Activity and Stability of Immobilized Enzyme on Silk Sericin Bead
Activity and Stability of Immobilized Enzyme on Silk Sericin Bead
International Journal of Industrial Entomology. 2013. Dec, 27(2): 329-332
Copyright © 2013, Korean Society of Sericultural Science
  • Received : December 10, 2013
  • Accepted : December 17, 2013
  • Published : December 31, 2013
Export by style
Cited by
About the Authors
Hanjin, Oh
National Instrumentation Center for Environmental Management, Seoul National University, Seoul 151-921, Korea
Ki Hoon, Lee
Research Institute for Agriculture and Life Sciences, Seoul National University, Seoul 151-921, Korea

In present preliminary report, we showed the possibility of silk sericin (SS) in enzyme immobilization. SS beads were prepared and enzymes were immobilized on it. The specific activity of immobilized α-chymotrypsin retained more than 87% compared to the free enzyme. The immobilized α-chymotrypsin has better stability against ethanol especially those immobilized on SS beads coagulated in methanol. Immobilized trypsin and lipase had also comparable apparent activity compared to free enzyme. Our result indicates that SS could be a good candidate for enzyme immobilization support due to its hydrophilicity.
Enzyme immobilization is a promising method for the application of enzymes in industrial scale. The immobilized enzyme can be reused, and therefore, it could solve the problem of high cost of the enzyme. Silk fibroin has been used as asupport of enzyme such as glucose oxidase (Asakura et al ., 1988; Kuzuhara et al ., 1987). Enzyme was entrapped in the matrix of regenerated silk fibroin film and retained their activity after immobilization. This entrapment method, however, has disadvantages such as diffusional limitation of substrate and leakage of enzyme from the matrix.
Covalent bonding of enzyme on the surface of non-porous carrier can solve these problems especially the leakage can be prevented. Previously, we have covalently immobilized enzyme on the surface of degummed silk fiber (Lee et al ., 2004). However, the activity of enzyme was far low compared to the free enzyme. To enhance the activity of enzyme, we introduced a spacer between the support and the enzyme. Among the spacers that used in previous study, silk sericin (SS) had the best results. Both the activity and stability of immobilized enzyme were increased by using the SS as a spacer. The hydrophilicity of SS might provide a favor environment to the immobilized enzyme.This result motivated us to use sericin itself as a support.
SS has high content of hydrophilic amino acids, such as serine, threonine, and aspartic acid, and thereby, much more hydrophilic compared to fibroin. In general, hydrophilic support is favored in enzyme immobilization (Secundo, 2013). Besides, for the immobilization of enzyme, a support must have sufficient binding sites in order to achieve high loading efficiency of enzyme. Compared to fibroin, SS has high content of lysine, arginine and histidine which provide reaction site during the covalent bonding of enzyme using glutaraldehyde (GA). These haracteristics of sericin can be advantages for the enzyme immobilization because it can provide hydrophilic environment to the enzyme and allows high loading efficiency. In the present study, we have prepared pure sericin beads and adopted for enzyme immobilization.
Materials and Methods
- Materials
Silkworm cocoons were kindly provided by Heung Jin Co. Ltd. All chemicals including trypsin, α-chymotrypsin, and lipase were purchased from Sigma-Aldrich (USA).
- Extraction of silk sericin
SS was extracted by boiling 25 g of Bombyx mori silkworm cocoons with 1 L of distilled water using an autoclave for 1 h at 120℃. The extracted solution was filtered with a nonwoven filter in order to remove the remaining cocoons. The SS solution was frozen at -70℃ for 4 h and lyophilized.
- Preparation and immobilization of enzyme on silk sericin beads
The lyophilized SS was dissolved in 1M LiCl/DMSO solution for 2 h at 50℃ to prepare a dope solution of 20% (w/v). The dope solution was dropped into alcohol coagulants through a 18G syringe using a syringe pump (KD scientific, USA). Methanol and ethanol were used as coagulants, and the obtained beads are designated as SS-M and SS-E, respectively. The SS beads were left in the coagulant bath for another 1 h. They were then filtered with a nonwoven filter and washed with the same coagulant to remove the residual LiCl and DMSO.
In order to immobilize enzyme on the SS beads, the amine groups of SS were activated with GA. To ten beads of SS, 1 mL of 10% (v/v) GA in 0.2 M sodium carbonate buffer (pH 9.2) was added to activate the SS. The reaction was continued for 1 h at 25℃. The activated SS beads were washed 2 times with distilled water and 3 times with 0.1 M sodium phosphate buffers (pH 7.4). An ice-cold buffer solution of enzyme (1 mg/mL) in 0.1 M sodium phosphate buffer (pH 7.4) was added to the activated SS beads and the reaction was carried out for overnight at 4℃. The unbound enzyme was washed out 2 times with ice-cold 0.5 M of NaCl in 0.1 M sodium phosphate buffer (pH 7.4) and followed by 3 times with the same buffer but without NaCl.
- Quantification and activity test of enzyme
The bound enzyme was measured by bicinchoninic acid assay methods using bovine serum albumin as standard. The amount of bound enzyme was calculated by subtracting the amount of remaining enzyme from the initial amount of enzyme. N-benzoyl-DL-tyrosine-p-nitroanilide hydrochloride (BTPNA) was used as substrate of α-chymotrypsin. The substrate solution were prepared by mixing 250 μL of 5 mM BTPNA in DMSO, 1 mL of distilled water and 150 μL of 0.1 M sodium phosphate buffer (pH 7.4). The substrate solution were added to the activated SS beads and incubated at 25℃ for 30 min. In order to measure the activity of the immobilized α-chymotrypsin, the increase of absorbance at 400 nm was measured using UV spectrometer (UVICON 923, Kontron Instruments, USA). If the value of absorbance exceeded 2, then it was diluted until it reached below 1.5. The activity of immobilized α-chymotrypsinwas defined as μmol BTPNA hydrolyzed in 1 min applying an absorbance coefficient of ε400 = 9520 M -1 cm -1 . The stability against ethanol was measured by incubating enzyme immobilized SS beads in ethanol for 1 h at 25℃. After that, the SS beads were washed 2 times with ice-cold 0.1 M sodium phosphate buffer pH 7.4, containing 0.5 M NaCl and 3 times with cold distilled water. The activity of immobilized enzyme after ethanol treatment was measured. For trypsin and lipase, 10 mM of N-benzoyl-DLarginin-p-nitroanilid hydrochloride and p-nitrophenyl caprylate, respectively, was used instead of BTPNA and the pH of added buffer solution were 8. The increase of absorbance at 405 and 348 nm was measured for trypsin and lipase, respectively. The relative activity of immobilized trypsin and lipase were compared with each free enzyme (1 mg/mL).
Results and Discussion
Base on the previous study (Lee et al ., 2004), we immobilized the enzyme on SS which is more hydrophilic than silk fibroin. SS were fabricated into beads as previously described (Oh et al ., 2007b). SS beads are unstable in water unless cross-linking
Amount of bound α-chymotrypsin and activity ofimmobilized α-chymotrypsin on silk sericin bead
PPT Slide
Lager Image
a: for immobilized enzyme it means bound protein on 10 beads
PPT Slide
Lager Image
Stability of immobilized α-chymotrypsin against 1 h of exposure against ethanol.
is performed (Kwak et al ., 2013). We omitted the cross-linking step because GA is used during the activation step. The activated SS beads were stable in water after activation indicating crosslinking was also accomplished during the activation step. Table 1 shows the results of immobilized α-chymotrypsin on the SS beads. Ten SS beads were used for each experiment, and the amounts of bound α-chymotrypsin were 22.6 and 28.1 μg for SS-M and SS-E beads, respectively. The activities of bound α-chymotrypsin were 10.2 and 12.4 μmol/min for SS-M and SS-E beads, respectively. It was surprising that the immobilizedα-chymotrypsin retained their specific activity more than 87% compared to the free one. The stability of immobilized enzyme was also improved upon immobilization. While the free α-chymotrypsin retained only about 45% of the initial activity after 1 h of exposure in ethanol, the immobilized enzyme retained much higher activity ( Fig. 1 .). It was interesting that α-chymotrypsin immobilized on SS-M bead had higher retainedactivity than that on SS-E bead. It has been known that SS
PPT Slide
Lager Image
Relative apparent activity of trypsin and lipase immobilized on silk sericin bead.
undergoes structural transition from random coil to aggregated structure in the presence of ethanol but not in methanol (Oh et al ., 2007a). Since we used ethanol as a denaturant, the structural transition might be occurred only in the case of SS-E. This structural transition might affect the enzyme that covalently bound on SS.
Trypsin and lipase were also immobilized onto SS-M bead. Compared to the free enzyme, trypsin and lipase retained their activity to 86 and 72%, respectively ( Fig. 2 ). Unfortunately, the exact amount of enzymes bound to the SS-M bead cannot be calculated. However, the apparent activity shows that these immobilized enzymes have high preservation of activity after immobilization.
The hydrophilicity (or hydrophobicity) of a support is important in enzyme immobilization. Enzymes are proteins that consist of hydrophilic and hydrophobic part. When enzymes are immobilized on a hydrophobic support, then water moleculeswould be expelled from the support, which result in less water molecules around the immobilized enzyme. Therefore, there is an increased hydrophobic interaction between the support and the hydrophobic core of enzyme. This induces structural transition of enzyme, and finally, the enzyme will lose the activity by denaturation. The opposite effect is expected when hydrophilic support is used. It will retain more water molecules at the surface of support and establishes friendlier environment to the enzyme. The good preservation of enzyme activity upon immobilization on SS bead might be explained in this manner.
Although more detailed study is required to prove the effectiveness of SS bead in enzyme immobilization, the current preliminary result shows that SS could be a good candidate material for enzyme immobilization support. SS hasbeen considered as useful biomaterial for long time (Zhang, 2002), but up to now, it has been shown very little application. Although application of SS in biomedical fields has been proposed (Aramwit et al ., 2012), there are still debates on the immunogenicity of SS, which hinders further application in this field. Application in polymeric fields has been also proposed but the mechanical properties of SS are still improper to use if not blended with synthetic polymer nor incorporated with fillers (Oh et al ., 2008; Yun et al ., 2013). Previously, we have suggested the use of SS in heavy metal adsorption (Kwak et al ., 2013). In this case, it is free from the safety concerns that rose in biomedicalapplication and did not require high mechanical integrity. The present study shows another possibility of the use of SS in biotechnological application. The high content of polar amino acids in SS that provides hydrophilicity and a lot of reactive sites is promising characteristic of SS in enzyme immobilization. We expect that SS could be used as a good support for enzyme immobilization.
Aramwit P , Siritientong T , Srichana T (2012) Potential applications of silk sericin, a natural protein from textile industry by-products. Waste Manage Res 30 217 - 224    DOI : 10.1177/0734242X11404733
Asakura T , Yoshimizu H , Kuzuhara A , Matsunaga T (1988) Mechanism of glucose oxidase immobilization with silk fibroin J Seri Sci Jpn 57 203 - 209
Kuzuhara K , Asakura T , Tomoda R , Matsunaga T (1987) Use of silk fibroin for enzyme membrane J Biotech 5 199 - 207    DOI : 10.1016/0168-1656(87)90016-2
Kwak HW , Yang YS , Kim MK , Lee JY , Yun H , Kim MH , Lee KH (2013) Chromium(VI) adsorption behavior of silk sericin beads. Int J Indust Entomol 26 47 - 53    DOI : 10.7852/ijie.2013.26.1.047
Lee KH , Kang GD , Shin BS , Park YH , Nahm JH (2004) Immobilization of trypsin onto silk fibroin fiber via spacer arms. Int J Indust Entomol 8 195 - 200
Oh HJ , Lee JY , Kim A , Ki CS , Kim JW , Park YH , Lee KH (2007a) Preparation of silk sericin seads using LiCl/DMSO solvent and their potential as a drug carrier for oral administration. Fiber Polym 8 470 - 476    DOI : 10.1007/BF02875867
Oh HJ , Lee JY , Kim A , Lee KH , Shin BS (2008) Preparation of PVA/ silk sericin blend fiber using LiCl/DMSO solvent. Text Sci Eng 45 1 - 5
Oh HJ , Lee JY , Lee YK , Lee KH (2007b) Enhanced mechanical property of silk sericin beads prepared from ethanol-precipitated sericin. Int J Indust Entomol 15 171 - 174
Secundo F (2013) Conformational changes of enzymes upon immobilization. Chem Soc Rev 42 6250 - 6261    DOI : 10.1039/c3cs35495d
Yun H , Kim MK , Kwak HW , Lee JY , Kim MH , Kim EH , Lee KH (2013) Preparation and characterization of silk sericin/glycerol/graphene oxide nanocomposite film. Fiber Polym 14 2111 - 2116    DOI : 10.1007/s12221-013-2111-2
Zhang YQ (2002) Applications of natural silk protein sericin in biomaterials. Biotechnol Adv 20 91 - 100    DOI : 10.1016/S0734-9750(02)00003-4