Experimental Investigation on Dielectric and Thermal Characteristics of Nanosized Alumina Filler Added Polyimide Enamel
Experimental Investigation on Dielectric and Thermal Characteristics of Nanosized Alumina Filler Added Polyimide Enamel
Journal of Electrical Engineering and Technology. 2014. May, 9(3): 978-983
Copyright © 2014, The Korean Institute of Electrical Engineers
  • Received : August 14, 2013
  • Accepted : December 28, 2013
  • Published : May 01, 2014
Download
PDF
e-PUB
PubReader
PPT
Export by style
Article
Author
Metrics
Cited by
TagCloud
About the Authors
C. Pugazhendhi Sugumaran
Corresponding Author: Division of High voltage Engineering Anna University, Chennai India. (cpsugumar@gmail.com)

Abstract
The polymer nano composite possess good priority recently for engineering applications. Especially the electrical insulating materials attract the high performance of nano composites. In this work the ballmill synthesiation process of nano sized Alumina (Al 2 O 3 ), the preparation of new nano composite material with an content of enamel and synthesized Alumina as 1wt%, 3wt% and 5wt%. Experimental investigation has been carried out for the prepared nano composites materials with respect to dielectric parameter measurements such as dielectric loss (tan δ), dielectric constant (ε), dielectric strength under various temperature. The partial discharge level also measured for all the samples and the PD inception voltage is also observed and compared. Weight loss of the material has been analyzed through TGA. It has been experimentally proved that 3wt% of Alumina nano filler added enamel has significant improvement in the dielectric and thermal properties.
Keywords
1. Introduction
The electrical equipments from small power rating to hundreds of MW, consists different types of insulating and dielectric materials. The proper selection of insulating material depends upon various parameters such as dielectric strength, permittivity, arc resistance, thermal conductivity, thermal coefficient of expansion, chemical resistance against corrosion. Recently, the development of nano composite has more attraction towards electrical insulation. Polymer nanocomposites with small quantities of well dispersed nanoparticles offer advantage compare with conventional composites [1] . It is a cumbersome task to optimize the size and wt% of fillers [2] . Currently more research is going on the effectiveness of nanofillers. It has been already proved by many researchers that when the sizes of nano fillers are very less, the interaction zones are so large that they start to interact at very low level of loadings [3] . The interactions between polymer matrix and nanoparticles alter polymer chemistry, i. e. chain mobility, degree of cure and generate new trap centers in the composite which brings about the significant changes in electrical properties [4] .
The insulating polymers have attracted wide interest as a method of enhancing, polymer properties and extending their utility [5 - 6] . The constituents of polymer composite are immiscible in turn produces a coarsely blended macro composite. This results in poor physical interaction between the organic and inorganic components [7] . The purpose of this work is to develop Alumina based new nanocomposite, that would be both resistant to electrical stress and exhibit a better thermal conductance, appropriate for copper wire coating which is used in electrical equipments.
In polymer nanocomposites, the interfacial region between nanoparticles and the matrix is high volume fraction because of the high surface to volume ration of the fillers. The previous studies aimed at providing an understanding of the charge storage and transport of an enamel containing ZrO 2 nanoparticles [1] . It has been shown that nanometric fillers mitigate the interfacial polarization characteristic of enamel with a reduction in the internal field accumulation. The effectiveness of 1wt%, 3wt% and 5wt% of ZrO 2 fillers addition with enamel are compared and proved that 1wt% of sample had better dielectric and thermal performance when compare to other samples [1] . Further in this investigation the dielectric and thermal properties has been obtained for the same base resin containing nano-fillers of Alumina.
2. Experimental Analysis
- 2.1 Sample preparation
The Alumina (Sigma Aldrich) is subjected to Scanning Electron Microscopy (SEM) for surface and structural property analysis as shown in Fig. 1 , which ensures micro metric size. The nano sized Alumina has been synthesized using Ball Milling Machine (‘Attritor’) at a room temperature about 300C with 20 balls and the machine is operated for 42 hours at 300 rpm. The synthesized alumina has been characterized with the help of SEM as shown in Fig. 2 . Then filtered nano filler Alumina with an average size of 50-80 nm is mixed with enamel in the concentration of 1wt%, 3wt% and 5wt% using conventional mechanical stirring for 90minutes at 30℃ and further mixing in an ultrasonic processor (Model: TPC 40) at 20 kHz. They were cast in moulds and fully cured. Three types of nanocomposite samples are prepared with the concentration of 1wt%, 3wt%, 5wt% of alumina respectively [1] . The samples are prepared in the size of 10 mm× 10 mm× 3 mm as per the methodology shown in Figs. 3 and 4 .
PPT Slide
Lager Image
SEM analysis of micro sized alumina
PPT Slide
Lager Image
SEM analysis of nano sized alumina
PPT Slide
Lager Image
Sample preparation scheme for base enamel
PPT Slide
Lager Image
Sample preparation scheme for nano alumina added enamel based nano composite
- 2.2 Measurement of dielectric strength
A standardized testing arrangement is used for the determination of the AC breakdown field strength of prepared samples as per IEC 60243 ˗ 1 [8] .
The breakdown test is conducted with an alternating voltage, which is increased from zero to the breakdown value within 10-20 second. The median value of the breakdown voltage is determined from five samples, if any value is more than 15% of the median value, 5 additional samples must be tested and the median value is then determined from the 10 samples. The breakdown field strength can be evaluated from the breakdown voltage and the smallest electrode spacing. The breakdown test is conducted as per test procedure [1] . In order to prevent the gliding discharges along the surface and edges of the insulating plate, the entire arrangement is embedded in an insulating liquid with an appropriate dielectric constant and higher dielectric strength [1] .
The dielectric strength of the nanocomposite at 1 wt%, 3 wt% and 5wt% of Alumina nano filler added enamel and enamel without nano filler are measured. The results are presented in Table 1 . It seems that there is a tendency of a change in AC breakdown strength with change in concentration of nano fillers. It can be ascertained from the table that the dielectric strength of 3wt% of Alumina added enamel is increased by 35% compared to base enamel. Further it is noticed that the lesser concentration of nano filler 1 wt% has 21% increases in dielectric strength. Higher concentration of nano filler 5wt% has 19% increase in the dielectric strength. However further increase in the wt% increases interfacial polarization which tends to reduce the dielectric strength. The physical bonding between nanoparticles and the polymer chain could be responsible for the increase in breakdown strength at 3wt %.
AC break down strength
PPT Slide
Lager Image
AC break down strength
- 2.3 Determination of dielectric parameters
Dielectric spectroscopy (Model : LCR HITESTER 3532-50) also known as Electrochemical Impedance Spectroscopy, is used here for the measurement of various parameters such as tan δ, Parallel capacitance (Cp), Series capacitance (Cs), Parallel resistance (Rp), Series resistance (Rs) as a function of frequency at 90℃, 120℃ and 180℃ temperature. This measurement is based on the interaction of an external field with the electric dipole moment of the sample.
The test is being carried out for frequency ranging between 50Hz to 5MHz at three different temperatures i.e., 90℃, 120℃ and 180℃, since the new nanocomposite is intended for coating of enamel wire which is used in an inverter fed motors, having very high switching frequency. From the parameters CP RP and dielectric constant (ε) could be determined using the following equations.
PPT Slide
Lager Image
PPT Slide
Lager Image
PPT Slide
Lager Image
The time required for electronic and ionic polarization to set in is very short as compared to time for the voltage sign change even for the highest frequencies which find practical use in electrical and radio engineering [6] . When the frequency of alternating voltage increases, the value of ε remains invariable but beginning with a certain critical frequency when polarization fails to settle, ε begins to drop to lower value at very high frequencies [9] .
Figs. 5(a) - (c) shows the permittivity of nanocomposite against frequency. It is observed that, the minimum permittivity is recorded for 3wt% Alumina added enamel independent of temperature. This is due to the fact that, addition of 3wt% Alumina nanofiller causes the electronic polarization, ionic polarization and the numbers of free dipoles present in the enamel to orient themselves. Hence the permittivity decreases, however, further increase in the wt% of Alumina nanofiller enhances the ionic displacement, intensifying the internal field and thereby reducing the electronic, orientation polarization. Thus resulting in higher permittivity [10 - 12] .
PPT Slide
Lager Image
Permittivity (ε) Vs frequency at 90℃ for pure enamel and 1, 3 and 5wt% of Alumina nano filler added enamel.
PPT Slide
Lager Image
Permittivity (ε) Vs frequency at 120℃ for enamel and 1, 3 and 5wt% of Alumina nano filler added enamel.
PPT Slide
Lager Image
Permittivity (ε) Vs frequency at 180℃ for pure enamel and 1, 3 and 5wt% of Alumina nano filler added enamel.
Figs. 6(a) - (c) shows the dielectric loss of the prepared nanocomposite samples with respect to frequency at various temperature of 90°, 120° and 180℃. It is observed that, the 3 wt% Alumina added enamel has lower dielectric loss with respect to frequency. The concentration of nano fillers doesn’t have a significant influence over the dielectric loss above 40 kHz at 90℃. Further increase in the temperature shows that dielectric loss is independent of frequency above 5 kHz and below 500 Hz. The 3 wt%, 1 wt % Alumina added enamel has lower dielectric loss in compared to 5 wt% and pure enamel.
PPT Slide
Lager Image
tan δ versus frequency at 90℃ for pure enamel, 1wt%, 3wt% and 5wt% of Alumina nano filler added enamel.
PPT Slide
Lager Image
tan δ versus frequency at 120℃ for pure enamel, 1wt%, 3wt% and 5wt% of Alumina nano filler added enamel.
PPT Slide
Lager Image
tan δ versus frequency at 180℃ for a enamel, 1wt%, 3wt% and 5wt% of Alumina nano filler added enamel.
Figs. 7(a) - (c) show the influence of percentage of addition of alumina nano filler at different temperature such as 90℃, 120℃, and 180℃ on dielectric loss. In this study, an increase in the values of tan δ is obtained with addition of inorganic filler as a source of charge carriers [1] . In a polymeric system reduction of electrical conductivity can be created by the charge transport mechanism through various links and interaction zones [13] . It is observed from Figs. 7(a) - 7(c) , that 3 wt% Alumina added enamel has lower dielectric loss. Further it is noticed that, the temperature doesn’t have significant influence on tan δ for 3wt% Alumina added enamel, irrespective of frequencies. The rate of rise of dielectric loss is more above 120℃ except for 3 wt% Alumina added enamel.
PPT Slide
Lager Image
tan δ versus temperature at 50 Hz for a pure, 1, 3 and 5wt% of Alumina added enamel.
PPT Slide
Lager Image
tan δ versus temperature at 1kHz for a pure, 1, 3 and 5wt% of Alumina added enamel.
PPT Slide
Lager Image
tan δ versus temperature at 1MHz for a pure, 1, 3 and 5wt% of Alumina added enamel.
- 2.4 Partial discharge measurement
In this current work, PD characteristics in Alumina filler based nanocomposites and enamel are investigated as per the test procedure specified in IEC 60270, 2003. PD detector system (Model: Mess Wandler-Bau) is used in this experiment. The background noise of the shielded room is maintained at 1.0 pC. The measured data is recorded by a digital oscilloscope (Model: Agilent 54621A). The value of inception, extinction voltages are measured for all the samples using uniform field electrode configuration and tabulated in Table 2 .
Partial discharge inception and extinction voltage
PPT Slide
Lager Image
Partial discharge inception and extinction voltage
Normally PD will concentrate on the surface of nano fillers in a nanocomposite sample due to the difference in permittivity, but the nano fillers are more resistant to PD [14 - 16] . Also it is observed from the experiment that more concentration will increase interfacing zones, thereby reducing PD resistance.
- 2.5 Surface resistance measurement
Practical insulation systems frequently comprise many dielectrics which are stressed in parallel. Thus, for example, the insulation resistance of a support insulator consists of the combination in parallel of surface resistance and volume resistance. While the volume resistance, commonly expressed as specific resistance (ΡS) in Ω cm, is often independent of surrounding medium, the surface resistance is appreciably influenced by ambient conditions such as pressure, temperature, humidity, dust etc [11] .
The live electrode, which also supports the plate-type sample, is arranged opposite a measuring electrode. The volume resistance is calculated from the direct voltage applied (100V or 1000V) and the current taken by the measuring electrode [10] . A guard arranged concentrically around the measuring electrode with a 1 mm gap prevents erroneous measurements caused by surface currents.
Special testing arrangements are available for tube-shaped insulating material samples, for insulating compounds which can be melted and for liquid insulating materials. Common insulating materials exhibit a specific volume resistance of 1012 to 1013 Ω cm, whereas superior materials can reach resistance values up to 1017 Ω cm or even higher.
To measure the surface resistance metallic knife-edges are used, set up at a gap spacing of 1 cm over a length of 10 cm on the surface of the insulating material under test and direct voltage is applied. From the voltage and current, the surface resistance (RS), expressed in ohms, is determined. From Table 3 , it is observed that the surface and volume resistances are increased by 1%.
Surface and volume resistance
PPT Slide
Lager Image
Surface and volume resistance
- 2.5 Thermo Gravimetric Analysis (TGA)
Thermo Gravimetry (TG) is a simple material characterization technique, where the mass of a sample in a controlled atmosphere is recorded continuously as a function of temperature or time, as the temperature of the sample is increased (usually linearly with time). In this research, the Perkin Elmer STA 6000 Instrument is used for TGA and all the samples are taken for investigation with equal weight of 8mg each. The measurements are taken in an air atmosphere and the temperature is raised at a rate of 20℃/min from 38℃ up to 800℃. It maintained consistent heating rate and gas flow. The weight loss as a function of temperature was recorded with a sensitivity of 0.2mg and 1.5%accuracy. This instrument measures sampling purity, reaction rate, identification, activation energy and heat of reactions [1] .
Fig. 8 shows that the percentage weight losses due to desorption of moisture or decomposition of enamel. It can be ascertained from the thermogram, the percentage weight loss does not show any significant changes with addition of nanofillers. Till 400°C the thermal stability of 5 wt% Alumina added enamel is high when compared to other samples. Further it is noticed from the DSC that, the Glass Transition Temperature (TG) value of 3wt% nano composite is increased by 6% compared to pure enamel.
PPT Slide
Lager Image
TGA comparison for enamel, 1wt%, 3wt% and 5wt% Alumina filler added enamel
3. Conclusion
This paper exhibits that the addition of Alumina nano-filler with enamel is very effective, in improving the dielectric and thermal characteristics. A fine nano sized alumina is synthesized and dispersed uniformly with enamel. The nano fillers has more interface zone, in which the movement of charge is controlled by interfacial polarization, through that the dielectric and thermal properties of nano composite gains a significant improvement. The following observations have been made
  • In a continues AC voltage rising test 3wt% samplehad 35%higher insulation breakdown strength than other samples. Increasing the concentration of nano filler reduce the strength by the interfacial polarization effect.
  • The dielectric loss of 3 wt% sample is lower compared to other samples. Further increase in concentration increases the dielectric loss.
  • From the results of PD measurement it is observed that PD resistance was stronger for Nano composite than enamel. Especially the 3wt% nanocomposite offer higher PD resistance in compare with other nano composite. The increased concentration of nanofiller reduce the PD resistance.
BIO
C. Pugazhendhi Sugumaran obtained his B. E degree from Manonmanium Sundaranar University, India, received M. E and Ph. D from Anna University India. Also he obtained Post Graduate Diploma in Electrical Safety and Safety Management with Distinction from Annamali University, India. His fields of interest are Nano dielectric and finite element analysis on coupled electro - thermal field in an electrical appliance. He is a Member of IEEE and IET (UK. ), EWB and SEMC. 983
References
Sugumaran C. Pugazhendhi , Mohan M. R. , Udayakumar K. 2010 “Investigation of Dielectric and Thermal properties of Nano Filler (ZrO2) mixed Enamel“ IEEE Transactions on Dielectrics and Electrical Insulation 17 (6) 1682 - 1686    DOI : 10.1109/TDEI.2010.5658217
Nelson J. Keith , Fothergill John C. , Dissado L. A. , Peasgood W. 2002 “Towards an understanding of nanometric dielectrics“ IEEE Annual Report Conference on Electrical Insulation and Dielectric Phenomena (CEIDP) 295 - 298
Inuzuka K. , Inano H. , Hayakawa N. , Hirose T. , Hamaguchi M. , Okubo H. 2006 “Partial discharge characteristics of nanocomposite enameled wire for inverter fed motor“ IEEE Annual Report Conference on Electrical Insulation and Dielectric Phenomena (CEIDP) 594 - 597
Singha Santanu , Thomas M. Joy 2008 “Permittivity and tan delta characteristics of epoxy nanocomposites in the frequency range of 1MHz-1GHz“ IEEE Transactions on Dielectrics and Electrical Insulation 15 (1) 2 - 11    DOI : 10.1109/T-DEI.2008.4446731
Tanaka Toshikatsu , Kozako Masahiro , Fuse Norikazu , ohki Yoshimichi 2005 “Proposal of a multi-cored model for polymer nanocomposite dielectrics“ IEEE Transactions on Dielectrics and Electrical Insulation 12 (4) 669 - 681    DOI : 10.1109/TDEI.2005.1511092
Tareev B. 1979 “Physics of dielectric materials“ Second edition Mir Publishers Moscow
Tanaka Toshikatsu 2005 “Dielectric nanocomposites with Insulating Porperties“ IEEE Transactions on Dielectrics and Electrical Insulation 12 (5) 914 - 926    DOI : 10.1109/TDEI.2005.1522186
1998 IEC 60243-1 “Electrical strength of insulating materials- Test methods-Part I-Test at Power Frequencies
Haq Saeed Ul , Jayaram Shesha H. , Cherney Edward A. 2007 “Performance of Nanofillers in Medium Voltage Magnet Wire Insulation under High Frequency Applications“ IEEE Transactions on Dielectrics and Electrical Insulation 14 (2) 417 - 426    DOI : 10.1109/TDEI.2007.344622
Imai Takahiro , Komiya Gen , Murayama Kiyoko , Ozaki Tamon 2008 “Improving Epoxy-based Insulating Materials with Nano-fillers toward Practical Application“ IEEE Annual Report Conference on Electrical Insulation and Dielectric Phenomena (CEIDP) 201 - 204
Kind Dieter , Kamer Hermann 1985 “High voltage insulation technology“
Fothergill J. C. , KNelson J. , Fu M. 2004 “Dielectric properties of epoxy nano composites containing TiO2, Al2O3 and ZnO fillers“ IEEE Transactions on Dielectrics and Electrical Insulation 406 - 409
Kirkici Hulya , Serkan Mert , Koppisetty K. 2005 “Nanodielectric materials in electrical insulation application“ IEEE Annual Conference on Industrial Electronics Society (IECON) 2395 - 2398
Zhang C. , Mason R. , Stevens G. C 2005 ” Dielectric Properties of Alumina - Polymer Nanocomoposites“ IEEE Annual Conference on Electrical Insulation 721 - 724
Lewis T. J. 1994 “Nanometric Dielectrics“ IEEE Transactions on Dielectrics and Electrical Insulation 1 (5) 812 - 825    DOI : 10.1109/94.326653
Tanaka T. , Montanari G. C. , Mulhaupt R. 2004 “Polymer Nanocomposties as Dielectrics and Electrical Insulation-perspectives for Processing Technologies, Material Characterization and Future Applications“ IEEE Transactions on Dielectrics and Electrical Insulation 11 (5) 763 - 784    DOI : 10.1109/TDEI.2004.1349782