Removal of Perchlorate Using Reverse Osmosis and Nanofiltration Membranes
Removal of Perchlorate Using Reverse Osmosis and Nanofiltration Membranes
Environmental Engineering Research. 2012. Dec, 17(4): 185-190
Copyright ©2012, Korean Society of Environmental Engineering
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : June 06, 2012
  • Accepted : November 11, 2012
  • Published : December 30, 2012
Download
PDF
e-PUB
PubReader
PPT
Export by style
Share
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Jonghun Han
Department of Chemistry and Environmental Sciences, Korea Army Academy at Youngcheon, Youngcheon 770-849, Korea
Choongsik Kong
Beautiful Environment Construction Co., Ltd., Seongnam 462-721, Korea
Jiyong Heo
Department of Civil and Environmental Engineering, University of South Carolina, Columbia, SC 29208, USA
Yeomin Yoon
Department of Civil and Environmental Engineering, University of South Carolina, Columbia, SC 29208, USA
Heebum Lee
Department of Chemistry and Environmental Sciences, Korea Army Academy at Youngcheon, Youngcheon 770-849, Korea
Namguk Her
Department of Chemistry and Environmental Sciences, Korea Army Academy at Youngcheon, Youngcheon 770-849, Korea
namguk@daum.net
Abstract
Rejection characteristics of perchlorate (ClO 4 - ) were examined for commercially available reverse osmosis (RO) and nanofiltration (NF) membranes. A bench-scale dead-end stirred-cell filtration system was employed to determine the toxic ion rejection and the membrane flux. Model water solutions were used to prepare ClO 4 - solutions (approximately, 1,000 μg/L) in the presence of background salts (NaCl, Na 2 SO 4 , and CaCl 2 ) at various pH values (3.5, 7, and 9.5) and solution ionic strengths (0.001, 0.01, and 0.01 M NaCl) in the presence of natural organic matter (NOM). Rejection by the membranes increased with increasing solution pH owing to increasingly negative membrane charge. In addition, the rejection of the target ion by the membranes increased with increasing solution ionic strength. The rejection of ClO 4 - was consistently higher for the RO membrane than for the NF membrane and ClO 4 - rejection followed the order CaCl 2 < NaCl < Na 2 SO 4 at conditions of constant pH and ionic strength for both the RO and NF membranes. The possible influence of NOM on ClO 4 - rejection by the membranes was also explored.
Keywords
1. Introduction
Perchlorate (ClO 4 - ), a highly oxidized (+7) chlorine oxidation, has been widely used as an oxidizer and as an explosive material in military and civilian applications. It has also generated increased interest as an inorganic contaminant in drinking water, groundwater, and surface water. Recently, numerous studies have reported the detection of ClO 4 - at various concentrations (from <1 to >1,000 μg/L) in groundwater, surface water, and drinking water [1 - 10] ; tea and soft drinks [4] ; milk [11] ; saliva [12] ; leafy vegetables [13] ; tobacco plants and tobacco products [14] ; and wastewater effluent [8] . These reports of ClO 4 - in water and food have given rise to serious concerns among regulatory agencies and among the general public. In particular, water contamination by ClO 4 - has become a major environmental and health concern in recent years , as evidence has emerged that the toxicological effects of ClO 4 - are associated with abnormal endocrine function [8 , 15] .
A recent study has shown the presence of ClO 4 - at various concentrations in the range of 0.05–60 μg/L in surface water of South Korea (i.e., river mainstream and tributaries), 0.56–22 μg/L in wastewater treatment plant effluent, and 0.2–35 μg/L in tap water [8] . However, these data in South Korea were fairly limited to the regional dispersion of perchlorate. In a separate study, we presented the following ClO 4 - detection data in South Korea: 1.99–6.41 μg/L (n = 37; mean, 4.59 ± 0.17 μg/L) for 12 different brands of dairy milk and 1.49–33.3 μg/kg (n = 26; mean, 7.83 ± 0.22 μg/kg) for 4 different brands of milk-based infant formula [16] . Those 37 dairy milk and 26 infant formula products constitute over 99% of the dairy milk and infant formula market in South Korea. In addition, among 520 tap-water samples from over 100 different locations in South Korea, ClO 4 - was detected in over 80% of tap-water samples, in concentrations ranging from <1.0 to 6.1 μg/L with a mean concentration of 0.56 μg/L [17] . In the same study, ClO 4 - was also detected in 23 of 48 bottled-water samples, with concentrations ranging from 0.04 to 0.29 μg/L with a mean of 0.07 ± 0.01 μg/L.
The United States Environmental Protection Agency (USEPA) has established an oral reference dose for perchlorate, with a drinking-water equivalent level of 24.5 μg/L [18] , while the Massachusetts Department of Environmental Protection promulgated a 2.0 μg/L drinking-water standard [19] . The California Department of Health Service (CDHS) has recently established an action level of 4 μg/L for ClO 4 - , which, if exceeded, the CDHS advises water utilities to remove drinking water supplies.
The removal of ClO 4 - from drinking water/the exclusion of ClO 4 - from drinking water sources is critical for the protection of human health. Several different technologies have been investigated for the removal of this toxic ion from drinking water sources and/or wastewater, including ion exchange [20] , biological treatment [15 , 21] , and membrane filtration [22 , 23] . Several recent studies have investigated the transport mechanisms of ions such as chromate, arsenate, and ClO 4 - through reverse osmosis (RO), nanofiltration (NF), and ultrafiltration membranes [23 - 26] . These studies have shown that the degree of rejection of inorganic compounds is governed by both size and electrostatic exclusion. However, it is still necessary to investigate the effects of recovery, pH, background ions, and natural organic matter (NOM) on ClO 4 - rejection. Therefore, the objective of this study is to verify the existing mechanisms (i.e., size and electrostatic exclusion) for the rejection of ClO 4 - by RO and NF membranes under various conditions. To accomplish this, the rejection of ClO 4 - was measured at various pH and ionic strength conditions in the presence of co- and counterions such as Cl - , SO 4 2- , Na + , and Ca 2+ in synthetic water or in the presence of NOM.
2. Materials and Methods
- 2.1. Membranes and Testing Unit
ClO 4 - rejection measurements were conducted using commercially available RO (RE8040-UE; Koch Membrane Systems Inc., Wilmington, MA, USA) and NF (TFC-SR3; Woongjin Chemical Co., Ltd., Seoul, Korea) membranes. The properties of the membranes are described in Table 1 . These membranes have ionizable functional groups (e.g., unreacted carboxylic acids) and different membrane pore sizes (assumed from the manufacturer’s nominal molecular weight cut-offs [MWCOs]). As shown in Table 1 , the RO membrane shows a relatively smaller value of high pure water permeability (PWP) than the NF membrane, presumably because permeability is influenced by pore size, pore density (porosity), and thickness. The surface charge of the membranes was estimated by measuring the streaming potential using a commercial electrokinetic analyzer. These membranes have similar hydrophobicity based on their contact angle values.
The experiments were performed in batch mode using a dead-end stirred cell that has been widely used for various membrane filtration studies [27 , 28] . Fig. 1 shows the schematic diagram of the dead-end bench-scale membrane system used in the experiments. Here, a brief description of the stirred cell is provided, the details of which are reported elsewhere [28] . The stirred cell (SEPA ST; GE Osmonics, Minnetonka, MN, USA) is made of stainless steel to improve chemical stability by minimizing unnecessary interactions (e.g., adsorption) between solutes and the cell. The cell has an active filtration area of 18.9 cm 2 and a working volume of 300 mL. All the experiments were conducted under the same operating conditions with a stirring speed of 300
RO and NF membranes and their characteristics, along with measured water flux, zeta potential, and contact anglePolyamide thin film composite for all the membranes.RO: reverse osmosis, NF: nanofiltration, MWCO: molecular weight cut-off, NA: not available.a-cData obtained from the manufacturer.dMeasured at pH 7 and conductivity 30 mS/m with NaCl.eAverage value (3 measurements).
PPT Slide
Lager Image
RO and NF membranes and their characteristics, along with measured water flux, zeta potential, and contact angle Polyamide thin film composite for all the membranes. RO: reverse osmosis, NF: nanofiltration, MWCO: molecular weight cut-off, NA: not available. a-cData obtained from the manufacturer. dMeasured at pH 7 and conductivity 30 mS/m with NaCl. eAverage value (3 measurements).
PPT Slide
Lager Image
Schematic diagram of the dead-end stirred cell testing unit.
rpm, as controlled by a magnetic stirrer, and different working pressures (2,070 kPa for the RO and 1,310 kPa for the NF) for a constant initial pure water flux controlled by a high-pressure nitrogen cylinder and a gas pressure regulator. A fresh membrane was used for each experiment and the membranes were pre-filtered with pure water at a pressure of 690 kPa (100 psi) for further stabilization prior to use. The stability of membrane permeability during the experiment was checked by comparing the pure water flux before and after each experiment. Only data for membranes with permeability changes of less than 5% are presented here.
The weight of the permeate was measured using a balance. The permeate flux is expressed in terms of the percentage of water recovery, defined as the percentage ratio of total permeate volume to initial feed volume. The rejection for species i, Ri , was calculated in the following manner:
PPT Slide
Lager Image
where Ci,p is the permeate solute concentration and Ci,f is the solute concentration in the feed solution. The concentration in the permeate was measured at a recovery of 20%.
- 2.2. Source Waters
Model water solutions were prepared with pure water from a commercial laboratory purification system (Milli-Q water purification system; Millipore, Billerica, MA, USA). The ClO 4 - anion (present at a concentration of 1,000 μg/L) was fed to the membrane test apparatus either as a pure component or in binary mixtures with other salts (NaCl, Na 2 SO 4 , or CaCl 2 ) at various pH values (3.5, 7, and 9.5) buffered by 1 mM sodium bicarbonate at various solution ionic strengths (0.001, 0.01, and 0.1 M). Sodium hydroxide or hydrochloric acid was added to the pure water to adjust the solution pH. In addition, the same procedure was carried out with the addition of NOM, in the form of humic acid (Sigma-Aldrich, St. Louis, MO, USA), to represent the dissolved organic carbon (DOC). Stock solutions of the NOM isolate were filtered using a 0.7 μm pore size Whatman (Kent, UK) GF/F glass microfiber filter prior to use.
- 2.3. Analyses
Determination of the ClO 4 - in samples was conducted using an ion chromatographic-mass spectrometry (IC-MS)/MS method based on EPA Method 332.0. Samples were analyzed using a Dionex ICS-2100 IC dual system (Dionex, Sunnyvale, CA, USA) consisting of a GS50 gradient pump, an Dionex ASRS 300 suppressor (2 mm), and a D26 conductivity detector (CD). A Dionex IonPac AS21 separation column (250 × 2 mm) connected to an IonPac AG21 guard column (50 × 2 mm) was used for separations. A Dionex AS-DV autosampler with 5-mL cartridges were used to inject 100 μL of sample into the IC column. A 15-mM KOH solution with a flow rate of 0.35 mL/min was used as an eluent. Calibration standards of 1 μg/L were run between every approximate 10 samples. MS was performed using an Agilent 6410 triple quadrupole MS (Agilent Technologies, Santa Clara, CA, USA) in the electrospray ionization (ESI) mode. The method detection limit was <0.1 μg/L for IC-MS/MS.
A commercial streaming potential analyzer (electrokinetic apparatus [EKA]; Brookhaven Instruments Corp., Holtsville, NY, USA) was used to measure the membrane surface charge at pH 7.5 and an ionic strength of 0.01 M NaCl. This instrument included an analyzer, a measuring cell, electrodes, and a data control system. We followed the same procedures and used the same EKA to measure streaming potential as described by a previous study [29] . The electrolyte solution was held in a jacketed reservoir kept at constant temperature by water circulating through a temperature controlled bath. External pH and conductivity sensors were placed in the electrolyte reservoir. Conductivity, temperature, pressure, and streaming potential were monitored with internal sensors. For the streaming potential measurements, membrane samples were cut to fit the measurement cell and were then wetted in NaCl solution at the desired pH, and stored in a refrigerator for the soaking time specified in the experimental design. Zeta potential (ZP) was calculated from the measured streaming potential based on the Helmholtz-Smoluchowski relationship with the assumption that the electrolyte solution, with conductivity k -1 ·m -1 ), carries most of the current. A goniometer (Model 100; Rame-Hart Inc., Netcong, NJ, USA) was used to measure the contact angle of the membrane. The rinsed membranes were dried in a desiccator prior to measurement. Membrane samples were cut into small pieces and were mounted on a support. Approximately 20 μL of pure water was placed on the membrane specimen, and the contact angle was measured using a photographic image and appropriate software.
PPT Slide
Lager Image
Comparison of ClO4- removal on reverse osmosis (RO) and nanofiltration (NF) membranes. Operating conditions: Co, 1,000 μg/L; pH, 7.0; NaCl, 0.01 M; natural organic matter, 3 mg/L. ●, RO; ▼, NF.
3. Results and Discussion
- 3.1. Effect of Recovery on Flux Decline and ClO4-Rejection
Recovery, a hydrodynamic operating parameter, was studied to determine its effects on perchlorate rejection and flux decline. Fig. 2 represents the effects of recovery on flux decline and perchlorate rejection at varying recoveries ranging from 10% to 90%. Under the specified operational conditions, the membranes showed different flux declines of 0.7–39.1% for the RO and 1.6– 58.9% for the NF membrane in Fig. 2 (a). The decrease in rejection with increasing recovery can be primarily attributed to concentration polarization. As shown in Fig. 2 (b), rejection trends generally decrease with increasing recovery, which is in accordance with the expectation that higher recoveries increase the product stream (permeate) and reduce the rejection stream (retention). The RO membrane showed a greater rejection of ClO 4 - (73–96%) than that of the NF membrane (39–82%). This is presumably because solute transport was dominated by the solution diffusion mechanism for the RO membrane, while steric/size and electrostatic exclusion mechanisms governed solute transport for the NF membrane [30] . Membrane surface charge was measured to predict ClO 4 - transport through the RO and NF membranes. Several qualitative predictions for the transport of this ion can be made from characterizations with the streaming potential measurements. The rejection of ClO 4 - may 1) increase with increasing pH owing to the increasingly negative membrane charge, 2) decrease in the presence of divalent counterions (Ca 2+ ) because of a less negative membrane charge, 3) decrease with increasing solution ionic strength owing to the decreasingly negative membrane charge, or 4) increase in the presence of NOM because of the increasingly negative membrane charge.
PPT Slide
Lager Image
Comparison of ClO4- removal on reverse osmosis (RO) and nanofiltration (NF) membranes at different pH. Operating conditions: Co, 1,000 μg/L; recovery, 20%; NaCl, 0.01 M; natural organic matter, 3 mg/L. ●, RO; ▼, NF.
- 3.2. Effect of Solution pH
Measurements of ClO 4 - rejection by the RO and NF membranes were made at various pH values at a recovery of 20% in the presence of 3 mg/L NOM. The rejection of ClO 4 - is plotted as a function of pH at a constant ionic strength of 0.01 M NaCl ( Fig. 3 ). In general, the rejection of ions by the membranes is dependent on the solution pH. A general trend of increased rejection of ClO 4 - was observed as the solution pH increased from 3.5 to 9.5. This effect is possibly attributable to adsorption of OH - in the inner plane at the membrane surface [31] or a greater degree of dissociation of fixed ionizable functional groups in the membrane. These results can also be explained by electrostatic exclusion since the membrane charge would become more negative with increasing pH resulting in increased electrostatic repulsion between the target ion and the membranes, thus increasing ion rejection. For the target toxic ion, the RO membrane, with a smaller pore size, exhibited higher rejection (88–91%) than the NF membrane, indicating that size exclusion is at least partially responsible for rejection. The rejection of ClO 4 - was 70–83% lower for the NF membrane with a relatively larger pore size, depending on the pH of the solution.
- 3.3. Effect of Mono- and Divalent Co- and Counterions and Ionic Strength
The effects of background ions and ionic strength on ClO 4 - rejection by both RO and NF membranes were determined using an ideal water model and a ClO 4 - concentration of 1,000 μg/L, using three different salts (NaCl, Na 2 SO 4 , and CaCl 2 ) as the primary background electrolyte at a constant pH of 7, and varying the ionic strength. The results are shown in Fig. 4 . Rejection of ClO 4 - follows the order CaCl 2 < NaCl < Na 2 SO 4 under conditions of constant pH and varying ionic strength for the RO and NF membranes tested. The RO membrane showed higher rejections (84–96%) than the NF membrane (66–94%) for all background ion and ionic strength conditionsn of ClO 4 - was lower in solutions containing CaCl 2 (divalent Ca 2+ ) than in those with NaCl and Na 2 SO 4 (monovalent Na + ) for both membranes. This is presumably because in terms of electrostatic interactions, Ca 2+ binding causes the absolute value of the membrane’s surface
PPT Slide
Lager Image
Comparison of ClO4- removal on reverse osmosis (RO) and nanofiltration (NF) membranes at different ionic strengths and background ion concentrations. Operating conditions: Co, 1,000 μg/L; pH, 7.0; recovery, 20%; natural organic matter, 3 mg/L. ●, RO+NaCl; ■, RO+Na2SO4; ▼, RO+CaCl2; ○, NF+NaCl; □, NF+Na2SO4; △, NF+CaCl2.
charge to decrease significantly [30] . The rejection of perchlorate by NF membrane in the presence of NaSO 4 was higher than RO membrane in the presence of CaCl 2 or NaCl at an ion concentration of 0.1 M. This result indicates that the electrostatic repulsion effect is stronger than the sieving effect on the rejection of perchlorate at a certain ion concentration condition. When dilute solutions containing Cl - or SO 4 2- anions are brought in contact with a membrane possessing a fixed negative charge, Donnan exclusion shows that the rejection of chloride and sulfate may be greater than if the membrane were completely uncharged [32] . In addition, it was mentioned earlier that Ca 2+ binding screens the co-ion adsorption; when charge screening by Ca 2+ occurs for the negatively charged membranes, anion rejection is significantly reduced. The background ion concentration at the membrane interface influences further Donnan exclusion (e.g., greater exclusion at low ion concentrations and high pH in the presence of more divalent anions). The rejection of ClO 4 - is also plotted as a function of ionic strength (0.001, 0.01, and 0.1 M) in Fig. 4 , which shows that the rejection of ClO 4 - increases with increasing solution ionic strength for both membranes. The results are inconsistent with the previous prediction that the rejection of ClO 4 - may decrease with increasing ionic strength of the solution, owing to the decreasingly negative membrane charge. This is presumably because background anion adsorption (Cl - and SO 4 2- ) occurring in the inner plane at the membrane surface is dominant, resulting in an increase in membrane negative charge under conditions of increased ionic strength.
- 3.4. Effect of NOM
Fig. 5 shows the effect of increased concentrations of NOM (3, 10, and 30 mg/L DOC) on the rejection of ClO 4 - at pH 7 and an ionic strength of 0.01 M NaCl for the RO and NF membranes. The NOM found in the natural water samples represents mediummolecular- weight NOM and is somewhat hydrophobic, based on its low specific UVA254 value. In general, humic acids are dominant in surface water. In general, the RO membrane exhibited a higher ClO 4 - rejection (90–96%) than the NF membrane (80–90%) at the various NOM concentrations determined. Alteration of the
PPT Slide
Lager Image
Comparison of ClO4- removal on reverse osmosis (RO) and nanofiltration (NF) membranes at different natural organic matter (NOM) concentrations. Operating conditions: Co, 1,000 μg/L; pH, 7.0; recovery, 20%; NaCl, 0.01 M. ●, RO; ▼, NF.
concentration of NOM had a significant effect on rejection; this may be as a result of the nature of NOM, which has various hydroxyl and carboxyl groups. Two assumptions were made to explain these results. It may be due to co-rejection of ClO 4 - with humic materials improving ClO 4 - rejection. Humic substances play a major role in the behavior and mobility of metals in aquatic environments. NOM is comprised of a range of organic materials, with average molecular weights of 1,000–10,000 Da [33] . Several studies have indicated a possible association between humic substances and ions/metals [34 , 35] . It was also assumed that once the membranes are fouled owing to the presence of NOM, the membranes become more negative, and this increases the electrostatic repulsion between ClO 4 - and the negatively charged membranes. In addition, more ClO 4 - complexes are produced at higher concentrations of humic acid. Therefore, the size of the complexes may be larger than the RO and NF membrane pores, which increases the rejection of ClO 4 - .
4. Conclusions
In this study, RO and NF membranes were tested to determine rejection rates of the toxic perchlorate anion. Rejection of ClO 4 - by the negatively charged RO and NF membranes was significantly greater than expected, based exclusively on steric/size exclusion because of electrostatic repulsion under all conditions with varying pH values, background ions, and NOM. The results also show that rejection of ClO 4 - by the negatively charged RO and NF membranes is significantly influenced by solution pH, possibly because membrane surface charge becomes more negative with increasing solution pH, thereby enhancing ClO 4 - rejection. The rejection of ClO 4 - increases with increasing solution ionic strength for the membranes, presumably because of an increase of electrostatic repulsion with increasing background anions such as Cl - and SO 4 2- . Furthermore, it is presumed that the presence of NOM resulted in an increase of ClO 4 - rejection since the membranes become more negatively charged and their pores become smaller in its presence.
Acknowledgements
The authors thank the Agency for Defense Development in South Korea (Project No. UC1000051D) for financial support.
References
Rajagopalan S , Anderson TA , Fahlquist L , Rainwater KA , Ridley M , Jackson WA 2006 Widespread presence of naturally occurring perchlorate in high plains of Texas and New Mexico Environ. Sci. Technol 40 3156 - 3162
Kannan K , Praamsma ML , Oldi JF , Kunisue T , Sinha RK 2009 Occurrence of perchlorate in drinking water, groundwater, surface water and human saliva from India Chemosphere 76 22 - 26
Wagner HP , Pepich BV , Pohl C 2007 Selective method for the analysis of perchlorate in drinking waters at nanogram per liter levels, using two-dimensional ion chromatography with suppressed conductivity detection J. Chromatogr. A 1155 15 - 21
Asami A , Kosaka K , Yoshida N 2009 Occurrence of chlorate and perchlorate in bottled beverages in Japan J. Health Sci. 55 549 - 553
Crawford-Brown D , Raucher B , Harrod M 2006 Intersubject variability of risk from perchlorate in community water supplies Environ. Health Perspect 114 975 - 979
Kimbrough DE , Parekh P 2007 Occurrence and co-occurrence of perchlorate and nitrate in California drinking water sources J. Am. Water Works Assoc 99 126 - 132
Kosaka K , Asami M , Matsuoka Y , Kamoshita M , Kunikane S 2007 Occurrence of perchlorate in drinking water sources of metropolitan area in Japan Water Res 41 3474 - 3482
Quinones O , Oh JE , Vanderford B , Kim JH , Cho J , Snyder SA 2007 Perchlorate assessment of the Nakdong and Yeongsan watersheds, Republic of Korea Environ. Toxicol. Chem 26 1349 - 1354
Snyder SA , Vanderford BJ , Rexing DJ 2005 Trace analysis of bromate, chlorate, iodate, and perchlorate in natural and bottled waters Environ. Sci. Technol 39 4586 - 4593
Stetson SJ , Wanty RB , Helsel DR , Kalkhoff SJ , Macalady DL 2006 Stability of low levels of perchlorate in drinking water and natural water samples Anal. Chim. Acta 567 108 - 113
Dyke JV , Ito K , Obitsu T , Hisamatsu Y , Dasgupta PK , Blount BC 2007 Perchlorate in dairy milk: comparison of Japan versus the United States Environ. Sci. Technol 41 88 - 92
Oldi JF , Kannan K 2009 Analysis of perchlorate in human saliva by liquid chromatography-tandem mass spectrometry Environ. Sci. Technol 43 142 - 147
Sanchez CA , Crump KS , Krieger RI , Khandaker NR , Gibbs JP 2005 Perchlorate and nitrate in leafy vegetables of North America Environ. Sci. Technol 39 9391 - 9397
Andrew Jackson W , Anandam SK , Anderson T 2005 Perchlorate occurrence in the Texas southern high plains aquifer system Ground Water Monit. Remediat 25 137 - 149
Srinivasan A , Viraraghavan T 2009 Perchlorate: health effects and technologies for its removal from water resources Int. J. Environ. Res. Public Health 6 1418 - 1442
Her N , Kim J , Yoon Y 2010 Perchlorate in dairy milk and milkbased powdered infant formula in South Korea Chemosphere 81 732 - 737
Her N , Jeong H , Kim J , Yoon Y 2011 Occurrence of perchlorate in drinking water and seawater in South Korea Arch. Environ. Contam. Toxicol 61 166 - 172
US National Research Council 2005 Health implications of perchlorate ingestion National Research Council Washington
US Environmental Protection Agency c2012 Technical fact sheets: FFRRO contaminants of concern US Environmental Protection Agency Washington Available from: http://www.epa.gov/fedfac/documents/emerging_contaminants.htm#perchlorate
Crittenden JC , Sanongraj S , Bulloch JL 1999 Correlation of aqueous-phase adsorption isotherms Environ. Sci. Technol 33 2926 - 2933
Logan BE , Wu J , Unz RF 2001 Biological perchlorate reduction in high-salinity solutions Water Res 35 3034 - 3038
Yoon J , Amy G , Chung J , Sohn J , Yoon Y 2009 Removal of toxic ions (chromate, arsenate, and perchlorate) using reverse osmosis, nanofiltration, and ultrafiltration membranes Chemosphere 77 228 - 235
Yoon J , Yoon Y , Amy G , Cho J , Foss D , Kim TH 2003 Use of surfactant modified ultrafiltration for perchlorate (Cl(O)(4-)) removal Water Res 37 2001 - 2012
Brandhuber P , Clark S , Morley K 2009 A review of perchlorate occurrence in public drinking water systems J. Am. Water Works Assoc 101 63 - 73
Ergican E , Gecol H , Fuchs A 2005 The effect of co-occurring inorganic solutes on the removal of arsenic (V) from water using cationic surfactant micelles and an ultrafiltration membrane Desalination 181 9 - 26
Muthukrishnan M , Guha BK 2008 Effect of pH on rejection of hexavalent chromium by nanofiltration Desalination 219 171 - 178
Lee S , Lueptow RM 2001 Reverse osmosis filtration for space mission wastewater: membrane properties and operating conditions J. Memb. Sci 182 77 - 90
Yoon Y , Lueptow RM 2005 Removal of organic contaminants by RO and NF membranes J. Memb. Sci 261 76 - 86
Chapman Wilbert M , Delagah S , Pellegrino J 1999 Variance of streaming potential measurements J. Memb. Sci 161 247 - 261
Yoon J , Yoon Y , Amy G , Her N 2005 Determination of perchlorate rejection and associated inorganic fouling (scaling) for reverse osmosis and nanofiltration membranes under various operating conditions J. Environ. Eng 131 726 - 733
Elimelech M , O’Melia CR 1990 Effect of electrolyte type on the electrophoretic mobility of polystyrene latex colloids Colloids Surf 44 165 - 178
Yoon YM , Amy G , Cho JW , Pellegrino J 2004 Systematic benchscale assessment of perchlorate (ClO4-) rejection mechanisms by nanotiltration and ultrafiltration membranes Sep. Sci. Technol 39 2105 - 2135
Westerhoff P , Aiken G , Amy G , Debroux J 1999 Relationships between the structure of natural organic matter and its reactivity towards molecular ozone and hydroxyl radicals Water Res 33 2265 - 2276
Baalousha M 2009 Aggregation and disaggregation of iron oxide nanoparticles: influence of particle concentration, pH and natural organic matter Sci. Total Environ 407 2093 - 2101
Tessier A , Fortin D , Belzile N , DeVitre RR , Leppard GG 1996 Metal sorption to diagenetic iron and manganese oxyhydroxides and associated organic matter: narrowing the gap between field and laboratory measurements. Geochim. Cosmochim. Acta 60 387 - 404