Lithium Diffusivity of Tin-based Film Model Electrodes for Lithium-ion Batteries
Lithium Diffusivity of Tin-based Film Model Electrodes for Lithium-ion Batteries
Journal of Electrochemical Science and Technology. 2015. Dec, 6(4): 116-120
Copyright © 2015, The Korean Electrochemical Society
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : July 13, 2015
  • Accepted : November 02, 2015
  • Published : December 31, 2015
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Sukhyun Hong
Department of Energy Science and Technology
Hyuntak Jo
Department of Energy Science and Technology
Seung-Wan Song
Department of Chemical Engineering & Applied Chemistry, Chungnam National University, Daejeon 305-764, Republic of Korea
swsong@cnu.ac.kr

Abstract
Lithium diffusivity of fluorine-free and -doped tin-nickel (Sn-Ni) film model electrodes with improved interfacial (solid electrolyte interphase (SEI)) stability has been determined, utilizing variable rate cyclic voltammetry (CV). The method for interfacial stabilization comprises fluorine-doping on the electrode together with the use of electrolyte including fluorinated ethylene carbonate (FEC) solvent and trimethyl phosphite additive. It is found that lithium diffusivity of Sn is largely dependent on the fluorine-doping on the Sn-Ni electrode and interfacial stability. Lithium diffusivity of fluorine-doped electrode is one order higher than that of fluorine-free electrode, which is ascribed to the enhanced electrical conductivity and interfacial stabilization effect.
Keywords
1. Introduction
Tin (Sn)-based materials have been recognized as one of the attractive anode materials, which can replace the commercialized graphite, primarily because of the larger theoretical capacity (~994 mAhg −1 ) of Sn than that of graphite (~372 mAhg −1 ) [1] .In addition, the Sn appeal its merits of appropriate operating voltage above lithium (Li) that prevents dendrite formation, high electric conductivity as metallic, ductile property that is convenient for a handy fabrication of the batteries in diverse architectures [2] , and a different reaction mechanism, which is based on Li-Sn alloy formation [1] , from Li + -intercalation mechanism of graphite. Improved battery safety and rate capability are then expected. Sn-based anode materials, however, suffer from a rapid performance fade due to a large volume change followed by particle cracking event during lithiation/delithiation and the loss of electrical contact between individual particles and between particles and current collector [1] . It has been established that interfacial instability of Sn electrode with electrolyte is due to the attack of LiPF 6 -derived acidic species (PF 5 , PF 3 O, HF) and this additionally deteriorates the electrical disintegration [3 - 5] . Interfacial stabilization and the formation of stable solid electrolyte interphase (SEI) have been suggested as one of the most effective approaches for enhancing the cycling performance of Sn-based anodes. Our earlier work showed that the use of trimethyl phosphite (P(OCH 3 ) 3 , TMP) as a Lewis base electrolyte additive, which captures the LiPF 6 -derived Lewis acids (PF 5 and PF 3 O), and fluorine (F)-doping on Sn, which produces positively charged Sn and induces to capture F ions from HF that is always present in LiPF 6 -contaiing carbonate-based electrolyte, were effective in enhancing the interfacial and SEI stability and cycling performance [5 , 6] .
Lithium diffusivity is an intrinsic property of Li + ion-conducting electrode material. It is generally proposed that the rate of lithiation process of electrode is controlled by lithium diffusivity [7] . Determination of lithium diffusivity and understanding of lithium diffusion behavior are crucial in controlling the charge-discharge cycling behavior and performance, and rate capability. Various methods have been used to determine the lithium diffusivity of Sn and silicon (Si) alloy anodes, such as galvanostatic intermittent titration technique (GITT) [8] , potentiostatic intermittent titration technique (PITT) [9] , electrochemical impedance spectroscopy (EIS) [10 , 11] and cyclic voltammetry (CV) [11 - 14] . However, the reported diffusivities of Sn are not consistent with each other being in the range of 10 −8 − 10 −7 cm 2 s −1 [1 , 8] , since the measurements were conducted under the condition of no control of interfacial stability to electrolyte. Then, electrolyte continued to be electrochemically reduced and decomposed with cycling, consuming an extra charge and resulting in irreversible electrochemical signals. In addition, since conductive material (e.g., graphite) was necessary for the bulk Sn-based anodes to accommodate the volume change [15 , 16] , lithium diffusivity of Sn alone was not able to be measured.
Studies of dense film model electrode can give a clearer insight into the intrinsic properties of electrode material without complications from carbon and polymeric binder additives that are necessary in bulk electrodes for enhanced electric conductivity and particle connection [3 - 5 , 17 - 23] . Film electrode homogeneously deposited on a conductive substrate can have a robust structure and strong adherence to the substrate, yielding a good model system for the study of lithium diffusion kinetics during electrochemical charge and discharge cycling. Our earlier work showed that interfacial stabilization of pulsed laser deposited (PLD) Si film model electrodes on Cu substrate by constructing the surface protective siloxane network at the electrode surface using silane additive provides the lithium diffusivity in the order of 10 −13 cm 2 s −1 [19 , 22] . There is no prior record of lithium diffusivity study for Sn-based film model electrodes prepared by PLD.
Here, we report the determination of lithium diffusivity of F-free and F-doped Sn-Ni PLD film model electrodes under the condition of interfacial stabilization, utilizing variable rate CV. The influences of F-doping on the lithium diffusivity and electrolyte composition are discussed.
2. Experimental
The 500 - 550 nm thick film model electrodes of fluorine (F)-free and F-doped Sn-Ni were deposited on stainless steel substrates by PLD at 40℃ in 0.9 mtorr of Ar back pressure, using a KrF excimer laser with an energy density of ~3 - 4 mJcm −2 at 10 Hz impinging on the targets which consisted of Sn and Ni (65:35 in mol%) or Sn, Ni and SnF 2 (64.35:34.65:1in mol%), respectively. Targets were prepared by ball-milling of Sn and Ni (and SnF 2 ) powders and then pressing at 200 kgcm −2 . The crystal structure, relative atomic ration of Sn to Ni, the thickness and surface morphology of as-deposited films were determined and confirmed as described in our earlier works [5] .
Proto-type three-electrodes lithium cells were assembled with the as-deposited F-free or F-doped Sn-Ni film electrode as a working electrode, lithium metal foils as a reference and a counter electrodes, and the electrolytes of 1M LiPF 6 /ethylene carbonate (EC):ethyl methyl carbonate (EMC) (30:70 volume% ratio, Panax E-Tec, H 2 O content < 10 ppm) and 1M LiPF 6 /fluoroethylene carbonate (FEC):diethyl carbonate (DEC) (50:50 volume% ratio, Panax E-Tec, H 2 O content < 10 ppm) with 3 wt% trimethyl phosphite (P(OCH 3 ) 3 , TMP, 99%, Aldrich) as an additive. Lithium cell assembly and electrochemical measurement were made in Ar-filled glove box at room temperature.
Variable rate CV was carried out at a sweep rate from 100 to 0.1 mVs −1 between 0.05 and 1.5 V vs . Li/Li + , using a potentiostat (VSP SP-150, Bio-Logic). The lithium diffusivity was calculated from the plot of peak current ( Ip ) vs . the square-root of sweep rate (n 1/2 ) using the least square method.
3. Results and Discussion
Fig. 1a - b show the CVs of the F-free Sn-Ni film electrodes in 1M LiPF 6 /EC:EMC and 1M LiPF 6 /FEC:DEC, respectively, with 3 wt% TMP additive. The y axes are expressed as pseudo capacitances ( I /ν) by normalizing the current I with the sweep rate n that varied from 100 to 0.1 mV/s. While the peak currents of both cathodic and anodic processes in the EC-based electrolyte ( Fig. 1a ) are broad and small in all sweep rates, those in the FEC-based electrolyte ( Fig. 1b ) are at a much higher peak resolution. This indicates that FEC is effective in improving the interfacial stability and consequently providing the increased electrochemical charge-discharge capacity and cycling reversibility of Sn. As decreasing the sweep rate ( Fig. 1b ), the pseudo capacitance of both cathodic and anodic peaks increases and peaks becomes sharper, then, they are separated into individual peaks. Thus, in Fig. 1b , the peak currents at the slowest sweep rate of 0.1 mVs −1 enable to be assigned; the cathodic peaks at 0.7, 0.53 and 0.37 V, due to lithiation process of Sn, correspond to the formation of Li 0.4 Sn, Li 2.33 Sn and Li 4.4 Sn, respectively [1 , 24] . The anodic peaks near 0.5, 0.61, 0.71 and 0.8 V, by delithiation from Li 4.4 Sn, are due to subsequent regeneration of Li 3.5 Sn, Li 2.33 Sn, LiSn and Sn, respectively [1 , 24] . In this study, we take the anodic peak at 0.61 V, which corresponds to the removal of 2.33 Li + from Li 2.33 Sn (Li 7 Sn 3 ), for determining the lithium diffusivity, as it is observed in common regardless of sweep rate.
PPT Slide
Lager Image
Cyclic voltammograms of the lithium cells with F-free Sn-Ni film electrodes in the electrolytes of (a) 1M LiPF6/EC:EMC with 3wt% TMP additive and (b) 1M LiPF6/FEC:DEC with 3wt% TMP at a variable sweep rate (n) from 100 to 0.1 mVs−1, and (c-d) the dependence of peak current (IP) on the square-root of sweep rate (ν1/2).
Fig. 1c - d reveal that the anodic peak current ( Ip ) at 0.61 V is linearly proportional to the square-root of sweep rate (ν 1/2 ) in the sweep rate region of 0.1 - 10 mVs −1 , rather than to the sweep rate (ν). This is characteristic of semi-infinite lithium diffusion process [25] , which may include the lithium diffusion to the SEI layer to Sn electrode. The slope of Ip vs . ν 1/2 was used for the determination of lithium diffusivity using Randles-Sevcik equation. 25)
PPT Slide
Lager Image
The determined diffusivities are 1.01 × 10 −7 cm 2 s −1 in the EC-based electrolyte and 8.12 × 10 −7 cm 2 s −1 in the FEC-based electrolyte respectively, as listed in Table 1 . The use of FEC-based electrolyte for F-free electrode results in an increase in the lithium diffusivity, which is ascribed to its effectiveness of interfacial stabilization.
Lithium diffusivity of F-free and F-doped Sn-Ni film electrodes in 1M LiPF6/EC:EMC (EC-based) and 1M LiPF6/FEC:DEC (FEC-based) electrolytes (EL) with 3wt% TMP additive.
PPT Slide
Lager Image
Lithium diffusivity of F-free and F-doped Sn-Ni film electrodes in 1M LiPF6/EC:EMC (EC-based) and 1M LiPF6/FEC:DEC (FEC-based) electrolytes (EL) with 3wt% TMP additive.
Fig. 2a - b exhibit the variable rate CVs of F-doped Sn-Ni electrode in 1M LiPF 6 /EC:EMC and 1M LiPF 6 /FEC:DEC, respectively, with 3 wt% TMP additive. Compared to the broad CVs of F-free electrodes ( Fig. 1a - b ), peaks resolution in the CVs of F-doped electrode ( Fig. 2a - b ) is significantly improved and a higher pseudo capacitance of cathodic and anodic peak are obtained. Fig. 2c - d show the plots of the anodic peak current ( Ip ) at 0.61 V vs . the squareroot of sweep rate (ν 1/2 ) in the sweep rate region of 0.1 - 10 mVs −1 . The determined lithium diffusivities of F-doped Sn-Ni electrodes are 2.21×10 6 cm 2 s −1 in the EC-based electrolyte and 1.22×10 6 cm 2 s −1 , as listed in Table 1 . These are one order higher than those of F-free electrodes. Recollect that the surface of both F-free and –doped Sn-Ni film electrodes possess a plenty of surface tin oxide, and the surface of F-doped electrode includes SnF 2 and O-Sn-F bond, as described in the earlier work [5 , 26] . This implies that F-doping occurs on not only Sn but also SnO 2 forming SnO 2y F y type material, which contributes to an increase in the electrical conductivity [5 , 26] . In general, lithium diffusivity is dependent on the electrical conductivity of electrode materials. Also recollect that the important role of F-doping on Sn is to capture F ions from HF present in the LiPF 6 -containing carbonate-based electrolyte while producing a surface protective SEI layer and providing a better preservation of electrode structure and composition [5] . It is thus determined that the higher lithium diffusivity of F-doped Sn-Ni electrodes than that of F-free electrodes is believed to be due to enhanced electrical conductivity and interfacial stability to electrolyte.
PPT Slide
Lager Image
Cyclic voltammograms of the lithium cells with F-doped Sn-Ni film electrodes in the electrolytes of (a) 1M LiPF6/EC:EMC with 3wt% TMP and (b) 1M LiPF6/FEC:DEC with 3wt% TMP at a variable sweep rate (n) from 100 to 0.1 mVs−1, and (c-d) the dependence of peak current (IP) on the square-root of sweep rate (ν1/2).
4. Conclusions
Lithium diffusivity of F-free and F-doped Sn-Ni film model electrodes in the EC-based and FEC-based electrolytes with trimethyl phosphite additive has been determined using cyclic voltammetry. While the lithium diffusivity of F-free Sn-Ni electrodes is in the order of 10 −7 cm 2 s −1 , it increases to one order higher level of 10 −6 cm 2 s −1 upon F-doping. The F-doping on the Sn-Ni film electrode is believed to promote lithium diffusivity by the enhancement of electrical conductivity and interfacial stability to electrolyte.
Acknowledgements
This work was supported by the Korean Ministry of Science, ICT & Future Planning (2013K000214), and Ministry of Education and National Research Foundation (2012026203).
References
Winter M. , Besenhard J. O. (1999) Electrochim. Acta 45 31 -    DOI : 10.1016/S0013-4686(99)00191-7
Kwon Y. H. , Woo S.-W. , Jung H.-R. , Yu H. K. , Kim K. , Oh B. H. , Ahn S. , Lee S.-Y. , Song S.-W. , Cho J. , Shin H.-C. , Kim J. Y. (2012) Adv. Mater 24 5192 -    DOI : 10.1002/adma.201202196
Song S.-W. , Baek S.-W. (2009) Electrochim. Acta 54 1312 -    DOI : 10.1016/j.electacta.2008.09.021
Baek S.-W. , Hong S.-J. , Kim D.-W. , Song S.-W. (2009) J. Power Sources 189 660 -    DOI : 10.1016/j.jpowsour.2008.09.035
Choo M.-H. , Nguyen C. C. , Hong S. , Kwon Y. H. , Woo S.- W. , Kim J. Y. , Song S.-W. (2013) Electrochim. Acta 112 252 -    DOI : 10.1016/j.electacta.2013.08.121
Hong S. , Choo M.-H. , Kwon Y. H. , Kim J. Y. , Song S.-W. (2014) J. Electrochem. Soc. 161 A1851 -    DOI : 10.1149/2.0661412jes
Park M. , Zhang X. , Chung M. , Less G. B. , Sastry A. M. (2010) J. Power Sources 195 7904 -    DOI : 10.1016/j.jpowsour.2010.06.060
Wang J. , Raistrick I. D. , Huggins R. A. (1986) J. Electrochem. Soc. 133 457 -    DOI : 10.1149/1.2108601
Xie J. , Imanishi N. , Zhang T. , Hirano A. , Takeda Y. , Yamamoto O. (2010) Mater. Chem. Phys. 120 421 -    DOI : 10.1016/j.matchemphys.2009.11.031
Churikov A. V. , Pridatko K. I. , Ivanishchev A. V. , Ivanishcheva I. A. , Gamayunova I. M. , Zapsis K. V. , Sycheva V. O. (2008) Russian J. Electrochem. 44 550 -    DOI : 10.1134/S1023193508050078
Zhang T. , Zhang H. P. , Yang L. C. , Wang B. , Wu Y. P. , Takamura T. (2008) Electrochim. Acta. 53 5660 -    DOI : 10.1016/j.electacta.2008.03.017
Nguyen S. H. , Lim J. C. , Lee J. K. (2012) Electrochim. Acta 74 53 -    DOI : 10.1016/j.electacta.2012.03.176
Li H. , Cheng F. , Zhu Z. , Bai H. , Tao Z. , Chen J. (2011) J. Alloys & Compds. 509 2919 -    DOI : 10.1016/j.jallcom.2010.11.156
Tasaki K. , Goldberg A. , Lian J.-J. , Walker M. , Timmons A. , Harris S. J. (2009) J. Electrochem. Soc. 156 A1019 -    DOI : 10.1149/1.3239850
Zhang W.-M. , Hu J.-S. , Guo Y.-G. , Zheng S.-F. , Zhong L.-S. , Song W.-G. , Wan L.-J. (2008) Adv. Mater. 20 1160 -    DOI : 10.1002/adma.200701364
Liu C.-J. , Hang H. , Cao G.-Z. , Xue F.-H. , Camacho R. A. P. , Dong X.-L. (2014) Electrochim. Acta 144 376 -    DOI : 10.1016/j.electacta.2014.07.068
Song S.-W. , Reade R. P. , Kostecki R. , Striebel K. A. (2006) J. Electrochem. Soc 153 A12 -    DOI : 10.1149/1.2128763
Song S.-W. , Baek S.-W. (2009) Electrochem. Solid-State Lett 12 A23 -    DOI : 10.1149/1.3028216
Nguyen C. C. , Song S.-W. (2010) Electrochim. Acta 55 3026 -    DOI : 10.1016/j.electacta.2009.12.067
Nguyen C. C. , Kim D.-W. , Song S.-W. (2011) J. Electrochem. Sci. & Tech. 2 8 -    DOI : 10.5229/JECST.2011.2.1.008
Nguyen C. C. , Woo S.-W. , Song S.-W. (2012) J. Phys. Chem. C 116 14764 -    DOI : 10.1021/jp3019815
Nguyen C. C. , Song S.-W. (2013) J. Electrochem. Sci. & Tech 4 108 -    DOI : 10.5229/JECST.2013.4.3.108
Nguyen C. C. , Choi H. , Song S.-W. (2013) J. Electrochem. Soc. 160 A906 -    DOI : 10.1149/2.118306jes
Courtney I. A. , Tse J. S. , Mao O , Hafner J. , Dahn J. R. (1998) Phys. Rev. B 58 583 -    DOI : 10.1103/PhysRevB.58.R583
Bard A. J. , Faulkner L. R. (2001) Electrochemical Methods: Fundamentals and Applications 2nd ed. John Wiley & Sons, Inc. New York
Mientus R. , Ellmer K. (1998) Surf. Coat. Technol. 98 1267 -    DOI : 10.1016/S0257-8972(97)00247-8