anal. Chem. 79 4827 -    DOI : 10.1021/ac062216a
Shin W. J. , Shin J. H. , Song J. Y. , Han S. Y. 2010 J. Am. Soc. Mass Spectrom. 22 989 -
Kim S. H. , Lee A. , Song J. Y. , Han S. Y. 2012 J. Am. Soc. Mass Spectrom.    DOI : 10.1007/s13361-012-0355-5
Hsu N.-Y. , Tseng S. Y. , Wu C.-Y. , Ren C.-T. , Lee Y.-C. , Wong C.-H. , Chen C.-H. 2008 Anal. Chem. 80 5203 -    DOI : 10.1021/ac800435r
Daves Jr. G. D. 1979 Acc. Chem. Res. 12 359 -    DOI : 10.1021/ar50142a002