Effects of Dried Days on Properties of Seawater and Freshwater Flooded CSPE in NPPs
Effects of Dried Days on Properties of Seawater and Freshwater Flooded CSPE in NPPs
Journal of Electrical Engineering and Technology. 2015. May, 10(3): 1162-1168
Copyright © 2015, The Korean Institute of Electrical Engineers
This is an Open-Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/)which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
  • Received : November 05, 2014
  • Accepted : January 08, 2015
  • Published : May 01, 2015
Download
PDF
e-PUB
PubReader
PPT
Export by style
Article
Author
Metrics
Cited by
TagCloud
About the Authors
Hwang-Hyun Jeon
Dept. of Electrical Engineering, Wonkwang University, Korea. (sepico1001@hanmail.net)
Jeong-U Lee
Dept. of Electrical Engineering, Wonkwang University, Korea. (sepico1001@hanmail.net)
Jun-Soo Jeon
Dept. of Electrical Engineering, Wonkwang University, Korea. (sepico1001@hanmail.net)
Seung-Hoon Lee
Dept. of Electrical Engineering, Wonkwang University, Korea. (sepico1001@hanmail.net)
Yong-Deok Shin
Corresponding Author: Dept. of Electrical Engineering, Wonkwang University, Korea. (ydshin@wku.ac.kr)

Abstract
Accelerated thermal aging of chlorosulfonated polyethylene (CSPE) was performed for 0 days, 80.82 days, and 161.63 days at 100℃, which is equivalent to 0 y, 40 y, and 80 y of aging, respectively, at 50℃. After freshwater flooding, the volume electrical resistivity of CSPE was highest after 180 days of drying, and its insulating property recovered when dried for more than 300 days. The dielectric constant of the CSPE was not measured after seawater flooding. The dielectric constant of the accelerated thermally aged CSPE was higher after freshwater flooding than that before seawater flooding. The bright, open pores of CSPE were converted into dark, closed pores after seawater flooding, and the dark, closed pores of the accelerated thermally aged CSPE samples were partly converted into bright, open pores after freshwater flooding. The apparent density of CSPE increased slightly whereas its elongation at break (EAB) decreased until 80 y of accelerated thermal aging before seawater flooding. The peak binding energies of oxygen in the non-accelerated and accelerated thermally aged CSPE for 40 y and 80 y were shifted by more than 1.0 eV after seawater and freshwater flooding. The CH2 content in the non-accelerated and accelerated thermally aged CSPE for 40 y and 80 y after seawater flooding for 5 days was lower than that before seawater flooding whereas atoms such as Cl, O, Pb, Al, Si, Sb, and S that are related to conducting ions such as Na + , Cl - , Mg 2+ , SO4 2- , and K + were relatively increased.
Keywords
1. Introduction
Countries with advanced atomic energy have been investigating methods for evaluating the aging of cables in nuclear power plants (NPPs) and investing on continued research efforts to explore new approaches [1 , 2] .
Cables used in NPPs must be designed to last through the plant life owing to the high cost of cable replacement and the complexity of the process. However, cables installed in certain areas such as containment buildings may degrade faster than the normal aging rate, thus affecting cable quality [3 , 4] .
An optimum degradation evaluation tool that can accurately determine the degree of deterioration of the insulation material or jacket of a cable and recommend an appropriate replacement time has been proposed and improved [5 - 7] . This method predicts the exact residual life of a cable via suitable condition monitoring.
The jacket of a cable installed in certain areas such as a containment building is exposed to poor surroundings including radioactive rays, steam, temperature, pressure, moisture, and chemical materials and may be submerged [8] .
Chlorosulfonated polyethylene (CSPE) is obtained via simultaneous chlorination and chlorosulfonation of polyethylene. It is a polymer comprising a modified polyethylene backbone with chloro- and sulfonyl chloride side groups. Crosslinking can be achieved by using different curing methods (e.g., sulfur, peroxides, and maleimide) to produce commercial generic Hypalon rubber [4 , 9] .
Chlorosulfonated polyethylene is an important and widely used rubber and is typically used as a sheathing material for electrical cables employed in nuclear power facilities. It is also used in auto supplies, life-saving equipment, and building materials [10 , 11] . In this study, the degree of deterioration of non-accelerated and accelerated thermally aged CSPE samples with number of dried days after seawater and freshwater flooding was determined. The electrical, physical, and chemical properties of nonaccelerated and accelerated thermally aged CSPE samples were evaluated through volume electrical resistivity, dielectric constant, apparent density, elongation at break (EAB), X-ray photoelectron spectroscopy (XPS), and Xray fluorescence (XRF) analyses.
2. Experimental Procedure
- 2.1. Sample preparation
A flat-type CSPE of 1-mm thickness (Taihan Electric Wire Co., Ltd.) was used as standard CSPE. To obtain soaked CSPE, the flat-type CSPE was soaked in seawater for 5 days and then dried for 5 days at room temperature. Further, to obtain cleaned CSPE, the soaked CSPE was cleaned for 5 days with freshwater and dried for 480 days at room temperature. Accelerated thermal aging of a CSPE was performed for 0 days, 80.82 days, and 161.63 days at 100℃, which is equivalent to 0 y, 40 y, and 80 y of aging, respectively, at 50℃, and these samples are referred to as CSPE-0y, CSPE-40y, and CSPE-80y, respectively, henceforth.
- 2.2. Measurement of volume electrical resistivity
The resistance of a CSPE cable varies with different parameters, such as the shape and size of the insulating material. However, the volume electrical resistivity is not affected by these parameters. The volume electrical resistivity of CSPE is measured using the three-terminal guard-ring electrode (patent number 10-1328994) proposed in [12] . The three-terminal guard-ring electrode is designed as in [13 - 15] and consists of two parallel-plate electrodes to apply 500 VDC to the CSPE and an additional guardring electrode to absorb the leakage current.
- 2.3. Measurement of dielectric constant
In order to compensate for the dielectric constant of CSPE, the electric capacity of the electrometer was measured as
PPT Slide
Lager Image
  • Cext: electric capacity of a known condenser or CSPE [F]
  • CE: electric capacity of electrometer [F]
  • V: applied voltage [V]
  • VE: charging voltage of CSPE [V]
As shown in [13 - 15] , if the contactor is switched on, electric voltage is applied to the CSPE. Contrarily, if the contactor is switched off, the charging voltage of CSPE can be measured with the electrometer.
- 2.4. Physical measurement
Microstructural analysis of CSPE was performed using a field-emission scanning electron microscope (FE-SEM, Hitachi & Horiba/S4800& EDS, Japan). The apparent density of CSPE was measured five times using the Archimedes’ method. The EAB of CSPE was measured three times according to the American Society for Testing and Materials (ASTM) standard D412.
- 2.5. Chemical measurement
Chemical variation in the deteriorated CSPE with respect to the number of drying days was analyzed using a wavelength dispersive X-ray fluorescence spectrometer (WD-XRF, S4 Pioneer, Bruker, Germany) and an X-ray photoelectron spectrometer (XPS, K-Alpha, Thermo Scientific, UK).
3. Experimental Results and Discussion
- 3.1. Volume electrical resistivity
As shown in Fig. 1 , the highest volume electrical resistivities of CSPE-0y, CSPE-40y, and CSPE-80y are 7.630×10 14 Ω·cm, 4.972×10 14 Ω·cm, and 7.253×10 14 Ω·cm when dried for 180 days at room temperature. The lowest volume electrical resistivities of the CSPE-0y, CSPE-40y, and CSPE-80y samples are 2.144×10 13 Ω·cm, 1.570×10 13 Ω·cm, and 1.924×10 13 Ω·cm, respectively, when dried for 300 days at room temperature. The volume electrical resistivities of the accelerated thermally aged CSPE samples are lower than those of the non-accelerated thermally aged CSPE samples, thus indicating that the ionic (electron or hole) conduction current increases when the branch chain of the CSPE polymer separates from the main chain of polyethylene owing to the thermal stress of accelerated thermal aging [5] . The insulating property of the CSPE soaked in seawater owing to tsunami was recovered between 330 and 480 dried days, and the insulating property of the non-accelerated thermally aged CSPE sample recovered faster than those of the accelerated thermally aged CSPE samples.
PPT Slide
Lager Image
Variation in volume electrical resistivity of CSPE with number of dried days after seawater and freshwater flooding for 5 days
- 3.2. Dielectric constant
As shown in Fig. 2 , the permittivities of the CSPE-0y, CSPE-40y, and CSPE-80y samples dried for 120 days at room temperature are 4.422, 4.032, and 4.209, respectively, which are the highest values. The dielectric constant of non-soaked CSPE is 2.856 at room temperature [15] . However, the dielectric constant of the seawater soaked CSPE is not measured. The dielectric constant of CSPE-0y was 4.03 when dried for 1 day, which is higher than that of the non-soaked CSPE sample [13 - 14] . The ionic polarization of CSPE-0y is caused by Na + , Cl - , Mg 2+ , SO 4 2- , Ca 2+ , and K + ions because of the salinity of seawater. At room temperature, the dielectric constants of CSPE-0y, CSPE-40y, and CSPE-80y are in the ranges of 4.422–2.786, 4.032-2.722, and 4.209-3.016, respectively. The dielectric constants of CSPE-0y, CSPE-40y, and CSPE-80y decrease slightly as the number of dried days at room temperature, as shown in Fig. 2 . Therefore, the number of Na + , Cl - , Mg 2+ , SO 4 2- , Ca 2+ , and K + ions in CSPE-0y, CSPE-40y, and CSPE-80y decrease as the number of dried days increase owing to the salinity of the seawater.
PPT Slide
Lager Image
Variation in dielectric constant of CSPE with number of dried days after seawater and freshwater flooding for 5 days.
- 3.3. Physical properties
The bright, open pores of the CSPE-0y sample convert to dark, closed pores after seawater flooding because of salinity, namely, owing to the presence of NaCl, MgCl 2 , NaSO 4 , CaCl, and KCl. The dark, closed pores of the soaked CSPE samples partly convert into bright, open pores after freshwater flooding because the salinity of the seawater decreases. As the number of bright, open pores in CSPE increases, the volume electrical resistivity increases, and as the number of dark, closed pores increases, the volume electrical resistivity of CSPE decreases, as was seen in the FE-SEM images [14 - 15] .
Fig. 3 shows the apparent densities of CSPE-0y, CSPE-40y, and CSPE-80y before seawater flooding. As can be seen, the apparent density increases slightly with accelerated thermal aging up to 80 y because of the effect of the degree of thermosetting.
PPT Slide
Lager Image
Variation in apparent density of CSPE with accelerated thermal aging.
Fig. 4 shows the EAB values of the CSPE-0y, CSPE-40y, and CSPE-80y samples before seawater flooding. We can see that the EAB value decreases until 80 y of accelerated thermal aging because of dependence on the degree of thermosetting. Thermosetting polymers harden permanently when heat is applied to CSPE and do not soften upon subsequent heating.
PPT Slide
Lager Image
Variation in EAB of CSPE with accelerated thermal aging.
- 3.4. Chemical properties
Fig. 5 shows that the peak binding energies of oxygen and sulfur in CSPE-0y shift from 532.08 eV to 530.08 eV and 163.08 eV to 164.08 eV, respectively; therefore, their peak binding energies are shifted by more than 1.0 eV.
PPT Slide
Lager Image
Binding energy of CSPE-0y
As shown in Fig. 6 , the peak binding energy of sulfur in CSPE-40y shifts from 164.08 eV to 167.08 eV.
PPT Slide
Lager Image
Binding energy of CSPE-40y.
Fig. 7 shows that the peak binding energies of oxygen, carbon, chlorine, and sulfur in CSPE-80y shift from 533.08 eV, 285.08 eV, 200.08 eV, and 165.08 eV to 531.08 eV, 284.08 eV, 199.08 eV, and 164.08 eV, respectively, with a shift of over 1.0 eV.
PPT Slide
Lager Image
Binding energy of CSPE-80y.
The binding mechanism of oxygen, carbon, chlorine, and sulfur is altered in the CSPE samples because their reactions are altered owing to salinity.
Figs. 8 and Fig. 9 show XRF analysis data of CSPE-0y, CSPE-40y, and CSPE-80y samples before and after seawater flooding.
As shown in Figs. 8 and Fig. 9 , the CH 2 component is reduced in the accelerated thermally aged CSPE samples after seawater flooding for 5 days whereas atoms such as Na, Cl, Mg, O, Pb, Al, Ca, K, Si, Sb, and S, which are related to conducting ions such as Na + , Cl + , Mg 2+ , SO 4 2+ , Ca 2+ , and K + , are relatively increased. The antioxidant additives of CSPE are PbO, Sb 2 O 3 , Al(OH) 3 , Mg(OH) 2 , and Ca(OH) 2 . Therefore, from XRF analysis, the antioxidant atoms of CSPE are plumbum, antimony, aluminum, and magnesium.
PPT Slide
Lager Image
Percentage of different atoms in CSPE before seawater flooding.
PPT Slide
Lager Image
Percentage of different atoms in CSPE after seawater flooding.
4. Conclusions
The physical, chemical, and electrical properties of accelerated thermally aged CSPE samples were analyzed to determine the degree of deterioration, and the following conclusions can be drawn.
1. The volume electrical resistivity of accelerated thermally aged CSPE is lower than that of non-accelerated thermally aged CSPE, and the insulating property of non-accelerated thermally aged CSPE recovers faster than that of accelerated thermally aged CSPE.
2. The dielectric constant of CSPE decreases slightly as the number of dried days at room temperature increases. Therefore, dielectric constant cannot be used to determine the degree of deterioration of accelerated thermally aged CSPE.
3. The apparent density of CSPE increases whereas the EAB value decreases with increasing number of thermal aging years because of the effect of degree of thermosetting.
4. The peak binding energies of oxygen, carbon, chlorine, and sulfur in CSPE-80y are shifted by more than 1.0 eV.
5. The XRF analysis shows that the antioxidant atoms of CSPE are plumbum, antimony, aluminum, and magnesium.
The insulation property of cables in NPPs is decreased because of seawater flooding, and the insulation property can be recovered through freshwater flooding. The volume electrical resistivity, peak binding energy, and microstructural analyses of CSPE suggest evaluating the possibility of the aging state of accelerated thermally aged CSPE based on the EAB and apparent density. Volume electrical resistivity, peak binding energy, atom analysis, EAB, and apparent density can be used as evaluation tools to determine the degree of deterioration of insulation material or jacket of a cable and find the appropriate replacement time.
Acknowledgements
This paper was supported by Wonkwang University in 2015.
BIO
Hwang-hyun Jeon He was born in Korea in 1958. He received his B.S. degree in electrical engineering from Wonkwang University, Iksan, Korea, in 1984, He worked at Saehan media Co., Ltd from 1984 to 1987. He worked at Semikron Co., Ltd from 1987 to 1991. He received his M.S degree from Joongang University, Seoul, Korea, in 2000. He is currently a Ph.D course in electrical engineering at Wonkwang University, Iksan, Korea. in 2013.
Jeong-U Lee He was born in Korea in 1989. He received B.S. degree in Electrical Engineering from Wonkwang University, Iksan, Korea, in 2014. Presently, he is pursuing a M.S. degree at Wonkwang University.
Jun-Soo Jeon He was born in Korea in 1986. He received B.S. degree in Electrical Engineering from Wonkwang University, Iksan, Korea, in 2012. Presently, he is pursuing a M.S. degree at Wonkwang University.
Seung-Hoon Lee He was born in Korea in 1988. He received B.S. degree in Electrical Engineering from Wonkwang University, Iksan, Korea, in 2013. Presently, he is pursuing a M.S. degree at Wonkwang University.
Yong-Deok Shin He was born in Korea in 1953. He received his B.S. degree in Electrical Engineering from Wonkwang University, Iksan, Korea, in 1983, where he worked as a research assistant and part-time lecturer from 1983 to 1988. He worked at the Center Research Institute of Keyang Electric Machinery Co., Ltd/ from 1988 to 1990. He received his ph. D. degree from Sungkyunkwan University, Seoul, Korea, in 1991. He was a visiting Professor at Pennsylvania State University, Pennsylvania, USA, in 1998 and 2005. Currently, he is a professor of the Department of Electrical Engineering at Wonkwang University, Iksan, Korea and a fellow member of the Korean Institute of Electrical Engineers (KIEE).
References
2012 U.S. Nuclear Regulatory Commission / Regulatory Guide 1.218, “Condition monitoring techniques for electric cables used in nuclear power plants,” Office of Nuclear Regulatory Research
Kim K. Y. , Lee C. , Kim J. H. , Seo J. M. 2003 “Accelerated Ageing Test of Cable Materials used in Nuclear Power Plants for the Evaluation of Lifetime,” Final Rep. KAERI
Kim I.-Y. , Goo C.-S. , Lee J.-H. , Shin Y.-D. 2011 “Condition monitoring of cable used in nuclear power plant through volume electrical resistivity,” A178, ICEE
Kim I.-Y. , Goo C.-S. , Lee J.-H. , Jin B.-S. , Kang M.-K. , Shin Y.-D. 2012 “A study of validation of condition monitoring method of NPPs cable through volume electrical resistivity,” ICHVE 76 - 79
1999 “Development of evaluation technique on aging degradation of organic polymer in nuclear power plant,” Final Rep.
Lee J.-H. , Kang M.-K. , Jeon J.-S. , Lee S.-H. , Kim I.-Y. , Park H.-S. , Shin Y.-D. 2014 “A study on the properties of CSPE according to accelerated thermal aging years,” J. Electr. Eng. Technol. 9 (2) 643 - 648    DOI : 10.5370/JEET.2014.9.2.643
Lee C.-H. 2011 “Characteristic and evaluation of polymeric insulating materials II,” Journal of the Electrical World/Monthly Magazine 42 - 52
Goo C. -S. , Ahn S. -P. 2001 “Condition monitoring of the safety related cable in nuclear power plant,” KIEE summer conference 1381 - 1383
Gu Z. , Song G. , Liu W. , Gao J. , Dou W. , Lu P. 2010 “Preparation and properties of chlorosulfonated polyethylene/organomontmorillonite nanocomposites,” J. Appl. Polym. Sci.
Chung S.-K. , Lee D.-C. 1996 “High voltage engineering,” Munundang
Gillen K. T. , Assink R. , Bernstein R. , Celina M. 2006 “Condition monitoring methods applied to degradation of chlorosulfonated polyethylene cable jacketing materials,” Polym. Degrad. Stabil.
Goo C.-S. , Kim I.-Y. , Choi Y.-H. , Shin Y.-D. , Lee J.-H. 2013 Patent number 10-1328994 Korea Institute of Nuclear Safety
Kang M.-K. , Lee J.-H. , Lee S.-H. , Jeon J.-S. , Park Y. , Park K.-Y. , Jeong K.-W. , Shin Y.-D. 2013 “Effects of freshwater flooding on the properties of CSPE with number of dried-days,” J. KIEEME 26 (83) 597 - 601
Kang M.-K. , Lee J.-H. , Lee S.-H. , Jeon J.-S. , Kim I.-Y. , Shin Y.-D. 2014 “Effects of freshwater flooding on the properties of the accelerated thermally aged CSPE,” Trans. KIEE 63 (3) 367 - 370
Kim I.-Y. , Goo C.-S. , Lee J.-H. , Jin B.-S. , Kang M.-K. , Shin Y.-D. 2013 “Effects of seawater flooding on the properties of CSPE,” Proc. ICAPP