Sorbent Characteristics of Montmorillonite for Ni<sup>2+</sup>Removal from Aqueous Solution
Sorbent Characteristics of Montmorillonite for Ni2+Removal from Aqueous Solution
Environmental Engineering Research. 2009. Mar, 14(1): 26-31
Copyright ©2009, Korean Society of Environmental Engineering
  • Received :
  • Published : March 31, 2009
Export by style
Cited by
About the Authors
Christianah Olakitan, Ijagbemi
Dong-Su, Kim

Sorption of Ni 2+ in aqueous solution was studied using montmorillonite. The experimental and equilibrium data fitted well to the Langmuir isotherm model. From the kinetics data for nickel sorption onto montmorillonite, the diffusion of Ni 2+ inside the clay particles was the dorminant step controlling the sorption rate and as such more important for Ni 2+ sorption than the external mass transfer. Ni 2+ was sorbed due to strong interactions with the active sites of the sorbent and the sorption process tends to follow the pseudo second-order kinetics. Thermodynamic parameters (ΔG ° , Δ H ° , and ΔS ° ) indicated a non spontaneous and endothermic adsorption process while the positive low value of the entropy change suggests low randomness of the solid/solution interface during the uptake of Ni 2+ by montmorilionite. Heavy metals such as Ni 2+ in aqueous bodies can effectively be sorbed by montmorillonite.
1. Introduction
Recovery of heavy metals from wastewaters and industrial wastes has become a very important environmental issue. Nickel has many useful applications in our life and equally harmful if discharged in appreciable quantities into natural water resources. 1) Ni 2+ is present in the effluents of silver refineries, electroplating, zinc base casting and storage battery industries. The acceptable limit of Ni 2+ in drinking water is 0.01 mg/L and 2.0 mg/L as industrial wastewater discharge. At higher concentrations, Ni 2+ can cause cancer of the lungs, nose and bone. Dermatitis- Ni itch which may occur as a result of contact with coins and costume jewelries is one of the most frequent effects of exposure to Ni 2+ . Ni carbonyl [Ni(CO) 4 ] has been estimated as lethal in humans at atmospheric exposures of 30 ppm for 30 min. 3) Acute poisoning of Ni 2+ causes headache, dizziness, nausea and vomiting, chest pain, tightness of the chest, dry cough and shortness of breath, rapid respiration, cyanosis and extreme weakness. 1 , 2) Hence, it is essential to remove Ni 2+ from industrial wastewaters before it pollutes natural water sources. Conventional methods for removal of Ni 2+ from wastewaters include chemical precipitation, ion exchange, adsorption unto activated carbon, filtration, chemical reduction, and electrodeposition. 4) Due to operational demerits and high cost of heavy metal treatment, some new technologies have been tried in recent times with less expensive adsorbents such as rice hull, 5) sphagnum peat 6) and chlorella vulgaris . 7) The adsorption of Cd 2+ , Zn 2+ , Pb 2+ onto natural clays have been studied and owing to the crystalchemical features of montmorillonite, heavy metal retention by this mineral can occur by adsorption and/or cation exchange reaction. The ability of montmorillonite, to adsorb heavy metal ions from water is significant for the removal of toxic pollutants from the environment.
Sorption characteristics of Ni 2+ onto montmorillonite and evaluation of the clay’s potentialities as sorbent material for removal of Ni 2+ from aqueous solution is the focus of this study. From batch adsorption studies, effects of pH, clay dosage, and concentration on Ni 2+ adsorption unto montmorillonite were investigated. Equilibrium studies relating to kinetics, adsorption isotherms and thermodynamics were as well experimentally conducted.
2. Experimental Methods
- 2.1. Adsorbent
Analytical grade of montmorillonite was purchased from Aldrich Chemicals. Clay fraction passed through a 150 μm sieve was used as received, unwashed powder. Its surface area as determined by the EGME method 8) was found to be 699 m 2 /g and from an extraction method with ammonium acetate, a CEC of 89 meq/100g was obtained.
- 2.2. Adsorbate
Stock solution of 1000 mg/L of Ni 2+ was prepared by dissolving 4.960 g of ultra pure Ni(NO 3 ) 2 . 6H 2 O in a double distilled water, acidified with nitric acid to prevent hydrolysis. All the solutions were made with double distilled water.
- 2.3. Adsorption Studies
Batch adsorption studies were conducted. Adsorption kinetics were carried out using 50 mL of metal ion solution containing the desired concentration (50-300 mg/L) at a pH of 5.5 with 1 g of adsorbent in 100 mL conical flasks agitated at 200 rpm inside a rotary shaker (25±1℃). Samples were separated by fast filtration and analyzed by Flame atomic absorption spectrometer. Studies on adsorption kinetics were carried out using different initial Ni 2+ concentrations with 1g of adsorbent dosage in 50 mL solution. 0.1 N of HCl and 0.1 N of NaOH were used to adjust the pH. The effect of hydrogen ion concentration was examined from solutions at pH ranging from 2.3 to 9.2, Ni 2+ removal was studied in the range of 2.5-9.0.
3. Result and Discussion
- 3.1. Effects of pH
Fig. 1 summarizes the sorption of Ni 2+ onto montmorillonite particles at various pH values. The maximum removal was achieved at pH values around 7-9 due to the nature of the chemical interactions of the metal ion with the montmorillonite surface. At pH above 9, Ni 2+ precipitates. Montmorillonite surface contains several different active sites 4) and metal ion removal depends on these active sites as well as on the nature of the metal ions in the solution. Greater number of negatively charged groups on montmorillonite favours electrostatic interactions between cationic species, and this negative charge may be responsible for metal binding. However, as the pH is lowered, hydrogen ions compete with metal ions for the sorption sites in the sorbent; the overall surface charge on the particles becomes positive and hinds the binding of positively charged metal ions (Ni 2+ ). Hydrogen ion concentration affects not only active sites dissociation, but also the metal speciation. Hydrolysis products of metal cations can also be investigated as metal cations at around pH 5 would be expected to interact with the negatively charged binding sites of montmorillonite. 9- 12)
- 3.2. Clay Dosage
Fig. 2 shows the adsorption of Ni 2+ as a function of clay dosage. Increase in montmorillonite dosage increased the adsorption of Ni 2+ , this may be attributed to availability of more func-
PPT Slide
Lager Image
Change in residual concentration of Ni2+ solution according to pH (amount of adsorbent: 1g; 25℃; 200 rpm; metal ion [Ni] = 100 mg/L).
PPT Slide
Lager Image
Variation of the adsorption of Ni2+ onto montmorillonite according to sorbent dosage (25℃; 200 rpm; pH∼5.5; metal ion [Ni] = 100 mg/L).
tional groups as well as active sites for adsorption. Large numberof sites were available for each fixed concentration of sorbatehence the increase in extent of adsorption.
- 3.3. Adsorption Kinetics (effect of contact time and initial metal ion concentration)
Solute uptake rate, governing residence time of sorption reactions is one of the important characteristics in defining sorption efficiency. The effect of agitation time and initial Ni 2+ concentration on adsorption is presented in Fig. 3 with the equilibrium time selected as the agitation time for the batch experiments. The progressive increase in adsorption and consequently the attainment of equilibrium adsorption may be due to limited mass transfer of the adsorbate molecules from the bulk liquid to the external surface of montmorillonite initially, and subsequently by slower internal mass transfer within the montmorillonite particles. Similar trends were also observed for polyvinyl alcohol adsorption onto montmorillonite. 13) Sorption kinetic was analyzed employing two models, first, using Lagergren equation, which allows the estimation of the adsorption rate k 1 (min -1 ) according to 14) :
PPT Slide
Lager Image
Changes in residual concentration of Ni2+ according to adsorption time for various Ni2+ concentrations.
PPT Slide
Lager Image
where, q is the amount adsorbed at any time t (mg/g), q e is the amount adsorbed at equilibrium time (mg/g), k 1 is the adsorption rate constant (min -1 ). Linear plots of log ( q e - q ) versus t (plot not shown) shows a poor applicability of Lagergren equation for montmorillonite, the k 1 values at different initial metal ion concentrations were calculated from slope of the plots and presented in Table 1 .
The pseudo-second-order model was equally applied using 14) :
PPT Slide
Lager Image
where t (min) is the contact time, q (mg/g) and q e (mg/g) the amount of metal ions sorbed at any time t and at equilibrium and k 2 (g/mg/min) is the pseudo-second-order rate constant. The second-order sorption rate constant k 2 and q e values were determined from the slopes and intercepts of the plots and were presented in Table 1 . The correlation coefficients (R 2 ), shown in Table 1 , are indications of the strength of the linear relationship, showing R 2 values greater than 0.98. Theoretical q e values agree well with the experimental qe values, suggesting that the sorption of Ni 2+ onto montmorillonite tends to follow the secondorder kinetics. Therefore, the rate-limiting step may be chemical sorption or chemisorption through sharing or exchange of electrons electrons between sorbent and adsorbate. Previous authors have reported that the sorption kinetics of Ni 2+ follows a pseudosecond- order reaction rate. 14) It was also noted that the pseudosecond- order rate constant ( k 2 ), decreased with increase in Ni 2+ concentration. As shown in Table 1 , the value of k 2 reduced from 0.305 to 0.175 g/mg/min as the initial montmorillonite concentration increased from 50 to 300 mg/L. This varying trend of pseudo- second order rate constant resulting from the model fitting was in good agreement with the experimental Ni 2+ adsorption kinetics, in which the time required for the equilibrium adsorption monotonically increased with increase in initial Ni 2+ concentration (Fig. 3) .
- 3.4. Adsorption Mechanisms
It is always important to predict the rate-limiting step in an adsorption process in order to understand the mechanism associated with the phenomena. For a solid liquid sorption process, the solute transfer may be characterized by an external mass transfer, intraparticle diffusion or by both transport phenomena. Three types of mechanisms are involved in adsorption process 15) : the film diffusion, which involves the movement of adsorbate molecules from the bulk of the solution towards the external surface of the adsorbent; the particle diffusion, where the adsorbate molecules move and being sorbed in the interior of the adsorbent particles; retention on active sites through sorption, complexation or intraparticle precipitation. Of the three steps, the third step is assumed to be very fast and hence considered negligible. Therefore for design purposes, it is required to clearly distinguish between film diffusion and particle diffusion in order to establish identify the slowest step in the adsorption process. Intraparticle diffusion is characterized by the relationship between specific sorption ( q ) and the square root of time 16 according to Equation 3
PPT Slide
Lager Image
where m is the mass of sorbent (g), q the amount of solute adsorbed at time t (mg/g) and K i is the initial rate of intraparticle diffusion (mg/Lsec -1/2 ). From Fig. 4 , the rate constant of intraparticle diffusion K i was determined by plotting q (mg/g) as a function of the square root of the time. 17)
Fig. 4 shows a non-linear distribution of points, with two separate portions of a curve and a linear plot for the sorption process and as such indicating the existence of intraparticle dif
Kinetic parameters for Ni2+uptake by montmorillonite at different concentrations
PPT Slide
Lager Image
Kinetic parameters for Ni2+ uptake by montmorillonite at different concentrations
PPT Slide
Lager Image
Equilibrium sorption for Ni2+ onto montmorillonite as a function of time-rate constant of intraparticle diffusion determination (metal ion: 100 mg/L; clay dosage:1g ; pH ∼ 5.5; T: 25 ± 1℃).
PPT Slide
Lager Image
Boyd plot for the adsorption of Ni2+ onto montmorillonite (metal ion: 100 mg/L; m: 1g; pH ∼ 5.5; T: 25 ± 1℃).
fusion process. According to the intraparticle diffusion model, if a plot of the amount of sorbate adsorbed per unit weight of sorbent, q , versus square root of contact time gives a linear plot, it indicates that intraparticle/pore diffusion is the rate limiting step in the adsorption process. The plot obtained in Fig. 4 contrasted the prediction of the intraparticle diffusion model. This indicates that intraparticle/pore diffusion is not the singular rate limiting step in the adsorption process. The first part is attributed to boundary layer (film) diffusion, the second to the intraparticle diffusion and chemical reaction in the sorption process and as such indicating the existence of intraparticle diffusion process. Due to the step by step nature of this plot, the linear portion was linearized. The second linear portion indicates the existence of intraparticle diffusion in the process. The intraparticle diffusion coefficient D i was determined by plotting log[1 - ( q/qe ) 2 ] against time (Fig. 5) , according to Urano and Tachikawa model. 18) If the plots are linear and pass through the origin, then the slowest (rate controlling) step in the adsorption process is the internal diffusion, and vice versa. From Fig. 5 , it was observed that the plot was linear but do not pass through the origin.
- 3.5. Adsorption Isotherms
The Langmuir model was originally developed to represent chemisorption on a set of well-defined localized adsorption sites independent of surface coverage; having the same adsorption energy; and with no interaction between adsorbed molecules. This model, also called as the ideal localized monolayer model, is valid for monolayer sorption onto a surface with a finite number of identical sites 19) and is given by Equation 4
PPT Slide
Lager Image
where Q o is a constant related to the area occupied by a monolayer of adsorbate, reflecting the maximum adsorption capacity (mg/g), C e is the equilibrium liquid-phase concentration (mg/L), KL is a direct measure of the intensity of adsorption (L/mg) and q e is the amount adsorbed at equilibrium (mg/g).This equation can be linearized as follows 19) :
PPT Slide
Lager Image
From the data of 1/ q e versus 1/ C e , K L and Q o can be determined from the slope and intercept.
The Freundlich adsorption isotherm usually fits the experimental data over a wide range of concentrations. This empirical expression encompasses the surface heterogeneity and exponential distribution of the active sites and their energies. The widely used empirical Freundlich equation based on sorption on a heterogeneous surface 19) is given by Equation 6
PPT Slide
Lager Image
where K F ((mg/g)(L/mg) 1/n ) and n (dimensionless) are constants incorporating all factors affecting the adsorption process such as adsorption capacity and intensity, respectively. This equation can be linearized as follows 19) :
PPT Slide
Lager Image
The values of n and K F were calculated from the slope and intercept of the plot of log q e versus log C e .On the basis of correlation coefficient, R 2 . Applicability of the isotherm equations was compared (Table 2) . It was clear that the Langmuir model yields a better fit than the Freundlich model for the adsorption of Ni 2+ onto montmorillonite.
Freundlich and Langmuir parameters for Ni2+sorption
PPT Slide
Lager Image
Freundlich and Langmuir parameters for Ni2+ sorption
- 3.6. Thermodynamic Parameters
The thermodynamic parameters for the adsorption process, Δ H ° and Δ S ° , were evaluated using the Van’t Hoff equation:
PPT Slide
Lager Image
The values of log K N were defined as follow:
PPT Slide
Lager Image
where ΔS ° and ΔH ° are entropy (kJ/mol K) and enthalpy (kJ/mol) change of adsorption, respectively, R is universal gas constant (8.314 J/mol K), and T is the absolute temperature (K). K N is the equilibrium constant and f is uptake percentage of adsorbate at equilibrium. The values of ΔH ° and ΔS ° were calculated from the slope and intercept of linear regression of ln K N versus (1/ T ). The values of Δ G ° were estimated by Equation 10
PPT Slide
Lager Image
The plot shown in Fig. 6 for Ni 2+ was linear at the range of temperature investigated. The calculated thermodynamic parameters such as ΔH ° , ΔS ° and ΔG ° are given in Table 3 . The positive values of ΔG ° indicate that the sorption of Ni 2+ onto montmorillonite is not a spontaneous process. The change in enthalpy (Δ H ° ) values is positive, showing that the sorption of Ni 2+ is endothermic in nature, ions uptake increased with increase in temperature. The sorption of Ni 2+ also requires a diffusion process, which is an endothermic process; i.e., increase in
PPT Slide
Lager Image
Plot of lnK vs 1/T for Ni2+ sorption unto montmorillonite.
Thermodynamic parameters for Ni2+uptake
PPT Slide
Lager Image
Thermodynamic parameters for Ni2+ uptake
temperature favors adsorbate transport within the particles of the adsorbent. The positive low values of ΔS ° indicate low randomness at the solid/solution interface during the uptake of Ni 2+ by montmorillonite.
4. Conclusion
Adsorption characteristics of Ni 2+ onto montmorillonite and the potential use of montmorillonite as sorbent material for Ni 2+ have been studied. Nickel as representative of heavy metals is chosen for this study as it is present in effluents of many industries. Ni 2+ was sorbed due to strong interactions with the active sites of the sorbent. Montmorillonite was able to remove Ni 2+ from aqueous solutions and the equilibrium experimental data fitted well to Langmuir than the Freundlich isotherm model. The pseudo first- order and pseudo-second-order models were employed to fit the adsorption kinetics and as such the adsorption of Ni 2+ onto montmorillonite followed the pseudo-secondorder kinetics. Diffusion of Ni 2+ inside the clay particle was confirmed as the rate-controlling step and more important for Ni 2+ adsorption rate than the external mass transfer. Thermodynamic parameters (Δ G ° , Δ H ° , and Δ S ° ) were determined and their values indicated that the adsorption process was not spontaneous, but endothermic in nature, with a low positive value for the entropy change. This study shows that montmorillonite can be used as an effective and favorable adsorbent for the removal of Ni 2+ and other heavy metals from aqueous solutions.
C e : equilibrium concentration of solution (mg/L)
ΔG ° : change in Gibb’s free energy of adsorption (kJ/mol)
ΔH ° : change in enthalpy of adsorption (kJ/mol)
ΔS ° : change in entropy of adsorption (kJ/mol K)
K F : Freundlich isotherm constant related to adsorption capacity ((mg/g)(L/mg) 1/n )
K L : intensity of adsorption (L/mg)
m : clay mass (g)
n : Freundlich isotherm constant related to adsorption intensity
q : amount of heavy metal adsorbed at time t (mg/g)
q e : amount of adsorbed heavy metal per unit clay mass (mg/g)
Q o : maximum adsorption capacity (mg/g)
R 2 : correlation coefficient
R : gas constant (Jmol/K)
V : volume of solution (L)
K N : Van’t Hoff equilibrium constant
f : uptake percentage of adsorbate at equilibrium.
T : absolute temperature (K)
t : time (min)
This work was supported by the Korea Science and Engineering Foundation (KOSEF) grant funded by the Korean Government. The support of the Ewha Womans University Exchange Program towards this research work is sincerely appreciated by the authors.
Parker S.P 1980 Encyclopedia of environmental science 2nd ed McGraw Hill New York
ATSDR 1997 Toxicological profile for nickel US Department of health and human services US Government printing office
Beliles R.P , Ed , Oehme F.W , Ed 1979 The lesser metals;Toxicityof heavy metals in the environment Marcel Dekker New York Ed Part 2 547 - 616
Lin S.H , Juang R.S 2002 Heavy metal removal from water by sorption using surfactant-modified montmorillonite Journal of Hazardous Materials 92 (3) 315 - 326    DOI : 10.1016/S0304-3894(02)00026-2
Oliveira E.A , Montanher S.F , Andrade A.D , Nobrega J.A , Rollemberg M.C 2005 Equilibrum studies for the sorption of chromium and nickel from aqueous solutions using raw rice bran Process Biochemistry 40 (11) 3485 - 3490    DOI : 10.1016/j.procbio.2005.02.026
Ho Y.S , McKay G 2000 The kinetics of sorption of divalent metal ions onto sphagnum moss peat Water Research 34 (3) 735 - 742    DOI : 10.1016/S0043-1354(99)00232-8
Aksu Z 2002 Determination of the equilibrium kinetic and thermodynamic parameters of the batch biosorption of nickel(II) ions onto chlorella vulgaris Process Biochemistry 38 89 - 99    DOI : 10.1016/S0032-9592(02)00051-1
Sparks D.L 1995 Environmental soil chemistry Academic Press San Diego 42 -
Benyahya L , Garnier J.M 1999 Effect of salicylic acidupon trace-metal sorption (CdIIZnIICoIIand MnII) onto alumina silica and kaolinite as a function of pH Environmental Science & Technology 33 (9) 1398 - 1407    DOI : 10.1021/es980509i
Kraepiel A.M.L , Keller K , Morel F.M.M 1999 A Model for Metal Adsorption on Montmorillonite Journal of Colloid and Interface Science 210 (1) 43 - 54    DOI : 10.1006/jcis.1998.5947
Ikhsan J , Wells J.D , Johnson B.B , Angove M.J 2005 Surface complexation modeling of the sorption of Zn(II) by montmorillonite Colloids and Surfaces A Physicochemical and Engineering Aspects 252 (1) 33 - 41    DOI : 10.1016/j.colsurfa.2004.10.011
Avena M.J , De Pauli C.P 1998 Proton Adsorption and Electrokinetics of an Argentinean Montmorillonite Journal of Colloid and Interface Science 202 (1) 195 - 204    DOI : 10.1006/jcis.1998.5402
de Bussetti S.G , Ferreiro E.A 2004 Adsorption of poly(vinyl alcohol) on montmorillonite Clays and Clay Minerals 52 (3) 334 - 340    DOI : 10.1346/CCMN.2004.0520308
Ho Y.S , McKay G 1999 Pseudo-second order model for sorption process Process Biochemistry 34 (5) 451 - 465    DOI : 10.1016/S0032-9592(98)00112-5
Behera S.K , Kim J.H , Guo X , Park H.S 2008 Adsorption equilibrium and kinetics of polyvinyl alcohol from aqueous solution on powdered activated carbon Journal of Hazardous Materials 153 (3) 1207 - 1214    DOI : 10.1016/j.jhazmat.2007.09.117
Ho Y.S , Wase D.A.J , Forster C.F 1996 Pseudo-second order model for sorption processes Environmental Technology 17 (1) 71 - 77    DOI : 10.1080/09593331708616362
McKay G , Poots V.J.P 1980 Kinetics and diffusionprocess in color removal from effluent using wood as an adsorbent Journal of Chemical Technology & Biotechnology 30 279 - 292
Urano K , Tachikawa H 1991 Process development for removal and recovery of phosphorus from wastewater by a new adsorbent II Adsorption rates and breakthrough curves Industrial & Engineering Chemistry Research 30 (8) 1897 - 1899    DOI : 10.1021/ie00056a033
Weber W.J 1972 Physicochemical processes for water quality control Wiley-Interscience New York NY